Paper dimensional stability in sheet-fed offset printing : Papperets dimensionsstabilitet i en arkoffsetpress

In offset printing, dampening solution is used to create a good balance in the process. If too much water is transferred to the paper, the sheet can change its size between the printing units, due to water absorption, and cause a problem with the colour register. This phenomenon is usually referred to as fanout. In this degree project, an investigation was made to see if the paper dimensions changed through its way in the sheet-fed printing process. The instrument Luchs Register Measuring Systems (Lynx) was used, and a method for measuring if the paper changed its dimensions with this instrument, was developed. Paper qualities with three different grammages were used, 90, 130 and 250 gsm. This investigation showed that all paper qualities changed their size with widening in the gripper edge in the range of 10 - 70 µm and in the trailing edge the increase was 10 - 130 µm. The elongations of the papers were in the range of 10- 300 µm. The papers with lowest grammage changed more than the heavier. To see if the print had been affected of the widening and elongation, print quality parameters like relative contrast, dot gain and mottle were correlated with the Lynx data from the sheets. The group of papers that gave correlations were in 130 gsm. The sheets had visual doubling and the combined standard deviation from the Lynx marks K3, K5 and K21 correlated with dot gain. When the variations increased so did the dot gain and this indicates that the doubling was due to the widening. There was also a correlation between the standard deviation from K3 and Mottle. The sheets widened with an average of 30 µm in the gripper edge and since there probably were doubling due to widening it also affected the Mottle values. What the widening depends on is hard to tell. Since widening was so small, it could be due to water absorption, papers being ironed out or maybe the sheets have been flattened out. It probably needs a more detailed investigation to find out what causes the widening. Further investigations about how print quality is affected by the register accuracy of a printing machine should include a print form with measuring areas close to the Lynx marks. The measuring areas should contain fine hairlines, negative text printed with at least two colours and some pictures to evaluate together with standard measuring should give a good knowledge about the subject.

Influence of Pigment and Opacifier on Dimensional Stability and Detail Reproduction of Maxillofacial Silicone Elastomer

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of opacifiers on dimensional stability and detail reproduction of maxillofacial silicone elastomer

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of microwave disinfection on the dimensional stability of intact and relined acrylic resin denture bases

Statement of problem. Microwave irradiation has been suggested as a method to disinfect denture bases. However, the effect of microwave heating on the dimensional stability of the relined denture bases is unknown.Purpose. The purpose of this study was to evaluate the dimensional stability of intact and relined acrylic resin denture bases after microwave disinfection.Material and methods. A standard brass cast simulating an edentulous maxillary arch was machined and used to fabricate 2- and 4-mm-thick denture bases (n=200), which were processed with heat-polymerized acrylic resin (Lucitone 550). The 2-mm thick-specimens (n=160) were relined with 2 mm of autopolymerizing resin (Tokuso Rebase Fast, Ufi Gel Hard, Kooliner, or New Truliner). Distances between 5 removable pins on the standard brass cast were measured with a Nikon optical comparator, and the area (mm(2)) formed by the distance between 5 pins was calculated and served as baseline. During fabrication, the pins were transferred to the intaglio surface of the specimens. Differences between the baseline area and those subsequently determined for the specimens were used to calculate the percent dimensional changes. The intact and relined denture bases were divided into 4 groups (n=10) and evaluated after: polymerization (control group P); 1 cycle of microwave disinfection (MW); daily microwave disinfection for 7 days (control group MW7); water storage for 7 days (WS7). Microwave irradiation was performed for 6 minutes at 650 W. Data were analyzed using 2-way ANOVA followed by Tukey's test (alpha=.05).Results. Intact specimens and those relined with Kooliner and New Truliner showed increased shrinkage after 1 (P=.05, .018, and .001, respectively) and 7 (P <.001, .003, and <.001, respectively) cycles of microwave disinfection. With the exception of specimens relined with Kooliner, intact specimens showed greater shrinkage than the relined specimens after 7 cycles of microwave disinfection.Conclusions. Microwave disinfection produced increased shrinkage of intact specimens and those relined with New Truliner and Kooliner.

Influence of Microwave Disinfection on the Dimensional Stability of Denture Reline Polymers

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Incorporation of Disinfectant Solutions on Setting Time, Linear Dimensional Stability, and Detail Reproduction in Dental Stone Casts

Purpose: The aim of this paper was to analyze the influence of incorporation of disinfectants during the cast die stone-setting time. Setting time, linear dimensional stability, and reproduction details on casts were measured.Materials and Methods: Die stone type IV specimens with disinfection solutions (sodium hypochlorite 1%, glutaraldehyde 2%, chlorhexidine 2%) were incorporated in two concentrations (50%, 100%). The detail reproduction, dimensional stability, and setting time were tested in accordance with ADA recommendations.Results: Disinfecting solutions promoted an increase in setting time compared to control; sodium hypochlorite was responsible for the highest setting time. The addition of undiluted sodium hypochlorite 1.0% led to contraction during setting, but the groups with 50% diluted sodium hypochlorite 1.0% and undiluted chlorhexidine 2.0% resulted in intermediate values compared to the other groups, thus matching the control. The others did not demonstrate any effect on expansion. For detail reproduction, it was observed that the control group presented results similar to the others, except those where sodium hypochlorite was added.Conclusions The addition of sodium hypochlorite in both dilutions significantly altered, negatively, all the evaluated properties. But the addition of glutaraldehyde and chlorhexidine did not promote any significant alterations in the evaluated properties.

