Determination of the mechanical properties of amorphous materials through instrumented nanoindentation

A novel methodology based on instrumented indentation is developed to determine the mechanical properties of amorphous materials which present cohesive-frictional behaviour. The approach is based on the concept of a universal hardness equation, which results from the assumption of a characteristic indentation pressure proportional to the hardness. The actual universal hardness equation is obtained from a detailed finite element analysis of the process of sharp indentation for a very wide range of material properties, and the inverse problem (i.e. how to extract the elastic modulus, the compressive yield strength and the friction angle) from instrumented indentation is solved. The applicability and limitations of the novel approach are highlighted. Finally, the model is validated against experimental data in metallic and ceramic glasses as well as polymers, covering a wide range of amorphous materials in terms of elastic modulus, yield strength and friction angle.

Comportamiento mecánico de nuevas aleaciones de wolframio en función de la temperatura

La presente memoria de tesis tiene como objetivo principal la caracterización mecánica en función de la temperatura de nueve aleaciones de wolframio con contenidos diferentes en titanio, vanadio, itria y lantana. Las aleaciones estudiadas son las siguientes: W-0.5%Y2O3, W-2%Ti, W-2% Ti-0.5% Y2O3, W-4% Ti-0.5% Y2O3, W-2%V, W- 2%Vmix, W-4%V, W-1%La2O3 and W-4%V-1%La2O3. Todos ellos, además del wolframio puro se fabrican mediante compresión isostática en caliente (HIP) y son suministradas por la Universidad Carlos III de Madrid. La investigación se desarrolla a través de un estudio sistemático basado en ensayos físicos y mecánicos, así como el análisis post mortem de las muestras ensayadas. Para realizar dicha caracterización mecánica se aplican diferentes ensayos mecánicos, la mayoría de ellos realizados en el intervalo de temperatura de 25 a 1000 º C. Los ensayos de caracterización que se llevan a cabo son: • Densidad • Dureza Vicker • Módulo de elasticidad y su evolución con la temperatura • Límite elástico o resistencia a la flexión máxima, y su evolución con la temperatura • Resistencia a la fractura y su comportamiento con la temperatura. • Análisis microestructural • Análisis fractográfico • Análisis de la relación microestructura-comportamiento macroscópico. El estudio comienza con una introducción acerca de los sistemas en los que estos materiales son candidatos para su aplicación, para comprender las condiciones a las que los materiales serán expuestos. En este caso, el componente que determina las condiciones es el Divertor del reactor de energía de fusión por confinamiento magnético. Parece obvio que su uso en los componentes del reactor de fusión, más exactamente como materiales de cara al plasma (Plasma Facing Components o PFC), hace que estas aleaciones trabajen bajo condiciones de irradiación de neutrones. Además, el hecho de que sean materiales nuevos hace necesario un estudio previo de las características básicas que garantice los requisitos mínimos antes de realizar un estudio más complejo. Esto constituye la principal motivación de la presente investigación. La actual crisis energética ha llevado a aunar esfuerzos en el desarrollo de nuevos materiales, técnicas y dispositivos para la aplicación en la industria de la energía nuclear. El desarrollo de las técnicas de producción de aleaciones de wolframio, con un punto de fusión muy alto, requiere el uso de precursores de sinterizado para lograr densificaciones más altas y por lo tanto mejores propiedades mecánicas. Este es el propósito de la adición de titanio y vanadio en estas aleaciones. Sin embargo, uno de los principales problemas de la utilización de wolframio como material estructural es su alta temperatura de transición dúctil-frágil. Esta temperatura es característica de materiales metálicos con estructura cúbica centrada en el cuerpo y depende de varios factores metalúrgicos. El proceso de recristalización aumenta esta temperatura de transición. Los PFC tienen temperaturas muy altas de servicio, lo que facilita la recristalización del metal. Con el fin de retrasar este proceso, se dispersan partículas insolubles en el material permitiendo temperaturas de servicio más altas. Hasta ahora se ha utilizado óxidos de torio, lantano e itrio como partículas dispersas. Para entender cómo los contenidos en algunos elementos y partículas de óxido afectan a las propiedades de wolframio se estudian las aleaciones binarias de wolframio en comparación con el wolframio puro. A su vez estas aleaciones binarias se utilizan como material de referencia para entender el comportamiento de las aleaciones ternarias. Dada la estrecha relación entre las propiedades del material, la estructura y proceso de fabricación, el estudio se completa con un análisis fractográfico y micrográfico. El análisis fractográfico puede mostrar los mecanismos que están implicados en el proceso de fractura del material. Por otro lado, el estudio micrográfico ayudará a