Unusual resistivity hysteresis in a bulk magnetoresistive ferromagnetic/ferrimagnetic composite (La0.7 Ca0.3 Mn O3 Mn3 O4): Role of demagnetization effects

The authors report an intriguing resistivity versus magnetic field dependence in polycrystalline composite samples containing a magnetoresistive manganite (ferromagnetic/conducting La0.7 Ca0.3 Mn O3) and a magnetic manganese oxide (ferrimagnetic/insulating Mn3 O4). At 10 K, when the magnetic field is scanned from positive to negative values, the resistance peak occurs at positive magnetic field, instead of zero or negative field as usually observed in polycrystalline manganite samples. The position of the resistance peak agrees well with the cancellation of the internal magnetic field, suggesting that the demagnetization effects are responsible for this behavior. © 2007 American Institute of Physics.

Evaluation of rare earth oxides doping SnO2.(Co1/4,Mn3/4)O-based varistor system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Vibrational spectroscopic study of the mineral tsumebite Pb2Cu(PO4,SO4) (OH)

The mineral tsumebite Pb2Cu(PO4)(SO4)(OH), a copper phosphate-sulfate hydroxide of the brackebuschite group has been characterised by Raman and infrared spectroscopy. The brackebuschite mineral group are a series of monoclinic arsenates, phosphates and vanadates of the general formula A2B(XO4)(OH,H2O), where A may be Ba, Ca, Pb, Sr, while B may be Al, Cu2+,Fe2+, Fe3+, Mn2+, Mn3+, Zn and XO4 may be AsO4, PO4, SO4,VO4. Bands are assigned to the stretching and bending modes of PO43- and HOPO3 units. Hydrogen bond distances are calculated based upon the position of the OH stretching vibrations and range from 2.759 Ã… to 3.205 Ã…. This range of hydrogen bonding contributes to the stability of the mineral.

Raman spectroscopy of the multi anion mineral arsentsumebite Pb2Cu(AsO4)(SO4)(OH) and in comparison with tsumebite Pb2Cu(PO4)(SO4)(OH)

The mineral arsentsumebite Pb2Cu(AsO4)(SO4)(OH), a copper arsenate-sulfate hydroxide of the brackebuschite group has been characterised by Raman spectroscopy. The brackebuschite mineral group are a series of monoclinic arsenates, phosphates and vanadates of the general formula A2B(XO4)(OH,H2O), where A may be Ba, Ca, Pb, Sr, while B may be Al, Cu2+,Fe2+, Fe3+, Mn2+, Mn3+, Zn and XO4 may be AsO4, PO4, SO4,VO4. Bands are assigned to the stretching and bending modes of SO42- AsO43- and HOAsO3 units. Raman spectroscopy readily distinguishes between the two minerals arsentsumebite and tsumebite. Raman bands attributed to arsenate are not observed in the Raman spectrum of tsumebite. Phosphate bands found in the Raman spectrum of tsumebite are not found in the Raman spectrum of arsentsumebite. Raman spectroscopy readily distinguishes the two minerals tsumebite and arsentsumebite.

Vibrational spectroscopic characterization of the phosphate mineral hureaulite – (Mn, Fe)5(PO4)2(HPO4)2·4(H2O)

This research was done on hureaulite samples from the Cigana claim, a lithium bearing pegmatite with triphylite and spodumene. The mine is located in Conselheiro Pena, east of Minas Gerais. Chemical analysis was carried out by Electron Microprobe analysis and indicated a manganese rich phase with partial substitution of iron. The calculated chemical formula of the studied sample is: (Mn3.23, Fe1.04, Ca0.19, Mg0.13)(PO4)2.7(HPO4)2.6(OH)4.78. The Raman spectrum of hureaulite is dominated by an intense sharp band at 959 cm−1 assigned to PO stretching vibrations of HPO42− units. The Raman band at 989 cm−1 is assigned to the PO43− stretching vibration. Raman bands at 1007, 1024, 1047, and 1083 cm−1 are attributed to both the HOP and PO antisymmetric stretching vibrations of HPO42− and PO43− units. A set of Raman bands at 531, 543, 564 and 582 cm−1 are assigned to the ν4 bending modes of the HPO42− and PO43− units. Raman bands observed at 414, and 455 cm−1 are attributed to the ν2 HPO42− and PO43− units. The intense A series of Raman and infrared bands in the OH stretching region are assigned to water stretching vibrations. Based upon the position of these bands hydrogen bond distances are calculated. Hydrogen bond distances are short indicating very strong hydrogen bonding in the hureaulite structure. A combination of Raman and infrared spectroscopy enabled aspects of the molecular structure of the mineral hureaulite to be understood.

