Evaluation of mineral trioxide aggregate and calcium hydroxide cement as pulp-capping agents in human teeth

This study evaluated the histomorphologic response of human dental pulps capped with mineral trioxide aggregate (MTA) and Ca(OH)(2) cement (CH). Pulp exposures were performed on the occlusal floor of 40 human permanent premolars. After that, the pulp was capped either with CH or MTA and restored with composite resin. After 30 and 60 days, teeth were extracted and processed for histologic exam and categorized in a histologic score system. The data were subjected to Kruskal-Wallis and Conover tests (alpha = .05). All groups performed well in terms of hard tissue bridge formation, inflammatory response, and other pulpal findings. However, a lower response of CH30 was observed for the dentin bridge formation, when compared with MTA30 and MTA60 groups. Although the pulp healing with calcium hydroxide was slower than that of MTA, both materials were successful for pulp capping in human teeth.

In vivo evaluation of the biocompatibility of three current bonding agents

The aim of this in vivo study was to evaluate the biocompatibility of three current bonding agents and calcium hydroxide cement. Sixty polyethylene tubes filled with the following materials: Group 1: Prime & Bond NT (PB - Dentsply, US; Group 2: Bond 1 (BO - Jeneric/Pentron, US); Group 3: Optibond Solo (OP - Kerr, US); and Group 4 (control): calcium hydroxide cement - Dycal (CH - Dentsply, US) were implanted into the connective tissue of 30 rats. After 15, 30 and 60 days, the implants were excised and the animals sacrificed. The biopsies were immersed in Karnovsky (pH, 7.2) fixative solution for 48 hours, and processed using routine histological technique. Six-micron-thick sections were cut and stained with hematoxilin and eosin and Masson's trichome technique. Microscopic evaluation was used to compare the connective tissue reactions caused by the experimental and control materials adjacent to the tube opening. At 15 days, the experimental and control materials triggered a moderate to intense inflammatory response which gave rise to a thick capsule adjacent to the tube opening. With time, the inflammatory reaction decreased. At 60 days, the connective tissue adjacent to the bonding agents exhibited a persistent inflammatory response mediated by macrophages and giant cells which were engulfing displaced resin components. on the other hand, for the control group (calcium hydroxide) no inflammatory response associated with a thin capsule adjacent to the material was observed even at the 30-day period. The hard-setting calcium hydroxide cement allowed complete healing and was considered more biocompatible than the bonding agents.

Biocompatibility of resin-based materials used as pulp-capping agents

Aim To evaluate and compare the response of pulps of rats capped with resin-modified glass-ionomer cement (RMGIC) or self-etching adhesive system.Methodology Class I cavities were prepared on the occlusal surface of 54 maxillary first molars of 27 rats. Pulp exposure was performed on the cavity floor. The following resin-based materials were applied as pulp-capping agents: G1, Clearfil Liner Bond 2V (CLB 2V; Kuraray Co., Japan); G2, Vitrebond (VIT; 3M/ESPE, USA). In group 3 (control group), a calcium hydroxide/saline paste (CH; Labsynth, Brazil) was used. The cavities were restored with amalgam. After 7, 30 and 60 days, the animals were sacrificed and the jaws were processed for microscopic evaluation.Results Despite the inflammatory response caused by the experimental and the control materials at 7 days, pulpal healing associated with calcified barrier formation was observed at 60 days following the pulp therapy. Both resin-based materials promoted a large zone of cell-rich fibrodentine matrix deposition on the pulp horn related to the pulp exposure site, which was larger to VIT than to CLB 2V specimens. Tertiary dentine underneath the fibrodentine matrix was deposited by a layer of elongated pulpal cells. The remaining pulpal tissue exhibited normal histological characteristics. In the control group, healing and dentine-bridge formation was observed at 30 days. Pulpal breakdown occurred only when bacterial infection occurred.Conclusion Both experimental pulp-capping agents allowed pulpal healing characterized by cell-rich fibrodentine and tertiary dentine deposition as well as calcified barrier formation.

Transdentinal protective role of sodium ascorbate against the cytopathic effects of H2O2 released from bleaching agents

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cytotoxicity of Portland Cement with Different Radiopacifying Agents: A Cell Death Study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of root-surface conditioning with acid and chelating agents on clot stabilization

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Antimicrobial activity of disinfectant agents incorporated into type IV dental stone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Peel bond strength of resilient liner modified by the addition of antimicrobial agents to denture base acrylic resin

