Effect of Three Methods for Cleaning Dentures on Biofilms Formed In Vitro on Acrylic Resin

Purpose: The aim of this study was to evaluate the effect of three denture hygiene methods against different microbial biofilms formed on acrylic resin specimens. Materials and methods: The set (sterile stainless steel basket and specimens) was contaminated (37 degrees C for 48 hours) by a microbial inoculum with 106 colony-forming units (CFU)/ml (standard strains: Staphylococcus aureus, Streptococcus mutans, Escherichia coli, Candida albicans, Pseudomonas aeruginosa, and Enterococcus faecalis; field strains: S. mutans, C. albicans, C. glabrata, and C. tropicalis). After inoculation, specimens were cleansed by the following methods: (1) chemical: immersion in an alkaline peroxide solution (Bonyplus tablets) for 5 minutes; (2) mechanical: brushing with a dentifrice for removable prostheses (Dentu Creme) for 20 seconds; and (3) a combination of chemical and mechanical methods. Specimens were applied onto a Petri plate with appropriate culture medium for 10 minutes. Afterward, the specimens were removed and the plates incubated at 37 degrees C for 48 hours. Results: Chemical, mechanical, and combination methods showed no significant difference in the reduction of CFU for S. aureus, S. mutans (ATCC and field strain), and P. aeruginosa. Mechanical and combination methods were similar and more effective than the chemical method for E. faecalis, C. albicans (ATCC and field strain), and C. glabrata. The combination method was better than the chemical method for E. coli and C. tropicalis, and the mechanical method showed intermediate results. Conclusion: The three denture hygiene methods showed different effects depending on the type of microbial biofilms formed on acrylic base resin specimens.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

THE EFFECT of E-GLASS FIBERS and ACRYLIC RESIN THICKNESS on FRACTURE LOAD IN A SIMULATED IMPLANT-SUPPORTED OVERDENTURE PROSTHESIS

Statement of problem. Implant overdenture prostheses are prone to acrylic resin fracture because of space limitations around the implant overdenture components.Purpose. The purpose of this study was to evaluate the influence of E-glass fibers and acrylic resin thickness in resisting acrylic resin fracture around a simulated overdenture abutment.Material and methods. A model was developed to simulate the clinical situation of an implant overdenture abutment with varying acrylic resin thickness (1.5 or 3.0 mm) with or without E-glass fiber reinforcement. Forty-eight specimens with an underlying simulated abutment were divided into 4 groups (n=12): 1.5 mm acrylic resin without E-glass fibers identified as thin with no E-glass fiber mesh (TN-N); 1.5 mm acrylic resin with E-glass fibers identified as thin with E-glass fiber mesh (TN-F); 3.0 mm acrylic resin without E-glass fibers identified as thick without E-glass fiber mesh (TK-N); and 3.0 mm acrylic resin with E-glass fibers identified as thick with E-glass fiber mesh (TK-F). All specimens were submitted to a 3-point bending test and fracture loads (N) were analyzed with a 2-way ANOVA and Tukey's post hoc test (alpha=.05).Results. The results revealed significant differences in fracture load among the 4 groups, with significant effects from both thickness (P<.001) and inclusion of the mesh (P<.001). Results demonstrated no interaction between mesh and thickness (P=.690). The TN-N: 39 +/- 5 N; TN-F: 50 +/- 6.9 N; TK-N: 162 +/- 13 N; and TK-F: 193 +/- 21 N groups were all statistically different (P<.001).Conclusions. The fracture load of a processed, acrylic resin implant-supported overdenture can be significantly increased by the addition of E-glass fibers even when using thin acrylic resin sections. on a relative basis, the increase in fracture load was similar when adding E-glass fibers or increasing acrylic resin thickness. (J Prosthet Dent 2011;106:373-377)

Bond strength between acrylic resin and maxillofacial silicone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Esthetic Interim Acrylic Resin Prosthesis Reinforced with Metal Casting