Energetics of rare earth manganese perovskites A1-xA ' xMnO3 (A = La, Nd, Y and A ' = Sr, La) systems

High temperature reaction calorimetry using molten lead berate as solvent has been used to study the thermochemistry of NdMnO3, YMnO3, La1-xSrxMnO3 (with 0 < x < 0.5), and Ln(0.5)Ca(0.5)MnO(3) (with Ln = La, Nd, Y), The enthalpies of formation of these multicomponent oxides from their binary constituents have been calculated from the measured enthalpy of drop solution, The energetic stability of the perovskite depends on the size of the A cation, The enthalpy of formation of YMnO3 (smallest A cation) is more endothermic than those of NdMnO3 and LaMnO3. The energetics of the perovskite also depends on the oxidation state of the B site's ions. In the La1-xSrxMnO3 system, the energetic stability of the structure increases with the Mn4+/Mn3+ ratio, The new values of the enthalpies of oxidations, with reliable standard entropies, were used to plot the phase stability diagram of the lanthanum-manganese-oxygen system in the temperature range 300-1100 K, The LaMnO3/MnO phase boundary evaluated in this study agrees with the one published by Atsumi et nl. calculated from thermogravimetric and conductivity measurements.

Spectroscopic investigations of manganese ions in microwave-prepared NaPO3-PbO glasses

The EPR spectra of microwave-prepared 70NaPO(3):30PbO glasses containing different weight percentages of manganese ions have been studied. The EPR spectra exhibit a well-resolved hyperfine pattern at g(eff) approximate to 2.0. Optical absorption, fluorescent emission and excitation spectra of the glasses have been examined. The absorption spectrum exhibits a peak near 500 nm and this has been attributed to the spin-allowed E-5(g) --> T-5(2g) transition of Mn3+ ions. The emission spectrum shows a band at 595 nm which has been assigned to the T-4(1g)(G) --> (6)A(1g)(S) spin-forbidden transition of Mn2+ ions in octahedral coordination. Concentration quenching of fluorescence was found to occur above 0.75 wt% of Mn2+ ions. The excitation spectra exhibit four bands characteristic of Mn2+ ions in octahedral coordination. From the observed band positions of the excitation spectra, the crystal field parameter D-q and the Racah interelectronic repulsion parameters, B and C have been calculated. A structural model is proposed based on the IR, Raman and MASNMR studies according to which Mn2+ ions are likely to occupy sites similar to Na+ ions in these glasses.

Phase transitions and rare-earth magnetism in hexagonal and orthorhombic $DyMnO_{3}$ single crystals

The floating-zone method with different growth ambiences has been used to selectively obtain hexagonal or orthorhombic DyMnO3 single crystals. The crystals were characterized by x-ray powder diffraction of ground specimens and a structure refinement as well as electron diffraction. We report magnetic susceptibility, magnetization and specific heat studies of this multiferroic compound in both the hexagonal and the orthorhombic structure. The hexagonal DyMnO3 shows magnetic ordering of Mn3+ (S = 2) spins on a triangular Mn lattice at T-N(Mn) = 57 K characterized by a cusp in the specific heat. This transition is not apparent in the magnetic susceptibility due to the frustration on the Mn triangular lattice and the dominating paramagnetic susceptibility of the Dy3+ (S = 9/2) spins. At T-N(Dy) = 3 K, a partial antiferromagnetic order of Dy moments has been observed. In comparison, the magnetic data for orthorhombic DyMnO3 display three transitions. The data broadly agree with results from earlier neutron diffraction experiments, which allows for the following assignment: a transition from an incommensurate antiferromagnetic ordering of Mn3+ spins at T-N(Mn) = 39 K, a lock-in transition at Tlock-in = 16 K and a second antiferromagnetic transition at T-N(Dy) = 5 K due to the ordering of Dy moments. Both the hexagonal and the orthorhombic crystals show magnetic anisotropy and complex magnetic properties due to 4f-4f and 4f-3d couplings.

