Effect of equal channel angular extrusion on wear and corrosion behavior of the orthopedic Ti-13Nb-13Zr alloy in simulated body fluid

We report investigations on the texture, corrosion and wear behavior of ultra-fine grained (UFG) Ti-13Nb-Zr alloy, processed by equal channel angular extrusion (ECAE) technique, for biomedical applications. The microstructure obtained was characterized by X-ray line profile analysis, scanning electron microscope (SEM) and electron back scattered diffraction (EBSD). We focus on the corrosion resistance and the fretting behavior, the main considerations for such biomaterials, in simulated body fluid. To this end. potentiodynamic polarization tests were carried out to evaluate the corrosion behavior of the UFG alloy in Hanks solution at 37 degrees C. The fretting wear behavior was carried out against bearing steel in the same conditions. The roughness of the samples was also measured to examine the effect of topography on the wear behavior of the samples. Our results showed that the ECAE process increases noticeably the performance of the alloy as orthopedic implant. Although no significant difference was observed in the fretting wear behavior, the corrosion resistance of the UFG alloy was found to be higher than the non-treated material. (c) 2012 Elsevier B.V. All rights reserved.

Effect of surface roughness of Ti, Zr, and TiZr on apatite precipitation from simulated body fluid

Some of the critical properties for a successful orthopedic or dental implant material are its biocompatibility and bioactivity. Pure titanium (Ti) and zirconium (Zr) are widely accepted as biocompatible metals, due to their non-toxicity. While the bioactivity of Ti and some Ti alloys has been extensively investigated, there is still insufficient data for Zr and titanium-zirconium (TiZr) alloys. In the present study, the bioactivity, that is, the apatite forming ability on the alkali and heat treated surfaces of Ti, Zr, and TiZr alloy in simulated body fluid (SBF), was studied. In particular, the effect of the surface roughness characteristics on the bioactivity was evaluated for the first time. The results indicate that the pretreated Ti, Zr and TiZr alloy could form apatite coating on their surfaces. It should be noted that the surface roughness also critically affected the bioactivity of these pretreated metallic samples. A surface morphology with an average roughness of approximately 0.6 microm led to the fastest apatite formation on the metal surfaces. This apatite layer on the metal surface is expected to bond to the surrounding bones directly after implantation.

Analysis of the bioactive surface of Ti-35Nb-7Zr alloy after alkaline treatment and solution body fluid

The purpose of this work was to evaluate the Ti-35Nb-7Zr experimental alloy after surface treatment and soaking in solution body fluid (SBF) to form bonelike apatite. The Ti-35Nb-7Zr alloy was produced from commercially pure materials (Ti, Nb and Zr) by an arc melting furnace. All ingots were submitted to sequences of heat treatment (1100 °C/2 h and water quenching), cold working by swaging procedures and heat treatment (1100 °C/2 h and water quenching). Discs with 13 mm diameter and 3 mm in thickness were cut. The samples were immersed in NaOH aqueous solution with 5 M at 60 °C for 72 h, washed with distilled water and dried at 40 °C for 24 h. After the alkaline treatment, samples were heat treated in both conditions: at 450 and 600 °C for 1 h in an electrical furnace in air. Then, they were soaking in SBF for 24 h to form an apatite layer on the surface. The surfaces were investigated by using scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), infrared spectroscopy (FTIR) and contact angle measurements. The results indicate that calcium phosphate could form on surface of Ti-35Nb-7Zr experimental alloy. © Springer-Verlag Berlin Heidelberg 2013.

Dynamics of the interaction between body fluid and Ti cp: the influence of surface functionalization in the first stages of osseointegration

INTRODUCTION: Regenerative therapies using biomaterials require accurate information on interactions between the implanted material and the human body. To improve the process of bone regeneration it is necessary to obtain a better understanding of the influence of the surfaces on the early stages of osseointegration. This work aims to investigate the dynamic interaction between simulated body fluid (SBF) and titanium surfaces (Ti cp) immediately after their first contact. METHODS: Ti cp samples were passed through physicochemical treatments after immersion in acid solution, alkaline solution and solutions containing TiO2 and Ca2+, to obtain three different surfaces. These were characterized by electron microscopy and free energy estimates. The evaluation of the interaction with SBF was performed by measuring the dynamic contact angles after contacting the surfaces. RESULTS: The effects of SBF wettability were more significant on surfaces according to high energy estimates. A comparative analysis of the three types of surfaces showed that fluid spreading was greater in samples with greater polar components, indicating that the surface nature influences interactions in the early stages of osseointegration. CONCLUSION: The results indicate the influence of polar interactions in the dynamic wettability of the SBF. It is possible that these interactions can also influence cellular viability on surfaces. Based on these results, new experiments are being designed to improve the presented methodology as a tool for the evaluation of biomaterials without the need for in vivo experiments.

