Effect of random/aligned nylon-6/MWCNT fibers on dental resin composite reinforcement

The aims of this study were (1) to synthesize and characterize random and aligned nanocomposite fibers of multi-walled carbon nanotubes (MWCNT)/nylon-6 and (2) to determine their reinforcing effects on the flexural strength of a dental resin composite.Nylon-6 was dissolved in hexafluoropropanol (10 wt%), followed by the addition of MWCNT (hereafter referred to as nanotubes) at two distinct concentrations (i.e., 0.5 or 1.5 wt%). Neat nylon-6 fibers (without nanotubes) were also prepared. The solutions were electrospun using parameters under low- (120 rpm) or high-speed (6000 rpm) mandrel rotation to collect random and aligned fibers, respectively. The processed fiber mats were characterized by scanning (SEM) and transmission (TEM) electron microscopies, as well as by uni-axial tensile testing. To determine the reinforcing effects on the flexural strength of a dental resin composite, bar-shaped (20 x 2 x 2 mm(3)) resin composite specimens were prepared by first placing one increment of the composite, followed by one strip of the mat, and one last increment of composite. Non-reinforced composite specimens were used as the control. The specimens were then evaluated using flexural strength testing. SEM was done on the fractured surfaces. The data were analyzed using ANOVA and the Tukey's test (alpha=5%).Nanotubes were successfully incorporated into the nylon-6 fibers. Aligned and random fibers were obtained using high- and low-speed electrospinning, respectively, where the former were significantly (p<0.001) stronger than the latter, regardless of the nanotubes'presence. Indeed, the dental resin composite tested was significantly reinforced when combined with nylon-6 fibrous mats composed of aligned fibers (with or without nanotubes) or random fibers incorporated with nanotubes at 0.5 wt%. (C) 2015 Elsevier Ltd. All rights reserved.

Knoop hardness of dental resin cements: Effect of veneering material and light curing methods

This study evaluated the Knoop hardness of one resin cement (dual-cure mode or light-cure mode) when illuminated directly or through restorative materials-ceramic (HeraCeram) or composite (Artglass)-by two light curing units. Light curing was carried out using a conventional quartz tungsten halogen (QTH) light source (XL2500) for 40 s, and a light emitting diodes (LED) light source (Ultrablue Is) for 40 s. Bovine incisors had their buccal faces flattened and hybridised. on these surfaces, a mould was seated and filled with cement. A disc of the veneering material (1.5 mm thickness) was positioned over this set for light curing. After storage (24 h/37 degrees C), samples (n = 10) were sectioned for hardness (KHN) measurements. Data were submitted to ANOVA and to Tukey's test (alpha = 0.05). In general, light curing with LED resulted in higher hardness values than QTH. Distinct cement behaviour was observed with different veneering material in association with different light curing units (LCUs). (C) 2006 Elsevier Ltd. All rights reserved.

Influence of cavity preparation and curing method on the marginal seal of resin composite restorations: an in vitro evaluation.

OBJECTIVE: To evaluate the influence of cavity design and photocuring method on the marginal seal of resin composite restorations. METHOD AND MATERIALS: Seventy-two bovine teeth were divided into 2 groups: group 1 received box-type cavity preparations, and group 2 received plate-type preparations. Each group was divided into 3 subgroups. After etching and bonding, Z250 resin composite (3M Espe) was applied in 2 equal increments and cured with 1 of 3 techniques: (1) conventional curing for 30 seconds at 650 mW/cm2; (2) 2-step photocuring, in which the first step was performed 14 mm from the restoration for 10 seconds at 180 mW/cm2 and the second step was performed in direct contact for 20 seconds at 650 mW/cm2; or (3) progressive curing using Jetlite 4000 (J. Morita) for 8 seconds at 125 mW/cm2 and then 22 seconds at 125 mW/cm2 up to 500 mW/cm2. The specimens were thermocycled for 500 cycles and then submitted to dye penetration with a 50% silver nitrate solution. Microleakage was assessed using a stereomicroscope. Data were analyzed using analysis of variance and Tukey test (5% level of significance). RESULTS: A statistically significant difference was found between groups when a double interaction between photocuring and cavity preparation was considered (P = .029). CONCLUSIONS: No one type of cavity preparation or photocuring method prevented micro-leakage. The plate-type preparation showed the worst dye penetration when conventional and progressive photocuring methods were used. The best results were found using the 2-step photocuring with the plate-type preparation.

