Reactive hot pressing of Ti-B-C and Ti-C at 1200 degrees C

Stoichiometric and non-stoichiometric powder mixtures of Ti-B4C and Ti-C with 1 wt% Ni were reactively hot pressed at 40 MPa, 1200 degrees C for 30 min. In both systems, the combined presence of Ni and non-stoichiometry enabled complete densification. While in Ti-C, non-stoichiometry by itself plays a significant role in promoting densification, the formation of intermediate borides in Ti-B4C powder mixtures requires the additional presence of Ni which promotes full reaction through the formation of a transient liquid as established previously in Ti-BN powder mixtures.

Materiale epigrafico per la ricostruzione dei contatti nel Mediterraneo tra il 1200 a.C. e il 500 a.C.

La Tesi Materiale epigrafico per la ricostruzione dei contatti nel Mediterraneo tra il 1200 a.C. e il 500 a.C. si propone di illustrare i complessi rapporti instauratisi tra i vari popoli che si affacciarono sulle rive del Mediterraneo e nelle sue vicinanze, tra il 1200 e il 500 a.C. circa, quali emergono dalle iscrizioni disponibili, principalmente greche e semitiche (soprattutto fenicie, ebraiche, aramaiche e assire), prendendo tuttavia in esame anche iscrizioni ittite, egiziane, frigie, etrusche e celtiche. Le date suddette riguardano due eventi cruciali, che sconvolsero il Mediterraneo: gli attacchi dei Popoli del Mare, che distrussero l'Impero Ittita e indebolirono l'Egitto, e le guerre Persiane. Le iscrizioni riportate sono 1546, quasi sempre traslitterate, tradotte, e accompagnate da un'immagine, da riferimenti bibliografici essenziali e da una breve motivazione del collegamento proposto. Il quadro che si delinea ben testimonia la complessità dei rapporti che si intrecciarono in quel periodo: si pensi alle centinaia di graffiti greci trovati a Naucrati, in Egitto, o alle decine di iscrizioni greche trovate a Gravisca. Anche le iscrizioni aramaiche e assire attestano gli stretti rapporti che si formarono tra Siria e Mesopotamia; ugualmente Iran e Arabia sono, direttamente o indirettamente, collegati a Etruria e Grecia; così troviamo un'iscrizione greca nel cuore dell'Impero Persiano, e un cratere laconico nel centro della Gallia. In realtà lo scopo di questo lavoro è anche quello di mettere in contatto due mondi sostanzialmente separati, ossia quello dei Semitisti e quello dei Grecisti, che solo apparentemente si conoscono e collaborano. Inoltre vorrei soavemente insinuare l'idea che la tesi di Joseph Naveh, che ipotizzò che gli alfabeti greci abbiano tratto origine in prima istanza dalle iscrizioni protocananaiche, nel XII sec. a.C., è valida, e che solo in un secondo tempo i Fenici abbiano dato il loro apporto.

Retention at room temperature of the tetragonal t ``-form in Sc(2)O(3)-doped ZrO(2) nanopowders

Synchrotron X-ray powder diffraction was applied to the study of the effect of crystallite size on the crystal structure of ZrO(2)-10 mol% Sc(2)O(3) nanopowders synthesized by a nitrate-lysine gel-combustion route Nanopowders with different average crystallite sizes were obtained by calcination at several temperatures, ranging from 650 to 1200 degrees C The metastable t""-form of the tetragonal phase, exhibiting a cubic unit cell and tetragonal P4(2)/nmc spatial symmetry, was retained at room temperature in fine nanocrystalline powders, completely avoiding the presence of the stable rhombohedral beta phase. Differently, this phase was identified in samples calcined at high temperatures and its content increased with increasing crystallite size The critical maximum crystallite size for the retention of the mestastable t""-form resulted of about 35 nm (C) 2009 Elsevier B.V All rights reserved

