Long lasting phosphorescence of Eu2+ in reduced SrO-B2O3 glasses

The blue long-lasting phosphorescence (LLP) phenomenon was observed for Eu2+-doped SrO-B2O3 glasses prepared in the reducing atmosphere. The phosphorescence peaks at about 450 nm due to the 4f5d -> 4f transition of Eu2+. With the doping of different amounts of Eu2+, the concentration-quenching phenomenon was observed for both the LLP and photoluminescence of the glasses, and the critical concentration for the two cases was same, i.e., 0.02 mol% Eu2+. And by the investigation of the TL curves, the content of Eu2+ had an effect on the trap depth of the samples. At last the possible mechanism of the LLP of the samples was suggested.

Study on the observation of Eu(2+) and Eu(3+) valence states in low silica calcium aluminosilicate glasses

The optical, magnetic and structural properties of Eu doped low silica calcium aluminosilicate glasses were investigated. The optical absorption coefficient presented two bands at 39 246 and 29 416 cm(-1), which were assigned respectively to the 4f(7) ((8)S(7/2)) -> 4f(6) (4F(J)) 5d (T(2g)), and 4f(7) ((8)S(7/2)) -> 4f(6) (4F(J)) 5d (E(g)) transitions of Eu(2+). The fluorescence measured at 300 K on a sample doped with 0.5 wt% of Eu(2)O(3) exhibited a broad band centered at 17 350 cm(-1), which is attributed to the 4f(6)5d -> 4f(7) transition of Eu(2+), whereas the additional peaks are due to the (5)D(0) -> (7)F(J) (J = 1, 2, 4) transitions of Eu(3+). From magnetization and XANES data it was possible to evaluate the fractions of Eu(2+) and Eu(3+) for the sample doped with 0.5 and 5.0 wt% of Eu(2)O(3), the values of which were approximately 30 and 70%, respectively.

Effect of network modifiers on spectroscopic properties of erbium-doped phosphate glasses

The integrated absorption cross section Sigma(abs), I peak emission cross section sigma(cmi), Judd-Ofeld intensity parameters Omega(iota) ( t = 2,4,6), and spontaneous emission probability A(R) of Er3+ ions were determined for Erbium doped alkali and alkaline earth phosphate glasses. It is found the compositional dependence of sigma(emi) 5 almost similar to that of Sigma(abs), which is determined by the sum, of Omega(1) (3 Omega(2) + 10 Omega(4) + 21 Omega(6)). In addition, the compositional dependence of Omega(1) was studied in these glass systems. As a result, compared with. Omega(4) and Omega(6) the Omega(2) has a stronger compositional dependence on the ionic radius and content of modifers. The covalency of Er-O bonds in phosphate glass is weaker than that in silicate glass, germanate glass, aluminate glass, and tellurate glass, since Omega(6) of phosphate glass is relatively large. A(R) is affected by the covalency of the Er3+ ion sites and corresponds to the Omega(6) value.

Thermal analysis of hydrotalcite synthesised from aluminate solutions

The aluminate hydrotalcites are proposed to have either of the following formulas: Mg4Al2(OH)12(CO3 2-)·xH2O or Mg4Al2(OH)12(CO3 2-, SO4 2-)·xH2O. A pure hydrotalcite phase forms when magnesium chloride and aluminate solns. are mixed at a 1:1 volumetric ratio at pH 14. The synthesis of the aluminate hydrotalcites using seawater results in the formation of an impurity phase bayerite. Two decompn. steps have been identified for the aluminate hydrotalcites: (1) removal of interlayer water (230 °C) and (2) simultaneous dehydroxylation and decarbonation (330 °C).

The synthesis and spectroscopic characterisation of hydrotalcite formed from aluminate solutions

Raman spectroscopy has been used to characterise nine hydrotalcites prepared from aluminate and magnesium solutions (magnesium chloride and seawater). The aluminate hydrotalcites are proposed to have the following formula Mg6Al2(OH)16(CO32-).xH2O, Mg6Al2(OH)16(CO32-,SO42-).xH2O, and Mg6Al2(OH)16(SO42-).xH2O. The synthesis of these hydrotalcites using seawater results in the intercalation of sulfate anions into the hydrotalcite interlayer. The spectra have been used to assess the molecular assembly of the cations and anions in the hydrotalcite structures. The spectra have been conveniently subdivided into spectral features based upon the carbonate anion, the hydroxyl units and water units. This investigation has shown the ideal conditions to form hydrotalcite from aluminate solutions is at pH 14 using magnesium chloride. Changes in synthesis conditions resulted in the formation of impurity products aragonite, thenardite, and gypsum.

Mesoporous bioactive glasses as drug delivery and bone tissue regeneration platforms

The use of mesoporous bioactive glasses (MBG) for drug delivery and bone tissue regeneration has grown significantly over the past 5 years. In this review, we highlight the recent advances made in the preparation of MBG particles, spheres, fibers and scaffolds. The advantages of MBG for drug delivery and bone scaffold applications are related to this material’s well-ordered mesopore channel structure, superior bioactivity, and the application for the delivery of both hydrophilic and hydrophobic drugs. A brief forward-looking perspective on the potential clinical applications of MBG in regenerative medicine is also discussed.