In order to prolong the clinical longevity of resilient denture relining materials and reduce plaque accumulation, incorporation of antimicrobial agents into these materials has been proposed. However, this addition may affect their properties. Objective: This study evaluated the effect of the addition of antimicrobial agents into one soft liner (Soft Confort, Dencril) on its peel bond strength to one denture base (QC 20, Dentsply). Material and Methods: Acrylic specimens (n=9) were made (75x10x3 mm) and stored in distilled water at 37 degrees C for 48 h. The drug powder concentrations (nystatin 500,000U - G2; nystatin 1,000,000U - G3; miconazole 125 mg - G4; miconazole 250 mg - G5; ketoconazole 100 mg - G6; ketoconazole 200 mg - G7; chlorhexidine diacetate 5% - G8; and 10% chlorhexidine diacetate - G9) were blended with the soft liner powder before the addition of the soft liner liquid. A group (G1) without any drug incorporation was used as control. Specimens (n=9) (75x10x6 mm) were plasticized according to the manufacturers' instructions and stored in distilled water at 37 degrees C for 24 h. Relined specimens were then submitted to a 180-degree peel test at a crosshead speed of 10 mm/min. Data (MPa) were analyzed by analysis of variance (alpha=0.05) and the failure modes were visually classified. Results: No significant difference was found among experimental groups (p=0.148). Cohesive failure located within the resilient material was predominantly observed in all tested groups. Conclusions: Peel bond strength between the denture base and the modified soft liner was not affected by the addition of antimicrobial agents.

Radiopacity of Portland Cement Associated With Different Radiopacifying Agents

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Endophytic microorganisms from coffee tissues as plant growth promoters and biocontrol agents of coffee leaf rust

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cardioplegia using low volumic cardioplegic agents: morphological study in isolated rabbit hearts

INTRODUÇÃO: A solução cardioplégica farmacológica busca eliminar as conseqüências do dano isquêmico, que é o resultado do desbalanço entre a oferta e o consumo de energia durante a parada dos batimentos cardíacos, nas cirurgias cardíacas com circulação extracorpórea. OBJETIVO: Este trabalho avalia experimentalmente as alterações estruturais e ultra-estruturais em coração isolado de coelhos submetidos à parada protegida pela Solução para Cardioplegia de Baixo Volume (SCBV). MÉTODO: O estudo compreendeu um grupo controle e dois grupos experimentais. No grupo I, a parada cardíaca foi obtida pela infusão da SCBV por 2 horas. No grupo II, o experimento foi conduzido da mesma forma até a parada protegida pela SCBV por duas horas, imediatamente procedeu-se à reperfusão com solução oxigenada de Ringer Locke (RL) por uma hora. No grupo controle os corações foram perfundidos com solução oxigenada de RL por duas horas. Após os experimentos, oito amostras de parede lateral do ventrículo esquerdo foram fixadas em formaldeído 10% e glutaraldeído 2,5% para análises histológica e ultra-estrutural. RESULTADOS: As células do miocárdio, fibroblastos e células endoteliais, observadas nos grupos experimentais I e II, apresentaram marginalização da heterocromatina, compactação do nucléolo, alteração na forma das mitocôndrias, compactação das cristas e aumento da densidade da matriz mitocondrial, indicando que tanto a estrutura nuclear quanto a das organelas citoplasmáticas foram alteradas em relação às células do grupo controle. CONCLUSÃO: As modificações estruturais foram decorrentes de uma adaptação fisiológica da célula, não sendo indicativas de oncose ou apoptose, sugerindo, portanto, que a solução cardioplégica utilizada foi eficiente para a preservação das células.

Ex vivo evaluation of the effectiveness of bleaching agents on the shade alteration of blood-stained teeth

Aim To evaluate ex vivo effectiveness of the three formulations of bleaching materials for intracoronal bleaching of root filled teeth using the walking bleach technique.Methodology Extracted premolar teeth were stained artificially with human blood. After biomechanical preparation, the root canals were filled and a 3-mm thick intermediate base of zinc phosphate cement was placed at the level of the cementoenamel junction. The teeth were divided into four groups (n = 12): C (control, without bleaching material), A1 (sodium perborate + distilled water), A2 (sodium perborate + 10% carbamide peroxide) and A3 (sodium perborate + 35% carbamide peroxide). The bleaching materials were changed at 7 and 14 days. Evaluation of shade was undertaken with aid of the VITA Easyshade (TM) (Delta E*ab) and was performed after tooth staining and at 7, 14 and 21 days after bleaching, based on the CIELAB system. Data were analysed by ANOVA for repeated measurements, Tukey and Dunnett tests (alpha = 0.05).Results The Tukey test revealed that group A1 (10.58 +/- 4.83 Delta E*ab) was statistically different from the others (A2, 19.57 +/- 4.72 Delta E*ab and A3, 17.58 +/- 3.33 Delta E*ab), which were not different from each other. At 7 days: A1 was significantly different from A2; at 14 and 21 days: A2 and A3 were significantly better than A1; the Dunnett test revealed that the control group was different from A1, A2 and A3 at all periods (P < 0.05).Conclusion Sodium perborate associated with both 10% and 35% carbamide peroxide was more effective than when associated with distilled water.

Influence of Potentially Remineralizing Agents on Bleached Enamel Microhardness

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)