Basileîs en combate : Fundamentos de la autoridad en Homero

Los poemas homéricos muestran una sociedad en transición entre dos mundos, el del oîkos y el de la pólis, que comparten valores como la centralidad de lo bélico, pero que traducen esos valores en formas de liderazgo y patrones de conducta diferentes, en función de la creciente institucionalización que anuncia el surgimiento del Estado. El conflicto entre Aquiles y Agamenón puede leerse como reflejo de esa tensión, en la que la centralidad de lo bélico adopta dos formas diferentes y antagónicas. Aquiles, el mejor de los guerreros homéricos, representa valores anclados en una sociedad poco estratificada, en la que el líder es aquel que sobresale por sus características personales y cuyo lugar debe ser ratificado constantemente. Agamenón, en cambio, expresa una lógica que aparece con las transformaciones que surgen con el tránsito hacia una sociedad más estratificada: su liderazgo sigue siendo militar, pero su preeminencia sobre los otros basileîs no se basa ya en su destreza marcial, sino en su capacidad de reclutar una mayor capacidad de guerreros. El de la Ilíada es un mundo en el cual ambas lógicas están en tensión, y cuyo conflicto, en consecuencia, no puede saldarse sin matices en favor de ninguno de ellos.

Basileîs en combate : Fundamentos de la autoridad en Homero

Los poemas homéricos muestran una sociedad en transición entre dos mundos, el del oîkos y el de la pólis, que comparten valores como la centralidad de lo bélico, pero que traducen esos valores en formas de liderazgo y patrones de conducta diferentes, en función de la creciente institucionalización que anuncia el surgimiento del Estado. El conflicto entre Aquiles y Agamenón puede leerse como reflejo de esa tensión, en la que la centralidad de lo bélico adopta dos formas diferentes y antagónicas. Aquiles, el mejor de los guerreros homéricos, representa valores anclados en una sociedad poco estratificada, en la que el líder es aquel que sobresale por sus características personales y cuyo lugar debe ser ratificado constantemente. Agamenón, en cambio, expresa una lógica que aparece con las transformaciones que surgen con el tránsito hacia una sociedad más estratificada: su liderazgo sigue siendo militar, pero su preeminencia sobre los otros basileîs no se basa ya en su destreza marcial, sino en su capacidad de reclutar una mayor capacidad de guerreros. El de la Ilíada es un mundo en el cual ambas lógicas están en tensión, y cuyo conflicto, en consecuencia, no puede saldarse sin matices en favor de ninguno de ellos.

Evaluation of CaO-CeO2-partially stabilized zirconia thermal barrier coatings

Plasma sprayable powders were prepared from ZrO2-CaO-CeO2 system using an organic binder and coated onto stainless steel substrates previously coated by a bond coat (Ni 22Cr 20Al 1.0Y) using plasma spraying. The coatings exhibited good thermal barrier characteristics and excellent resistance to thermal shock at 1000 degrees C under simulated laboratory conditions (90 half hour cycles without failure) and at 1200 degrees C under accelerated burner rig test conditions (500 2 min cycles without failure). No destabilization of cubic/tetragonal ZrO2 phase fraction occured either during the long hours (45 h cumulative) or the large number of thermal shock tests. Growth of a distinct SiO2 rich region within the ceramic was observed in the specimens thermal shock cycled at 1000 degrees C apart from mild oxidation of the bond coat. The specimens tested at 1200 degrees C had a glassy appearance on the top surface and exhibited severe oxidation of the bond coat at the ceramic-bond coat interface. The glassy appearance of the surface is due to the formation of a liquid silicate layer attributable to the impurity phase present in commercial grade ZrO2 powder. These observations are supported by SEM analysis and quantitative EDAX data.

Validation of processing maps for 304L stainless steel using hot forging, rolling and extrusion

The development of a microstructure in 304L stainless steel during industrial hot-forming operations, including press forging (mean strain rate of 0.15 s(-1)), rolling/extrusion (2-5 s(-1)), and hammer forging (100 s(-1)) at different temperatures in the range 600-1200 degrees C, was studied with a view to validating the predictions of the processing map. The results have shown that excellent correlation exists between the regimes exhibited by the map and the product microstructures. 304L stainless steel exhibits instability bands when hammer forged at temperatures below 1100 degrees C, rolled/extruded below 1000 degrees C, or press forged below 800 degrees C. All of these conditions must be avoided in mechanical processing of the material. On the other hand, ideally, the material may be rolled, extruded, or press forged at 1200 degrees C to obtain a defect-free microstructure.

