UV-Vis and surface photovoltage spectra of Fe2O3/polystyrene composite microspheres

Fe2O3 sol with the particle diameter of 3-5 nm was flocculated by the addition of SDS, and the flocculate formed was redispersed by the further addition of that surfactant. Thus the surfactant bilayer was formed on the surface of Fe2O3. The emulsion polymerization of styrene (St) adsolubilized oil the surfactant adsorbed bilayer was carried out by initiator potassium persulfate (KPS). The UV-Vis and surface photovoltage spectra (SPS) indicate that the Fe2O3 particles were encapsulated in polystyrene(PSt) successfully.

Isothermal and nonisothermal melt-crystallization kinetics of syndiotactic polystyrene

Analyses of the isothermal and nonisothermal melt kinetics for syndiotactic polystyrene have been performed with differential scanning calorimetry, and several kinetic analyses have been used to describe the crystallization process. The regime II-->III transition, at a crystallization temperature of 239degrees, is found. The values of the nucleation parameter K-g for regimes II and III are estimated. The lateral-surface free energy, sigma = 3.24 erg cm(-2), the fold-surface free energy, sigma(e) = 52.3 +/- 4.2 erg cm(-2), and the average work of chain folding, q = 4.49 +/- 0.38 kcal/mol, are determined with the (040) plane assumed to be the growth plane. The observed crystallization characteristics of syndiotactic polystyrene are compared with those of isotactic polystyrene. The activation energies of isothermal and nonisothermal melt crystallization are determined to be DeltaE = -830.7 kJ/mol and DeltaE = -315.9 kJ/mol, respectively.

Compatibilization effects of block copolymers in high density polyethylene/syndiotactic polystyrene blends

Three triblock copolymers of poly[styrene-b-(ethylene-co-butylene)-b-styrene] (SEBS) of different molecular weights and one diblock copolymer of poly[styrene-b-(ethylene-co-butylene)] (SEB) were used to compatibilize high density polyethylene/syndiotactic polystyrene (HDPE/sPS, 80/20) blend. Morphology observation showed that phase size of the dispersed sPS particles was significantly reduced on addition of all the four copolymers and the interfacial adhesion between the two phases was dramatically enhanced. Tensile strength of the blends increased at lower copolymer content but decreased with increasing copolymer content. The elongation at break of the blends improved and sharply increased with increments of the copolymers. Drop in modulus of the blend was observed on addition of the rubbery copolymers. The mechanical performance of the modified blends is strikingly dependent not only on the interfacial activity of the copolymers but also on the mechanical properties of the copolymers, particularly at the high copolymer concentration. Addition of compatibilizers to HDPE/sPS blend resulted in a significant reduction in crystallinity of both HDPE and sPS. Measurements of Vicat softening temperature of the HDPE/sPS blends show that heat resistance of HDPE is greatly improved upon incorporation of 20 wt% sPS.

Characterization of Y2O3 : Eu coated with polystyrene

The core-shell Y2O3:Eu3+/polystyrene particles was prepared by surface modification with citric acid and emulsion polymerization method of styrene. The DTA curve of coated particles exhibits a small and wide exothermic peak of organic compound around 387 degreesC. The carbonyl stretching vibration band was shifted to low wavenumber in FTIR spectrum and the binding energy of Y3d5/2 was shifted to high-energy band in XPS spectrum. The results of FTIR and XPS show that citric acid was coupled to the particles surface. The hydrophilic surface became amphiphilic by modification of citric acid. So styrene could adsorb on particles surface to form emulsion structure which inorganic core was inside. EDS spectra show that Y2O3:Eu3+ particles were coated uniformly with polystyrene.

Investigating mechanical response of single chain polystyrene particles by scanning probe techniques

Single chain polystyrene particles were obtained by dilute solution casting method. The sample with both single chain polystyrene particles and multi-chain (more than 1000 molecular chains) polystyrene particles was obtained by a little more concentrate solution. Force modulation technique showed that single chain polystyrene particles were softer than multichain polystyrene particles. On the other hand, nanoindentation experiments on multi-chain particles and bulk polystyrene manifested that the elastic modulus of multi-chain polystyrene particles was very close to that of bulk polystyrene. Therefore, it was concluded that single chain polystyrene particles were softer than bulk polystyrene,which indicated that the density of intrachain entanglement points in the single chain polystyrene particles was not as large as that of the interchain entanglement points in the bulk state.