Preparation, characterisation and in vivo osteogenesis of mesoporous bioactive glasses

Bone defects, especially large bone defects, remain a major challenge in orthopaedic surgery. Autologous bone transplantation is considered the most effective treatment, but insufficient donor tissue, coupled with concerns about donor site morbidity, has hindered this approach in large-scale applications. Alternative approaches include implanting biomaterials such as bioactive glass (BG), which has been widely used for bone defect healing, due to having generally good biocompatibility, and can be gradually biodegraded during the process of new bone formation. Mesoporous bioactive glass (MBG) is a newly developed bioactive glass which has been proven to have enhanced in-vitro bioactivity; however the in-vivo osteogenesis has not been studied. A critical problem in using the bone tissue engineering approach to restore large bone defects is that the nutrient supply and cell viability at the centre of the scaffold is severely hampered since the diffusion distance of nutrients and oxygen for cell survival is limited to 150-200µm. Cobalt ions has been shown to mimic hypoxia, which plays a pivotal role in coupling angiogenesis with osteogenesis in-vivo by activating hypoxia inducing factor-1α (HIF-1α) transcription factor, subsequently initiating the expression of genes associated with tissue regeneration. Therefore, one aim of this study is to investigate the in-vivo osteogenesis of MBG by comparison with BG and β-TCP, which are widely used clinically. The other aim is to explore hypoxia-mimicking biomaterials by incorporating Cobalt into MBG and β-TCP. MBG and β-TCP incorporated with 5% cobalt (5Co-MBG and 5CCP) have also been studied in-vivo to determine whether the hypoxic effect has a beneficial effect on the bone formation. The composition and microstructure of synthesised materials (BG, MBG, 5Co-MBG, 5CCP) were characterised, along with the mesopore properties of the MBG materials. Dissolution and cytotoxicity of the Co-containing materials were also investigated. Femoral samples with defects harvested at 4 and 8 weeks were scanned using micro-CT followed by processing for histology (H&E staining) to determine bone formation. Histology of MBG showed a slower rate of bone formation at 4 weeks than BG, however at 8 weeks it could be clearly seen that MBG had more bone formation. The in-vivo results show that the osteogenesis of MBG reciprocates the enhanced performance shown in-vitro compared to BG. Dissolution study showed that Co ions can be efficiently released from MBG and β-TCP in a controllable way. Low amounts of Co incorporated into the MBG and β-TCP showed no significant cytotoxicity and the Co-MBG powders maintained a mesopore structure although not as highly ordered as pure MBG. Preliminary study has shown that Co incorporated samples showed little to no bone formation, instead incurring high lymphocyte activity. Further studies need to be done on Co incorporated materials to determine the cause for high lymphocyte activity in-vivo, which appear to hinder bone formation. In conclusion, this study demonstrated the osteogenic activity of MBG and provided some valuable information of tissue reaction to Co-incorporated MBG and TCP materials.

Organo-LDH synthesized via tricalcium aluminate hydration in the present of Na-dodecylbenzenesulfate aqueous solution and subsequent investigated by near-infrared and mid-infrared

Na-dodecylbenzenesulfate (SDBS), a natural anionic surfactant, has been successfully intercalated into a Ca based LDH host structure during tricalcium aluminate hydration in the presence of SDBS aqueous solution (CaAl-SDBS-LDH). The resulting product was characterized by powder X-ray diffraction (XRD), mid-infrared (MIR) spectroscopy combined with near-infrared (NIR) spectroscopy technique, thermal analysis (TG–DTA) and scan electron microscopy (SEM). The XRD results revealed that the interlayer distance of resultant product was expanded to 30.46 Å. MIR combined with NIR spectra offered an effective method to illustrate this intercalation. The NIR spectra (6000–5500 cm−1) displayed prominent bands to expound SDBS intercalated into hydration product of C3A. And the bands around 8300 cm−1 were assigned to the second overtone of the first fundamental of CH stretching vibrations of SDBS. In addition, thermal analysis showed that the dehydration and dehydroxylation took place at ca. 220 °C and 348 °C, respectively. The SEM results appeared approximately hexagonal platy crystallites morphology for CaAl-SDBS-LDH, with particle size smaller and thinner.

Removal of methyl orange from aqueous solutions through adsorption by calcium aluminate hydrates

Methyl orange (MO) is a kind of anionic dye and widely used in industry. In this study, tricalcium aluminate hydrates (Ca-Al-LDHs) are used as an adsorbent to remove methyl orange (MO) from aqueous solutions. The resulting products were studied by X-ray diffraction (XRD), infrared spectroscopy (MIR), thermal analysis (TG-DTA) and scanning electron microscope (SEM). The XRD results indicated that the MO molecules were successfully intercalated into the tricalcium aluminate hydrates, with the basal spacing of Ca-Al-LDH expanding to 2.48 nm. The MIR spectrum for CaAl-MO-LDH shows obvious bands assigned to the N@N, N@H stretching vibrations and S@O, SO_ 3 group respectively, which are considered as marks to assess MO_ ion intercalation into the interlayers of LDH. The overall morphology of CaAl-MOLDH displayed a ‘‘honey-comb’’ like structure, with the adjacent layers expanded.

Effective removal of zinc (II) from aqueous solutions by tricalcium aluminate (C3A)

Recently, studies have identified high zinc levels in various environmental resources, and excessive intake of zinc has long been considered to be harmful to human health. The aim of this research was to investigate the effectiveness of tricalcium aluminate (C3A) as a removal agent of zinc from aqueous solution. Inductively coupled plasma-atomic emission spectrometer (ICP-AES), X-ray diffraction (XRD) and scanning electron microscopy (SEM) have been used to characterize such removal behavior. The effects of various factors such as pH influence, temperature and contact time were investigated. The adsorption capacity of C3A for Zn2+ was computed to be up to 13.73 mmol g−1, and the highest zinc removal capacity was obtained when the initial pH of Zn(NO3)2 solution was between 6.0 and 7.0, with temperature around 308 K. The XRD analysis showed that the resultant products were ZnAl-LDHs. Combined with the analysis of solution component, it was proved the existence of both precipitation and cation exchange in the removal process. From the experimental results, it was clear that C3A could be potentially used as a cost-effective material for the removal of zinc in aqueous environment.