Effect of combined bending strain and thermal cycling on the voltage-current characteristic curves of Bi-2223 tapes

High critical temperature superconductors are evolving from a scientific research subject into large-scale application devices. In order to meet this development demand they must withstand high current capacity under mechanical loads arising from thermal contraction during cooling from room temperature down to operating temperature (usually 77 K) and due to the electromagnetic forces generated by the current and the induced magnetic field. Among the HTS materials, the Bi2Sr2Ca2Cu3Ox, compound imbedded in an Ag/AgMg sheath has shown the best results in terms of critical current at 77 K and tolerance against mechanical strain. Aiming to evaluate the influence of thermal stress induced by a number of thermal shock cycles we have evaluated the V-I characteristic curves of samples mounted onto semicircular holders with different curvature radius (9.75 to 44.5 mm). The most deformed sample (epsilon = 1.08%) showed the largest reduction of critical current (40%) compared to the undeformed sample and the highest sensitivity to thermal stress (I-c/I-c0 = 0.5). The V-I characteristic curves were also fitted by a potential curve displaying n-exponents varying from 20 down to 10 between the initial and last thermal shock cycle.

Effect of mechanical loading on the I-c degradation behavior of Bi-2223 tapes

During the winding process of HTS coils the tapes of Bi-2223 are subjected to the influence of bending strain, axial strain, compressive force and torsional deformation resulting in I-c degradation. In the literature the effects of the individual strain components are separately analyzed in spite of during coil winding and energizing the strain-stress effects are combined. In this work using commercial tapes of Bi-2223 Ag/AgMg with and without stainless steel reinforcement several samples were wound on cylindrical FRP G-10 holder in which different combined strains are applied. Measurements of I - V characteristic curves are done to determine the degree of critical current degradation and the operational limits. The results are compared with the I, values of short samples and other specimens subjected to deformation generated by loading types such as tensile and bending strain.

Critical current degradation of Bi-2223 composite tapes induced by cyclic deformation and fatigue-related effects

Application of high temperature superconductor Bi2Sr2Ca2Cu3Ox. (Bi-2223) compound embedded in an Ag matrix requires the knowledge of critical current as a function of mechanical properties. Commercial tapes available in different types have been developed in industrial production scale in which a combination of small diameter filaments, long tape lengths and a ductile matrix results in a conductor with low crack formation and good tolerance against strain. The measurement of critical current and the evaluation of n-index from V-I characteristic curves of Bi-2223/Ag composite tapes subjected to an initial bending strain as a function of number of thermal cycles were done for two types of Bi-2223/Ag composite tapes: with and without steel tape reinforcement. The results showed that tapes with reinforcement presented small critical current degradation as a function of the number of thermal cycles whereas tapes without reinforcement exhibited steadily critical current degradation caused by the propagation of cracks. The n-index followed the same critical current behavior.

Anisotropic AC Behavior of Multifilamentary Bi-2223/Ag Tapes

In this communication, we report on the anisotropy of the superconducting properties of multifilamentary Bi-based tapes experimentally investigated by AC magnetic susceptibility measurements. The susceptibility $\chi= \chi' - j \chi''$ was measured using a commercial system and a couple of orthogonal pick-up coils. The $\chi''$ vs. temperature curves were shown to exhibit two peaks. The smaller of the peaks, occurring near T = 72K, was only visible for particular field directions and within a given frequency window. Such results point out the role played by the phase difference between the applied magnetic field and the internal magnetic field seen by the filaments.

Intergranular and intragranular properties of superconducting multifilamentary Bi 2223 Ag tapes : comparison of electrical transport and magnetic measurement methods

Several experimental techniques have been used in order to characterize the properties of multifilamentary Bi-2223 / Ag tapes. Pristine samples were investigated by electrical resistivity, current-voltage characteristics and DC magnetic moment measurements. Much emphasis is placed on comparing transport (direct) and magnetic (indirect) methods for determining the critical current density as well as the irreversibility line and resolving usual lacks of consistency due to the difference in measurement techniques and data analysis. The effect of an applied magnetic field, with various strengths and directions, is also studied and discussed. Next, the same combination of experiments was performed on bent tapes in order to bring out relevant information regarding the intergranular coupling. A modified Brandt model taking into account different types of defects within the superconducting filaments is proposed to reconciliate magnetic and transport data.

