Objective: Biological and mechanical implant-abutment connection complications and failures are still present in clinical practice, frequently compromising oral function. The purpose of this study was to evaluate the reliability and failure modes of anterior single-unit restorations in internal conical interface (ICI) implants using step-stress accelerated life testing (SSALT). Materials and methods: Forty-two ICI implants were distributed in two groups (n = 21 each): group AT-OsseoSpeed™ TX (Astra Tech, Waltham, MA, USA); group SV-Duocon System Line, Morse Taper (Signo Vinces Ltda., Campo Largo, PR, Brazil). The corresponding abutments were screwed to the implants and standardized maxillary central incisor metal crowns were cemented and subjected to SSALT in water. Use-level probability Weibull curves and reliability for a mission of 50,000 cycles at 200 N were calculated. Differences between groups were assessed by Kruskal-Wallis along with Bonferroni's post-hoc tests. Polarized-light and scanning electron microscopes were used for failure analyses. Results: The Beta (β) value derived from use level probability Weibull calculation was 1.62 (1.01-2.58) for group AT and 2.56 (1.76-3.74) for group SV, indicating that fatigue was an accelerating factor for failure of both groups. The reliability for group AT was 0.95 and for group SV was 0.88. Kruskal-Wallis along with Bonferroni's post-hoc tests showed no significant difference between the groups tested (P > 0.27). In all specimens of both groups, the chief failure mode was abutment fracture at the conical joint region and screw fracture at neck's region. Conclusions: Reliability was not different between investigated ICI connections supporting maxillary incisor crowns. Failure modes were similar. © 2012 John Wiley & Sons A/S.

Comportamento mecânico e biológico de implante dentário com interface cônica interna

The general aim of this study was to evaluate the conical interface of pilar/implant. The specific aims were to evaluate the influence of hexagonal internal index in the microleakage and mechanical strength of Morse taper implants; the effect of axial loading on the deformation in cervical region of Morse taper implants of different diameters through strain gauge; the effect of axial loading in cervical deformation and sliding of abutment into the implant by tridimensional measurements; the integrity of conical interface before and after dynamic loading by microscopy and microleakage; and the stress distribution in tridimensional finite element models of Morse taper implants assembled with 2 pieces abutment. According to the obtained results, could be concluded that the diameter had influence in the cervical deformation of Morse taper implants; the presence of internal hexagonal index in the end of internal cone of implant didn´t influenced the bacterial microleakage under static loading neither reduced the mechanical strength of implants; one million cycles of vertical and off-center load had no negative influence in Morse taper implant integrity.

Long way to go: how outflows from large galaxies propagate through the hot halo gas

Using hydrodynamic simulations, we study the mass-loss due to supernova-driven outflows from Milky Way type disc galaxies, paying particular attention to the effect of the extended hot halo gas. We find that the total mass-loss at inner radii scales roughly linearly with total mass of stars formed, and that the mass loading factor at the virial radius can be several times its value at inner radii because of the swept up hot halo gas. The temperature distribution of the outflowing material in the inner region (similar to 10 kpc) is bimodal in nature, peaking at 10(5) K and 10(6.5) K, responsible for optical and X-ray emission, respectively. The contribution of cold/warm gas with temperature <= 10(5.5) K to the outflow rate within 10 kpc is approximate to 0.3-0.5. The warm mass loading factor, eta(3e5) (T <= 3 x 10(5) K) is related to the mass loading factor at the virial radius (eta(v)) as eta(v) approximate to 25 eta(3e5) (SFR/M-circle dot yr(-1))(-0.15) for a baryon fraction of 0.1 and a starburst period of 50 Myr. We also discuss the effect of multiple bursts that are separated by both short and long periods. The outflow speed at the virial radius is close to the sound speed in the hot halo, less than or similar to 200 km s(-1). We identify two `sequences' of outflowing cold gas at small scales: a fast (approximate to 500 km s(-1)) sequence, driven by the unshocked free-wind; and a slow sequence (approximate to +/- 100 km s(-1)) at the conical interface of the superwind and the hot halo.