entender este comportamiento a través de la identificación de las posibles fases presentes. La medida del tamaño de grano es una parte de la caracterización microestructural. En esta investigación, la medida del tamaño de grano se llevó a cabo por ataque químico selectivo para revelar el límite de grano en las muestras preparadas. Posteriormente las micrografías fueron sometidas a tratamiento y análisis de imágenes. El documento termina con una discusión de los resultados y la compilación de las conclusiones más importantes que se alcanzan después del estudio. Actualmente, el desarrollo de nuevos materiales para aplicación en los componentes de cara al plasma continúa. El estudio de estos materiales ayudará a completar una base de datos de características que permita hacer una selección de ellos más fiable. The main goal of this dissertation is the mechanical characterization as a function of temperature of nine tungsten alloys containing different amounts of titanium, vanadium and yttrium and lanthanum oxide. The alloys under study were the following ones: W-0.5%Y2O3, W-2%Ti, W-2% Ti-0.5% Y2O3, W-4% Ti-0.5% Y2O3, W-2%V, W- 2%Vmix, W-4%V, W-1%La2O3 and W-4%V-1%La2O3. All of them, besides pure tungsten, were manufactured using a Hot Isostatic Pressing (HIP) process and they were supplied by the Universidad Carlos III de Madrid. The research was carried out through a systematic study based on physical and mechanical tests as well as the post mortem analysis of tested samples. Diverse mechanical tests were applied to perform this characterization; most of them were conducted at temperatures in the range 25-1000 ºC. The following characterization tests were performed: • Density • Vickers hardness • Elastic modulus • Yield strength or ultimate bending strength, and their evolution with temperature • Fracture toughness and its temperature behavior • Microstructural analysis • Fractographical analysis • Microstructure-macroscopic relationship analysis This study begins with an introduction regarding the systems where these materials could be applied, in order to establish and understand their service conditions. In this case, the component that defines the conditions is the Divertor of magnetic-confinement fusion reactors. It seems obvious that their use as fusion reactor components, more exactly as plasma facing components (PFCs), makes these alloys work under conditions of neutron irradiation. In addition to this, the fact that they are novel materials demands a preliminary study of the basic characteristics which will guarantee their minimum requirements prior to a more complex study. This constitutes the motivation of the present research. The current energy crisis has driven to join forces so as to develop new materials, techniques and devices for their application in the nuclear energy industry. The development of production techniques for tungsten-based alloys, with a very high melting point, requires the use of precursors for sintering to achieve higher densifications and, accordingly, better mechanical properties. This is the purpose of the addition of titanium and vanadium to these alloys. Nevertheless, one of the main problems of using tungsten as structural material is its high ductile-brittle transition temperature. This temperature is characteristic of metallic materials with body centered cubic structure and depends on several metallurgical factors. The recrystallization process increases their transition temperature. Since PFCs have a very high service temperature, this facilitates the metal recrystallization. In order to inhibit this process, insoluble particles are dispersed in the material allowing higher service temperatures. So far, oxides of thorium, lanthanum and yttrium have been used as dispersed particles. Tungsten binary alloys are studied in comparison with pure tungsten to understand how the contents of some elements and oxide particles affect tungsten properties. In turn, these binary alloys are used as reference materials to understand the behavior of ternary alloys. Given the close relationship between the material properties, structure and manufacturing process, this research is completed with a fractographical and micrographic analysis. The fractographical analysis is aimed to show the mechanisms that are involved in the process of the material fracture. Besides, the micrographic study will help to understand this behavior through the identification of present phases. The grain size measurement is a crucial part of the microstructural characterization. In this work, the measurement of grain size was carried out by chemical selective etching to reveal the boundary grain on prepared samples. Afterwards, micrographs were subjected to both treatment and image analysis. The dissertation ends with a discussion of results and the compilation of the most important conclusions reached through this work. The development of new materials for plasma facing components application is still under study. The analysis of these materials will help to complete a database of the features that will allow a more reliable materials selection.

