Incorporação de cinzas da casca de café na produção de placas cerâmicas para revestimento

Brazil is the world s leading coffee producer. In 2008, 45.99 million of 60 kg bags of benefited coffee were produced. In the process of improvement 50% is grain and 50% is husk, thus, 1.38 million tons of coffee husk are produced annually. The husk is used as combustible in the drying and improvement ovens in the coffee farms, generating ash as residue. These ashes contain a high concentration of alkaline metals and earth metals, mainly K2O and CaO. This work studies the use of this residue in the ceramic tiles industry, as fluxing agents in substitution to the feldspar. Ten mixtures with equal ratios of clay and kaolin, proceeding from Bahia and the residue (varying from 30 to 5%) were defined and produced in uniaxial tool die of 60x20mm with approximately 5 mm of thickness and 45MPa compacting pressure. The samples were fired in four different temperatures: 1100 °C, 1150 °C, 1185 °C and 1200 °C during 60 minutes and characterized by means of X-ray fluorescence, X-ray diffraction, gravimetric thermal analysis and differential thermal analysis. The results of water absorption, apparent porosity, linear shrinkage, XRD, dilatometry, flexural strength and SEM were also analysed. The test specimen with addition of 10% of ash fired in 1200 °C resulted in 0.18% water absorption and 40.77 MPa flexural strength, being classified as porcelain stoneware tiles according to ABNT, UNI and ISO norms

Estudo da potencialidade da incorporação de resíduo de granito e da queima da casca do café em cerâmica vermelha

The industrial production of ornamental rocks and the burning of coffee husk generate waste that is discarded into the environment. However, with the study of the incorporation of these residues in ceramic products, may be found an alternative to reducing environmental impacts and detrimental effects on human health caused by its indiscriminate disposal of waste in nature. Thus, this work aimed to study the addition of ashes of the coffee husk and granite residue in matrix of red ceramic. The raw materials were dry milled and sieved to mesh 100. To characterize the raw materials were carried out analyzes of X-ray diffraction (XRD), X-ray fluorescence (XRF), particle size analysis (PSA), differential thermal analysis (DTA) and thermogravimetric analysis (TG). Six formulations were prepared where the clay content was kept constant (70%wt) and ashes contents and granite residue varied from 10, 15, 20 and 30%. Dilatometrics analyzes were performed at four selected formulations, containing them: 100% clay (A100); 70% clay and 30% ashes (A70C30); 70% clay and 30% granite residue (A70G30); and 70% clay, 15% granite residue and 15% ashes (A70G15C15). The samples were prepared by uniaxial compaction with pressure of 25 MPa, and fired at temperatures of 800°C, 850ºC, 900ºC, 950ºC, 1000ºC and 1100°C. Assays were performed to determine the linear shrinkage of burning (LSB), water absorption (WA), apparent porosity (AP), density (D) and tensile bending. Also were performed analyzes of X-ray diffraction (XRD) and scanning electron microscopy (SEM) of the samples fired. The formulations incorporating granite residue and/or ashes reached the required limits of water absorption according to NBR 15270-1 and NBR 15310 and tensile bending according to classical literature (SANTOS, 1989) necessary for the production of tiles and ceramic block for masonry sealing

Estudo da potencialidade da incorporação de resíduo de granito e da queima da casca do café em cerâmica vermelha

The industrial production of ornamental rocks and the burning of coffee husk generate waste that is discarded into the environment. However, with the study of the incorporation of these residues in ceramic products, may be found an alternative to reducing environmental impacts and detrimental effects on human health caused by its indiscriminate disposal of waste in nature. Thus, this work aimed to study the addition of ashes of the coffee husk and granite residue in matrix of red ceramic. The raw materials were dry milled and sieved to mesh 100. To characterize the raw materials were carried out analyzes of X-ray diffraction (XRD), X-ray fluorescence (XRF), particle size analysis (PSA), differential thermal analysis (DTA) and thermogravimetric analysis (TG). Six formulations were prepared where the clay content was kept constant (70%wt) and ashes contents and granite residue varied from 10, 15, 20 and 30%. Dilatometrics analyzes were performed at four selected formulations, containing them: 100% clay (A100); 70% clay and 30% ashes (A70C30); 70% clay and 30% granite residue (A70G30); and 70% clay, 15% granite residue and 15% ashes (A70G15C15). The samples were prepared by uniaxial compaction with pressure of 25 MPa, and fired at temperatures of 800°C, 850ºC, 900ºC, 950ºC, 1000ºC and 1100°C. Assays were performed to determine the linear shrinkage of burning (LSB), water absorption (WA), apparent porosity (AP), density (D) and tensile bending. Also were performed analyzes of X-ray diffraction (XRD) and scanning electron microscopy (SEM) of the samples fired. The formulations incorporating granite residue and/or ashes reached the required limits of water absorption according to NBR 15270-1 and NBR 15310 and tensile bending according to classical literature (SANTOS, 1989) necessary for the production of tiles and ceramic block for masonry sealing