Fabrication of an interim prosthesis is an important procedure in oral rehabilitation because it aids in determining the esthetics, phonetics, and occlusal relationship of the definitive restoration. The typical material (acrylic resin) used in interim prostheses commonly fails due to fractures. During extended oral rehabilitation with fixed partial prostheses, high strength interim prostheses are often required to protect hard and soft tissues, avoid dental mobility, and to allow the clinician and patient a chance to evaluate cosmetics and function before the placement of the definitive prosthesis. Furthermore, a satisfactory interim prosthesis can serve as a template for the construction of the definitive prosthesis. The maintenance of this prosthesis is important during treatment for protection of teeth and occlusal stability. Procedures to reinforce interim prostheses help to improve performance and esthetics in long-term treatment. Due to the low durability of acrylic resin in long-term use, the use of reinforcing materials, such as metal castings or spot-welded stainless steel matrix bands, is indicated in cases of extensive restoration and long-term treatment. This paper describes an easy technique for fabricating a fixed interim prosthesis using acrylic resin and a cast metallic reinforcement.

Bond strength of denture teeth to acrylic resin: effect of thermocycling and polymerisation methods

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of weathering and thickness on the superficial microhardness of acrylic resin and ocular button

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microscopical analysis of Candida albicans biofilms on heat-polymerised acrylic resin after chlorhexidine gluconate and sodium hypochlorite treatments

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of microwave disinfection on the dimensional stability of intact and relined acrylic resin denture bases

Statement of problem. Microwave irradiation has been suggested as a method to disinfect denture bases. However, the effect of microwave heating on the dimensional stability of the relined denture bases is unknown.Purpose. The purpose of this study was to evaluate the dimensional stability of intact and relined acrylic resin denture bases after microwave disinfection.Material and methods. A standard brass cast simulating an edentulous maxillary arch was machined and used to fabricate 2- and 4-mm-thick denture bases (n=200), which were processed with heat-polymerized acrylic resin (Lucitone 550). The 2-mm thick-specimens (n=160) were relined with 2 mm of autopolymerizing resin (Tokuso Rebase Fast, Ufi Gel Hard, Kooliner, or New Truliner). Distances between 5 removable pins on the standard brass cast were measured with a Nikon optical comparator, and the area (mm(2)) formed by the distance between 5 pins was calculated and served as baseline. During fabrication, the pins were transferred to the intaglio surface of the specimens. Differences between the baseline area and those subsequently determined for the specimens were used to calculate the percent dimensional changes. The intact and relined denture bases were divided into 4 groups (n=10) and evaluated after: polymerization (control group P); 1 cycle of microwave disinfection (MW); daily microwave disinfection for 7 days (control group MW7); water storage for 7 days (WS7). Microwave irradiation was performed for 6 minutes at 650 W. Data were analyzed using 2-way ANOVA followed by Tukey's test (alpha=.05).Results. Intact specimens and those relined with Kooliner and New Truliner showed increased shrinkage after 1 (P=.05, .018, and .001, respectively) and 7 (P <.001, .003, and <.001, respectively) cycles of microwave disinfection. With the exception of specimens relined with Kooliner, intact specimens showed greater shrinkage than the relined specimens after 7 cycles of microwave disinfection.Conclusions. Microwave disinfection produced increased shrinkage of intact specimens and those relined with New Truliner and Kooliner.

Effect of relining, water storage and cyclic loading on the flexural strength of a denture base acrylic resin

