Phase transition and conformational variation of N-alkylated branched poly(ethyleneimine) comblike polymer

A series of branched poly(ethyleneimine) (PEI) derived polymers with different lengths of n-alkyl side chains, denoted as PEI(n)Cs (n = 12, 14, 16, 18, 20, number of carbon atoms in alkyl side group), have been prepared by a N-alkylation method, and systematically characterized by differential scanning calorimertry (DSC) and wide-angle X-ray diffraction (WARD) as well as Fourier transform infrared spectroscopy (FTIR). The side chains grafted on these comblike polymers are long enough to form crystalline phase composed of paraffin-like crystallites. The crystallization of the side chains forces the branched poly(ethyleneimine) molecules to pack into layered structure, between which the crystallites are located. The melting temperatures of the side chain crystallites increase from -12.36 to +51.49 degreesC with increasing the length of the side chains from n. = 12 to n = 20, which are a little bit lower than the corresponding pristine n-alkanes. PEI18C was taken as an example in this work for the investigation of phase transition and conformational variation of the side chains with temperature changing.

Ordering transformation in icosahedral quasicrystals and related crystalline phases

Arcs of diffuse intensity appear in various shapes and positions in the diffraction patterns from the icosahedral phase, violating the parity rule for simple icosahedral (SI) symmetry. In the process of annealing treatment, the diffuse spots also evolve in the centre of the arcs and become sharp. These extra diffuse spots change the symmetry of the quasilattice from P-type to F-type. The ordered and disordered structures in quasicrystal have been linked to the ordered and disordered structures present in the crystalline alpha (Al-Mn-Si) and alpha (Al-Fe-Si) alloys.

Fabrication and Phase Transformation in Crystalline Nanoparticles of PbZrO3 Derived By Sol-Gel

In this research fabrication of crystalline PbZrO3 (PZ) nanoparticles and their phase transformation behavior is investigated. A novel sol-gel method was used for the synthesis of air-stable and precipitate-free diol-based sol of PZ, which was dried at 150 degrees C and then calcined at 300-700 degrees C for 1 h. The morphology, crystallinity and phase formation of as synthesized nanoparticles were studied by the selected-area electron diffraction (SAED), X-ray diffraction (XRD), thermal gravimetric analysis/differential scanning calorimetry (TGA-DSC), and high resolution transmission electron microscope (HRTEM). The XRD, SAED, and TGA-DSC analyses confirmed the tetragonal lead rich zirconia phase (t-Z phase) and monoclinic zirconia phase (m-Z phase) as the intermediate phases during the calcinations process followed by crystallization of single orthorhombic PZ phase at about 700 degrees C. The average PZ particle size was observed about 20 nm as confirmed by TEM study. Energy-dispersive X-ray spectroscopy (EDX) analysis demonstrated that stoichiometric PbZrO3 was formed.

Theory Of Phase Transformation And Reorientation In Single Crystalline Shape Memory Alloys

A constitutive model, based on an (n + 1)-phase mixture of the Mori-Tanaka average theory, has been developed for stress-induced martensitic transformation and reorientation in single crystalline shape memory alloys. Volume fractions of different martensite lattice correspondence variants are chosen as internal variables to describe microstructural evolution. Macroscopic Gibbs free energy for the phase transformation is derived with thermodynamics principles and the ensemble average method of micro-mechanics. The critical condition and the evolution equation are proposed for both the phase transition and reorientation. This model can also simulate interior hysteresis loops during loading/unloading by switching the critical driving forces when an opposite transition takes place.

Hydrogen-induced morphotropic phase transformation of single-crystalline vanadium dioxide nanobeams.