Phase Equilibria in the System $Al_{2}O_{3}-CaO-CoO$ and Gibbs Energy of Formation of $Ca_{3}CoAl_{4}O_{10}$

The floating-zone method with different growth ambiences has been used to selectively obtain hexagonal or orthorhombic DyMnO3 single crystals. The crystals were characterized by x-ray powder diffraction of ground specimens and a structure refinement as well as electron diffraction. We report magnetic susceptibility, magnetization and specific heat studies of this multiferroic compound in both the hexagonal and the orthorhombic structure. The hexagonal DyMnO3 shows magnetic ordering of Mn3+ (S = 2) spins on a triangular Mn lattice at T-N(Mn) = 57 K characterized by a cusp in the specific heat. This transition is not apparent in the magnetic susceptibility due to the frustration on the Mn triangular lattice and the dominating paramagnetic susceptibility of the Dy3+ (S = 9/2) spins. At T-N(Dy) = 3 K, a partial antiferromagnetic order of Dy moments has been observed. In comparison, the magnetic data for orthorhombic DyMnO3 display three transitions. The data broadly agree with results from earlier neutron diffraction experiments, which allows for the following assignment: a transition from an incommensurate antiferromagnetic ordering of Mn3+ spins at T-N(Mn) = 39 K, a lock-in transition at Tlock-in = 16 K and a second antiferromagnetic transition at T-N(Dy) = 5 K due to the ordering of Dy moments. Both the hexagonal and the orthorhombic crystals show magnetic anisotropy and complex magnetic properties due to 4f-4f and 4f-3d couplings.

Phase conversions in calcium manganites with changing Ca/Mn ratios and their influence on the electrical transport properties

The phase-interconversions between the spinel-, brownmillerite-, defect rocksalt and perovskite-type structures have been investigated by way of (i) introducing deficiency in A-sites in CaxMn2-xO3 (0.05 <= x <= 1) i.e., by varying Ca/Mn ratio from 0.025 to 1 and (ii) nonstoichiometric CaMnO3-delta (CMO) with 0.02 <= delta <= 1. The temperature dependence of resistivity (rho-T) have been investigated on nonstoichiometric CaMnO3-delta (undoped) as well as the CMO substituted with donor impurities such as La3+, Y3+, Bi3+ or acceptor such as Na1+ ion at the Ca-site. The rho-T characteristics of nonstoichiometric CaMnO3-delta is strongly influenced by oxygen deficiency, which controls the concentration of Mn3+ ions and, in turn, affects the resistivity, rho. The results indicated that the substitution of aliovalent impurities at Ca-site in CaMnO3 has similar effects as of CaMnO3-delta ( undoped) annealed in atmospheres of varying partial pressures whereby electron or hole concentration can be altered, yet the doped samples can be processed in air or atmospheres of higher P-O2. The charge transport mechanisms of nonstoichiometric CaMnO3-delta as against the donor or acceptor doped CaMnO3 (sintered in air, P-O2 similar to 0.2 atm) have been predicted. The rho (T) curves of both donor doped CaMnO3 as well as non-stoichiometric CaMnO3-delta, is predictable by the small polaron hopping (SPH) model, which changes to the variable range hopping (VRH) at low temperatures whereas the acceptor doped CaMnO3 exhibited an activated semiconducting hopping ( ASH) throughout the measured range of temperature (10-500 K).

EPR study on the role of Mn in enhancing PTC of BaTiO3

Low concentration of Mn (< 0.05 atom%) added to lanthanide-doped ceramics for enhancing the PTC effect did not show any EPR signal due to Mn in the tetragonal phase. Above Tc (400 K) it showed the six-line signal arising from Mn2+. This is explained on the basis of Mn existing as Mn3+ ion with short relaxation time at room temperature. Oxidation state changes to Mn2+ above Tc; thus Mn3+ acts as an electron trap. This augments the function of activated defect centres (VBa /ag VBa) in diminishing the charge carrier concentration across the phase transformation.

Role of Mn impurity in the deterioration of ZnS:Cu, Br electroluminescent phosphors

ZnS:Cu, Br powder EL phosphors showed 6-line EPR signal at 25°C whose intensity increases with Cu content and on annealing in Zn-vapour. The signal arises from native Mn impurity. The starting material does not show any EPR signal since Mn2+ acts as an affinity potential well for a hole in ZnS, forming Mn3+ - a chemically uncommon situation in sulfides. In doped ZnS, holes are trapped at Cu such that Mn2+ persists. Deterioration of EL brightness is accompanied by the decrease in EPR signal intensity due to field assisted hole transference to Mn2+. Intentional addition of Mn in ZnS:Cu, Br decreases the brightness and shortens life time. Stable phosphors require ZnS with Mn content less than 1014 cm−3.

