Does the casting mode influence microstructure, fracture and properties of different metal ceramic alloys?

The aim of the present study was to evaluate the tensile strength, elongation, microhardness, microstructure and fracture pattern of various metal ceramic alloys cast under different casting conditions. Two Ni-Cr alloys, Co-Cr and Pd-Ag were used. The casting conditions were as follows: electromagnetic induction under argon atmosphere, vacuum, using blowtorch without atmosphere control. For each condition, 16 specimens, each measuring 25 mm long and 2.5 mm in diameter, were obtained. Ultimate tensile strength (UTS) and elongation (EL) tests were performed using a Kratos machine. Vickers Microhardness (VM), fracture mode and microstructure were analyzed by SEM. UTS, EL and VM data were statistically analyzed using ANOVA. For UTS, alloy composition had a direct influence on casting condition of alloys (Wiron 99 and Remanium CD), with higher values shown when cast with Flame/Air (p < 0.05). The factors "alloy" and "casting condition" influenced the EL and VM results, generally presenting opposite results, i.e., alloy with high elongation value had lower hardness (Wiron 99), and casting condition with the lowest EL values had the highest VM values (blowtorch). Both factors had significant influence on the properties evaluated, and prosthetic laboratories should select the appropriate casting method for each alloy composition to obtain the desired property.

Microstructures and properties of melt-spun and as-cast Mg-20Gd binary alloy

Mg-20Gd(%, mass fraction) samples were prepared using melt-spinning and copper mold casting techniques. Microstructures and properties of the Mg-20Gd were investigated. Results show that the melt-spun ribbon is mainly composed of supersaturated alpha-Mg solid solution phase and the as-east ingot mainly contains alpha-Mg solid solution and Mg5Gd phase. The differential scanning calorimeter (DSC) curve of the ribbon exhibits a small exothermic peak in the temperature range from 630 to 680 K, which indicates that the ribbon contains a metastable phase (amorphous). Tensile strength at room temperature of the melt-spun ribbon and as-cast specimen are 308 and 254 MPa, respectively. The elongations of the two samples are less than 2%. The fracture surfaces demonstrate that the fracture mode of the as-cast Mg-20Gd is a typical cleavage fracture and that of the melt-spun sample is a combination of brittle fracture and ductile fracture.

Facile preparation and thermoelectric properties of Bi₂Te₃ based alloy nanosheet/PEDOT:PSS composite films

Bi2Te3 based alloy nanosheet (NS)/poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) (PEDOT:PSS) composite films were prepared separately by spin coating and drop casting techniques. The drop cast composite film containing 4.10 wt % Bi2Te3 based alloy NSs showed electrical conductivity as high as 1295.21 S/cm, which is higher than that (753.8 S/cm) of a dimethyl sulfoxide doped PEDOT:PSS film prepared under the same condition and that (850-1250 S/cm) of the Bi2Te3 based alloy bulk material. The composite film also showed a very high power factor value, ∼32.26 μWm(-1) K(-2). With the content of Bi2Te3 based alloy NSs increasing from 0 to 4.10 wt %, the electrical conductivity and Seebeck coefficient of the composite films increase simultaneously.

Fadiga de grampos de retenção em prótese parcial removível. Efeito de ligas, espessuras e técnicas de fusão. Parte I.

The authors looked for the verification of the fatigue of retentive clasps utilized on the removable partial denture. According to this, it was idealized and built on assay machine, that through movements, simulate the insertion and removal of the clasp for a pattern tooth, manufactured on cobalt-chromium which has all the preparation normally utilized to the correct confection of this type of prosthesis. It was utilized three different commercial alloys based on cobalt-chromium: L1-Biosil; L2-Steldent; L3-Duracron. It was utilized the T clasp of Roach, with was tested upon three different proportions among width and thickness: E1-1.7;E2-2.0 and E3-2.3 and was casted through two casting techniques: F1-oxygen-gas and F2-oxygen-acetylene. The clasps were tested on the machine, which allowed the reading of the number of insertion and removal cycles made until fatigue appeared. The obtained results were submitted to the statistic analysis and the authors concluded that: a) L3 (Duracrom) obtained the best results followed by L1 (Biosil) and finally L3 (Steldent); b) among the analyzed thickness, the best results were obtained by E3, followed by E2 and after this E1; c) form the casting techniques, F2 gave us the best results.