Effect of repeated torque/mechanical loading cycles on two different abutment types in implants with internal tapered connections: an in vitro study

Internal tapered connections were developed to improve biomechanical properties and to reduce mechanical problems found in other implant connection systems. The purpose of this study was to evaluate the effects of mechanical loading and repeated insertion/removal cycles on the torque loss of abutments with internal tapered connections. Sixty-eight conical implants and 68 abutments of two types were used. They were divided into four groups: groups 1 and 3 received solid abutments, and groups 2 and 4 received two-piece abutments. In groups 1 and 2, abutments were simply installed and uninstalled; torque-in and torque-out values were measured. In groups 3 and 4, abutments were installed, mechanically loaded and uninstalled; torque-in and torque-out values were measured. Under mechanical loading, two-piece abutments were frictionally locked into the implant; thus, data of group 4 were catalogued under two subgroups (4a: torque-out value necessary to loosen the fixation screw; 4b: torque-out value necessary to remove the abutment from the implant). Ten insertion/removal cycles were performed for every implant/abutment assembly. Data were analyzed with a mixed linear model (P <= 0.05). Torque loss was higher in groups 4a and 2 (over 30% loss), followed by group 1 (10.5% loss), group 3 (5.4% loss) and group 4b (39% torque gain). All the results were significantly different. As the number of insertion/removal cycles increased, removal torques tended to be lower. It was concluded that mechanical loading increased removal torque of loaded abutments in comparison with unloaded abutments, and removal torque values tended to decrease as the number of insertion/removal cycles increased. To cite this article:Ricciardi Coppede A, de Mattos MdaGC, Rodrigues RCS, Ribeiro RF. Effect of repeated torque/mechanical loading cycles on two different abutment types in implants with internal tapered connections: an in vitro study.Clin. Oral Impl. Res. 20, 2009; 624-632.doi: 10.1111/j.1600-0501.2008.01690.x.

Analysis of drop formation at conical tips : 1. Theory

The phenomenon of drop formation at conical tips under near zero flow conditions has been investigated using a theoretical approach. The analysis permits the prediction of drop profile and drop volume, until the onset of instability. A semiempirical approach based on the similarity of drop shapes has been adopted to predict the detaching drop volumes at conical tips. The effects of base diameter of the cone, cone angle, interfacial tension, and the densities of the drop and the surrounding fluid on the maximum and detached drop volumes are predicted.

Leakage of Saliva Through the Implant-Abutment Interface: In Vitro Evaluation of Three Different Implant Connections Under Unloaded and Loaded Conditions

Purpose: Bacterial leakage along the implant-abutment interface, with consequent species harboring the inner parts of two-part dental implant systems, has been reported in the literature. The aim of this in vitro study was to evaluate bacterial leakage from human saliva to the internal part of the implants along the implant-abutment interface under loaded and unloaded conditions using DNA Checkerboard. Materials and Methods: Sixty denial implants-20 each of external-hexagon, internal-hexagon, and Morse cone-connection designs-and their conical abutments were used in this study. Each group was subdivided into two groups of 10 loaded and 10 unloaded implants. The assemblies were immersed in human saliva and either (1) loaded with 500,000 cycles at 120 N (experimental group) or (2) incubated in static conditions for 7 days at 35 degrees C (unloaded control group). Results: Microorganisms were found in the internal surfaces of all types of connections. The Morse cone connection presented the lowest count of microorganisms in both the unloaded and loaded groups. Loaded implants presented with higher counts of microorganisms than unloaded implants for external- and internal-hex connections. Conclusion: Bacterial species from human saliva may penetrate along the implant-abutment interface under both unloaded and loaded conditions for all connections evaluated. Morse cone-connection implants showed the lowest counts of microorganisms for both conditions. External- and internal-hex implants showed a higher incidence of bacteria and higher bacterial counts after simulated loading. INT J ORAL MAXILLOFAC IMPLANTS 2012;27:551-560.