Influence of Microwave Disinfection on the Linear Dimensional Stability of Complete Dentures: A Clinical Study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of disinfectant agents on dimensional stability of elastomeric impression materials.

STATEMENT OF PROBLEM: Difficulties in sterilizing impressions by traditional methods have led to chemical disinfection as an alternative, and some studies have shown that disinfectants may adversely affect impressions. PURPOSE: This study investigated the effect of disinfection methods on the dimensional stability of 6 elastomeric materials. MATERIAL AND METHODS: Impression materials were submitted to the following treatments: immersion in 5.25% sodium hypochlorite solution for 10 minutes, immersion in 2% glutaraldehyde solution for 30 minutes, and no immersion (control). After treatments, impressions were poured, and respective stone casts were measured with a Nikon Profile projector and compared with the master model. RESULTS: The elastomeric materials had different reproduction capacities, and the disinfecting treatments did not differ from the control.

Effect of disinfection and accelerated ageing on dimensional stability and detail reproduction of a facial silicone with nanoparticles

The aim of the present study was to evaluate the effect of disinfection and accelerated ageing on the dimensional stability and detail reproduction of a facial silicone with different types of nanoparticle. A total of 60 specimens were fabricated with Silastic MDX 4-4210 silicone and they were divided into three groups: colourless and pigmented with nanoparticles (make-up powder and ceramic powder). Half of the specimens of each group were disinfected with Efferdent tablets and half with neutral soap for 60 days. Afterwards, all specimens were subjected to accelerated ageing. Both dimensional stability and detail reproduction tests were performed after specimen fabrication (initial period), after chemical disinfection, and after accelerated ageing periods (252, 504 and 1008 hours). The dimensional stability test was conducted using AutoCAD software, while detail reproduction was analysed using a stereoscope magnifying glass. Dimensional stability values were statistically evaluated by analysis of variance (ANOVA) followed by Tukey's test (p < 0.01). Detail reproduction results were compared using a score. Chemical disinfection and also accelerated ageing affected the dimensional stability of the facial silicone with statistically significant results. The silicone's detail reproduction was not affected by these two factors regardless of nanoparticle type, disinfection and accelerated ageing. © 2012 Informa UK, Ltd.

Dimensional stability of an addition silicone after disinfection/sterilization

Poster presented at the “From Basic Sciences to Clinical Research” – First International Congress of CiiEM. Egas Moniz, Caparica, Portugal, 27-28 November 2015

Improvement of termite resistance, dimensional stability and mechanical properties of pine wood by paraffin impregnation

Paraffin has been used as surface protection of wood throughout the ages but its use for impregnation to improve wood resistance to biodegradation is recent. This study determined the main improvements on wood properties with paraffin impregnation. Healthy Pinus pinaster Ait. wood was impregnated with paraffin at different levels using a hot–cold process. Weight gain, equilibrium moisture content and dimensional stability (ASE) at 35 and 65 % relative humidity, termite durability against Reticulitermes grassei (Clément), bending strength, bending stiffness (MOE) and Janka hardness were determined. Density increased from 0.57 to 0.99, ASE ranged between 38–96 % and 16–71 % for 35 and 65 % relative humidity, respectively. Equilibrium moisture content decreased from 9.9 and 12.0 % to 0.8 and 3.6 % for 35 and 65 % relative humidity. Termite durability improved from level 4 to level 3 of attack, and higher termite mortality was found in treated wood (52 % against 17 %). Bending strength (MOR) increased with paraffin weight gain, reaching a 39 % increase. MOE also increased by about 13 % for wood with a weight gain around 80 %. Janka hardness increased significantly reaching about 40 % for wood with 80 % weight gain. Paraffin impregnated wood has improved properties with regard to equilibrium moisture content, dimensional stability and density, bending strength and Janka hardness, and resistance against termites.

Effect of residual stresses and metallographic stability on the over all performance of integral diaphragm material

The integral diaphragm pressure transducer consists of a diaphragm machined from precipitation hardened martensitic (APX4) steel. Its performance is quite significant as it depends upon various factors such as mechanical properties including induced residual stress levels, metallurgical and physical parameters due to different stages of processing involved. Hence, the measurement and analysis of residual stress becomes very important from the point of in-service assessment of a component. In the present work, the stress measurements have been done using the X-ray diffraction (XRD) technique, which is a non-destructive test (NDT). This method is more reliable and widely used compared to the other NDT techniques. The metallurgical aspects have been studied by adopting the conventional metallographic practices including examination of microstructure using light microscope. The dimensional measurements have been carried out using dimensional gauge. The results of the present investigation reveals that the diaphragm material after undergoing series of realization processes has yielded good amount of retained austenite in it. Also, the presence of higher compressive stresses induced in the transducer results in non-linearity, zero shift and dimensional instability. The problem of higher retained austenite content and higher compressive stress have been overcome by adopting a new realization process involving machining and cold and hot stabilization soak which has brought down the retained austenite content to about 5–6% and acceptable level of compressive stress in the range −100 to −150 MPa with fine tempered martensitic phase structure and good dimensional stability. The new realization process seems to be quite effective in terms of controlling retained austenite content, residual stress, metallurgical phase as well as dimensional stability and this may result in minimum zero shift of the diaphragm system.