Influence of fabrication steps on optical and electrical properties of InN thin films

This paper reports on a case study of the impact of fabrication steps on InN material properties. We discuss the influence of annealing time and sequence of device processing steps. Photoluminescence (PL), surface morphology and electrical transport (electrical resistivity and low frequency noise) properties have been studied as responses to the adopted fabrication steps. Surface morphology has a strong correlation with annealing times, while sequences of fabrication steps do not appear to be influential. In contrast, the optical and electrical properties demonstrate correlation with both etching and thermal annealing. For all the studied samples PL peaks were in the vicinity of 0.7 eV, but the intensity and full width at half maximum (FWHM) demonstrate a dependence on the technological steps followed. Sheet resistance and electrical resistivity seem to be lower in the case of high defect introduction due to both etching and thermal treatments. The same effect is revealed through 1/f noise level measurements. A reduction of electrical resistivity is connected to an increase in 1/f noise level.

Properties of granular analogue model materials: A community wide survey

We report the material properties of 26 granular analogue materials used in 14 analogue modelling laboratories. We determined physical characteristics such as bulk density, grain size distribution, and grain shape, and performed ring shear tests to determine friction angles and cohesion, and uniaxial compression tests to evaluate the compaction behaviour. Mean grain size of the materials varied between c. 100 and 400 μm. Analysis of grain shape factors shows that the four different classes of granular materials (14 quartz sands, 5 dyed quartz sands, 4 heavy mineral sands and 3 size fractions of glass beads) can be broadly divided into two groups consisting of 12 angular and 14 rounded materials. Grain shape has an influence on friction angles, with most angular materials having higher internal friction angles (between c. 35° and 40°) than rounded materials, whereas well-rounded glass beads have the lowest internal friction angles (between c. 25° and 30°). We interpret this as an effect of intergranular sliding versus rolling. Most angular materials have also higher basal friction angles (tested for a specific foil) than more rounded materials, suggesting that angular grains scratch and wear the foil. Most materials have an internal cohesion in the order of 20–100 Pa except for well-rounded glass beads, which show a trend towards a quasi-cohesionless (C < 20 Pa) Coulomb-type material. The uniaxial confined compression tests reveal that rounded grains generally show less compaction than angular grains. We interpret this to be related to the initial packing density after sifting, which is higher for rounded grains than for angular grains. Ring-shear test data show that angular grains undergo a longer strain-hardening phase than more rounded materials. This might explain why analogue models consisting of angular grains accommodate deformation in a more distributed manner prior to strain localisation than models consisting of rounded grains.

Investigation of ultrafast laser-photonic material interactions: Challenges for directly written glass photonics

Currently, direct-write waveguide fabrication is probably the most widely studied application of femtosecond laser micromachining in transparent dielectrics. Devices such as buried waveguides, power splitters, couplers, gratings, and optical amplifiers have all been demonstrated. Waveguide properties depend critically on the sample material properties and writing laser characteristics. In this paper, we discuss the challenges facing researchers using the femtosecond laser direct-write technique with specific emphasis being placed on the suitability of fused silica and phosphate glass as device hosts for different applications.