Fretting wear behaviour of hydroxyapatite-titanium composites in simulated body fluid, supplemented with 5 g l(-1) bovine serum albumin

Damaged articulating joints can be repaired or replaced with synthetic biomaterials, which can release wear debris due to articulation, leading to the osteolysis. In a recent work, it has been shown that it is possible to achieve a better combination of flexural strength/fracture toughness as well as in vitro bioactivity and cytocompatibility properties in spark plasma sintered hydroxyapatite-titanium (HA-Ti) composites. Although hydroxyapatite and titanium are well documented for their good biocompatibility, nanosized hydroxyapatite (HA) and titanium (Ti) particles can cause severe toxicity to cells. In order to address this issue, fretting wear study of HA-Ti composites under dry and wet (1x SBF, supplemented with 5 g l(-1) bovine serum albumin (BSA)) condition was performed to assess the wear resistance as well as wear debris formation, in vitro. The experimental results reveal one order of magnitude lower wear rate for HA-10 wt% Ti (7.5 x 10(-5) mm(3) N-1 m(-1)) composite than monolithic HA (3.9 x 10(-4) mm(3) N-1 m(-1)) in simulated body fluid. The difference in the tribological properties has been analyzed in the light of phase assemblages and mechanical properties. Overall, the results suggest the potential use of HA-Ti composites over existing HA-based biocomposites in orthopedic as well as dental applications.

Evaluation of Corrosion Fatigue Behaviour of Laser-welded NiTi Alloys using Bending Rotation Fatigue Test in Simulated Body Fluid

Shape memory NiTi alloys have been used extensively for medical device applications such as orthopedic, dental, vascular and cardiovascular devices on account of their unique shape memory effect (SME) and super-elasticity (SE). Laser welding is found to be the most suitable method used to fabricate NiTi-based medical components. However, the performance of laser-welded NiTi alloys under corrosive environments is not fully understood and a specific focus on understanding the corrosion fatigue behaviour is not evident in the literature. This study reveals a comparison of corrosion fatigue behaviour of laser-welded and bare NiTi alloys using bending rotation fatigue (BRF) test which was integrated with a specifically designed corrosion cell. The testing environment was Hanks’ solution (simulated body fluid) at 37.5oC. Electrochemical impedance spectroscopic (EIS) measurement was carried out to monitor the change of corrosion resistance at different periods during the BRF test. Experiments indicate that the laser-welded NiTi alloy would be more susceptible to the corrosion fatigue attack than the bare NiTi alloy. This finding can serve as a benchmark for the product designers and engineers to determine the factor of safety of NiTi medical devices fabricated using laser welding.

Corrosion Fatigue Behaviour of Laser-welded Shape Memory NiTi Wires in a Simulated Body Fluid

Corrosion fatigue is a fracture process as a consequence of synergistic interactions between the material structure, corrosive environment and cyclic loads/strains. It is difficult to be detected and can cause unexpected failure of engineering components in use. This study reveals a comparison of corrosion fatigue behaviour of laser-welded and bare NiTi wires using bending rotation fatigue (BRF) test coupled with a specifically-designed corrosion cell. The testing medium was Hanks’ solution (simulated body fluid) at 37.5 oC. Electrochemical impedance spectroscopic (EIS) measurement was carried out to monitor the change of corrosion resistance of sample during the BRF test at different periods of time. Experiments indicate that the laser-welded NiTi wire would be more susceptible to the corrosion fatigue attack than the bare NiTi wire. This study can serve as a benchmark for the product designers and engineers to understand the corrosion fatigue behaviour of the NiTi laser weld joint and determine the fatigue life safety factor for NiTi medical devices/implants involving laser welding in the fabrication process.

Obstructive Sleep Apnea Severity and Overnight Body Fluid Shift before and after Hemodialysis.

