Relative cognitive impairments are common along the schizophrenia spectrum reflecting potential psychopathological markers. Yet stress, a vulnerability marker in schizophrenia (including its spectrum), is likewise related to cognitive impairments. We investigated whether one such cognitive marker (attenuated functional hemispheric asymmetry) during stressful life periods might be linked to individuals' schizotypal features or rather to individuals' stress-related experiences and behaviours. A total of 58 students performed a left hemisphere dominant (lateralised lexical decisions) and right hemisphere dominant (sex decisions on composite faces) task. In order to account for individual differences in stress sensitivity we separated participants into groups of high or low cognitive reserve according to their average current marks. In addition, participants filled in questionnaires on schizotypy (short O-LIFE), perceived stress, stress response, and a newly adapted questionnaire that enquired about potential stress compensation behaviour (elevated substance use). The most important finding was that enhanced substance use and cognitive disorganisation contributed to a right and left hemisphere shift in language dominance, respectively. We discuss that (i) former reports on right hemisphere shifts in language dominance with positive schizotypy might be explained by an associated higher substance use and (ii) cognitive disorganisation relates to unstable cognitive functioning that depend on individuals' life circumstances, contributing to published reports on inconsistent laterality-schizotypy relationships.

Experimental analyses of the poly(vinyl chloride) foams' mechanical anisotropic behavior

Assessing a full set of mechanical properties is a rather complicate task in the case of foams, especially if material models must be calibrated with these results. Many issues, for example anisotropy and heterogeneity, influence the mechanical behavior. This article shows through experimental analyses how the microstructure affects different experimental setups and it also quantifies the degree of anisotropy of a poly(vinyl chloride) foam. Monotonic and cyclic experimental tests were carried out using standard compression specimens and non-standard tensile specimens. Results are complemented and compared with the aid of a digital image correlation technique and scanning electron microscopy analyses. Mechanical properties (e.g., elastic and plastic Poisson's ratios) are evaluated for compression and tensile tests, for two different material directions (normal and in-plane). The material is found to be transversely isotropic. Differences in the results of the mechanical properties can be as high as 100%, or even more depending on the technique used and the loading direction. Also, the experimental analyses show how the material's microstructure behavior, like the evolution of the herein identified yield fronts and a spring back phenomenon, can influence the phenomenological response and the failure mechanisms as well as the hardening curves. POLYM. ENG. SCI., 52:2654-2663, 2012. (C) 2012 Society of Plastics Engineers

Study of partially encased composite beams with innovative position of stud bolts

In this article, static behavior of three partially encased composite beams under flexural condition is investigated in the context of studying some alternative positions for the headed studs. Shear resistance between the I-shaped beam and the concrete was provided by headed studs in two positions: vertically welded oil the bottom flange and horizontally welded on the faces of the web. Experimental results show that the headed studs provide the composite action and increase the bending strength. The most remarkable position seems to be the headed studs vertically welded oil the bottom flange. Ail analytical method to estimate the bending capacity of the encased beams is also proposed, giving a good prediction of the experimental results (C) 2008 Elsevier Ltd. All rights reserved.

Contribution of headed studs to the composite behavior of the partially encased beams

The use of mechanical shear connectors, mainly headed stud bolts, is the most common way to achieve steel-concrete composite action. The encasement of the steel beam in the depth slab results in increase of strength and stiffness, reducing the total height of the floor. In this investigation, three partially encased composite beams were tested under flexural conditions and the main objective was to investigate some alternative positions for the headed studs. To provide longitudinal shear resistance between the I-shaped beam and the concrete, two positions of the,studs were investigated: vertically welded on the bottom flange and horizontally welded on the faces of the web. The experimental results have shown that the headed studs are effective to provide the composite action and increase the bending strength. Furthermore, the headed studs welded vertically on the bottom flange proved to be the most reliable position.