The effect of care solutions on the bulk and surface properties of soft contact lenses

Purpose: Soft contact lenses for continuous wear require the use of cleaning regimes which utilise hydrogen peroxide systems or multipurpose cleaning solutions (MPS). The compositions of MPS are becoming increasingly complex and often include disinfectants, cleaning agents, preservatives, wetting agents, demulcents, chelating and buffering agents. Recent research on solution–lens interactions has focused on specific ocular parameters such as corneal staining. However the effect of a solution on the lens, particularly silicone hydrogel lenses, itself has received less attention. The purpose of this work was to establish and understand the effects that care solutions have on selected bulk and surface material properties. Methods: Selected bulk and surface properties of each material (etafilcon A, vifilcon A, balafilcon A, senofilcon A, lotrafilcon A and lotrafilcon B, galyfilcon A) were measured after a 24 h soak in a variety of care solutions. Additionally the lenses were soaked for 24 h in hyperosmolar (680 mOsm L-1) and hyposmolar (170 mOsm L-1) PBS. A bulk property parameter the total diameter (TD) was measured using an Optimec contact lens analyser. The surface property related CoF of soaked lenses was measured on a nano-tribometer with conditions of load 30 mN, at a distance of 20 mm and speed 30 mm/min. Results: In terms of bulk properties, change is related to the EWC of the lens, the higher the EWC of the lens the greater the TD changes. Silicone hydrogel lenses have EWCs of <47% and little or no TD changes were observed; lotrafilcon A exhibited no change irrespective of the cleaning solution. Conventional contact lenses have higher EWCs (58% for etafilcon A and 55% for vifilcon A) and the TD was seen to change to a greater extent, for example the etafilcon A material in ReNu MPS had an increase to 14.45± 0.07 mm from the cited 14.2 mm. Other lenses increased or decreased in TD depending on the solution used. The osmolarity of the solution although important is not the only factor governing change in the TD, for example soaking senofilcon A in hyperosmolar PBS (680 mOsm L-1) for 24 h increased the TD of the lens (+0.25 ± 0.07 mm), however when the same lens type was soaked for 24 h in a MPS with a lower osmolarity there was a similar effect. Biotribology measurements demonstrated that some solution–lens combinations can reduce the CoF by 55%, when compared with biotribology with the native packing solution. An increase in the CoF was observed for other solution–lens combinations. Conclusions: There is a dramatic difference in bulk and surface performance of specific lens materials with particular care solutions. Individual components of the care solutions have effects on the bulk and surface properties of contact lenses. The affects are not as great with the silicone hydrogel as compared with conventional hydrogels.

Analysis of powder caking in multicomponent powders using atomic force microscopy to examine particle properties

Atomic force microscopy has been used to study the surface properties of model spray dried powders. Phase imaging, nanoindentation and force modulation microscopy have differentiated between the different surface material properties of the particles, revealing a regular dispersion of soft, oil rich areas distributed across the particles' surface. Humidity and temperature cycling effects on the caking behavior of the particles have also been investigated, with significant morphology changes and onset of caking found to occur within relatively short periods of time.

A decade of silicone hydrogel development:surface properties, mechanical properties, and ocular compatibility

Since the initial launch of silicone hydrogel lenses, there has been a considerable broadening in the range of available commercial material properties. The very mobile silicon–oxygen bonds convey distinctive surface and mechanical properties on silicone hydrogels, in which advantages of enhanced oxygen permeability, reduced protein deposition, and modest frictional interaction are balanced by increased lipid and elastic response. There are now some 15 silicone hydrogel material variants available to practitioners; arguably, the changes that have taken place have been strongly influenced by feedback based on clinical experience. Water content is one of the most influential properties, and the decade has seen a progressive rise from lotrafilcon-A (24%) to efrofilcon-A (74%). Moduli have decreased over the same period from 1.4 to 0.3 MPa, but not solely as a result of changes in water content. Surface properties do not correlate directly with water content, and ingenious approaches have been used to achieve desirable improvements (e.g., greater lubricity and lower contact angle hysteresis). This is demonstrated by comparing the hysteresis value of the earliest (lotrafilcon-A, >40°) and most recent (delefilcon-A, <10°) coated silicone hydrogels. Although wettability is important, it is not of itself a good predictor of ocular response because this involves a much wider range of physicochemical and biochemical factors. The interference of the lens with ocular dynamics is complex leading separately to tissue–material interactions involving anterior and posterior lens surfaces. The biochemical consequences of these interactions may hold the key to a greater understanding of ocular incompatibility and end of day discomfort.

