Background: The method of porosity analysis by water absorption has been carried out by the storage of the specimens in pure water, but it does not exclude the potential plasticising effect of the water generating unreal values of porosity. Objective: The present study evaluated the reliability of this method of porosity analysis in polymethylmethacrylate denture base resins by the determination of the most satisfactory solution for storage (S), where the plasticising effect was excluded. Materials and methods: Two specimen shapes (rectangular and maxillary denture base) and two denture base resins, water bath-polymerised (Classico) and microwave-polymerised (Acron MC) were used. Saturated anhydrous calcium chloride solutions (25%, 50%, 75%) and distilled water were used for specimen storage. Sorption isotherms were used to determine S. Porosity factor (PF) and diffusion coefficient (D) were calculated within S and for the groups stored in distilled water. anova and Tukey tests were performed to identify significant differences in PF results and Kruskal-Wallis test and Dunn multiple comparison post hoc test, for D results (alpha = 0.05). Results: For Acron MC denture base shape, FP results were 0.24% (S 50%) and 1.37% (distilled water); for rectangular shape FP was 0.35% (S 75%) and 0.19% (distilled water). For Classico denture base shape, FP results were 0.54% (S 75%) and 1.21% (distilled water); for rectangular shape FP was 0.7% (S 50%) and 1.32% (distilled water). FP results were similar in S and distilled water only for Acron MC rectangular shape (p > 0.05). D results in distilled water were statistically higher than S for all groups. Conclusions: The results of the study suggest that an adequate solution for storing specimens must be used to measure porosity by water absorption, based on excluding the plasticising effect.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of thermocycling on the flexural and impact strength of urethane-based and high-impact denture base resins

Objective: Mechanical properties of the acrylic resins used for denture fabrication may be influenced by water and temperature. Thus, the aim of this study was to evaluate the effect of thermocycling on the flexural and impact strength of a high-impact (Lucitone 199) and a urethane-based denture material (Eclipse).Materials and methods: Flexural strength (64 x 10 x 3.3 mm) and impact strength (60 x 6 x 4 mm) specimens were made following the manufacturers' instructions and assigned to two groups (n = 10): control (C) - not thermocycled - and T - thermocycled (5000 cycles between 5 and 55 degrees C). Specimens were submitted to three-point bending and Charpy impact tests.Results: Flexural strength (MPa) and impact strength (kJ/m(2)) data were analysed with two-way ANOVA (p = 0.05). The flexural strength of material Eclipse (C, 136.5; T, 130.7) was significantly higher than that of resin Lucitone 550 (C, 99.4; T, 90.1). Material Eclipse exhibited significantly higher impact strength (C, 6.9; T, 5.3) than the resin Lucitone 550 (C, 3.5; T, 3.0). For both materials, a significant decrease in flexural and impact strengths was observed when the specimens were thermocycled.Conclusion: Flexural and impact strengths were higher for Eclipse than for Lucitone 550, in both groups. Thermocycling decreased the flexural and impact strengths of Eclipse and Lucitone 550.

Effect of water storage on the shear strength and fatigue limit of the reline resin bond to denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Reliability of a method for evaluating porosity in denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of microwave disinfection on the surface roughness of three denture base resins after tooth brushing

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cytotoxicity of denture base resins: Effect of water bath and microwave postpolymerization heat treatments

Purpose: This study compared the effect of two postpolymerization heat treatments on the cytotoxicity of three denture base resins on L929 cells using 3H-thymidine incorporation and MTT assays. Materials and Methods: Sample disks of Lucitone 550, QC 20, and Acron MC resins were fabricated under aseptic conditions and stored in distilled water at 37°C for 48 hours. Specimens were then divided into three groups: (1) heat treated in microwave oven for 3 minutes at 500 W; (2) heat treated in water bath at 55°C for 60 minutes; and (3) no heat treatment. Eluates were prepared by placing three disks into a sterile glass vial with 9 mL of Eagle's medium and incubating at 37°C for 24 hours. The cytotoxic effect from the eluates was evaluated using the 3H-thymidine incorporation and MTT assays, which reflect DNA synthesis levels and cell metabolism, respectively. Results: The components leached from the resins were cytotoxic to L929 cells when 3H- thymidine incorporation assay was employed. In contrast, eluates from all resins revealed noncytotoxic effects as measured by MTT assay. For both MTT assay and 3H-thymidine incorporation, the heat treatments did not decrease the cytotoxicity of the materials tested. Conclusion: Resins were graded by 3H-thymidine incorporation assay as slightly cytotoxic and by MTT assay as noncytotoxic. Cytotoxicity of the denture base materials was not influenced by microwave or water bath heat treatment.

