Carbon-supported Pd–Ir catalyst as anodic catalyst in direct formic acid fuel cell

It was reported for the first time that the electrocatalytic activity of the Carbon-supported Pd-Ir (Pd-Ir/C) catalyst with the suitable atomic ratio of Pd and Ir for the oxidation of formic acid in the direct formic acid fuel cell (DFAFC) is better than that of the Carbon-supported Pd (Pd/C) catalyst, although Ir has no electrocatalytic activity for the oxidation of formic acid. The potential of the anodic peak of formic acid at the Pd-Ir/C catalyst electrode with the atomic ratio of Pd and Ir = 5:1 is 50 mV more negative than that and the peak current density is 13% higher than that at the Pd/C catalyst electrode.

A carbon-supported Pd-P catalyst as the anodic catalyst in a direct formic acid fuel cell

In this paper, it is reported for the first time that a carbon-supported Pd-P (Pd-P/C) catalyst for the anodic catalyst in the direct formic acid fuel cell (DFAFC) can be prepared. The Pd-P/C catalyst shows that its electrocatalytic activity and especially its stability for the oxidation of formic acid are much higher than that of a Pd/C catalyst. Therefore, the Pd-P/C catalyst may have practical applications in DFAFCs.

Structure-activity relationship of surfactant for preparing DMFC anodic catalyst

Three kinds of surfactants as stabilizer were applied to the preparation of electrocatalysts for direct methanol fuel cell (DMFC). The catalysts have been characterized by examining their catalytic activities, morphologies and particle sizes by means of cyclic voltammetry, chronoamperometry, X-ray diffraction and transmission electron microscopy (TEM). It is found that the surfactants with different structures have a significantly influence on the catalyst shape and activity. The catalysts prepared with non-ionic surfactants as the stabilizer show higher activity for direct oxidation of methanol. The structure-activity relationship (SAR) analysis has been explored and the effect of hydrophile-lipophile balance (HLB value) has also been discussed.

Determination of ionic resistance and optimal composition in the anodic catalyst layers of DMFC using AC impedance

In the present study, a method based on transmission-line mode for a porous electrode was used to measure the ionic resistance of the anode catalyst layer under in situ fuel cell operation condition. The influence of Nafion content and catalyst loading in the anode catalyst layer on the methanol electro-oxidation and direct methanol fuel cell (DMFC) performance based on unsupported Pt-Ru black was investigated by using the AC impedance method. The optimal Nafion content was found to be 15 wt% at 75 degrees C. The optimal Pt-Ru loading is related to the operating temperature, for example, about 2.0 mg/cm(2) for 75-90 degrees C, 3.0 mg/cm2 for 50 degrees C. Over these values, the cell performance decreased due to the increases in ohmic and mass transfer resistances. It was found that the peak power density obtained was 217 mW/cm(2) with optimal catalyst and Nafion loading at 75 degrees C using oxygen. (c) 2005 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.

Study of carbon-supported Au catalyst as the cathodic catalyst in a direct formic acid fuel cell prepared using a polyvinyl alcohol protection method

In this paper, it is reported for the first time that a carbon-supported Au (Au/C) catalyst for the cathodic catalyst in a direct formic acid fuel cell (DFAFC) was prepared using a polyvinyl alcohol (PVA) protection method. The results indicated that for oxygen reduction, the electrocatalytic activity of the Au/C catalyst prepared with the PVA protection method is much better than that of a Au/C catalyst prepared with the pre-precipitation method. This is due to the small average size and low relative crystallinity of the An particles in the Au/C catalyst prepared by the PVA protection method, compared to that of the Au/C catalyst prepared by the pre-precipitation method, illustrating that the average size and the relative crystallinity of the ALL particles has an effect on the electrocatalytic activity of the Au/C catalyst for oxygen reduction. In addition, because An has no electrocatalytic activity for the oxidation of formic acid, the Au/C catalyst possesses a high formic acid tolerance. After the electrocatalytic activity of the Au/C catalyst for the oxygen reduction is improved, it is suitable to be used as the cathodic catalyst in DFAFC.

Physical and electrochemical characterizations of PtRu/C catalysts by spray pyrolysis for electrocatalytic oxidation of methanol

In this paper, it was reported that the carbon-supported Pt-Ru(Pt-Ru/C) catalyst used as the anodic catalyst in the direct methanol fuel cell (DMFC) was synthesized with a two-step spray pyrolysis (SP) method using the Pt and Ru metal salt as the precursors and polyethylene glycol (PEG) with the different molecular weights (Mw= 200,600,and 1000 analytical reagent) as cosolvent. PEG as a cosolvent plays a crucial role in producing PtRu/C catalysts. It was found that the Mw of PEG could affect the electrocatalytic activity of Pt-Ru and the morphology of the Pt-Ru particles in the Pt-Ru/C catalysts prepared with this method. When the Mw of PEG is 600, the Pt-Ru particles in the Pt-Ru/C catalyst prepared with this method possess the small average size, narrow size distribution, uniform dispersion, and high electrochemically active specific surface area. The electrocatalytic activity of the Pt-Ru/C catalyst prepared with this method using the cosolvent PEG with Mw = 600 for the methanol oxidation is much higher than that of the commercial E-TEK Pt-Ru/C catalyst. Therefore, the two-step SP method is an excellent method for the preparation of the Pt-Ru/C catalyst used in DMFCs.