Fadiga de grampos de retenção em prótese parcial removível. Efeito de ligas, espessuras e técnicas de fusão. Parte II.

The authors tested the T clasp of Roach in three differents proportions among width and thickness: E1-1.7; E2-2.0 and E3-2.3, with a constant length of 15 mm. These clasps were casted with three cobalt-chromium alloys (L1-Biosil; L2-Steldent and L3-Duracrom), through two casting techniques (F1-oxygen-gas and F2-oxygen-acetylene). The fatigue of the clasps were verified by using and assay machine, that through movements, simulate the insertion and removal of the clasps for a pattern which were obtained from a premolar, prepared in a surveyor. This machine detect the fatigue of the clasps and count the number of cycles of insertion and removal realized. The obtained results of the interaction between the analysed factors, were submitted to the statistic analysis and the authors concluded that: a) the interaction of factors, Alloy x Thickness, Alloy x Casting Technique and Thickness x Casting Technique did not change the order of effects that the factors showed separately but gave rise to effects of different magnitude for any observed sense; b) the simultaneous interaction of the factors Alloy x Thickness x Casting Technique confirmed the superiority of the L3 alloy, the thickness E3 and the F2 casting technique.

Production and heat treatment of cast graphitic steels with additions of niobium

The optimal combination of the mechanical characteristics of austempered spheroidal graphitic cast steel together with modern casting techniques yielded an economically promising product. The maximum potential of the usage of these steels is related to fabrication and characterization techniques, among which, one of the most important is the cooling diagram (TTT curve). In this work, 3 heats of graphitic steels with the following nominal compositions were cast: 1.0 % C, 2.3 % Si, 0.4 % Mn, and with niobium contents of. 0.0 %, 0.5 % and 1.0 %. TTT curves were determined by dilatometric testing and test specimens of these steels were austempered. The samples were then characterized by hardness testing and optical and SEM microscopy. Tensile, impact (no notch) and wear testing were also performed. The addition of niobium produced significant alterations in the TTT diagrams. Increasing niobium content moves the pearlite transformation nose to the right and the bainitic transformation nose to the left. Tensile strength of these alloys was high, in the range of 1700 MPa and impact values were around of 45 Joules for alloy with 1 % Nb, 49 Joules for alloy with 0.5 % Nb and fracture did not occur for the alloy without the addition of Nb.

Production and heat treatment of cast graphitic steels with additions of niobium

The optimal combination of the mechanical characteristics of austempered spheroidal graphitic cast steel together with modern casting techniques yielded an economically promising product. The maximum potentiality of the usage of these steels is related to fabrication and characterization techniques, among which, one of the most important is the cooling diagram (TTT curve). In this work, 3 heats of graphitic steels with the following nominal compositions were cast: 1.0%C, 2.3%Si, 0.4% Mn, and with niobium contents of 0.0%, 0.5% and 1.0%. TTT curves were determined by dilatometric testing and test specimens of these steels were austempered. The samples were then characterized by hardness testing and optical and SEM microscopy. Tensile, impact (no notch) and wear testing were also performed. The addition of niobium produced significant alterations in the TTT diagrams. Increasing niobium content moves the pearlite transformation nose to the right and the bainitic transformation nose to the left. Tensile strength of these alloys was high, in the range of 1700 MPa and impact values were around of 45 Joules for alloy with 1% Nb, 49 Joules for alloy with 0.5% Nb and fracture did not occur for the alloy without the addition of Nb.