Effect of a post-polymerization treatments on the flexural strength and vickers hardness of reline and acrylic denture base resins

This study evaluated the effect of water-bath and microwave post-polymerization treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II-D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard C-UGH) and one heat-polymerized acrylic resin (Lucitone 550-L), processed using two polymerization cycles (short cycle - 90 minutes at 73°C and 100°C for 30 minutes; and long cycle - 9 hours at 71°C). For each material, thirty specimens (64 x 10 x 3.3 mm) were made and divided into 3 groups (n=10). Specimens were tested after: processing (control group); water-bath at 55°C for 10 minutes (reline materials) or 60 minutes (L); and microwave irradiation. Flexural strength tests were performed at a crosshead speed of 5 mm/min using a three-point bending device with a span of 50 mm. The flexural strengths values were calculated in MPa. One fragment of each specimen was submitted to Vickers hardness test. Data were analyzed by 2-way ANOVA followed by Tukey's HSD test (α=0.05). L microwaved specimens (short cycle) exhibited significantly higher flexural strength means than its respective control group (p<0.05). Water-bath promoted a significant increase (p<0.05) in flexural strength of K and L (long cycle). The hardness of the tested materials was not influenced by the post-polymerization treatments. Post-polymerization treatments could be used to improve the flexural strength of some materials tested.

Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins

This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (mTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artifcial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm 2 were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4°C and 60°C). mTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (a=0.05). There was no statisti-caly signifcant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean mTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The mTBS of Biotone artifcial teeth to the denture base acrylic resins was not infuenced by the polymer type, surface treatment or thermocycling.

Metabolism of L929 cells after contact with acrylic resins. Part 1: Acrylic denture base resins

The purpose of this study was to evaluate the effectiveness of complementary heat treatment and water storage in reducing cytotoxicity of acrylic resins denture bases used in Brazil by the MTT assay. Material and Methods: First, nine specimens were fabricated from metal matrix in the form of discs with 14 mm in diameter and 1.2 mm of thick. Immediately after making, 24 or 48 hours after storage in distilled water, the samples of heat-polymerized resins were divided into 3 groups (n = 3) according to the type of thermal treatment: Group 1: samples were individually exposed to microwave energy (500 W for 3 minutes); Group 2: samples were immersed in water at 550 C for 60 minutes; Group 3: samples did not receive heat treatment. To prepare the extracts, 3 samples of each group were placed into vials containing 3 mL of culture medium and stored at 37°C for 24 hours. L929 cells were used and the MTT assay was performed to analyze the cellular metabolism. Two-factor analysis of variance was used to detect significant among groups at 5% significance. Results: After statistical analysis, the materials were classified according to the cytotoxic effect: non-cytotoxic, slightly cytotoxic; moderately cytotoxic; and strongly cytotoxic. The results showed that the resins ranged from moderately cytotoxic to non-cytotoxic, but no statistically significant difference among experimental groups. Furthermore, the water storage and thermal treatments reduced the cytotoxicity of the resins. Conclusions: It was concluded that the resins studied are potentially toxic and that treatments can decrease their cytotoxicity.