Effects of age condition on the distribution and integrity of inorganic fillers in dental resin composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Lanthanide complex/polymer composite optical resin with intense narrow band emission, high transparency and good mechanical performance

Novel composite resins possessing good luminescent properties have been synthesized through a free radical copolymerization of styrene, alpha-methylacrylic acid and the binary or ternary complexes of lanthanide ions (Eu3+ and Tb3+). These polymer-based composite resins not only possess good transparency and mechanical performance but also exhibit an intense narrow band emission of lanthanide complexes under UV excitation. We characterized the molecular structure, physical and mechanical performance, and luminescent properties of the composite resins. Spectra investigations indicate that alpha-methyl-acrylic acid act as both solubilizer and ligand. Photoluminescence measurements indicate that the lanthanide complexes show superior emission lines and higher intensities in the resin matrix than in the corresponding pure complex powders, which can be attributed to the restriction of molecular motion of complexes by the polymer chain networks and the exclusion of water molecules from the complex. We also found that the luminescence intensity decreased with increasing content of alpha-methylacrylic acid in the copolymer system. The lifetime of the lanthanide complexes also lengthened when they were incorporated in the polymer matrix. In addition, we found that the relationships between emission intensity and Tb (Eu) content exhibit some extent of concentration quenching.

In vitro evaluation of surface roughness of 4 resin composites after the toothbrushing process and methods to recover superficial smoothness.

OBJECTIVE: This study evaluated the efficiency of repolishing, sealing with surface sealant, and the joining of both in decreasing the surface roughness of resin-based composites after a toothbrushing process. METHOD AND MATERIALS: Ten specimens of each composite (Alert, Z100, Definite, and Prodigy Condensable), measuring 2 mm in thickness and 4 mm in diameter, were made and submitted to finishing and polishing processes on both sides of the specimens using the Sof-Lex system. The specimens were then subjected to toothbrushing (30,000 cycles), and surface roughness (Ra) was analyzed with a Surfcorder SE 1700 profilometer. The upper surface of each composite was etched with 37% phosphoric acid, and the surface-penetrating sealant Protect-it was applied on 1 surface. The roughness of these surfaces was again measured. On the other side, the surface of the specimen was repolished, and the efficiency of this procedure was measured using the profilometer. The surface roughness resulting from the joining of the 2 methods was verified by applying, in the final stage, the surface-penetrating sealant on the repolished surface. Data were analyzed with analysis of variance and Tukey test (P <.05). RESULTS: Results showed that the lowest surface roughness values were obtained for Definite, Z100, and Prodigy Condensable after the repolishing process and after the repolishing plus sealing. For Alert, the joining of repolishing plus sealing promoted the lowest values of surface roughness. CONCLUSION: Of the resin-based composites, Alert demonstrated the highest values of surface roughness in all the techniques tested.

The effects of exposure time on the surface microhardness of three dual-cured dental resin cements

This study evaluated the exposure time of light-curing of the polymers used for cementation on microhardness test in different storage times. The polymers (specifically called resin cements) were RelyX ARC, RelyX U100, and SET. Five specimens of each group were prepared and photo-polymerized with exposure times of 20 s and 180 s, using a LED polymerization unit with wavelength of 440 ~ 480 nm and light output was consistently 1,500 mW/cm2. The Vickers hardness test was performed in a MMT-3 Microhardness Tester. Data were submitted to ANOVA and Tukey's test (α = 0.05). The values of RelyX ARC showed statistically significant difference to groups with light exposure when considering only chemical cure (p < 0.05). The groups with light exposure (20 s and 180 s) showed no significant difference between them (p > 0.05). The RelyX U100 cured only chemically showed statistically significant difference between 48 h and 7 days (p < 0.05). The SET resin cement showed no significant difference to groups without light exposure for all storage times (p > 0.05). The values of hardening of the dual-cured resin cements improved after setting by light and chemical activation demonstrating the importance of light curing. © 2011 by the authors.