Valence states and magnetic properties of LaNi1-xMnxO3 (for 0≤x≤0.2 and x=0.5)

Single-phase LaNi1-xMnxO3 samples in the compositional range 0<or=x<or=0.2 were prepared by the decomposition of precursor hydroxide solid solutions, and La2NiMnO6 was prepared from a mixture of carbonates. All the samples contained a disordered array of nickel and manganese ions. X-ray absorption and XPS measurements indicate the presence of Mn(III) and Ni(III) valence states at room temperature for x=0.1, 0.2 and 0.5. Magnetic susceptibility data suggest Mn4+ solute ions and Stoner-enhanced Pauli paramagnetism of the metallic solvent for x=0.01 with a smooth transition to Mn3+ solute ions and a spontaneously magnetised solvent conduction band at x=0.05. Below 200K, the x=0.05 sample forms superparamagnetic clusters, and below 40K there is evidence for an antiferromagnet spin-density wave. Comparisons with LaCo0.95Mn0.05O3 and La0.98Sr0.02CoO3 confirm that the long-range magnetic coupling occurs via solvent electrons in a narrow conduction band. The conductivity changes from that of a narrow-band metal for x<0.01 to that more characteristic of diffusive motion for x>0.05, but any motional enthalpy appears to remain small ( Delta Hm approximately=0). The x=0.1 sample exhibits ferrimagnetic spin glass behaviour below 40K, and the ferromagnetic interactions increase with manganese concentration. The oxide with x=0.50 is ferromagnetic with a well defined Curie temperature.

Synthesis, structural and ferromagnetic properties of La1-xKxMnO3 (0.0 &lt;= x &lt;= 0.25) phases by solution combustion method

We describe the solution combustion synthesis and characterization of La1-xKxMnO3 (0.0 &lt;= x &lt;= 0.25) perovskite phases, which is a low temperature initiated, rapid route to prepare metal oxides. As-synthesized compounds are amorphous in nature; crystallinity was observed on heating at 800 degrees C for 5 min. Structural parameters were determined by the Rietveld refinement method using powder XRD data. Parent LaMnO3 compound crystallizes in the orthorhombic structure (space group Pbnm, No. 62). Potassium substituted compounds were crystallized with rhombohedral symmetry (space group R-3c, No. 167). The ratio of the Mn3+/Mn4+ was determined by the iodometric titration. The Fourier transform infrared spectrum (FTIR) shows two absorption bands for Mn-O stretching vibration (v, mode), Mn-O-Mn deformation vibration (v(b) mode) around 600 cm(-1) and 400 cm(-1) for the compositions, x = 0.0, 0.05 and 0-10. Four-probe electrical resistivity measurements reveal a composition controlled metal to insulator transition (TM-1), the maximum TM-1 was observed for the composition La0.85K0.15MnO3 at 287 K. Room temperature vibrating sample magnetometer data indicate that for the composition up to x = 0-10, the compounds are paramagnetic whereas composition with x = 0.15, 0.20 and 0.25 show magnetic moments of 27, 29 and 30 emu/g, respectively.

Uncoupled surface spin induced exchange bias in α-MnO 2 nanowires

We have studied the microstructure, surface states, valence fluctuations, magnetic properties, and exchange bias effect in MnO2 nanowires. High purity α-MnO 2 rectangular nanowires were synthesized by a facile hydrothermal method with microwave-assisted procedures. The microstructure analysis indicates that the nanowires grow in the [0 0 1] direction with the (2 1 0) plane as the surface. Mn3+ and Mn2+ ions are not found in the system by X-ray photoelectron spectroscopy. The effective magnetic moment of the manganese ions fits in with the theoretical and experimental values of Mn4+ very well. The uncoupled spins in 3d3 orbitals of the Mn 4+ ions in MnO 6 octahedra on the rough surface are responsible for the net magnetic moment. Spin glass behavior is observed through magnetic measurements. Furthermore, the exchange bias effect is observed for the first time in pure α-MnO2 phase due to the coupling of the surface spin glass with the antiferromagnetic α-MnO2 matrix. These α-MnO2 nanowires, with a spin-glass-like behavior and with an exchange bias effect excited by the uncoupled surface spins, should therefore inspire further study concerning the origin, theory, and applicability of surface structure induced magnetism in nanostructures.