Evaluation of Vickers hardness of different types of acrylic denture base resins with and without glass fibre reinforcement

Objective: To evaluate the Vickers hardness of different acrylic resins for denture bases with and without the addition of glass fibres. Background: It has been suggested that different polymerisation methods, as well as the addition of glass fibre (FV) might improve the hardness of acrylic. Materials and methods: Five types of acrylic resin were tested: Vipi Wave (VW), microwave polymerisation; Vipi Flash (VF), auto-polymerisation; Lucitone (LT), QC20 (QC) and Vipi Cril (VC), conventional heat-polymerisation, all with or without glass fibre reinforcement (GFR) and distributed into 10 groups (n = 12). Specimens were then submitted to Vickers hardness testing with a 25-g load for 30 s. All data were submitted to ANOVA and Tukey's HSD test. Results: A significant statistical difference was observed with regard to the polymerisation method and the GFR (p < 0.05). Without the GFR, the acrylic resin VC presented the highest hardness values, and VF and LT presented the lowest. In the presence of GFR, VC resin still presented the highest Vickers hardness values, and VF and QC presented the lowest. Conclusions: The acrylic resin VC and VW presented higher hardness values than VF and QC resins. Moreover, GFR increased the Vickers hardness of resins VW, VC and LT.

Effect of thermal cycling on microleakage between hard chairside relines and denture base acrylic resins

Objectives:Microleakage is a pre-stage of debonding between hard chairside relines and denture base acrylic resins. Therefore, it is important to assess them with regard to the longevity of the relined denture. This study investigated the effect of thermal cycling on the microleakage at the interface of three hard chairside reline resins and three denture base resins.Material and methods:Rectangular bars (12 mm x 3 mm x 3 mm) of Lucitone 550, Acron MC and QC 20 were made and relined with Kooliner, Tokuyama Rebase Fast II and Ufi Gel Hard, Lucitone 550, Acron MC and QC 20 resins. Specimens were divided into one control and two test groups (n = 10). In specimens of the control group, the microleakage was performed after the reline procedure. In Test Group 1, the specimens were stored for 24 h in distilled water at room temperature and in Test Group 2; the specimens were thermal cycled from 5 to 55 degrees C for 5000 cycles with a 30-s dwell time. Subsequently, all specimens were immersed in 50% silver nitrate solutions for 24 h. All specimens were sectioned longitudinally into three fractions and the lateral sections were examined (n = 20). Silver nitrate stain penetration was examined under a stereoscopic lens with x30 magnification, and the images were captured. Leica Qwin image analysis software was used to determine microleakage at the interface of the materials. Data were analysed using the Kruskal-Wallis test at a 95% level of significance.Results:For all cycles, there were no statistically significant differences between thermal cycled and non-thermal cycled groups (p > 0.05).Conclusion:It can be concluded that thermal cycling had no effect on the microleakage.

Effect of microwave irradiation and water storage on the viscoelastic properties of denture base and reline acrylic resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Biocompatibility of denture base acrylic resins evaluated M culture of L929 cells. Effect of polymerisation cycle and postpoymerisation treatments

Objective: the purpose of this study was to evaluate the effect of two post-polymerisation treatments and different cycles of polymerisation on the cytotoxicity of two denture base resins.Materials and methods: the resins tested were Lucitone 550 and QC 20. Discs of resins were fabricated following the manufacturer's instructions. Lucitone 550 was processed by long cycle or short cycle. The resin QC 20 was processed by reverse cycle or normal cycle. The specimens were divided into groups: (i) post-polymerised in microwave for 3 min at 500 W; (ii) post-polymerised in water-bath at 55 degrees C for 60 min and (iii) without post-polymerisation. Eluates were prepared by placing three discs into a sterile glass vial with 9 ml of Eagle's medium and incubated at 37 degrees C for 24 hours. L929 cells were seeded into 96 3 well culture plates and DNA synthesis was assessed by H-thymidine incorporation assay.Results: the results were submitted to two-way ANOVA and Tukey HSD test. QC 20 specimens polymerised by the normal cycle and submitted to microwave post-polymerisation were graded as moderately cytotoxic. Similar results were observed for Lucitone 550 processed by long cycle without post-polymerisation. The other experimental groups were graded as not cytotoxic. After water-bath post-polymerisation, specimens of Lucitone 550 processed by long cycle produced significantly lower inhibition of DNA synthesis than the other groups.Conclusion: the long cycle increased the cytotoxicity of Lucitone 550 and water-bath post-polymerisation reduced the cytotoxicity of Lucitone 550 processed by long cycle.