Crystal form transition during heating of solvent-induced crystalline syndiotactic polystyrene

The phase transition of two kinds of solvent-induced crystalline syndiotactic polystyrene (sPS). gamma-sPS and delta(c)-sPS, has been studied via WAXD and DSC. gamma-sPS transform to a-sPS at 195-225 degrees C before melt during heating, whereas delta(e)-sPS transform to first gamma-sPS and then a-sPS at 100-200 degrees C and 200-215 degrees C, respectively. The transition of delta(e)-gamma and gamma-a occurs for below melting point of sPS indicates they are all solid-solid transition.

Initiation and termination of crazes in high impact polystyrene

Initiation and termination of crazes in high impact polystyrene (HIPS) were studied by transmission electron microscope. Instead of the first initiation of crazes in the vicinity of the equator or rubber particles, ribbon-shaped crazes beyond the region were observed on the TEM photos. The starting point and the end point of each ribbon were noticed not to be randomly located on the surface of the cellar particles in HIPS. The spots connecting to the ligaments between the PS rigid inclusions in the cellar particle are found to be the locations where crazes were initiated and terminated preferentially. In addition, the crazes generated at those spots were much thicker and longer. The thoughness of high impact polystyrene was enhanced by the multiple crazes formed in the matrices, through the reduction of the craze stress at room temperature with increasing the volume fraction of polybutadiene at these spots in the dispersed phase. These results conducted that not only the cell structure of the domains in HIPS was not homogeneous but also the polybutadiene ligaments between PS rigid inclusions in the domains were inhomogeneous. Therefore, the responsibility of those polybutadiene ligaments with different thickness to the stresses was different and it forced the crazing initiation and growing preferentially. The crazes were created in some regions in the matrices; On the contrary, rare crazes were formed in the other regions in spite of these regions surrounded around the same dispersed particles. The relation between the spots on the surface and the inner structure of the cellar particle was discussed in this paper.

Influence of intermolecular entanglements on the glass transition and structural relaxation behaviors of macromolecules. 2. Polystyrene and phenolphthalein poly(ether sulfone)

The effect of entanglements on the glass transition and structural relaxation behaviors has been studied for polystyrene (PS) and phenolphthalein poly(ether sulfone) (PES-C) samples by fast evaporation of the solution of concentrations varying from above the overlapping concentration to far below it, and compared to the results we have studied previously in PC. It has been found that for all the polymers we have studied, in the concentrated solution region, the T-g of the samples obtained from solution are independent of the change of concentration and are very close to that of normal bulk samples, whereas in the dilute solution region the T-g of the samples decrease with the logarithm of decreasing concentration. The critical concentrations that divide the two distinct regions for the three polymers are 0.9% g/mL for PC, 0.1% g/mL for PS, and 1% g/mL for PES-C. The decrease of T-g of the samples is interpreted by the decrease of intermolecular entanglements as the isolation of polymer chains, and the entanglement of polymer chains restrained the mobility of the segments. The structural relaxation behavior of the polymers is also found to be different from that of normal bulk samples. The enthalpies of single-chain samples are lower than that of the bulk ones, which correspond to the lower glass transition temperature; the peaks are lower and broader, and the relaxed enthalpy is much lower as compared to that of bulk samples. In the three polymers we have studied, the influence of change of entanglements on both the decrease in glass transition temperature and relaxed enthalpy is the most significant for PS and the least for PES-C. It is indicated that the interactions in the flexible polymers are weak; thus, the restraint of the entanglements on the mobility of the segments plays a more important role in the flexible polymers, and the change of entanglement in the flexible polymers has a more significant influence on the physical properties.

