Chemical stability and electrical properties of Nb doped BaCe 0.9Y 0.1O 3-δ as a high temperature proton conducting electrolyte for IT-SOFC

BaCe 0.9-xNb xY 0.1O 3-δ (where x=0, 0.01, 0.03 and 0.05) powders were synthesized by solid-state reaction to investigate the influence of Nb concentration on chemical stability and electrical properties of the sintered samples. The dense electrolyte pellets were formed from the powders after being uniaxially pressed and sintered at 1550 °C. The electrical conductivities determined by impedance measurements in temperature range of 550-750 °C in different atmospheres (dry argon and wet hydrogen) showed a decreasing trend with an increase of Nb content. For all samples higher conductivities were observed in the wet hydrogen than in dry argon atmosphere. The chemical stability was enhanced with increasing of Nb concentration. It was found that BaCe 0.87Nb 0.03Y 0.1O 3-δ is the optimal composition that satisfies the opposite demands for electrical conductivity and chemical stability, reaching 0.8×10 -2 S cm -1 in wet hydrogen at 650 °C compared to 1.01×10 -2 S cm -1 for undoped electrolyte. © 2012 Elsevier Ltd and Techna Group S.r.l.

Enhanced stability in CO2 of Ta doped BaCe0.9Y 0.1O3-δ electrolyte for intermediate temperature SOFCs

The influence of Ta concentration on the stability of BaCe 0.9-xTaxY0.1O3-δ (where x=0.01, 0.03 and 0.05) powders and sintered samples in CO2, their microstructure and electrical properties were investigated. The ceramic powders were synthesized by the method of solid state reaction, uniaxially pressed and sintered at 1550 °C to form dense electrolyte pellets. A significant stability in CO2 indicated by the X-ray analysis performed was observed for the samples with x≥0.03. The electrical conductivities determined by impedance measurements in the temperature range of 550-750 °C and in various atmospheres (dry argon, wet argon and wet hydrogen) increased with temperature but decreased with Ta concentration. The highest conductivities were observed in the wet hydrogen atmosphere, followed by those in wet argon, while the lowest were obtained in the dry argon atmosphere for each dopant concentration. The composition with Ta content of 3 mol% showed satisfactory characteristics: good resistance to CO2 in extreme testing conditions, while a somewhat reduced electrical conductivity is still comparable with that of BaCe0.9Y0.1O3-δ. © 2012 Elsevier Ltd and Techna Group S.r.l.

Influence of a co-substituted A-site on structural characteristics and ferroelectricity of (Pb, Ba, Ca)TiO3 complex perovskites: analysis of local-, medium- and long-range order

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Spin-strain coupling in a 3-D transition metal oxides

ab-initio Hartree Fock (HF), density functional theory (DFT) and hybrid potentials were employed to compute the optimized lattice parameters and elastic properties of perovskite 3-d transition metal oxides. The optimized lattice parameters and elastic properties are interdependent in these materials. An interaction is observed between the electronic charge, spin and lattice degrees of freedom in 3-d transition metal oxides. The coupling between the electronic charge, spin and lattice structures originates due to localization of d-atomic orbitals. The coupling between the electronic charge, spin and crystalline lattice also contributes in the ferroelectric and ferromagnetic properties in perovskites. The cubic and tetragonal crystalline structures of perovskite transition metal oxides of ABO3 are studied. The electronic structure and the physics of 3-d perovskite materials is complex and less well considered. Moreover, the novelty of the electronic structure and properties of these perovskites transition metal oxides exceeds the challenge offered by their complex crystalline structures. To achieve the objective of understanding the structure and property relationship of these materials the first-principle computational method is employed. CRYSTAL09 code is employed for computing crystalline structure, elastic, ferromagnetic and other electronic properties. Second-order elastic constants (SOEC) and bulk moduli (B) are computed in an automated process by employing ELASTCON (elastic constants) and EOS (equation of state) programs in CRYSTAL09 code. ELASTCON, EOS and other computational algorithms are utilized to determine the elastic properties of tetragonal BaTiO3, rutile TiO2, cubic and tetragonal BaFeO3 and the ferromagentic properties of 3-d transition metal oxides. Multiple methods are employed to crosscheck the consistency of our computational results. Computational results have motivated us to explore the ferromagnetic properties of 3-d transition metal oxides. Billyscript and CRYSTAL09 code are employed to compute the optimized geometry of the cubic and tetragonal crystalline structure of transition metal oxides of Sc to Cu. Cubic crystalline structure is initially chosen to determine the effect of lattice strains on ferromagnetism due to the spin angular momentum of an electron. The 3-d transition metals and their oxides are challenging as the basis functions and potentials are not fully developed to address the complex physics of the transition metals. Moreover, perovskite crystalline structures are extremely challenging with respect to the quality of computations as the latter requires the well established methods. Ferroelectric and ferromagnetic properties of bulk, surfaces and interfaces are explored by employing CRYSTAL09 code. In our computations done on cubic TMOs of Sc-Fe it is observed that there is a coupling between the crystalline structure and FM/AFM spin polarization. Strained crystalline structures of 3-d transition metal oxides are subjected to changes in the electromagnetic and electronic properties. The electronic structure and properties of bulk, composites, surfaces of 3-d transition metal oxides are computed successfully.