Thermal shock characteristics of plasma sprayed mullite coatings

Commercially available mullite (3Al(2)O(3). 2SiO(2)) powders containing oxides of calcium and iron as impurities, have been made suitable for plasma spraying by using an organic binder. Stainless steel substrates covered with Ni-22Cr-10Al-1.0Y bond coat were spray coated with mullite, The 425 mu m thick coatings were subjected to thermal shock cycling under burner rig conditions between 1000 and 1200 degrees C and less than 200 degrees C with holding times of 1, 5, and 30 min. While the coatings withstood as high as 1000 shock cycles without failure between 1000 and 200 degrees C, spallation occurred early at 120 cycles when shocked from 1200 degrees C, The coatings appeared to go through a process of self erosion at high temperatures resulting in loss of material. Also observed were changes attributable to melting of the silicate grains, which smooth down the surface. Oxidation of the bond coat did not appear to influence the failure, These observations were supported by detailed scanning electron microscopy and quantitative chemical composition analysis, differential thermal analysis, and surface roughness measurements.

Mechanical processing and microstructural control in hot working of hot isostatically pressed P/M IN-100 superalloy

The hot deformation behavior of hot isostatically pressed (HIPd) P/M IN-100 superalloy has been studied in the temperature range 1000-1200 degrees C and strain rate range 0.0003-10 s(-1) using hot compression testing. A processing map has been developed on the basis of these data and using the principles of dynamic materials modelling. The map exhibited three domains: one at 1050 degrees C and 0.01 s(-1), with a peak efficiency of power dissipation of approximate to 32%, the second at 1150 degrees C and 10 s(-1), with a peak efficiency of approximate to 36% and the third at 1200 degrees C and 0.1 s(-1), with a similar efficiency. On the basis of optical and electron microscopic observations, the first domain was interpreted to represent dynamic recovery of the gamma phase, the second domain represents dynamic recrystallization (DRX) of gamma in the presence of softer gamma', while the third domain represents DRX of the gamma phase only. The gamma' phase is stable upto 1150 degrees C, gets deformed below this temperature and the chunky gamma' accumulates dislocations, which at larger strains cause cracking of this phase. At temperatures lower than 1080 degrees C and strain rates higher than 0.1 s(-1), the material exhibits flow instability, manifested in the form of adiabatic shear bands. The material may be subjected to mechanical processing without cracking or instabilities at 1200 degrees C and 0.1 s(-1), which are the conditions for DRX of the gamma phase.

Study of (Ba3MMWO9)-M-II-W-IV (M-II = Ca, Zn; M-IV = Ti, Zr) perovskite oxides: Competition between 3C and 6H perovskite structures

We describe an investigation of (Ba3MMWO9)-M-II-W-IV oxides for M-II = Ca, Zn, and other divalent metals and M-IV = Ti, Zr. In general, a 1:2-ordered 6H (hexagonal, P6(3)/mmc) perovskite structure is stabilized at high temperatures (1300 degrees C) for all of the (Ba3MTiWO9)-Ti-II oxides investigated. An intermediate phase possessing a partially ordered 1:1 double perovskite (3C) structure with the cation distribution, Ba-2(Zn2/3Ti1/3)(W2/3Ti1/3)O-6, is obtained at 1200 degrees C for Ba3ZnTiWO9. Sr substitution for Ba in the latter stabilizes the cubic 3C structure instead of the 6H structure. A metastable Ba3CaZrWO9 that adopts the 3C (cubic, Fm (3) over barm) structure has also been synthesized by a low-temperature metathesis route. Besides yielding several new perovskite oxides that may be useful as dielectric ceramics, the present investigation provides new insights into the complex interplay of crystal chemistry (tolerance factor) and chemical bonding (anion polarization and d(0)-induced distortion of metal-oxygen octahedra) in the stabilization of 6H versus 3C perovskite structures for the (Ba3MMWO9)-M-II-W-IV series.