Objectives: This study investigated the effect of relining, water storage and cyclic loading on the ultimate flexural strength (FSU) and on the flexural strength at the proportional limit (FSPl) of a denture base acrylic resin (Lucitone 550-L).Methods: Rectangular bars of L were made (64 mm x 10 mm x 2 mm) and relined (1.3 mm) with four relining resins (Kooliner-K, Ufi Gel Hard-UGH, Tokuso Rebase Fast-TR and New Truliner-NT). In addition, specimens relined with L and intact L specimens were made (64 mm x 10 mm x 3.3 mm). A three-point flexural test was applied on the specimens (n = 10) after (1) polymerization; (2) water storage (30 days); (3) cyclic loading (10,000 cycles at 5 Hz) and (4) water storage (30 days) + cyclic loading. Data (MPa) were analyzed with three-way ANOVA and Tukey's HSD tests (alpha = 0.05). To test for a possible correlation between FSU and FSPl, a linear regression coefficient 'r' was calculated.Results: After water storage, L-UGH and L-TR demonstrated an increased FSU (41.4950.64 MPa and 49.95-57.36 MPa, respectively) (P < 0.05). Only L-TR demonstrated an increased FSPl (20.58-24.21 MPa) after water storage (P < 0.05). L-L had the highest FSU (between 78.57 and 85.09 MPa) and FSPl (between 31.30 and 34.17 MPa) (P < 0.05). The cyclic loading decreased the FSU and FSPl of all materials (P < 0.05). Regression analysis showed a strong linear correlation between the two variables (r = 0.941).Conclusions: Water storage improved the FSU of L-UGH and L-TR and the FSPl of L-TR. L-L produced the highest FSU and FSPl. The FSU and FSPl of all materials were detrimentally influenced by cyclic loading.

The effect of disinfectant solutions on the hardness of acrylic resin denture teeth

This investigation studied the effects of disinfectant solutions on the hardness of acrylic resin denture teeth. The occlusal surfaces of 64 resin denture teeth were ground flat with abrasives up to 400-grit silicon carbide paper. Measurements were made after polishing and after the specimens were stored in water at 37 degreesC for 48 h. The specimens were then divided into four groups and immersed in chemical disinfectants (4% chlorhexidine; 1% sodium hypochlorite and sodium perborate) for 10 min. The disinfection methods were performed twice to simulate clinical conditions and hardness measurements were made. Specimens tested as controls were immersed in water during the same disinfection time. Eight specimens were produced for each group. After desinfection procedures, testing of hardness was also performed after the samples were stored at 37 degreesC for 7, 30, 60, 90 and 120 days. Data were analysed using two-way analysis of variance (anova) and Tukey's test at 95% confidence level. According to the results, no significant differences were found between materials and immersion solutions (P > 0.05). However, a continuous decrease in hardness was noticed after ageing (P < 0.05). It was conclude that the surfaces of both acrylic resin denture teeth softened upon immersion in water regardless the disinfecting solution.

Adherence in vitro of Candida albicans to plasma treated acrylic resin. Effect of plasma parameters, surface roughness and salivary pellicle

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Peel bond strength of resilient liner modified by the addition of antimicrobial agents to denture base acrylic resin

In order to prolong the clinical longevity of resilient denture relining materials and reduce plaque accumulation, incorporation of antimicrobial agents into these materials has been proposed. However, this addition may affect their properties. Objective: This study evaluated the effect of the addition of antimicrobial agents into one soft liner (Soft Confort, Dencril) on its peel bond strength to one denture base (QC 20, Dentsply). Material and Methods: Acrylic specimens (n=9) were made (75x10x3 mm) and stored in distilled water at 37 degrees C for 48 h. The drug powder concentrations (nystatin 500,000U - G2; nystatin 1,000,000U - G3; miconazole 125 mg - G4; miconazole 250 mg - G5; ketoconazole 100 mg - G6; ketoconazole 200 mg - G7; chlorhexidine diacetate 5% - G8; and 10% chlorhexidine diacetate - G9) were blended with the soft liner powder before the addition of the soft liner liquid. A group (G1) without any drug incorporation was used as control. Specimens (n=9) (75x10x6 mm) were plasticized according to the manufacturers' instructions and stored in distilled water at 37 degrees C for 24 h. Relined specimens were then submitted to a 180-degree peel test at a crosshead speed of 10 mm/min. Data (MPa) were analyzed by analysis of variance (alpha=0.05) and the failure modes were visually classified. Results: No significant difference was found among experimental groups (p=0.148). Cohesive failure located within the resilient material was predominantly observed in all tested groups. Conclusions: Peel bond strength between the denture base and the modified soft liner was not affected by the addition of antimicrobial agents.