Fracture and viscoelastic properties of asphalt binders during fatigue and rest periods

Viscoelastic asphalt binder plays an important role in bonding individual aggregate particles and contributes to the durability and stability of asphalt pavement. When asphalt binder is subjected to cyclic loading, deformation and fracture may develop simultaneously within it, leading to the deterioration of material properties and eventually fatigue failure. Research has found that some degree of recovery may develop if rest periods are applied after fatigue deterioration. However, it is not clear whether such recovery is caused by fracture healing, viscoelastic recovery, or both. This paper presents an analysis to differentiate the contributions of fracture healing and viscoelastic recovery to the asphalt binder during rest periods. It also evaluates the damage caused by deformation and fracture during a fatigue process. It is found that viscoelastic recovery plays an important role in the instant increase in the dynamic shear modulus at the beginning of the rest period. The effect of fracture healing on dynamic shear modulus recovery is more dominant in the long term. A healing index is developed based only on the fracture healing of asphalt binder, excluding the effect of viscoelastic recovery. It can be used to evaluate the true healing properties of different asphalt binders. Copyright © 2014 by ASTM International.

Facile synthesis of polymer-peptide conjugates via direct amino acid coupling chemistry

Polymer-peptide conjugates (also known as biohy-brids) are attracting considerable attention as injectable materials owing to the self-assembling behavior of the peptide and the ability to control the material properties using the polymer component. To this end, a simple method for preparing poly(ethylene oxide)-oligophenylalanine polymer-peptide conjugates (mPEOm-F n-OEt) using isobutylchloroformate as the activating reagent has been identified and developed. The synthetic approach reported employs an industrially viable route to produce conjugates with high yield and purity. Moreover, the approach allows judicious selection of the precursor building blocks to produce libraries of polymer-peptide conjugates with complete control over the molecular composition. Control over the molecular make-up of the conjugates allows fine control of the physicochemical properties, which will be exploited in future studies into the prominent self-assembling behavior of such materials. © 2013 Wiley Periodicals, Inc.

On the material dependence of experimental shear fracture orientation

Peer reviewed

Evaporative Moisture Loss from Heterogeneous Stone: Material- Environment Interactions During Drying

The complexities of evaporation from structurally and mineralogically heterogeneous sandstone (Locharbriggs Sandstone) are investigated through a laboratory-based experiment in which a variety of environmental conditions are simulated. Data reported demonstrate the significance of material-environment interactions on the spatial and temporal variability of evaporative dynamics. Evaporation from porous stone is determined by the interplay between environmental, material and solution properties, which govern the rate and mode by which water is transmitted to, and subsequently removed from, an evaporating surface. Initially evaporation is marked by high rates of moisture loss controlled by external atmospheric conditions; then, when a critical level of surface moisture content is reached, hydraulic continuity between the stone surface and subsurface is disrupted and the drying front recedes
beneath the surface, evaporation rates decrease and are controlled by the ability of the material to transport water vapour to the surface. Pore size distribution and connectivity, as well as other material properties, control the timing of each stage of evaporation and the nature of the transition.

These experimental data highlight the complexity of evaporation, demonstrating that different regions of the same stone can exhibit varying moisture dynamics during drying and that the rate and nature of evaporative loss differs under different environmental conditions. The results identify the importance of material-environment interactions during drying and that stone micro-environmental conditions cannot be inferred from ambient data alone.
These data have significance for understanding the spatial distribution of stone surface weathering-related morphologies in both the natural and built environments where mineralogical and/or structural heterogeneity creates differences in moisture flux and hence variable drying rates. Such differences may provide a clearer explanation for the initiation and subsequent development of complex weathering responses where areas of significant deterioration can be found alongside areas that exhibit little or no evidence surface breakdown.