Shear strengthening of damaged reinforced concrete beams with hybrid composite plates

This paper aims to evaluate experimentally the potentialities of Hybrid Composite Plates (HCPs) technique for the shear strengthening of reinforced concrete (RC) beams that were previously subjected to intense damage in shear. HCP is a thin plate of Strain Hardening Cementitious Composite (SHCC) reinforced with Carbon Fiber Reinforced Polymer (CFRP) laminates. For this purpose, an experimental program composed of two series of beams (rectangular and T cross section) was executed to assess the strengthening efficiency of this technique. In the first step of this experimental program, the control beams, without steel stirrups, were loaded up to their shear failure, and fully unloaded. Then, these pre-damaged beams were shear strengthened by applying HCPs to their lateral faces by using a combination of epoxy adhesive and mechanical anchors. The bolts were applied with a certain torque in order to increase the concrete confinement. The obtained results showed that the increase of load carrying capacity of the damaged strengthened beams when HCPs were applied with epoxy adhesive and mechanical anchors was 2 and 2.5 times of the load carrying capacity of the corresponding reference beams (without HCPs) for the rectangular and T cross section beam series, respectively. To further explore the potentialities of the HCPs technique for the shear strengthening, the experimental tests were simulated using an advanced numerical model by a FEM-based computer program. After demonstration the good predictive performance of the numerical model, a parametric study was executed to highlight the influence of SHCC as an alternative for mortar, as well as the influence of torque level applied to the mechanical anchors, on the load carrying capacity of beams strengthened with the proposed technique.

Is the Front Line Prepared for the Changing Faces of Patients? Predictors of Cross-Cultural Preparedness Among Clinical Nurses and Resident Physicians in Lausanne, Switzerland.

UNLABELLED: Phenomenon: Assuring quality medical care for all persons requires that healthcare providers understand how sociocultural factors affect a patient's health beliefs/behaviors. Switzerland's changing demographics highlight the importance of provider cross-cultural preparedness for all patients-especially those at risk for social/health precarity. We evaluated healthcare provider cross-cultural preparedness for commonly encountered vulnerable patient profiles. APPROACH: A survey on cross-cultural care was mailed to Lausanne University hospital's "front-line healthcare providers": clinical nurses and resident physicians at our institution. Preparedness items asked "How prepared do you feel to care for ... ?" (referring to example patient profiles) on an ascending 5-point Likert scale. We examined proportions of "4 - well/5 - very well prepared" and the mean composite score for preparedness. We used linear regression to examine the adjusted effect of demographics, work context, cultural-competence training, and cross-cultural care problem awareness, on preparedness. FINDINGS: Of 885 questionnaires, 368 (41.2%) were returned: 124 (33.6%) physicians and 244 (66.4%) nurses. Mean preparedness composite was 3.30 (SD = 0.70), with the lowest proportion of healthcare providers feeling prepared for patients "whose religious beliefs affect treatment" (22%). After adjustment, working in a sensitized department (β = 0.21, p = .01), training on the history/culture of a specific group (β = 0.25, p = .03), and awareness regarding (a) a lack of practical experience caring for diverse populations (β = 0.25, p = .004) and (b) inadequate cross-cultural training (β = 0.18, p = .04) were associated with higher preparedness. Speaking French as a dominant language and physician role (vs. nurse) were negatively associated with preparedness (β = -0.26, p = .01; β = -0.22, p = .01). Insights: The state of cross-cultural care preparedness among Lausanne's front-line healthcare providers leaves room for improvement. Our study points toward institutional strategies to improve preparedness: notably, making sure departments are sensitized to cross-cultural care resources and increasing provider diversity to reflect the changing Swiss demographic.