Avaliação da desadaptação marginal de estruturas metálicas obtidas com variações quanto aos tipos de cera e às técnicas de inclusão e fundição

Pós-graduação em Odontologia - FOA

Comparação da desadaptação marginal de infra-estruturas metálicas obtidas com variações na técnica de fundição, revestimentos e material para obtenção dos padrões

Pós-graduação em Odontologia - FOA

Comparação da adaptação cervical de estruturas metálicas para metalo-cerâmica obtidas através de técnica de fundição rápida e convencional, utilizando três revestimentos comerciais

Pós-graduação em Odontologia - FOA

Reação exotérmica e expansões de presa e térmica de revestimentos frente às técnicas de fundição convencional e rápida

Pós-graduação em Odontologia - FOA

Corrosion behaviour of aluminium syntactic functionally graded composites

Syntactic Functionally Graded Metal Matrix Composites (SFGMMC) are a type of composites reinforced by microballoons exhibiting a graded reinforcement distribution. These materials constitute a promising new generation of lightweight structural materials for aerospace, marine and shielding/insulation applications. In this work, A356 alloy reinforced with silica-alumina microballoons (SiO2-Al2O3) was processed by casting techniques. The influence of the microballoon distribution gradient on the corrosion behaviour of the composite was investigated by potentiodynamic polarisation and Electrochemical Impedance Spectroscopy (EIS). Composite surfaces were analysed before and after testing by Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) to determine the influence of microstructural changes.

3D documentation of footwear impressions and tyre tracks in snow with high resolution optical surface scanning

The three-dimensional documentation of footwear and tyre impressions in snow offers an opportunity to capture additional fine detail for the identification as present photographs. For this approach, up to now, different casting methods have been used. Casting of footwear impressions in snow has always been a difficult assignment. This work demonstrates that for the three-dimensional documentation of impressions in snow the non-destructive method of 3D optical surface scanning is suitable. The new method delivers more detailed results of higher accuracy than the conventional casting techniques. The results of this easy to use and mobile 3D optical surface scanner were very satisfactory in different meteorological and snow conditions. The method is also suitable for impressions in soil, sand or other materials. In addition to the side by side comparison, the automatic comparison of the 3D models and the computation of deviations and accuracy of the data simplify the examination and delivers objective and secure results. The results can be visualized efficiently. Data exchange between investigating authorities at a national or an international level can be achieved easily with electronic data carriers.

Creep and fatigue of a single crystal nickel base superalloy

The introduction of single crystal casting techniques has led to the development of existing nickel-base superalloys to produce materials with optimum mechanical properties in the single crystal condition. As single crystals are known to be anisotropic, a study is needed to determine the general mechanical properties of these materials, and determine the effects of crystal orientation upon them. A study has been carried out to identify the effect of orientation and temperature on the creep and fatigue properties of a development single crystal superalloy, SRR 99. Creep testing and crystal rotation experiments have been made on SRR 99 and an earlier development alloy, SRR 9. Fatigue experiments at elevated temperatures have been carried out on both notched and un-notched specimens of alloy SRR 99. To aid in this analysis, several analytical techniques have been employed including Laue x-ray orientation analysis, measurement of strain by photographic methods and microstructural examination. Crystal rotation experiments have indicated that shear of 1 precipitates by lbrace111rbrace< 112> slip systems is operative during primary creep deformation at temperatures of 750oC and 850oC. The effect of orientation variation obtained by standard casting practices was not found to be significant. Creep rupture was found to be associated with multiple crack initiation from micropores. Fatigue crack initiation in un-notched specimens was found to be related to microporosity and microstructural defects. Failure was predominantly by crystallographic crack growth on lbrace111rbrace planes. The use of linear elastic fracture mechanics to describe fatigue crack propagation in alloy SRR 99 was found to be acceptable at temperatures up to 850oC. Variation of temperature, frequency and crystal orientation was found to have only moderate effect upon crack propagation rates.