BACKGROUND AND OBJECTIVES: Obstructive sleep apnea is associated with significantly increased cardiovascular morbidity and mortality. Fluid overload may promote obstructive sleep apnea in patients with ESRD through an overnight fluid shift from the legs to the neck soft tissues. Body fluid shift and severity of obstructive sleep apnea before and after hemodialysis were compared in patients with ESRD. DESIGN, SETTING, PARTICIPANTS, & MEASUREMENTS: Seventeen patients with hemodialysis and moderate to severe obstructive sleep apnea were included. Polysomnographies were performed the night before and after hemodialysis to assess obstructive sleep apnea, and bioimpedance was used to measure fluid overload and leg fluid volume. RESULTS: The mean overnight rostral fluid shift was 1.27±0.41 L prehemodialysis; it correlated positively with fluid overload volume (r=0.39; P=0.02) and was significantly lower posthemodialysis (0.78±0.38 L; P<0.001). There was no significant difference in the mean obstructive apnea-hypopnea index before and after hemodialysis (46.8±22.0 versus 42.1±18.6 per hour; P=0.21), but obstructive apnea-hypopnea index was significantly lower posthemodialysis (-10.1±10.8 per hour) in the group of 12 patients, with a concomitant reduction of fluid overload compared with participants without change in fluid overload (obstructive apnea-hypopnea index +8.2±16.1 per hour; P<0.01). A lower fluid overload after hemodialysis was significantly correlated (r=0.49; P=0.04) with a lower obstructive apnea-hypopnea index. Fluid overload-assessed by bioimpedance-was the best predictor of the change in obstructive apnea-hypopnea index observed after hemodialysis (standardized r=-0.68; P=0.01) in multivariate regression analysis. CONCLUSIONS: Fluid overload influences overnight rostral fluid shift and obstructive sleep apnea severity in patients with ESRD undergoing intermittent hemodialysis. Although no benefit of hemodialysis on obstructive sleep apnea severity was observed in the whole group, the change in obstructive apnea-hypopnea index was significantly correlated with the change in fluid overload after hemodialysis. Moreover, the subgroup with lower fluid overload posthemodialysis showed a significantly lower obstructive sleep apnea severity, which provides a strong incentive to further study whether optimizing fluid status in patients with obstructive sleep apnea and ESRD will improve the obstructive apnea-hypopnea index.

In situ impedance spectroscopy study of the electrochemical corrosion of Ti and Ti-6Al-4V in simulated body fluid at 25 degrees C and 37 degrees C

The corrosion resistance of Ti and Ti-6Al-4V was investigated through electrochemical impedance spectroscopy, EIS, potentiodynamic polarisation curves and UV-Vis spectrophotometry. The tests were done in Hank solution at 25 degrees C and 37 degrees C. The EIS measurements were done at the open circuit potential at specific immersion times. An increase of the resistance as a function of the immersion time was observed, for Ti (at 25 degrees C and 37 degrees C), and for Ti-6Al-4V (at 25 degrees C), which was interpreted as the formation and growth of a passive film on the metallic surfaces. (C) 2009 Elsevier Ltd. All rights reserved.

Dietary omega-3 fatty acids modify body fluid and cardiovascular homeostasis

Dietary omega-3 fatty acids are important for optimal nutrition. This research demonstrated the significant beneficial effects of these fatty acids on body fluid balance in aging and the regulation of blood pressure. A significant findng was that omega-3 fatty acids reduce neuro-inflammation (inflammation in the brain)

Control of biodegradation of a Mg alloy in simulated body fluid

Mg alloy AZ31 is an attractive candidate for coronary artery stents, as it possesses excellent biocompatibility in human body and good mechanical properties. However, AZ31 magnesium alloys generally have poor corrosion resistance in the body environment. This paper reports on the early stages of an investigation into the corrosion mechanism and the morphology of corrosion of AZ31 in simulated body fluid (SBF). The investigation will also consider ways of improving corrosion resistance of this alloy in SBF through the use of ionic liquids. The results to date have shown that AZ31 suffers severe localized pitting corrosion in SBF. The pits mainly develop adjacent to the Al-Mn intermetallic second phase in the α matrix. Energy Dispersive X-Ray Spectroscopy results revealed the presence of Mg, O, Ca, and P in the layer of corrosion product. Treatment of the AZ31 alloy prior to corrosion testing in SBF with the ionic liquid trimethyl (butyl) phosphonium diphenyl phosphate (P1444DPP) produced some increase in the corrosion resistance of the alloy.

Ionic liquid pretreatment as a means to control the corrosion behavior of magnesium alloys in simulated body fluid

Recently, the use of magnesium alloys as metallic implant materials for biodegradable coronary artery stents has been steadily growing in interest. However, AZ31 magnesium alloys present poor corrosion resistance in the body environment. This work reports on the use of a treatment with low-toxicity IL Trimethyl (butyl) phosphonium diphenyl phosphate P₁₄₄₄DPP, which provides corrosion protection for magnesium alloy AZ31 in simulated body fluid (SBF). Before IL treatment, surface was cleaned by HNO₃ and H₃PO₄ acid pickling solution. The effect of ionic liquid treatment on the corrosion performance of magnesium alloys AZ31in simulated body fluid has been investigated by electrochemical tests and the observation of surface morphology. The results show that this IL treatment succeeded in increasing the corrosion resistance of AZ31 when exposed to SBF.