Clustering phenomena in Al-4.4 at. % Zn alloy with 0.03 and 0.08 at. % Ag additions

The influence of 0.03 and 0.08 at. % Ag additions on the clustering of Zn atoms in an Al-4.4 at. % Zn alloy has been studied by resistometry. The effect of quenching and ageing temperatures shows that the ageing-ratio method of calculating the vacancy-solute atom binding energy is not applicable to these alloys. Zone-formation in Al-Zn is unaffected by Ag additions, but the zone-reversion process seems to be influenced. Apparent vacancy-formation energies in the binary and ternary alloys have been used to evaluate the v-Ag atom binding energy as 0.21 eV. It is proposed that, Ag and Zn being similar in size, the relative vacancy binding results from valency effects, and that in Al-Zn-Ag alloys clusters of Zn and Ag may form simultaneously, unaffected by the presence of each other. © 1970 Chapman and Hall Ltd.

Ti_(0.17)Zr_(0.08)V_(0.34)Nb_(0.01)Cr_(0.1)Ni_(0.3)氢化物电极合金微观结构及电化学性能研究

采用XRD、FESEM-EDS、ICP及EIS等方法研究了Ti0.17Zr0.08V0.34Nb0.01Cr0.1Ni0.3氢化物电极合金微观结构和电化学性能。X射线衍射分析表明:该合金由体心立方结构(bcc)的V基固溶体主相和少量六方结构的C14型Laves相组成;FESEM及EDS分析表明:V基固溶体主相形成树枝晶,C14型Laves相呈网格状围绕着树枝晶的晶界,元素在两相中的分布呈现镜像关系。电化学性能测试结果表明:该合金的氢化物电极在303￣343K较宽的温度区间内,表现出较高的电化学容量,在303K和343K时,电化学容量分别为337.0mAh·g-1和327.9mAh·g-1。在303K循环100周后,容量为282.7mAh·g-1。ICP分析结果表明,氢化物电极在充放电循环过程中,V及Zr元素向KOH电解质中的溶出较为严重。EIS研究表明,金属氢化物电极表面电化学反应的电荷转移电阻(RT)随循环次数的增加而增加,相应的交换电流密度则随循环次数的增加而降低。氢化物电极循环过程中RT的增大以及V和Zr元素的溶解,可能是导致电极容量衰减的主要原因。

Estudo da resistência à corrosão de ligas Ni-Cr-Mo-Ta E Ni-Cr-Mo-W em solução NaF 0,08 mol/L, pH 4,7 para aplicações odontológicas

A large number of metal alloys are used in Dentistry for the manufacture of fixed and removable dentures. In the oral cavity, these structures are exposed to a chemically aggressive medium, like saliva and mechanical efforts, like mastication. In addition, acidic solutions containing fluoride ions are also frequently used in dental treatments to prevent dental plates and decays development. In this context, it was considered important to investigate the influence that a fourth element could exert when added to the ternary alloy Ni-Cr-Mo, largely used in Brazil. Therefore, electrochemical tests were done to evaluate the resistance to corrosion of quaternary alloy 65Ni-25Cr-5Mo-5Ta and 65Ni-25Cr-5Mo-5W in NaF solution 0,08mol / L, pH = 4.7. For greater understanding the microstructure and morphology of alloys were studied, through metallographic analysis, using optics microscopy and electron microscopy scanning. For the electrochemical tests were applied techniques traditionally used in corrosion researches, such as: potential measures in open circuit (OCP) and cyclic polarization (CP). It was found that both quaternary alloys showed very similar results. Comparing these quaternary alloys with the ternary 65Ni-25Cr-10Mo, it was found that the quaternary alloys exhibit greater resistance to corrosion, in other words, less passivation current density than the ternary alloy, showing that it is advantageous to add a fourth element in the alloy

Estudo da resistência à corrosão de ligas Ni-Cr-Mo-Ta E Ni-Cr-Mo-W em solução NaF 0,08 mol/L, pH 4,7 para aplicações odontológicas

A large number of metal alloys are used in Dentistry for the manufacture of fixed and removable dentures. In the oral cavity, these structures are exposed to a chemically aggressive medium, like saliva and mechanical efforts, like mastication. In addition, acidic solutions containing fluoride ions are also frequently used in dental treatments to prevent dental plates and decays development. In this context, it was considered important to investigate the influence that a fourth element could exert when added to the ternary alloy Ni-Cr-Mo, largely used in Brazil. Therefore, electrochemical tests were done to evaluate the resistance to corrosion of quaternary alloy 65Ni-25Cr-5Mo-5Ta and 65Ni-25Cr-5Mo-5W in NaF solution 0,08mol / L, pH = 4.7. For greater understanding the microstructure and morphology of alloys were studied, through metallographic analysis, using optics microscopy and electron microscopy scanning. For the electrochemical tests were applied techniques traditionally used in corrosion researches, such as: potential measures in open circuit (OCP) and cyclic polarization (CP). It was found that both quaternary alloys showed very similar results. Comparing these quaternary alloys with the ternary 65Ni-25Cr-10Mo, it was found that the quaternary alloys exhibit greater resistance to corrosion, in other words, less passivation current density than the ternary alloy, showing that it is advantageous to add a fourth element in the alloy

Production of K*(892)(0) and phi(1020) in pp collisions at root s=7 TeV

The production of K*(892)(0) and phi(1020) in pp collisions at root s = 7 TeV was measured by the ALICE experiment at the LHC. The yields and the transverse momentum spectra d(2)N/dydp(T) at midrapidity vertical bar y vertical bar < 0.5 in the range 0 < p(T) < 6 GeV/c for K*(892)(0) and 0.4 < p(T) < 6 GeV/c for phi(1020) are reported and compared to model predictions. Using the yield of pions, kaons, and Omega baryons measured previously by ALICE at root s = 7 TeV, the ratios K*/K-, phi/K*, phi/ K-, phi/pi(-), and (Omega + <(Omega)over bar>)/phi are presented. The values of the K*/K-, phi/K* and phi/K- ratios are similar to those found at lower centre-of-mass energies. In contrast, the phi/pi(-) ratio, which has been observed to increase with energy, seems to saturate above 200 GeV. The (Omega + (Omega) over bar)/phi ratio in the p(T) range 1-5 GeV/ c is found to be in good agreement with the prediction of the HIJING/B (B) over bar v2.0model with a strong colour field.