Other-race faces : limitations of expert face recognition /

Adults' expert face recognition is limited to the kinds of faces they encounter on a daily basis (typically upright human faces of the same race). Adults process own-race faces holistically (Le., as a gestalt) and are exquisitely sensitive to small differences among faces in the spacing of features, the shape of individual features and the outline or contour of the face (Maurer, Le Grand, & Mondloch, 2002), however this expertise does not seem to extend to faces from other races. The goal of the current study was to investigate the extent to which the mechanisms that underlie expert face processing of own-race faces extend to other-race faces. Participants from rural Pennsylvania that had minimal exposure to other-race faces were tested on a battery of tasks. They were tested on a memory task, two measures of holistic processing (the composite task and the part/whole task), two measures of spatial and featural processing (the JanelLing task and the scrambledlblurred faces task) and a test of contour processing (JanelLing task) for both own-and other-race faces. No study to date has tested the same participants on all of these tasks. Participants had minimal experience with other-race faces; they had no Chinese family members, friends or had ever traveled to an Asian country. Results from the memory task did not reveal an other-race effect. In the present study, participants also demonstrated holistic processing of both own- and other-race faces on both the composite task and the part/whole task. These findings contradict previous findings that Caucasian adults process own-race faces more holistically than other-race faces. However participants did demonstrate an own-race advantage for processing the spacing among features, consistent with two recent studies that used different manipulations of spacing cues (Hayward et al. 2007; Rhodes et al. 2006). They also demonstrated an other-race effect for the processing of individual features for the Jane/Ling task (a direct measure of featural processing) consistent with previous findings (Rhodes, Hayward, & Winkler, 2006), but not for the scrambled faces task (an indirect measure offeatural processing). There was no own-race advantage for contour processing. Thus, these results lead to the conclusion that individuals may show less sensitivity to the appearance of individual features and the spacing among them in other-race faces, despite processing other-race faces holistically.

Influence of surface sealants on microleakage of composite resin restorations

Purpose: The purpose of this study was to verify the influence of surface sealants and dentin adhesive systems on the microleakage of composite restorations. Methods: Class V cavities were made on the buccal faces of 100 permanent third molars and restored with Z250. After 24 hours, they were submitted to polishing and finishing processes. The teeth were divided into groups according to the sealant agent: group 1 - Single Bond; group 2 - Opti Bond Solo Plus; group 3 - Fortify; group 4 - Fortify Plus; and group 5 - control without sealant. The analysis of immediate microleakage was performed in 10 restorations from each group, soon after the sealing. The other 10 specimens from each group were submitted to tooth-brushing and thermal cycles. The teeth were isolated and immersed in 2% methylene blue solution, washed in tap water, and sectioned in the buccolingual direction. The percentage of marginal leakage was calculated using an image analysis program, and results were submitted to analysis of variance and Tukey's test. Results: All the sealed groups demonstrated lower microleakage values compared to the control group. Group 3, sealed with Fortify, presented the lowest mean microleakage values. Conclusion: The application of surface sealants effectively decreased the microleakage in composite resin restorations.

Advanced Non-Destructive Inspections focused on composite materials application for the automotive and marine sectors

The goal of this master thesis is to explain in detail the application of Non-Destructive-Inspection on the Automotive and the Marine sectors. Nowadays, these two particular industries faces many challenges, including increased global competition, the need for higher performance, a reduction in costs and tighter environmental and safety requirements. The materials used for these applications play key roles in overcoming these challenges. So, also an NDI procedure need to be planned in order to avoid problems during the manufacturing process and the after sale life of the structures. The entire thesis work has been done in collaboration with Vetorix Engineering.

Effect Of Composite Containing An Iodonium Salt On The Bond Strength Of Brackets To Bovine Enamel.

This study investigated the effect of the incorporation of an iodonium salt in experimental composites, on the bond strength of metallic brackets bonded to bovine teeth. Two hundred and seventy bovine teeth were embedded in self-curing acrylic resin and divided into 18 groups (n=15), according to the experimental composite with an iodonium salt at molar concentrations 0 (control), 0.5, or 1%; the light-activation times (8, 20 and 40 s); and the storage times (10 min or 24 h). Metallic brackets were fixed on the tooth surface using experimental composites. Photoactivation was performed with a quartz-tungsten-halogen light-curing unit curing unit for 8, 20 and 40 s. The specimens were stored in distilled water at 37 °C for 10 min or 24 h and submitted to bond strength test at 0.5 mm/min. The data were subjected to three-way ANOVA and Tukey's test (α=0.05). The Adhesive Remnant Index (ARI) was used to classify the failure modes. The shear bond strengths (MPa) at 10 min for light-activation times of 8, 20 and 40 s were: G1 - 4.6, 6.9 and 7.1; G2 - 8.1, 9.2 and 9.9; G3 - 9.1, 10.4 and 10.7; and at 24 h were: G1 - 10.9, 11.1 and 11.7; G2 - 11.8, 12.7 and 14.2; G3 - 12.1, 14.4 and 15.8. There was a predominance of ARI score 3 for groups with 10 min storage time, and ARI score 2 for groups with 24 h storage time. In conclusion, the addition of iodonium salt (C05 and C1) to the experimental composite may increase the bond strength of brackets to bovine enamel using reduced light exposure times.