Seven-Year Clinical Performance of Resin Composite Versus Resin-Modified Glass lonomer Restorations in Noncarious Cervical Lesions

Purpose: The purpose of this study was to comparatively assess the seven-year clinical performance of a one-bottle etch-and-rinse adhesive with resin composite (RC) and resin-modified glass ionomer (RMGI) restorations in noncarious cervical lesions.Methods and Materials: One operator placed 70 restorations (35 restorations in each group) in 30 patients under rubber dam isolation without mechanical preparation. The restorations were directly assessed by two independent examiners, using modified US Public Health Service criteria at baseline and 6, 12, 24, 60, and 84 months. The obtained data were tabulated and statistically analyzed using the Fisher and McNemar tests. A difference was significant if p<0.05.Results: Twenty patients were available for recall after seven years (66.6%), and 25 RC and 26 RMGI restorations out of 70 restorations were evaluated. Excellent agreement was registered for all criteria between examiners (kappa >= 0.85). Alfa and bravo scores were classified as clinically acceptable. The McNemar test detected significant differences within RC restorations between baseline and seven-year evaluations for anatomic form, marginal integrity, and retention (p<0.05). For RMGI restorations, a significant difference was identified for marginal integrity (p<0.05). As to material comparison, the Fisher exact showed a better retention performance for RMGI restorations than for RC restorations (p<0.05). Twelve composite restorations were dislodged (52.0% retention) and three ionomer restorations were lost (88.5% retention). The cumulative success rate for RC and RMGI was 30% and 58.1%, respectively.Conclusions: After seven years of service, the clinical performance of RMGI restorations was superior to that of the adhesive system/resin composite restorations in this study.

Relevance of In-vitro Tests of Adhesive and Composite Dental Materials. A Review in 3 Parts. Part 2: Non-standardized tests of composite materials

Summary The first part of this review examined ISO approval requirements and in vitro testing. In the second part, non-standardized test methods for composite materials are presented and discussed. Physical tests are primarily described. Analyses of surface gloss and alterations, as well as aging simulations of dental materials are presented. Again, the importance of laboratory tests in determining clinical outcomes is evaluated. Differences in the measurement protocols of the various testing institutes and how these differences can in?uence the results are also discussed. Because there is no standardization of test protocols, the values determined by different institutes cannot be directly compared. However, the ranking of the tested materials should be the same if a valid protocol is applied by different institutes. The modulus of elasticity, the expansion after water sorption, and the polishability of the material are all clinically relevant, whereas factors measured by other test protocols may have no clinical correlation. The handling properties of the materials are highly dependent on operators' preferences. Therefore, no standard values can be given.

Relevance of in vitro tests of adhesive and composite dental materials, a review in 3 parts. Part 1: Approval requirements and standardized testing of composite materials according to ISO specifications

The first part of this three-part review on the relevance of laboratory testing of composites and adhesives deals with approval requirements for composite materials. We compare the in vivo and in vitro literature data and discuss the relevance of in vitro analyses. The standardized ISO protocols are presented, with a focus on the evaluation of physical parameters. These tests all have a standardized protocol that describes the entire test set-up. The tests analyse flexural strength, depth of cure, susceptibility to ambient light, color stability, water sorption and solubility, and radiopacity. Some tests have a clinical correlation. A high flexural strength, for instance, decreases the risk of fractures of the marginal ridge in posterior restorations and incisal edge build-ups of restored anterior teeth. Other tests do not have a clinical correlation or the threshold values are too low, which results in an approval of materials that show inferior clinical properties (e.g., radiopacity). It is advantageous to know the test set-ups and the ideal threshold values to correctly interpret the material data. Overall, however, laboratory assessment alone cannot ensure the clinical success of a product.

Resinas para facetas estéticas de próteses fixas. III. Análise conjunta das variáveis alteração dimensional e alteração de peso em função de materiais, condição de armazenamento e tempos.

The authors analysed the simultaneous effects of the dimensional and weight alteration of resins utilized for esthetic facets submitted to warehousing conditions and periods of time. The resins showed different behaviour and a neat correlation between dimensional alteration and weight. The condition of immersion promoted dimensional alteration 50% lower and an alteration of weight three times higher.

Abordaje conservador y mínimamente invasivo de la hipomineralización molar-incisivo (HMI) - Relato de casos clínicos

Molar-Incisor Hypomineralization (MIH) is a qualitative developmental enamel defect that affects one to four permanent first molars, with or without involvement of permanent incisors. Enamel defects may produce many symptoms that have physical, social and psychological effects and influence day-to-day living or quality of life. The available treatment modalities for teeth with MIH are extensive, ranging from prevention, restoration, to extraction. Factors such as age, patient expectations, severity of the lesion and materials should be considered in the treatment of the patient with MIH. Restoration with composite resin is an alternative choice for posterior and anterior MIH defective teeth and its use has been show acceptable results. This article describes two clinical cases involving pediatric patients with MIH whose procedure of cavity preparation was based on the use of CVD ultrasound diamond tips and restored using composite resin obtaining favorable esthetics results after a 1 year follow-up.

Physical properties of a hybrid and a nanohybrid dental light-cured resin composite.