Radiation effects on the immiscible polymer blend of nylon1010 and high-impact polystyrene (HIPS) I: Gel/dose curves, mathematical expectation theorem and thermal behaviour

This paper studies the radiation properties of the immiscible blend of nylon1010 and HIPS. The gel fraction increased with increasing radiation dose. The network was found mostly in nylon1010, the networks were also found in both nylon1010 and HIPS when the dose reaches 0.85 MGy or more. We used the Charleby-Pinner equation and the modified Zhang-Sun-Qian equation to simulate the relationship with the dose and the sol fraction. The latter equation fits well with these polymer blends and the relationship used by it showed better linearity than the one by the Charleby-Pinner equation. We also studied the conditions of formation of the network by the mathematical expectation theorem for the binary system. Thermal properties of polymer blend were observed by DSC curves. The crystallization temperature decreases with increasing dose because the cross-linking reaction inhibited the crystallization procession and destroyed the crystals. The melting temperature also reduced with increasing radiation dose. The dual melting peak gradually shifted to single peak and the high melting peak disappeared at high radiation dose. However, the radiation-induced crystallization was observed by the heat of fusion increasing at low radiation dose. On the other hand, the crystal will be damaged by radiation. A similar conclusion may be drawn by the DSC traces when the polymer blends were crystallized. When the radiation dose increases, the heat of fusion reduces dramatically and so does the heat of crystallization. (C) 1999 Elsevier Science Ltd. All rights reserved.

Effects of pressure and molecular weight on the miscibility of polystyrene and cyclohexane

With the aid of Sanchez-Lacombe lattice fluid theory (SLLFT), the phase diagrams were calculated for the system cyclohexane (CH)/polystyrene (PS) with different molecular weights at different pressures. The experimental data is in reasonable agreement with SLLFT calculations. The total Gibbs interaction energy, g*(12) for different molecular weights PS at different pressures was expressed, by means of a universal relationship, as g(12)* =f(12)* + (P - P-0) nu*(12) demixing curves were then calculated at fixed (near critical) compositions of CH and PS systems for different molecular weights. The pressures of optimum miscibility obtained from the Gibbs interaction energy are close to those measured by Wolf and coworkers. Furthermore, a reasonable explanation was given for the earlier observation of Saeki et al., i.e., the phase separation temperatures of the present system increase with the increase of pressure for the low molecular weight of the polymer whereas they decrease for the higher molecular weight polymers. The effects of molecular weight, pressure, temperature and composition on the Flory Huggins interaction parameter can be described by a general equation resulting from fitting the interaction parameters by means of Sanchez-Lacombe lattice fluid theory.

Synthesis and characterization of novel sodium sulfonate-functionalized poly(ether ether ketone)s containing cyclohexyl side groups

Novel water insoluble sodium sulfonate-functionalized poly(ether ether ketone)s containing cyclohexylidene in the main chain with degree of sulfonation up to 2.0 were synthesized from nucleophilic polycondensation of 5, 5'-carbonylbis (2-fluorobenzenesulfonate), 4, 4'-difluorobenzophenone and 4, 4'-cyclohexylidenebisphenol. The polymers showed excellent thermal stability and good water resistance as well. The DSC diagrams and WAXD patterns indicated an amorphous morphological structure of these polymers. A comprison of some properties between these copolymers and polymers derived from bisphenol A was given.

Preparation and characterization of nanometer-sized CeO2/polystyrene hybrid material

Nanometer-sized CeO2/polystyrene hybrid material was prepared using reversed micelles microemulsion method. XRD analysis revealed that the CeO2 nanoparticles in polystyrene were amorphous. XPS patterns indicated that the hybrid material was not a simply physical mixture, but a certain strength of chemical bond between CeO2 nanoparticles and polystyrene existed. FTIR patterns revealed that the absorption of Ce-O bond in hybrid material was blue-shifted.

Synthesis of poly(ether ether ketone)s with high content of sodium sulfonate groups as gas dehumidification membrane materials

Sodium sulfonate-functionalized polyether ether ketone)s derived from Bisphenol A with a degree of sulfonation up to 2.0 were synthesized by aromatic nucleophilic polycondensation of various amounts of 5,5-carbonylbis(2-fluorobenzenesulfonate) (1), 4,4'-diflurobenzophenone (2) and Bisphenol A (2). Copolymers showed excellent thermal stability and good mechanical properties. The selectivity of water vapor over nitrogen of membranes prepared from copolymers 3a and 3h was determined to be 3.43 x 10(6) and 1.05 x 10(7), respectively.