We report a morphotropic phase transformation in vanadium dioxide (VO2) nanobeams annealed in a high-pressure hydrogen gas, which leads to the stabilization of metallic phases. Structural analyses show that the annealed VO2 nanobeams are hexagonal-close-packed structures with roughened surfaces at room temperature, unlike as-grown VO2 nanobeams with the monoclinic structure and with clean surfaces. Quantitative chemical examination reveals that the hydrogen significantly reduces oxygen in the nanobeams with characteristic nonlinear reduction kinetics which depend on the annealing time. Surprisingly, the work function and the electrical resistance of the reduced nanobeams follow a similar trend to the compositional variation due mainly to the oxygen-deficiency-related defects formed at the roughened surfaces. The electronic transport characteristics indicate that the reduced nanobeams are metallic over a large range of temperatures (room temperature to 383 K). Our results demonstrate the interplay between oxygen deficiency and structural/electronic phase transitions, with implications for engineering electronic properties in vanadium oxide systems.

Melt structure and its transformation by sequential crystallization of the two blocks within poly(L-lactide)-block-poly(epsilon-caprolactone) double crystalline diblock copolymers

Sequential crystallization of poly(L-lactide) (PLLA) followed by poly(epsilon-caprolactone) (PCL) in double crystalline PLLA-b-PCL diblock copolymers is studied by differential scanning calorimetry (DSC), polarized optical microscopy (POM), wide-angle X-ray scattering (WAXS) and small-angle X-ray scattering (SAXS). Three samples with different compositions are studied. The sample with the shortest PLLA block (32 wt.-% PLLA) crystallizes from a homogeneous melt, the other two (with 44 and 60% PLLA) from microphase separated structures. The microphase structure of the melt is changed as PLLA crystallizes at 122 degrees C (a temperature at which the PCL block is molten) forming spherulites regardless of composition, even with 32% PLLA. SAXS indicates that a lamellar structure with a different periodicity than that obtained in the melt forms (for melt segregated samples). Where PCL is the majority block, PCL crystallization at 42 degrees C following PLLA crystallization leads to rearrangement of the lamellar structure, as observed by SAXS, possibly due to local melting at the interphases between domains. POM results showed that PCL crystallizes within previously formed PLLA spherulites. WAXS data indicate that the PLLA unit cell is modified by crystallization of PCL, at least for the two majority PCL samples. The PCL minority sample did not crystallize at 42 degrees C (well below the PCL homopolymer crystallization temperature), pointing to the influence of pre-crystallization of PLLA on PCL crystallization, although it did crystallize at lower temperature. Crystallization kinetics were examined by DSC and WAXS, with good agreement in general. The crystallization rate of PLLA decreased with increase in PCL content in the copolymers. The crystallization rate of PCL decreased with increasing PLLA content. The Avrami exponents were in general depressed for both components in the block copolymers compared to the parent homopolymers. Polarized optical micrographs during isothermal crystalli zation of (a) homo-PLLA, (b) homo-PCL, (c) and (d) block copolymer after 30 min at 122 degrees C and after 15 min at 42 degrees C.

An in situ electron microscope investigation of the icosahedral-to-decagonal quasicrystalline transformation in Al-20 at.% Mn

The solid-state transformation behaviour of the icosahedral phase in rapidly solidified Al-20 at.% Mn has been investigated by in situ heating experiments in the transmission electron microscope. As-rapidly-solidified Al-20 at.% Mn consists mainly of a dendritic icosahedral phase, with a small amount of interdendritic f.c.c. agr-Al. During subsequent heat treatment at temperatures below about 500°C, the dendritic icosahedral phase grows and consumes the interdendritic agr-Al. At about 500°C the decagonal phase nucleates near icosahedral dendrite and grain boundaries and then grows into the icosahedral matrix by lateral motion of ledges 10-20 nm high across facet planes normal to the twofold symmetry axes. At about 600°C the decagonal phase transforms into a crystalline phase. The present study suggests that solid-state decomposition of the icosahedral phase is the mechanism of decagonal phase formation in as-rapidly-solidified Al-Mn alloys.

