Short-range order kinetics in alpha-AgZn for various states of post-deformation defect annealing after cold-rolling

Kinetics of short-range ordering (SRO) in Ag with 21, 23 and 28 at% Zn is investigated by residual resistometry during isochronal and isothermal heat treatment for different states of post-deformation defect annealing after cold-rolling to about 30 and 60% thickness reduction. Resistivity changes due to pure ordering can be separated from the as-measured total resistivity change which includes defect annealing. Although the initial state of SRO of the as-rolled material can be estimated to be comparably low, for as-rolled and partially annealed states by appropriate thermal treatment evolution of SRO is achieved which corresponds quite well to that of recrystallized samples. It is observed, however, that quenched-in surplus vacancies contribute considerably to the ordering process for the recrystallized state and that this contribution is still increased by the grain growth during the final stage of annealing. It therefore turns out that SRO-kinetics under equilibrium vacancy conditions can be better observed in a state of post-deformation annealing, for which deformation induced point defects are annealed-out, but a relatively high dislocation density is still present to act as a vacancy sink. Copyright (C) 1996 Acta Metallurgica Inc.

Resistometric study of short-range order kinetics in alpha-AgZn

Short-range ordering (SRO) kinetics was investigated under temperature conditions of isochronal and isothermal annealing in completely recrystallized Ag-21, -23, -28 at.% Zn by residual resistometry. The SRO kinetics deviated considerably from a single exponential relaxation process and was therefore analysed using a log-normal spectrum of SRO relaxation times. This yields activation enthalpies for changes in the degree of SRO in good accordance with literature data. Isothermal SRO relaxation of undeformed samples was compared with that of cold-rolled and partially annealed samples.

Changes of microstructure in alpha AgZn during post-deformation annealing after cold-rolling

The annealing processes of deformation-induced defects after cold-rolling to about 30 and 60% thickness reduction were investigated for Ag-21, 23, 28 at% Zn by means of residual electrical resistivity, microhardness, light microscopy and transmission electron microscopy (TEM) Three annealing stages have been detected and consistently interpreted as annealing-out of mainly point defects and their agglomerates (stage I), formation of dislocation cells and recrystallized strain-free grains (stage II) and grain growth (stage III). Further, it is tried to determine the evolution of defect production (point defects and dislocations) during rolling deformation from measured changes of electrical resistivity and microhardness. Copyright (C) 1996 Acta Metallurgica Inc.