The role of material characterisation in the crush modelling of thermoplastic composite structures

The predictive capability of high fidelity finite element modelling, to accurately capture damage and crush behaviour of composite structures, relies on the acquisition of accurate material properties, some of which have necessitated the development of novel approaches. This paper details the measurement of interlaminar and intralaminar fracture toughness, the non-linear shear behaviour of carbon fibre (AS4)/thermoplastic Polyetherketoneketone (PEKK) composite laminates and the utilisation of these properties for the accurate computational modelling of crush. Double-cantilever-beam (DCB), four-point end-notched flexure (4ENF) and Mixed-mode bending (MMB) test configurations were used to determine the initiation and propagation fracture toughness in mode I, mode II and mixed-mode loading, respectively. Compact Tension (CT) and Compact Compression (CC) test samples were employed to determine the intralaminar longitudinal tensile and compressive fracture toughness. V-notched rail shear tests were used to measure the highly non-linear shear behaviour, associated with thermoplastic composites, and fracture toughness. Corresponding numerical models of these tests were developed for verification and yielded good correlation with the experimental response. This also confirmed the accuracy of the measured values which were then employed as input material parameters for modelling the crush behaviour of a corrugated test specimen.

Optimization and Prediction of Mechanical and Thermal Properties of Graphene/LLDPE Nanocomposites by Using Artificial Neural Networks

The focus of this work is to develop the knowledge of prediction of the physical and chemical properties of processed linear low density polyethylene (LLDPE)/graphene nanoplatelets composites. Composites made from LLDPE reinforced with 1, 2, 4, 6, 8, and 10 wt% grade C graphene nanoplatelets (C-GNP) were processed in a twin screw extruder with three different screw speeds and feeder speeds (50, 100, and 150 rpm). These applied conditions are used to optimize the following properties: thermal conductivity, crystallization temperature, degradation temperature, and tensile strength while prediction of these properties was done through artificial neural network (ANN). The three first properties increased with increase in both screw speed and C-GNP content. The tensile strength reached a maximum value at 4 wt% C-GNP and a speed of 150 rpm as this represented the optimum condition for the stress transfer through the amorphous chains of the matrix to the C-GNP. ANN can be confidently used as a tool to predict the above material properties before investing in development programs and actual manufacturing, thus significantly saving money, time, and effort.

Laboratory performance evaluation of CIR-emulsion and its comparison against CIR-foam test results from Phase III, TR-578

Currently, no standard mix design procedure is available for CIR-emulsion in Iowa. The CIR-foam mix design process developed during the previous phase is applied for CIR-emulsion mixtures with varying emulsified asphalt contents. Dynamic modulus test, dynamic creep test, static creep test and raveling test were conducted to evaluate the short- and long-term performance of CIR-emulsion mixtures at various testing temperatures and loading conditions. A potential benefit of this research is a better understanding of CIR-emulsion material properties in comparison with those of CIR-foam material that would allow for the selection of the most appropriate CIR technology and the type and amount of the optimum stabilization material. Dynamic modulus, flow number and flow time of CIR-emulsion mixtures using CSS-1h were generally higher than those of HFMS-2p. Flow number and flow time of CIR-emulsion using RAP materials from Story County was higher than those from Clayton County. Flow number and flow time of CIR-emulsion with 0.5% emulsified asphalt was higher than CIR-emulsion with 1.0% or 1.5%. Raveling loss of CIR-emulsion with 1.5% emulsified was significantly less than those with 0.5% and 1.0%. Test results in terms of dynamic modulus, flow number, flow time and raveling loss of CIR-foam mixtures are generally better than those of CIR-emulsion mixtures. Given the limited RAP sources used for this study, it is recommended that the CIR-emulsion mix design procedure should be validated against several RAP sources and emulsion types.