Structural and mechanical properties of La0.6Sr0.4M0.1Fe0.9O3-δ (M: Co, Ni and Cu) perovskites

La0.6Sr0.4M0.1Fe0.9O3-δ (M: Co, Ni and Cu) perovskite nanostructures were synthesized using low frequency ultrasound assisted synthesis technique and effect of substitution of Fe by Co, Ni and Cu on crystal structure and mechanical properties in La0.6Sr0.4FeO3-δ perovskite were studied. The HRTEM and Rietveld refinement analyses revealed the uniform equi-axial shape of the obtained nanostructures with the existence of La0.6Sr0.4M0.1Fe0.9O3−δ with mixed rhombohedral and orthorhombic structures. Substitution of Cu decreases the melting point of La0.6Sr0.4FeO3-δ. The results of mechanical characterizations show that La0.6Sr0.4Co0.1Fe0.9O3−δ and La0.6Sr0.4Ni0.1Fe0.9O3−δ have ferroelastic behavior and comparable elastic moduli, however, subtitution of Ni shows higher hardness and lower fracture toughness than Co in Bsite doping

Unfavorable Outcomes During Treatment Of Multiple Sclerosis With High Doses Of Vitamin D.

346

Caracterização físico-química de filmes comestíveis de amido adicionado de acerola (Malphigia emarginata D.C.)

Edibles films are an alternative to synthetic materials used for packing food products. Barbados cherry is rich in vitamin C and carotenoids. The aim of this study was to characterize and develop films by casting from cassava starch, lyophilized Barbados cherry pulp and glycerol. The films were characterized with respect to thickness, water vapor permeability (WVP), water solubility, vitamin C, carotene and mechanical properties. The interaction of pulp and glycerol reduced film thickness. An increase in pulp concentration up to 60% increased WVP but beyond this concentration reduced both WVP and solubility leading to an increased level of vitamin C and β carotene in the films.

Estudo inicial da degradação in vivo de poli(L-co-D,L ácido lático), sintetizado em laboratório, aplicado como prótese tibial em coelhos

The copolymer poly (L-co-D,L lactic acid), PLDLA, has gained prominence in the field of temporary prostheses due to the fact that their time of degradation is quite compatible with the requirement in the case of osseous fracture. In this work the in vivo degradation of devices from copolymer, as a system of plates and screws, used in fixation of the tibia of rabbits was studied. The devices were implanted in 15 adult rabbits, albinos, New Zealand race, and they were used as control devices of alloys of titanium (Ti-6Al-4V/ V grade). The use of copolymers, synthesized in the laboratory, was tested in the repair of fracture in rabbits'tibias, being assessed in the following times: 2 weeks, 2 months and 3 months. Morphological analysis of tissue surrounding the plate and screw system, for 2 weeks of implantation, showed the presence of osteoblasts, indicating a pre bone formation. After 2 months there was new bone formation in the region in contact with the polymer. This bone growth occurred simultaneously with the process of PLDLA degradation, invading the region where there was polymer and after 3 months there was an intense degradation of the copolymer and hence greater tissue invasion compared to 2 months which characterized bone formation in a region where the polymer degraded. The in vivo degradation study of the devices for PLDLA by means of histological evaluations during the period of consolidation of the fracture showed the efficiency of plate and screw system, and it was possible to check formation of bone tissue at the implantation site, without the presence of inflammatory reaction