Phase transformation and semiconductor-metal transition in thin films of VO2 deposited by low-pressure metalorganic chemical vapor deposition

Thin films of the semiconducting, monoclinic vanadium dioxide, VO2(M) have been prepared on ordinary glass by two methods: directly by low-pressure metalorganic chemical vapor deposition (MOCVD), and by argon-annealing films of the VO2(B) phase deposited by MOCVD. The composition and microstructure of the films have been examined by x-ray diffraction, scanning electron microscopy, and transmission electron microscopy. Films made predominantly of either the B or the M phase, as deposited, can only be obtained over a narrow range of deposition temperatures. At the lower end of this temperature range, the as-deposited films are strongly oriented, although the substrate is glass. This can be understood from the drive to minimize surface energy. Films of the B phase have a platelet morphology, which leads to an unusual microstructure at the lower-deposition temperatures. Those grown at similar to370 degreesC convert to the metallic, rutile (R) phase when annealed at 550 degreesC, whereas those deposited at 420 degreesC transform to the R phase only at 580 degreesC. (When cooled to room temperature, the annealed films convert reversibly from the R phase to the M phase.) Electron microscopy shows that annealing leads to disintegration of the single crystalline VO2(B) platelets into small crystallites of VO2(R), although the platelet morphology is retained. When the annealing temperature is relatively low, these crystallites are nanometer sized. At a higher-annealing temperature, the transformation leads to well-connected and similarly oriented large grains of VO2(R), enveloped in the original platelet. The semiconductor-metal transition near 68 degreesC leads to a large jump in resistivity in all the VO2(M) films, nearly as large as in epitaxial films on single-crystal substrates. When the annealed films contain well-connected large grains, the transition is very sharp. Even when preferred orientation is present, the transition is not as sharp in as-deposited VO2(M), because the crystallites are not densely packed as in annealed VO2(B). However, the high degree of orientation in these films leads to a narrow temperature hysteresis. (C) 2002 American Institute of Physics.

Characterization of phase transformation behaviour and microstructural development of electroless Ni-B coating

Phase transformation behaviour of amorphous electroless Ni-B coating with a targeted composition of Ni-6wt% B is characterized in conjunction with microstructural development and hardness. Microscopic observations of the as-deposited coating display a novel microstructure which is already phase separated at multiple length scales. Spherical colonies of similar to 5 mu m consist of 2-3 mu m nodular regions which are surrounded by similar to 2-3 mu m region that contains fine bands ranging from 10 to 70 nm in width. The appearance of three crystalline phases in this binary system at different stages of heat treatment and the concomitant variation in hardness are shown to arise from nanoscale fluctuations in the as-deposited boron content from 4 to 8 wt%. High temperature annealing reveals continuous crystallization up to 430 degrees C, overlapping with the domain of B loss due to diffusion into the substrate. The implications of such a microstructure for optimal heat treatment procedures are discussed. (C) 2011 Elsevier B.V. All rights reserved.

Evolution of crystallinity of free gold agglomerates and shape transformation

We report the shape evolution of free gold agglomerates with different morphologies that transform to ellipsoidal and then to spherical shapes during the heating cycle. The shape transformation is associated with a structural transition from polycrystalline to single crystalline. The structural transition temperature is shown to be dependent on the final size of the particles and not on the initial morphologies of the agglomerates. It is also shown that the transition occurs well below the melting temperature which is in contrast with the melt-freeze process reported in the literature.

Electron microscopy of microstructural transformation in electrodeposited Ni-rich, Ag-Ni film

Ag-Ni films were electrodeposited over a Cu substrate. Structural characterization revealed a fibrous microstructure with an amorphous structure for the as-deposited film. Isothermal annealing at 400 degrees C of the film inside transmission electron microscope led to amorphous-to-crystalline transition along with the evolution of nano-sized particles in the microstructure. The crystalline phase was Ni-Ag solid solution. The relative volume fraction of the nano-sized particles increased gradually with time. There was however no detectable decomposition of solid solution phase till about 4 h of annealing. Beyond 4 h phase separation initiated and pure Ag and Ni phases formed in the film. This study provides a methodology by which microstructural engineering of as-electrodeposited amorphous Ag-Ni films can be conducted to isolate a particular microstructure in order to tap specific potentially usable functionalities. (C) 2013 Elsevier B.V. All rights reserved.