Influence Of Successive Light-activation On Degree Of Conversion And Knoop Hardness Of The First Layered Composite Increment.

To evaluate the influence of light-activation of second, third and fourth increments on degree of conversion (DC) and microhardness (KHN) of the top (T) and bottom (B) surface of the first increment. Forty samples (n = 5) were prepared. In groups 1-4, after each increment light-activation (multiple irradiation), T and B of the first increment were measured in DC and KHN. In groups 5-8, only the first increment was made (single irradiation) and measurements of DC and KHN were taken at 15 min intervals. The light-activation modes were (XL) 500 mW/cm(2) × 38 s (G1/G5); (S) 1000 mW/cm(2) × 19 s (G2/G6), (HP) 1400 mW/cm(2) × 14 s (G3/G7); (PE) 3200 mW/cm(2) × 6 s (G4/G8). Data for DC and KHN were analyzed separately by using PROC MIXED for repeated measures and Tukey-Kramer test (α = 0.05). For KHN, B showed lower values than T. PE resulted in lower values of KHN in B surface. For single and multiple irradiations, T and B of first measurement showed the lowest KHN and the fourth measurement showed the highest, with significant difference between them. For single irradiation, first and second increments presented similar KHN, different from the third and fourth increment, which did not differ between them. For multiple irradiations, the second light-activation resulted in KHN similar to first, third and fourth increments. For DC, except QTH, T presented higher DC than B. The light-activation of successive increments was not able to influence the KHN and DC of the first increment.

Fracture resistance of weakened roots restored with composite resin and glass fiber post

This study evaluated the fracture resistance of weakened roots restored with glass fiber posts, composite resin cores and complete metal crowns. Thirty maxillary canines were randomly divided into 3 groups of 10 teeth each: teeth without weakened roots (control); teeth with partially weakened roots (PWR) and teeth with and largely weakened roots (LWR). The control group was restored with glass fiber posts and a composite resin core. Teeth in the PWR and LWR groups were flared internally to standardized dimensions in order to simulate root weakness. Thereafter, the roots were partially filled with composite resin and restored in the same way as in the control group. The specimens were exposed to 250,000 cycles in a controlled chewing simulator. All intact specimens were subjected to a static load (N) in a universal testing machine at 45 degrees to the long axis of the tooth until failure. Data were analyzed by one-way ANOVA and Dunnett's test for multiple comparisons (p=0.05). There were statistically significant difference differences (p<0.01) among the groups (control group = 566.73 N; PWR = 409.64 N; and LWR = 410.91 N), with significantly higher fracture strength for the control group. There was no statistically significant difference (p>0.05) between the weakened groups. The results of this study showed that thicker root dentin walls significantly increase the fracture resistance of endodontically treated teeth.

Effects of light-curing time on the cytotoxicity of a restorative composite resin on odontoblast-like cells

This in vitro study evaluated the cytotoxicity of an experimental restorative composite resin subjected to different light-curing regimens. METHODS: Forty round-shaped specimens were prepared and randomly assigned to four experimental groups (n=10), as follows: in Group 1, no light-curing; in Groups 2, 3 and 4, the composite resin specimens were light-cured for 20, 40 or 60 s, respectively. In Group 5, filter paper discs soaked in 5 µL PBS were used as negative controls. The resin specimens and paper discs were placed in wells of 24-well plates in which the odontoblast-like cells MDPC-23 (30,000 cells/cm²) were plated and incubated in a humidified incubator with 5% CO2 and 95% air at 37ºC for 72 h. The cytotoxicity was evaluated by the cell metabolism (MTT assay) and cell morphology (SEM). The data were analyzed statistically by Kruskal-Wallis and Mann-Whitney tests (p<0.05). RESULTS: In G1, cell metabolism decreased by 86.2%, indicating a severe cytotoxicity of the non-light-cured composite resin. On the other hand, cell metabolism decreased by only 13.3% and 13.5% in G2 and G3, respectively. No cytotoxic effects were observed in G4 and G5. In G1, only a few round-shaped cells with short processes on their cytoplasmic membrane were observed. In the other experimental groups as well as in control group, a number of spindle-shaped cells with long cytoplasmic processes were found. CONCLUSION: Regardless of the photoactivation time used in the present investigation, the experimental composite resin presented mild to no toxic effects to the odontoblast-like MDPC-23 cells. However, intense cytotoxic effects occurred when no light-curing was performed.