Study of (Ba3MMWO9)-M-II-W-IV (M-II = Ca, Zn; M-IV = Ti, Zr) perovskite oxides: Competition between 3C and 6H perovskite structures

We describe an investigation of (Ba3MMWO9)-M-II-W-IV oxides for M-II = Ca, Zn, and other divalent metals and M-IV = Ti, Zr. In general, a 1:2-ordered 6H (hexagonal, P6(3)/mmc) perovskite structure is stabilized at high temperatures (1300 degrees C) for all of the (Ba3MTiWO9)-Ti-II oxides investigated. An intermediate phase possessing a partially ordered 1:1 double perovskite (3C) structure with the cation distribution, Ba-2(Zn2/3Ti1/3)(W2/3Ti1/3)O-6, is obtained at 1200 degrees C for Ba3ZnTiWO9. Sr substitution for Ba in the latter stabilizes the cubic 3C structure instead of the 6H structure. A metastable Ba3CaZrWO9 that adopts the 3C (cubic, Fm (3) over barm) structure has also been synthesized by a low-temperature metathesis route. Besides yielding several new perovskite oxides that may be useful as dielectric ceramics, the present investigation provides new insights into the complex interplay of crystal chemistry (tolerance factor) and chemical bonding (anion polarization and d(0)-induced distortion of metal-oxygen octahedra) in the stabilization of 6H versus 3C perovskite structures for the (Ba3MMWO9)-M-II-W-IV series.

Effect of fuel on the formation structure, transport and magnetic properties of LaMnO3+nanopowders

Single-step low-temperature solution combustion (LCS) synthesis was adopted for the preparation of LaMnO3+ (LM) nanopowders. The powders were well characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS),surface area and Fourier transform infrared spectroscopy (FTIR). The PXRD of as-formed LM showed a cubic phase but, upon calcination (900degrees C, 6 h), it transformed into a rhombohedral phase. The effect of fuel on the formation of LM was examined, and its structure and magnetoresistance properties were investigated. Magnetoresistance (MR) measurements on LM were carried out at 0, 1, 4 and 7 T between 300 and 10 K. LM (fuel-to-oxidizer ratio; = 1) showed an MR of 17% at 1 T, whereas, for 4 and 7 T, it exhibited an MR of 45 and 55%, respectively, near the TM-I. Metallic resistivity data below TM-I showed that the double exchange interaction played a major role in this compound. It was interesting to observe that the sample calcined at 1200 degrees C for 3 h exhibited insulator behavior.

Synthesis and Densification of Monolithic Zirconium Carbide by Reactive Hot Pressing

Synthesis and densification of monolithic zirconium carbide (ZrC) has been carried out by reactive hot pressing of zirconium (Zr) and graphite (C) powders in the molar ratios 1:1, 1.25:1, 1.5:1, and 2:1 at 40 MPa, 1200 degrees-1600 degrees C. Monolithic ZrC could be synthesized with a C/Zr ratio similar to 0.5-1.0 and the post heat-treated samples have the lattice parameter in the range 4.665 to 4.698 A. Densification improves with an increasing deviation from the stoichiometry. Fine-grained (similar to 1 mu m) and nearly fully dense material (99% RD) could be obtained at a temperature as low as 1200 degrees C with C/Zr similar to 0.67. Microstructural and XRD observations suggest that densification occurred at low temperatures with nonstoichiometric Zr-C powder mixtures.

Characterisation of dynamic recrystallisation in nickel using processing map for hot deformation

The hot deformation behaviour of polycrystalline nickel has been characterised in the temperature range 750-1200-degrees-C and strain rate range 0.0003-100 s-1 using processing maps developed in the basis of the dynamic materials model. The efficiency of power dissipation, given by [2m/(m + 1)]. where m is the strain rate sensitivity, is plotted as a function of temperature and strain rate to obtain a processing map. A domain of dynamic recrystallisation has been identified, with a peak efficiency of 31% occurring at 925-degrees-C and 1 s-1. The published results are in agreement with the prediction of the processing map. The variations of efficiency of power dissipation with temperature and strain rate in the dynamic recrystallisation domain are identical to the corresponding variation of hot ductility. The stress-strain curves exhibited a single peak in a single peak in the dynamic recrystallisation domain, whereas multiple peaks and 'drooping' stress-strain curves were observed at lower and higher strain rates, respectively. The results are explained on the basis of a simple model which considers dynamic recrystallisation in terms of rates of interface formation (nucleation) and migration (growth). It is shown that dynamic recrystallisation in nickel is controlled by the rate of nucleation, which is slower than the rate of migration. The rate of nucleation itself depends on the process of thermal recovery by climb, which in turn depends on self-diffusion.