Adição de subprodutos da cinza da casca de café (coffea canephora) em massa cerâmica para porcelanato

To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d Ávila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 °C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles

Adição de subprodutos da cinza da casca de café (coffea canephora) em massa cerâmica para porcelanato

To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d Ávila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 °C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles

Solubilização de fontes alternativas de potássio pelos ácidos húmicos, cítrico e casca de café

This study was to evaluate the solubility of nepheline syenite rocks and glauconite as alternative sources of K by organic humic acid arrays, citrus and coffee pods at various times from 0 to 180 days of incubation. The experiment was conducted in the fertility laboratory in the Department of Soil Science at the Federal University of Lavras in a completely randomized design with 90 treatments and 3 replications. The treatments were arranged in a factorial arrangement (2 x 3 x 7 + 3), 2 nepheline syenite rocks and glauconite incubated with water and 3 matrix organic humic acid, citric acid and coffee husk in six different incubation times of 0, 7, 15, 30, 75, 120 and 180 days, incubation were performed with the three above-mentioned organic matrix in increasing doses of 0, 1, 2, 5 and 10% humic acids and citric 0, 5, 10 20 and 40% for coffee husk. We evaluated the K2O content by different extractants soluble in 2% citric acid and water all treatments at all incubation times quoted above. Incubation and the application of organic matrix rocks nepheline syenite and generally glauconite provided a significant increase in solubility of K of the rocks studied in this work. Among the organic matrix has been observed that the coffee husk which provided the greatest release of K2O in both rocks mainly into the extractor 2% citric acid showed that the most efficient extraction K2O in all treatments.

Efeito da fermentação fúngica no teor de compostos fenólicos em casca de café robusta

Coffee husk is an abundant by-product generated by the coffee industry and it can be used for the production of-value-added phenolic compounds. Currently, this residue has no commercial use due to the presence of anti-nutritional compounds and it is returned to the soil or burned. The aim of this study was to evaluate the content of phenolic compounds in Robusta coffee husk, the adequacy of this residue as substrate for fermentation processes, as well as evaluating the influence of fungal solid state fermentation to obtain phenolic compounds from this residue. In the present study, the use of different solvents for the extraction of polyphenols was evaluated and the content was found to be in the range of 96.9-159.5 mg of galic acid (GA).g(-1) substrate, depending on the solvent used. The best solvent was acetone, therefore it was selected for extraction. Studies were carried out to evaluate the effect of solid-state fermentation in the release of phenolic compounds, using the filamentous fungi Penicillium purpurogenum. The total phenolic content increased from 159.5 up to 243.2 mg GA.g(-1) substrate as a result the solid-state fermentation.

Caracterização físico-mecânica de painéis de partículas de bambu com adição de casca de café

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Uso de resíduos de queima de casca de café e argila da região sul da Bahia na obtenção de isolador elétrico cerâmico

The electrical ceramic insulators industry, uses noble raw materials such as siliceous and aluminous clays of white burning, in order to provide plasticity of the mass and contribute to electrical and mechanical properties required of the product, and feldspar with the flux function In literature references the composition of the masses indicates that the clay participates in percentage between 20 and 32, and feldspar 8 to 35, these materials have significant cost. In this research was performed the total replacement of commercial clay, for white burning clay from Santa Luzia region in southern Bahia and partial replacement of feldspar by ash residue of husk conilon coffee burning, from extreme south of Bahia. The objective of replacement these raw materials is to aver its technical feasibility and call attention for the embryo pole of ceramic industry for the existing in the south and extreme south of Bahia, which has significant reserves of noble raw materials such as clay white burning, kaolin, quartz and feldspar, and generates significant volume of gray husk conilon coffee as alternate flux. Clay Santa Luzia is prima noble material whose current commercial application is the production of white roofing. The residue of coffee husk ash is discarded near of production sites and is harmful to the environment. Phase diagrams and statistic design of experiments, were used for optimization and cost savings in research. The results confirmed the expectations of obtaining electrical ceramic insulators, with white burning clay of Santa Luzia and partial replacement up to 35.4% of feldspar, by treaty residue of conilon ash coffee husk burning. The statistic design that showed best results was for formulation with percentages of: clay 26.4 to 30.4%; kaolin 14.85 to 17.1%; feldspar 12.92 to 16.96%; R2 residue 7.08 to 9.2% and Quartz 32.5 to 38.75%, relative to the total mass of the mixture. The best results indicated; 0.2 to 1.4% apparent porosity , water absorption 0.1 to 0.7%, flexural strength 35 to 45MPa , dielectric strength 35-41 kV/cm , the transverse resistivity 8x109 2.5x1010 Ω.cm and for the dielectric constant ε/ε0 7 to 10.4, specification parameters for manufacturing ceramic electrical insulators of low and medium voltage.