Effect of deproteinization and tubular occlusion on microtensile bond strength and marginal microleakage of resin composite restorations

Dentin adhesion procedure presents limitations, especially regarding to lifetime stability of formed hybrid layer. Alternative procedures have been studied in order to improve adhesion to dentin. OBJECTIVE: The aim of this study was to evaluate in vitro the influence of deproteinization or dentin tubular occlusion, as well as the combination of both techniques, on microtensile bond strength (µTBS) and marginal microleakage of composite resin restorations. MATERIAL AND METHODS: Extracted erupted human third molars were randomly divided into 4 groups. Dentin surfaces were treated with one of the following procedures: (A) 35% phosphoric acid gel (PA) + adhesive system (AS); (B) PA + 10% NaOCl + AS; (C) PA + oxalate + AS and (D) PA + oxalate + 10% NaOCl + AS. Bond strength data were analyzed statistically by two-way ANOVA and Tukey's test. The microleakage scores were analyzed using Kruskal-Wallis and Mann-Whitney non-parametric tests. Significance level was set at 0.05 for all analyses. RESULTS: µTBS data presented statistically lower values for groups D and B, ranking data as A>C>B>D. The use of oxalic acid resulted in microleakage reduction along the tooth/restoration interface, being significant when used alone. On the other hand, the use of 10% NaOCl alone or in combination with oxalic acid, resulted in increased microleakage. CONCLUSIONS: Dentin deproteinization with 10% NaOCl or in combination with oxalate significantly compromised both the adhesive bond strength and the microleakage at interface. Tubular occlusion prior to adhesive system application seems to be a useful technique to reduce marginal microleakage.

Abrasion wear resistance of different artificial teeth opposed to metal and composite antagonists

One of the most important properties of artificial teeth is the abrasion wear resistance, which is determinant in the maintenance of the rehabilitation's occlusal pattern. OBJECTIVES: This in vitro study aims to evaluate the abrasion wear resistance of 7 brands of artificial teeth opposed to two types of antagonists. MATERIAL AND METHODS: Seven groups were prepared with 12 specimens each (BIOLUX & BL, TRILUX & TR, BLUE DENT & BD, BIOCLER & BC, POSTARIS & PO, ORTHOSIT & OR, GNATHOSTAR & GN), opposed to metallic (M & nickel-chromium alloy), and to composite antagonists (C & Solidex indirect composite). A mechanical loading device was used (240 cycles/min, 4 Hz speed, 10 mm antagonist course). Initial and final contours of each specimen were registered with aid of a profile projector (20x magnification). The linear difference between the two profiles was measured and the registered values were subjected to ANOVA and Tukey's test. RESULTS: Regarding the antagonists, only OR (M = 10.45 ± 1.42 µm and C = 2.77 ± 0.69 µm) and BC (M = 6.70 ± 1.37 µm and C = 4.48 ± 0.80 µm) presented statistically significant differences (p < 0.05). Best results were obtained with PO (C = 2.33 ± 0.91 µm and M = 1.78 ± 0.42 µm), followed by BL (C = 3.70 ± 1.32 µm and M = 3.70 ± 0.61 µm), statistically similar for both antagonists (p>0.05). Greater result variance was obtained with OR, which presented the worse results opposed to Ni-Cr (10.45 ± 1.42 µm), and results similar to the best ones against composite (2.77 ± 0.69 µm). CONCLUSIONS: Within the limitations of this study, it may be concluded that the antagonist material is a factor of major importance to be considered in the choice of the artificial teeth to be used in the prosthesis.