Crystal structures and textures in the hot-forged Ni-Mn-Ga shape memory alloys

Three ferromagnetic shape-memory alloys with the chemical compositions of Ni₅₃Mn₂₅Ga₂₂, Ni₄₈Mn₃₀Ga₂₂, and Ni₄₈Mn₂₅Ga₂₂Co₅ were prepared by the induction-melting and hot-forging process. The crystal structures were investigated by the neutron powder diffraction technique, showing that Ni₅₃Mn₂₅Ga₂₂ and Ni₄₈Mn₂₅Ga₂₂Co₅ have a tetragonal, 14/mmm martensitic structure at room temperature, while Ni₄₈Mn₃₀Ga₂₂ has a cubic, L2₁ austenitic structure at room temperature. The development of textures in the hot-forged samples shows the in-plane plastic flow anisotropy from the measured pole figures by means of the neutron diffraction technique. Significant texture changes were observed for the Ni₄₈Mn₂₅Ga₂₂Co₅ alloy after room temperature deformation, which is due to the deformation-induced rearrangements of martensitic variants. An excellent shape-memory effect (SME) with a recovery ratio of 74 pct was reported in this Ni₄₈Mn₂₅Ga₂₂Co₅ polycrystalline alloy after annealing above the martensitic transformation temperature, and the “shape-memory” influence also occurs in the distributions of grain orientations.

Crystal structures and textures of hot forged Ni48Mn30Ga22 alloy investigated by neutron diffraction technique

A ferromagnetic shape memory alloy of Ni48Mn30Ga22 prepared by induction melting was successfully hot forged. Strong textures and a large anisotropy of in plane plastic flow were developed during the hot forging process. The crystal structures, both in austenitic and martensitic states, were investigated by means of neutron powder diffraction technique. The result suggests that Ni48Mn30Ga22 has a cubic L21 Heusler structure at room temperature, the same as that in the stoichiometric Ni2MnGa. When cooled to 243 K, the Ni48Mn30Ga22 alloy changes into a seven layered orthorhombic martensitic structure. No substantial change of the neutron diffraction pattern was observed upon further cooling to 19 K, indicating that there is no intermartensitic transformation in the investigated alloy, which is different from the transformation processes in the Ni–Mn–Ga alloys with higher martensitic transformation temperatures.