Thermoluminescence characteristics of rare-earth-doped LiCaBO3 phosphor

LiCaBO3 was synthesized by high-temperature solid-state reaction. The influence of different rare earth dopants, i.e. Dy3+, Tb3+. TM3+ and Ce3+, on thermoluminescence (TL) of LiCaBO3 phosphor was discussed. We studied the TL properties and some dosimetric characteristics of Ce3+-activated LiCaBO3 phosphor in detail. The effect of the concentration of Ce3+ on TL was investigated, the result of which showed that the optimum Ce3+ concentration was 1 mol%. The TL kinetic parameters of LiCaBO3:0.01 Ce3+ were studied by computer glow curve deconvolution (CGCD) method.

Synthesis, photoluminescence, thermoluminescence and dosimetry properties of novel phosphor KSr4(BO3)(3):Ce

Polycrystalline powder sample of KSr4(BO3)(3) was synthesized by high-temperature solid-state reaction. The influence of different rare earth dopants, i.e. Tb3+, TM3+ and Ce3+, on thermoluminescence (TL) of KSr4(BO3)(3) Phosphor was discussed. The TL, photoluminescence (PL) and some dosimetric properties of Ce3+-activated KSr4(BO3)(3) phosphor were studied. The effect of the concentration of Ce3+ on TL intensity was investigated and the result showed that the optimum Ce3+ concentration was 0.2 mol%. The TL kinetic parameters of KSr4(BO3)(3):0.002 Ce3+ phosphor were calculated by computer glow curve deconvolution (CGCD) method. Characteristic emission peaking at about 407 and 383 nm due to the 4f(0)5d(1) -> F-2((5/2),(7/2)) transitions of Ce3+ ion were observed both in PL and three-dimensional (3D) TL spectra. The dose-response of KSr4(BO3)(3):0.002 Ce3+ to gamma-ray was linear in the range from 1 to 1000 mGy. In addition, the decay of the TL intensity of KSr4(BO3)(3):0.002 Ce3+ was also investigated.

Thermoluminescence properties of natural zoisite mineral under gamma-irradiations and high temperature annealing

Natural silicate mineral of zoisite, Ca(2)Al(3)(SiO(4))(Si(2)O(7))O(OH), has been investigated concerning gamma-radiation, UV-radiation and high temperature annealing effects on thermoluminescence (TL). X-ray diffraction (XRD) measurement confirmed zoisite structure and X-ray fluorescence (XRF) analysis revealed besides Si, Al and Ca that are the main crystal components, other oxides of Fe, Mg, Cr, Na, K, Sr, Ti, Ba and Mn which are present in more than 0.05 wt%. The TL glow curve of natural sample contains (130-150), (340-370) and (435-475)degrees C peaks. Their shapes indicated a possibility that they are result of composition of two or more peaks strongly superposed, a fact confirmed by deconvolution method. Once pre-annealed at 600 degrees C for 1 h, the shape of the glow curves change and the zoisite acquires high sensitivity. Several peaks between 100 and 400 degrees C appear superposed, and the high temperature peak around 435 degrees C cannot be seen. The ultraviolet radiation, on the other hand, produces one TL peak around 130 degrees C and the second one around 200 degrees C and no more. (C) 2010 Elsevier B.V. All rights reserved.

Thermoluminescence, infrared reflectivity and electron paramagnetic resonance properties of hemimorphite

Silicate mineral hemimorphite has been investigated concerning its TL, IR and EPR properties. A broad TL peak around 180 degrees C and a weaker and narrower peak around 360 degrees C were found in a sample annealed at 600 degrees C for I h and then irradiated. The deconvolution using the CGCD method revealed peaks around 132, 169, 222 and 367 degrees C. The reflectivity measurements showed several bands in the NIR region due to H(2)O, OH and Al-OH complexes. No band was observed in the visible region. The thermal treatments were carried out from similar to 110 to 940 degrees C and dehydration was observed, first causing a diminishing optical absorption in general and the disappearance of water and hydroxyl absorption bands. The EPR spectrum of natural hemimorphite, presented Cu(2+) signals at g = 2.4 and g = 2.1 plus E(1)` signal superposed to Fe(3+) signal around g = 2.0. (C) 2008 Elsevier Ltd. All rights reserved.