Intragranular and intergranular behaviour of multifilamentary Bi-2223/Ag tapes

This communication aims at reporting the superconducting properties of Bi-2223/Ag tapes determined by using various measuring techniques. First, the original samples have been characterized by electrical resistance, AC susceptibility, and DC magnetization. The transport (intergranular) critical current vs. magnetic field was also determined at T = 77 K using pulsed currents up to 40 A. Next, the same combination of experiments was performed on bent tapes in order to bring out relevant information concerning the strength of the intergranular coupling. The results show that intergranular and intragranular currents differ by at least one order of magnitude. Finally, additional magnetic measurements were carried out in order to determine the anisotropy ratio Jc ab/Jc c, which was found to lie around 30. © 2002 Elsevier Science B.V. All rights reserved.

Bi-2223 precursor billets for pit wire production

High temperature superconductor precursor billets (feed rods) have been developed for loading into silver tubes. The billets are loaded prior to rolling or drawing operations in PIT wire manufacture. Investigations have shown that wires and tapes prepared from feed rod loaded tubes show enhanced uniformity of electrical transport properties when compared with conventional powder packing, especially in wires drawn to long lengths. Analysis on production feed rods have shown carbon content to be as low as 110 ppm. © 1999 IEEE.

V、Nb、Ta对促进Bi系超导体中2223相生成作用研究

自发现BiSrCaCuO超导体以来,为了稳定2223高T_C相结构、增加其在超导体中的含量,在该体系中引入掺杂元素Pb被公认是最有效的方法。我们系统研究了V~(5+)、Nb~(5+)、Ta~(5+)高价离子的单独掺入Bi系中对

Nb(Ba)加强Bi系中2223相生成作用研究

固相法合成系列名义组成为Bi_(2-x)Nb_xSr_2Ca_2Cu_3Oy(x=0—1.0)的样品,电学和磁学测量表明,当掺入x=0.2—0.3的Nb有明显加强2223相生成的作用,配比为Bi_(1.7)Nb_(0.3)Sr_2Ca_2Cu_3Oy时最佳;当掺Ba以部分取代Sr后有明显协同Nb促进22 23相生成的作用,比单掺Nb效果更为显著,其中以Bi_(1.7)Nb_(0.3)Sr_(1.8)Ba_(0.2)Ca_2Cu_3Oy为最优组成。热重分析(TGA)实验显示,掺Nb(Ba)后样品在～600°C出现吸氧增重;XPS中的O_(1s)峰显示掺Nb(Ba)后除～531eV的主峰外,在～529eV的肩峰更加明显;讨论了Nb(Ba)对晶体结构的可能影响。

Monofilamentary Ag/Bi:2212 tapes - Effects of silver powder addition

The Bi-Sr-Ca-Cu-O system has been one of the most studied superconducting ceramic materials for industry applications. The most of the studies with this aim are on silver/ceramic composites, due to the benefits and great compatibility of this metal with the oxide. Tapes made by the powder in tube (PIT) method have been successfully tested in pilot power plants in many countries but in Brazil. In this paper, 5, 10, and 20-wt% silver powders are introduced to compose the core of the tape along with the Bi:2212 ceramic powder. The results of electrical experiments are compared with those made with no silver addition Ag tapes. The best current density, at 60 K and no applied magnetic field, was found for the 10-wt% silver proportion, doubling the value obtained for the tape with no silver in the core.

The changes on microstructure and electrical properties of Bi:2223/Ag composite as a function of the granulation and the content of the added silver powder

The Bi-Sr-Ca-Cu-O system has been one of the most studied superconducting ceramic materials for industry applications. The most of the studies with this aim are on silver/ceramic composites, due to the benefits and great compatibility of this metal with the oxide. In this paper we describe a systematic and comparative study on Ag/BSCCO composite, made by the citrate route, in which the ceramic pellets are sintered in the presence of silver powder using several proportions and having several granulations. It was observed that the introduction of fine (0.5 and 2 μm) silver powder in the proportions of 5 wt. % always implies in a better critical current density compared to the no silver pellet. According to the results, the silver powder in excess of 5 wt.% may not promote best electrical properties, depending on the size of the silver particles.