Utilização de resíduos de catalisador (ECAT) e cinzas da casca de arroz (CCA) na elaboração de vidros silicatos soda-cal destinados a embalagem

Dissertação (Mestrado em Tecnologia Nuclear)

Estudo de Argamassas com Cinza de Casca de Amêndoa

Perante o elevado consumo de materiais naturais no processo e produtos na área da construção civil, o reaproveitamento de resíduos é uma das soluções a ser estudada. As cinzas agroindustriais têm lugar de destaque entre estes resíduos, pois têm a possibilidade de aplicação em materiais cimentícios, reduzindo assim o consumo de cimento de Portland. O presente estudo debruça-se sobre a substituição parcial (1,5% e 5%) de cimento de Portland por cinzas de casca de amêndoa. Realizaram-se provetes com diferentes tipos de argamassas: (i) uma de controlo sem substituição de cimento (ARF); (ii) uma com 1,5% de substituição parcial de cimento por cinzas de casca de amêndoa (CCA 1,5%); (iii) e uma com 5% de substituição parcial de cimento por cinza de casca de amêndoa (CCA 5%). Executaram-se ensaios para resistências mecânicas aos 3, 7, 14, 28 e 41 dias de idade. A nível químico pode-se concluir que esta cinza de casca de amêndoa não apresentou qualquer potencial pozolânico. A trabalhabilidade na generalidade diminui ligeiramente, contendo cinza de casca de amêndoa, mas ainda assim considerando-se de fácil manuseamento. Em relação às resistências mecânicas, pode-se concluir que o ideal é a substituição parcial de cimento com 1,5%, pois as resistências diminuem com o uso de uma maior percentagem de substituição, ou seja, o ideal é substituir em pequenas percentagens. Com os dados obtidos, conclui-se que as cinzas testadas não apresentam características necessárias para serem consideradas pozolanas e se será viável a sua utilização mesmo como filer.

Beneficiamentos da cinza de casca de arroz residual com vistas à produção de cimento composto e/ou pozolânico

A cinza de casca de arroz é um resíduo agro-industrial decorrente do processo de queima da casca de arroz, sendo largamente encontrada no Rio Grande do Sul, pois, historicamente, este Estado é o maior produtor de arroz no Brasil, com cerca de 45% da produção nacional. Empregada como fonte de energia, a casca de arroz é queimada em diversas empresas; algumas, devido à sua natureza, incorporam a cinza ao produto, mas a maioria não encontra outro destino que não o descarte em forma de aterro, criando, assim, um problema ambiental de poluição do solo, do ar e de rios e córregos. No entanto, devido à presença de elevado percentual de sílica (SiO2) na sua constituição, a cinza de casca de arroz pode ter vários empregos. Na construção civil, pode ser empregada como pozolana, conforme vários estudos já vêm demonstrando. Porém, encontra restrições por motivos como sua cor escura, que confere aos cimentos, argamassas e concretos aos quais é adicionada, uma coloração também escura, e a falta de uniformidade apresentada em termos de características químicas e, principalmente, mineralógicas. A cor escura não é um problema de ordem técnica, mas estética e de aceitação no mercado. Já a composição mineralógica está associada à atividade pozolânica e a falta de uniformidade do material disponível implica na incerteza do grau de reatividade. Este trabalho teve o objetivo de verificar a viabilidade técnica do emprego de cinzas de casca de arroz residuais na confecção de cimentos Portland composto e/ou pozolânico, a partir de beneficiamentos das mesmas, que associam tratamentos físicos, químicos e/ou térmicos, os quais têm como finalidade reverter e/ou minimizar os aspectos negativos citados. Para tanto, foram empregadas três cinzas de casca de arroz, oriundas de diferentes processos de produção e com composições mineralógicas distintas. Após definidos os tratamentos a serem aplicados, através de seleção pelos critérios de cor e composição mineralógica, as cinzas tratadas foram avaliadas quanto à sua pozolanicidade, pelo Índice de Atividade Pozolânica (IAP) da NBR 5752 e também por um IAP alterado, proposto neste trabalho. A produção de cimentos com CCA beneficiada se deu a partir de um cimento base com substituição por CCA, em massa e em diferentes percentuais. Tais cimentos foram avaliados quanto à resistência à compressão, aos tempos de pega, à pozolanicidade e à expansibilidade a quente. A análise dos dados obtidos indica que os tratamentos propostos e/ou a associação deles resultam em beneficio no desempenho das cinzas, em pelo menos um dos vários aspectos considerados. A presente pesquisa permite concluir que as CCA residuais têm potencial para serem empregadas na produção de cimentos, tanto aquelas menos cristalinas, quanto as mais cristalinas. Para tanto, devem ser beneficiadas, sendo pelo menos submetidas a tratamento físico para redução de sua granulometria. Se outros objetivos forem pretendidos, como coloração clara, os tratamentos térmico ou químico podem ser empregados.

Avaliação da liberação de potássio por resíduos do benefício de café

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)