This work was aimed at the study of some physical properties of two current light-cured dental resin composites, Rok (hybrid) and Ice (nanohydrid). As filler they both contain strontium aluminosilicate particles, however, with different size distribution, 40 nm-2.5 mum for Rok and 10 nm-1 mum for Ice. The resin matrix of Rok consists of UDMA, that of Ice of UDMA, Bis-EMA and TEGDMA. Degree of conversion was determined by FT-IR analysis. The flexural strength and modulus were measured using a three-point bending set-up according to the ISO-4049 specification. Sorption, solubility and volumetric change were measured after storage of composites in water or ethanol/water (75 vol%) for 1 day, 7 or 30 days. Thermogravimetric analysis was performed in air and nitrogen atmosphere from 30 to 700 degrees C. Surface roughness and morphology of the composites was studied by atomic force microscopy (AFM). The degree of conversion was found to be 56.9% for Rok and 61.0% for Ice. The flexural strength of Rok does not significantly differ from that of Ice, while the flexural modulus of Rok is higher than that of Ice. The flexural strengths of Rok and Ice did not show any significant change after immersion in water or ethanol solution for 30 days. The flexural modulus of Rok and Ice did not show any significant change either after immersion in water for 30 days, while it decreased significantly, even after 1 day immersion, in ethanol solution. Ice sorbed a higher amount of water and ethanol solution than Rok and showed a higher volume increase. Thermogravimetric analysis showed that Rok contains about 80 wt% inorganic filler and Ice about 75 wt%.

Effects of Resinous Monomers Used in Restorative Dental Modeling on the Cohesive Strength of Composite Resin

Purpose: The purpose of this study was to evaluate the cohesive strength of the composite using different resinous monomers to lubricate instruments used in the Restorative Dental Modeling Insertion Technique (RDMIT).Materials and Methods: The composite specimens were made by using a prefabricated Teflon device. Different resinous monomers were used at the interface to lubricate the instruments, for a total of 72 specimens divided into 6 groups: 1. control group, no resinous monomer was used; 2. Composite Wetting Resin; 3. C & B Liquid; 4. Scotchbond Multi-Purpose Adhesive; 4. Adper Single Bond Adhesive; 6. Prime & Bond NT. Specimens were submitted to the circular area tensile test to evaluate the cohesive strength at the composite interfaces. Data were analyzed using ANOVA and Tukey's test (alpha = 0.05).Results: ANOVA showed a value of p < 0.0001, which indicated that there were significant differences among the groups. The means (SD) for the different groups were: Adper Single Bond Adhesive: 26 (12) a; control group: 28 (3) ab; Prime & Bond NT: 32 (12) ab; Composite Wetting Resin: 36 (9) abc; C&B Liquid: 38 (7) bc; Scotchbond Multi-Purpose Adhesive: 46 (10) c. Groups denoted with the same letters were not significantly different. Only Scotchbond Multi-Purpose Adhesive, used for direct restorations, had a statistically significantly higher bond strength than the control group, Adper Single Bond Adhesive, and Prime & Bond NT. Adper Single Bond with Adhesive showed a statistically significantly lower mean value than C & B Liquid.Conclusion: The results of this study indicate that the resinous monomers used for lubricating the instruments in the RDMIT did not alter the mechanical properties of the composite, and therefore did not reduce the cohesive bond strength at the composite interfaces.

Effect of the Insertion and Polymerization Technique in Composite Resin Restorations: Analysis of Marginal Gap by Atomic Force Microscopy

This in vitro study evaluated the marginal gap at the composite tooth/resin interface in class V cavities under the influence of two insertion techniques and a curing system by means of atomic force microscopy (AFM). Forty enamel and dentin cavities were prepared on the buccal surface in bovine teeth with quadratic forms measuring 2 mm X 2 mm and depth of 1.5 mm. The teeth were then divided into four groups: group A, 10 cavities were restored in one increment, light cured by halogen light; group B, 10 cavities filled with bulk filling, light cured by the light emitting diodes (LED); group C, 10 cavities were restored by the incremental technique, light cured by halogen light; group D, 10 cavities were restored by the incremental technique, light cured by the LED. The teeth underwent the polishing procedure and were analyzed by AFM for tooth/restoration interface evaluation. The data were compared between groups using the nonparametric Kruskall-Wallis and Mann-Whitney tests (p < 0.05). The results showed a statistically significant difference between groups A and B and groups A and C. It was concluded that no insertion and polymerization technique was able to completely seal the cavity.