Vitaminas D e C para poedeiras na fase inicial de produção de ovos

Um experimento foi conduzido com o objetivo de avaliar os efeitos de duas fontes de vitamina D e três níveis de vitamina C sobre as características de desempenho, a qualidade interna e externa dos ovos, os níveis de cálcio total e iônico séricos e a resistência óssea de poedeiras. Foram utilizadas 288 galinhas da linhagem ISA Babcock B300® com 23 semanas de idade, durante um período experimental de 12 semanas. Utilizou-se o delineamento inteiramente ao acaso em arranjo fatorial 2 × 3, com os fatores: fontes de vitamina D (colecalciferol e 25-hidroxicolecalciferol - 25(OH)D3) e de vitamina C (0, 100 e 200 ppm), totalizando seis tratamentos com oito repetições de seis aves. O nível basal de colecalciferol foi de 2.756 UI/kg, correspondendo a 5,51 g do produto comercial Hy.D®/t de ração, como fonte de 25(OH)D3. Os fatores estudados não influenciaram o consumo de ração, a produção, o peso e a massa de ovos. Observou-se efeito da interação de fontes de vitamina sobre a conversão alimentar, que foi melhor quando utilizado metabólito 25(OH)D3 na ausência de vitamina C. Interações foram observadas para porcentagem de albúmen e porcentagem de gema, que aumentaram na presença de 200 ppm de vitamina C. O peso específico dos ovos, as concentrações de cálcio sérico, cinzas ósseas e a resistência à quebra não foram influenciadas pelas fontes de vitamina D e C. Houve interação para porcentagem e espessura de casca, cujos maiores valores foram obtidos com a suplementação de vitamina C na presença de 25(OH)D3. Em poedeiras na fase inicial de produção, a conversão alimentar é melhor com a utilização do 25(OH)D3 e a espessura e porcentagem de casca também melhoram com a utilização de 25(OH)D3 e a suplementação de vitamina C nas dietas (100 ou 200 ppm, respectivamente).

Synthesis of novel O-acylated-D-ribono-1,5-lactones and structural assignment supported by conventional NOESY-NMR and x-ray analysis

A practical method for the structural assignment of 3,4-O-benzylidene-D-ribono-1,5-lactones and analogues using conventional NMR techniques and NOESY measurements in solution is described. 2-O-Acyl-3,4-O-benzylidene-D-ribono-1,5-lactones were prepared in good yields by acylation of Zinner’s lactone with acyl chlorides under mildly basic conditions. Structural determination of 2-O-(4-nitrobenzoyl)-3,4-O-benzylidene-D-ribono-1,5-lactone was achieved by single crystal x-ray diffraction, which supports the results based on spectroscopic data.

High resolution study of 104Pd(d,t)103Pd

Information collected in the present high resolution study of 104Pd(d,t)103Pd is interpreted within the systematics of the A ~ 100 region. The paper complements data previously presented by the S.Paulo Group, which were taken with the Pelletron-Enge-Spectrograph facility. A one-to-one correspondence to gamma ray results for 103Pd, collected by the Nuclear Data Sheets (NDS), was achieved and at least four open questions were settled. More reliable spectroscopic strengths were extracted in the present study.

Redescription of Hiatella meridionalis d'Orbigny, 1846 (Mollusca, Bivalvia, Hiatellidae) from Argentina

The redescription of Hiatella meridionalis (d’Orbigny, 1846) is provided as first attempt to improve the systematics of the genus in the regions of Atlantic and western Pacific. This reanalysis is based on specimens collected in the vicinity of the type localities and is based on detailed morphology of samples that some researches consider a single, wide ranging species. From the morphological characters, the more interesting are: a high quantity of papillae at incurrent siphon; the retractor muscles of siphon divided in two bundles; the small size of the palps; the muscular ring in the stomach; and the zigzag fashion of the short intestinal loops. These characters distinguish the species from the other hiatellids so far examined. Type material of the species was examined, by first time illustrated, and the lectotype is designated.

A new species of Dicrepidius Eschscholtz from Brazil and new records for D. ramicornis (Palisot de Beauvois) (Coleoptera, Elateridae, Elaterinae)

Dicrepidius brasilianus sp. nov., from Pará and Mato Grosso is described and illustrated. This is the second species of this genus recorded from Brazil. D. ramicornis (Palisot de Beauvois, 1805) is widely distributed from south of United States to south of Brazil. From Brazil, it was recorded from Minas Gerais, Rio de Janeiro, São Paulo and Santa Catarina states, but now other records are included. A comparison between the two Brazilian species and a discussion, including intraspecific variations, are presented.

The effects of the experimental infection from a focus of transmission of Schistosoma mansoni in a population of Biomphalaria tenagophila (D'Orbigny, 1835) in the region of "Vale do Ribeira de Iguape", Brazil

To observe the effects of the parasitic infection on the biology of B. tenagophila, field and laboratory populations of this mollusk from Itariri, in Vale do Ribeira, Brazil, were experimentally infected. Each mollusk received 10 miracidia of Schistosoma mansoni (SJ lineage) and was observed throughout the parasite's development. The biological variables were compared according to the criteria "group" and "infectious phase". The main damage caused by the parasitic infection manifested itself in reproduction, longevity and lesions on the shell of the mollusks in the patent phase. An infection rate of 58.8% was observed. Microanatomical study of the mollusk's digestive gland and ovotestis revealed the presence of evolving larval forms and cercariae. It was concluded that the effects of the parasitic infection on both populations were moderate, despite the low survival rate of the infected mollusks, the damage did not prevent either reproduction or the elimination of cercariae, which continued for a long time.