Single crystalline magnetite, maghemite, and hematite nanoparticles with rich coercivity

One-pot synthesis of amorphous iron oxide nanoparticles with two different dimensions (<5 nm and 60 nm) has been achieved using the reverse micelle method, with <5 nm nanoparticles separated from the stable colloid by exploiting their magnetic behaviour. The transformation of the as-prepared amorphous powders into Fe3O4 and Fe2O3 phases (gamma and alpha) is achieved by carrying out controlled annealing at elevated temperatures under different optimized conditions. The as-prepared samples resulting from micellar synthesis and the corresponding annealed ones are thoroughly characterized by powder X-ray diffraction, transmission electron microscopy (TEM), and by Raman and X-ray photoelectron spectroscopies. Expectedly, the magnetic characteristics of Fe3O4 and Fe2O3 phase (gamma and alpha) nanoparticles are found to have strong dependence on their phase, dimension, and morphology. The coercivity of Fe3O4 and Fe2O3 (gamma and alpha) nanoparticles is reasonably high, even though high resolution TEM studies bring out that these nanoparticles are single crystalline. This is in contrast with previous reports wherein poly-crystallinity of iron oxides nanoparticles has been regarded as a prerequisite for high coercivity.

Stable Crystalline Salts of Haloperidol: A Highly Water-Soluble Mesylate Salt

Haloperidol, an antipsychotic drug, was screened for new solid crystalline phases using high throughput crystallization in pursuit of solubility improvement. Due to the highly basic nature of the API, all the solid forms with acids were obtained in the form of salts. Eleven crystalline salts in the form of oxalate (1:1), benzoate (1:1), salicylate (1:1 and 1:2), 4-hydroxybenzoate (1:1), 4-hydroxybenzoate ethyl acetate solvate (1:1:1), 3,4-dihydroxybenzoate (1:1), 3,5-dihydroxybenzoate (1:1), mesylate (1:1), besylate (1:1), and tosylate (1:1) salt were achieved. There is an insertion of carboxylate or sulfonate anion into the hydrogen bonding pattern of haloperidol. The salts with the aliphatic carboxylic acids were found to be more prone to form salt hydrates compared with aromatic carboxylate salts. All the salts were subjected to solubility measurement in water at neutral pH. There was no direct correlation observed between the solubility of the salt and its coformer. All the salts are stable at room temperature as well as after 24 h slurry experiment except the oxalate salt, which showed an unusual phase transformation from its hydrated form to the anhydrous form. A structureproperty relationship was examined to analyze the solubility behavior of the solid forms.

A Thermodynamic Constitutive Model for Stress Induced Phase Transformation in Shape Memory Alloys

In this paper a thermodynamic constitutive model is developed for stress induced phase transformation in single crystalline and polycrystalline shape memory alloys (SMAs). Volume fractions of different martensite variants are chosen as internal variables to describe the evolution of microstructure state in the material. This model is then used in prediction the transformation behavior of a SMA (Cu-Al-Zn-Mn) under complex thermomechanical load (including complete and incomplete transformation in mechanical cycling, and proportional/non-proportional loading). (C) 2002 Elsevier Science Ltd. All rights reserved.

Reversible Resistance Switching Effect in Amorphous Ge1Sb4Te7 Thin Films without Phase Transformation

We demonstrate a reversible resistance switching effect that does not rely on amorphous-crystalline phase transformation in a nanoscale capacitor-like cell using Ge1Sb4Te7 films as the working material. The polarity and amplitude of the applied electric voltage switches the cell resistance between low- and high-resistance states, as revealed in the current-voltage characteristics of the film by conductive atomic force microscopy (CAFM). This reversible SET/RESET switching effect is induced by voltage pulses and their polarity. The change of electrical resistance due to the switching effect is approximately two orders of magnitude.