Electrostatic layer-by-layer a of platinum-loaded multiwall carbon nanotube multilayer: A tunable catalyst film for anodic methanol oxidation

A simple layer-by-layer (LBL) electrostatic adsorption technique was developed for deposition of films composed of alternating layers of positively charged poly(diallyldimethylammonium chloride) (PDDA) and negatively charged multiwall carbon nanotubes bearing platinum nanoparticles (Pt-CNTs). PDDA/Pt-CNT film structure and morphology up to six layers were characterized by scanning electron microscopy and ultraviolet-visible spectroscopy, showing the Pt-CNT layers to be porous and uniformly deposited within the multilayer films.

Surface-enhanced resonant Raman spectroscopy (SERRS) of single-walled carbon nanotubes absorbed on the Ag-coated anodic aluminum oxide (AAO) surface

In this paper, we developed a new kind of substrate, the silver-coated anodic aluminum oxide (AAO), to investigate the characters of surface-enhanced resonant Raman scattering (SERRS) of the dilute single-walled carbon nanotubes. Homogeneous Ag-coated AAO substrate was obtained by decomposing the AgNO3 on the surface of AAO. single-walled carbon nanotubes (SWNTs) were directly grown onto this substrate through floating catalyst chemical vapor deposition method (CVD). SERRS of SWNTs was carried out using several different wavelength lasers. The bands coming from metallic SWNTs were significantly enhanced. The two SERRS mechanisms, the "electromagnetic" and "chemical" mechanism, were mainly responsible for the experiment results. (c) 2005 Elsevier B.V. All rights reserved.

WO3/C hybrid material as a highly active catalyst support for formic acid electrooxidation

The hybrid material based on WO3 and Vulcan XC-72R carbon has been used as the support of Pd nano-catalysts. The resultant Pd-WO3/C catalysts in a large range of WO3 content exhibit excellent catalytic activity and stability for formic acid electrooxidation. The great improvement in the catalytic performance is attributed to the uniform dispersion of Pd with less particle sizes on the WO3/C support and the hydrogen spillover effect which greatly accelerates the dehydrogenation of HCOOH on Pd.

Effect of pretreatment of black carbon on electrocatalytic activity of Pt/C catalyst for methanol oxidation

Direct methanol fuel cell (DMFC) has attracted wide attention due to its many advantages. However, its practical application is limited by the low electrocatalytic activity of the anodic Pt/C catalyst usually used for the methanol oxidation. In this paper, in order to increase the electrocatalytic performance of the Pt/C catalyst for the methanol oxidation, the black carbon, usually used as the supporter, was pretreated with CO2, air, HNO3 or H2O2. The cyclic voltarnmetric results indicated that the current densities of the anodic peak of methanol oxidation at the Pt/C catalysts with the black carbon pretreated with CO2,air, HN03, H202 and untreated black carbon were 39, 33, 32, 20 and 18 mA center dot cm(-2), respectively, illustrating that among the above five kinds of the Pt/C catalysts, the Pt/C catalyst with the black carbon pretreated with CO2 shows the best electrocatalytic activity and stability for the methanol oxidation. Its main reason is that the CO2 pretreatment could reduce the content of the oxygen-containing groups on the surface of the black carbon and increase the content of graphite in the black carbon, leading to the low resistance of the black carbon and the increase in the dispersion extent of the Pt particles in the Pt/C catalyst.

Oxygen reduction reaction on a Pt/carbon fuel cell catalyst in the presence of trace quantities of ammonium ions: An RRDE study

The effect of trace quantities of ammonia on oxygen reduction reaction (ORR) on carbon-supported platinum catalysts in perchloric acid solutions is assessed using rotating ring disk electrode (RRDE) technique. The study demonstrates that ammonia has detrimental effects on ORR. The most significant effect takes place in the potential region above 0.7 V vs RHE. The effect is explained by the electrochemical oxidation of ammonia, which blocks Pt active sites and increases the formation of H2O2. This leads to losses in the disk currents and increments in the ring currents. The apparent losses in ORR currents may occur in two ways, namely, through the blocking of the active sites for ORR as well as by generating a small anodic current, which is believed to have a lower contribution. In addition, a detrimental effect of sodium cations in the potential range below 0.75 V vs RHE was demonstrated. This effect is most likely due to the co-adsorption of sodium cations and perchlorate anions on the Pt surface. Copyright (C) 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.