Magnetic behavior of basic iron(III) compounds. I. Magnetic behavior of the basic iron sulphates and basic iron chromate. II. Magnetic behavior of delta ferric oxide hydroxide

I. The thermomagnetic behavior and infrared spectroscopic features of KFe₃(SO₄)₂(OH)₆ (jarosite), (H₃O)Fe₃(SO₄)₂ (OH)₆ (hydronium jarosite), KFe₃(CrO₄)₂ (OH)₆, Fe(OH)SO₄ (basic iron sulfate), and Fe(OH)CrO₄ (basic iron chromate) are reported. Fe(OH)CrO₄ and KFe₃(CrO₄)₂ (OH)₆ are shown to be weak ferro magnets with Curie temperatures of 73 and 71 °K, respectively. This unusual magnetic behavior is rationalized in terms of the ionic spin configurations of the phases. Exchange coupling through chromate bridging groups is shown to be weak.

II. The magnetic behavior and the influence of preparative history on the magnetic behavior of δFeO(OH) is reported. δFeO(OH) is shown to be a fine-particulate, uniaxial, magnetic species. Magnetization data for this species are shown to be consistent with the existence of magnetically inactive layers surrounding magnetic particles.

Chromate replacement in coatings for corrosion protection of aerospace aluminium alloys

Mixed rare earth organophosphates have been investigated as potential corrosion inhibitors for AA2024-T3 with the aim of replacing chromate-based technologies. Cerium diphenyl phosphate (Ce(dpp) 3) and mischmetal diphenyl phosphate (Mm(dpp) 3) were added to epoxy coatings applied to AA2024-T3 panels and they were effective in reducing the amount and rate of filiform corrosion in high humidity conditions. Ce(dpp) 3 was the most effective and characterisation of the coating formulations showed approximately a factor of 5 reduction in both the number of corrosion filaments initiated as well as the length of these. Mm(dpp) 3 appeared to reduce the corrosion growth rate by a factor of 2 although it was the more effective inhibitor in solution studies. Spectroscopic characterisation of the coatings indicated that the cerium based inhibitor may disrupt network formation in the epoxy thus resulting in a coating that absorbed more water and allowed greater solubilisation of the corrosion inhibiting compound.

The effect of chromate on the pitting susceptibility of AA7075-T651 studied using potentiostatic transients

The effect of chromate on metastable pitting of AA7075-T651 as determined via potentiostatic polarisation is reported. A systematic study of metastable pitting and its correlation with stable pits was conducted in various concentrations of sodium chromate (Na2CrO4), revealing the metastable pitting rate was able to provide a quantitative metric for pitting corrosion. The size and number of metastable pits decreased significantly in the presence of chromate. The present study is intended as a general baseline for the assessment of future chromate replacement technologies, as elaborated herein. © 2014 Elsevier Ltd.

Influence of chromate, molybdate and tungstate on pit formation in chloride medium

It has been characterized and evaluated the 2024-T351 and 7050-T7451 aluminum alloys pitting corrosion in naturally aerated chloride aqueous solutions containing chromate, molybdate and tungstate. It has been carried out electrochemical and non-electrochemical immersion corrosion tests accompanied by surface metallography analysis using an optical microscopy. Chromate for the two alloys and in molybdate for 7050 has corrosion inhibiting effects, whereas tungstate promotes the pitting corrosion for these alloys. Quantitative surface analysis upon the alloys after immersion has indicated that pits are predominantly conical or quasi-conical and irregular. In general, pits have been wider than deep and the widest have been also the deepest. Despite inhibitor presence, when pits have been nucleated, they grow with the same intensity. © 2005 Elsevier B.V. All rights reserved.

The Staining Effect of the Hydrochloric Acid-Chromate Trioxide Solution on the Minerals of the Chalcocite-Stibnite-Galena Ternary System.

The object of this work has been to devise a method by which the different phases in the chalcocite-stibnite-galena ternary system may be identified. As the mineralogists have no precise methods for the identification of these phases, a hydrochloric acid-chromate trioxide staining solution was employed.

The Extraction of Chromate Salts from Montana Chromite

In this thesis I have tried to determine the suit­able temperature, time and the amount of soda ash and lime needed for the calcining process. The leaching and purification tests were studied experimentally. The earlier process for making chromate from chromite was not the same as is used today. There­fore I have found it useful to put into this thesis the newest method for making chromate salts and their important uses.

Sorption of chromate by Dowex 1 /

A laboratory investigation was made to explore the use of Dowex 1 for the removal of chromate ion from neutral solution. It was found that chromate ion is sorbed by Dowex 1 under a variety of conditions.