Consolidation of Bi-2223 superconducting powders by spark plasma sintering

The spark plasma sintering (SPS) technique, by using a compacting pressure of 50 MPa, was used to consolidate pre-reacted powders of Bi1.65Pb0.35Sr2Ca2Cu3O10+delta (Bi-2223). The influence of the consolidation temperature, T-D, on the structural and electrical properties has been investigated and compared with those of a reference sample synthesized by the traditional solid-state reaction method and subjected to the same compacting pressure. From the X-ray diffraction patterns, performed in both powder and pellet samples, we have found that the dominant phase is the Bi-2223 in all samples but traces of the Bi2Sr2CaCu2O8+x (Bi-2212) were identified. Their relative density were similar to 85% of the theoretical density and the temperature dependence of the electrical resistivity, rho(T), indicated that increasing T-D results in samples with low oxygen content because the SPS is performed in vacuum. Features of the rho(T) data, as the occurrence of normal-state semiconductor-like behavior of rho(T) and the double resistive superconducting transition, are consistent with samples comprised of grains with shell-core morphology in which the shell is oxygen deficient. The SPS samples also exhibited superconducting critical current density at 77 K, J(c)(77K), between 2 and 10A/cm(2), values much smaller than similar to 22A/cm(2) measured in the reference sample. Reoxygenation of the SPS samples, post-annealed in air at different temperatures and times, was found to improve their microstructural and transport properties. Besides the suppression of the Bragg peaks belonging to the Bi-2212 phase, the superconducting properties of the post-annealed samples and particularly J(c)(77K) were comparable or better than those corresponding to the reference sample. Post-annealed samples at 750 degrees C for 5min exhibited J(c)(77K) similar to 130A/cm(2) even when uniaxially pressed at only 50 MPa. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4768257]

An investigation on the effects of Ag addition in the powder — in tube processing of long multifilamentary (Bi,Pb) - 2223/Ag superconducting tapes

It is important that long superconducting tape must have desired strain tolerance (less reduction of Jc with applied strains) and stress tolerance (less reduction of JC in applied stresses) for its use as coils and magnets. Ag addition to the BPSCCO system has many advantages with its physical and chemical inertness to the system, reduces the processing temperature, and promotes the grain growth, grain alignment and connectivity. All these not only enhance the critical current density of the tapes but also improve the mechanical properties. But the published results show very much scattering on the type of Ag additive to be selected, method of addition and its optimum percentage. Also there are some negative reports in this regard. The present work has been undertaken to study the effect of silver addition in different forms (Ag powder, Ag2O, AgNO3) on the superconducting and mechanical properties of (Bi,Pb)-2223/Ag tapes and to find out a suitable form of Ag additive and its optimum percentage to have better superconducting and mechanical properties. Also it is the aim of the present work is to optimise the process parameters needed to prepare (Bi,Pb)-2223/Ag multifilamentary tapes of length ~ 12 m in solenoid and pancake coil forms with good critical current density and homogeneity of J C along the length of the tapes.

Studies On Preparation And Characterization Of Hts Current Leads Using Multifilamentary Ag And Ag-Alloy Sheathed (Bi,Pb)-2223 Superconducting Tapes

The application vistas of superconductors have widened very much since the discovery of high TC superconductors (HTS) as many of the applications can be realised at 77 K rather than going down to 4.2 K, the liquid He temperature. One such application is the HTS current lead which is used to connect a superconducting system with a room temperature power source. Minimising heat leak to the cryogenic environment is the main advantage of introducing current leads into superconducting systems. The properties of HTSS likes zero resistance (avoiding joule heating) and very low thermal conductivity (minimized conductive heat transfer) make them ideal candidates to be used as current leads. There are two forms of HTS current leads. (i) bulk form (tube or rod) prepared either from YBCO or BSCCO and (ii) tape form prepared from Bi-2223 multifilamentary tapes. The tape form of current leads has many advantages with respect to the mechanical and thermal stability related criteria. Crucial information on various aspects of HTS current lead development are not available in the literature as those are kept proprietary by various companies around the world. The present work has been undertaken to tailor the properties of multifilamentary tapes for the current lead application and to optimise the processing parameters of the same for enhanced critical current density and field tolerance. Also it is the aim of the present investigation is to prepare prototype current leads engineered for operation in conduction cooled mode and test them for operational stability