Factors affecting the strength of denture repairs: Topics of interest

Fracture of dentures is a common clinical finding in daily prosthodontic practice, resulting in great inconvenience to both patient and dentist. A satisfactory repair should be cost-effective, simple to perform, and quick; it should also match the original color and not cause distortion to the existing denture. Different repair materials, surface designs, and mechanical and chemical surface treatments have been recommended in order to obtain stronger repairs. This article reviews some of the available literature with regard to the most important factors that may influence the strength of denture repairs. © 2007 by The American College of Prosthodontists.

Immediate X delayed loading dental implants: An overview

The aim of this investigation was to accomplish an overview about the principles of the indication and of the success parameters involving immediate and delayed loading dental implants procedures. Studies about the philosophies (immediate and delayed loading dental implants) and their clinical indications will be discussed in order to overview the rules for the clinical success in both techniques. In addition, studies regarding the criteria for immediate loading implants as primary stabilization, surface treatments and bone density and amount will be also analyzed. More important than the philosophy selection, is how and when to use it according to biomechanical rules and principles. Among the vast limitations pointed by the literature regarding procedures of immediate and delayed loading are evidenced the parafunctional habits, primary stabilization, bone quality, surface treatments and the number of dental implants. The anterior region of the jaw seems to be associated with a major percentage of satisfactory results, regardless of rehabilitation procedures. Although several studies have demonstrated high success rates for the immediate loading dental implants, several aspects remain without an explicit definition and further studies are needed to elucidate some reservations.

Resin microtensile bond strength to feldspathic ceramic: Hydrofluoric acid etching vs tribochemical silica coating

This study aimed to compare the microtensile bond strength of resin cement to alumina-reinforced feldspathic ceramic submitted to acid etching or chairside tribochemical silica coating. Ten blocks of Vitadur-α were randomly divided into 2 groups according to conditioning method: (1) etching with 9.6% hydrofluoric acid or (2) chairside tribochemical silica coating. Each ceramic block was luted to the corresponding resin composite block with the resin cement (Panavia F). Next, bar specimens were produced for microtensile testing. No significant difference was observed between the 2 experimental groups (Student t test, P> .05). Both surface treatments showed similar microtensile bond strength values.

Microtensile bond strength of a repair composite to leucite-reinforced feldspathic ceramic

The purpose of this study was to evaluate the microtensile bond strength of a repair composite resin to a leucite-reinforced feldspathic ceramic (Omega 900, VITA) submitted to two surface conditionings methods: 1) etching with hydrofluoric acid + silane application or 2) tribochemical silica coating. The null hypothesis is that both surface treatments can generate similar bond strengths. Ten ceramic blocks (6x6x6 mm) were fabricated and randomly assigned to 2 groups (n=5), according to the conditioning method: G1- 10% hydrofluoric acid application for 2 min plus rinsing and drying, followed by silane application for 30 s; G2- airborne particle abrasion with 30 μm silica oxide particles (CoJet-Sand) for 20 s using a chairside air-abrasion device (CoJet System), followed by silane application for 5 min. Single Bond adhesive system was applied to the surfaces and light cured (40 s). Z-250 composite resin was placed incrementally on the treated ceramic surface to build a 6x6x6 mm block. Bar specimens with an adhesive area of approximately 1 ± 0.1 mm2 were obtained from the composite-ceramic blocks (6 per block and 30 per group) for microtensile testing. No statistically significant difference was observed between G1 (10.19 ± 3.1 MPa) and G2 (10.17 ± 3.1 MPa) (p=0.982) (Student's t test; á = 0.05). The null hypothesis was, therefore, accepted. In conclusion, both surface conditioning methods provided similar microtensile bond strengths between the repair composite resin and the ceramic. Further studies using long-term aging procedures should be conducted.

Shear bond strength of resin cement bonded to alumina ceramic after treatment by aluminum oxide sandblasting or silica coating

Purpose: To evaluate the shear bond strength and bond durability between a dual-cured resin cement (RC) and a high alumina ceramic (In-Ceram Alumina), subjected to two surface treatments. Materials and Methods: Forty disc-shaped specimens (sp) (4-mm diameter, 5-mm thick) were fabricated from In-Ceram Alumina and divided into two groups (n = 20) in accordance with surface treatment: (1) sandblasting by aluminum oxide particles (50 μm Al 2O 3) (SB) and (2) silica coating (30 μm SiO x) using the CoJet system (SC). After the 40 sp were bonded to the dual-cured RC, they were stored in distilled water at 37°C for 24 hours. After this period, the sp from each group were divided into two conditions of storage (n = 10): (a) 24 h-shear bond test 24 hours after cementation; (b) Aging-thermocycling (TC) (12,000 times, 5 to 55°C) and water storage (150 days). The shear test was performed in a universal test machine (1 mm/min). Results: ANOVA and Tukey (5%) tests noted no statistically significant difference in the bond strength values between the two surface treatments (p= 0.7897). The bond strengths (MPa) for both surface treatments reduced significantly after aging (SB-24: 8.2 ± 4.6; SB-Aging: 3.7 ± 2.5; SC-24: 8.6 ± 2.2; SC-Aging: 3.5 ± 3.1). Conclusion: Surface conditioning using airborne particle abrasion with either 50 μm alumina or 30 μm silica particles exhibited similar bond strength values and decreased after long-term TC and water storage for both methods. © 2011 by The American College of Prosthodontists.

Influence of acid-etching and ceramic primers on the repair of a glass ceramic

The objective of this study was to evaluate the influence of different primers on the microtensile bond strength (μT BS) between a feldspathic ceramic and two composites. Forty blocks (6.0 × 6.0 × 5.0 mm 3) were prepared from Vita Mark II . After polishing, they were randomly divided into 10 groups according to the surface treatment: Group 1, hydrofluoric acid 10% (HF) + silane; Group 2, CoJet + silane; Group 3, HF + Metal/Zirconia Primer; Group 4, HF + Clearfil Primer; Group 5, HF + Alloy Primer; Group 6, HF + V-Primer; Group 7, Metal/Zirconia Primer; Group 8, Clearfil Primer; Group 9, Alloy Primer; Group 10, V-Primer. After each surface treatment, an adhesive was applied and one of two composite resins was incrementally built up. The sticks obtained from each block (bonded area: 1.0 mm2 ± 0.2 mm) were stored in distilled water at 37°C for 30 days and submitted to thermocycling (7,000 cycles; 5°C/55°C ± 1°C). The μT BS test was carried out using a universal testing machine (1.0 mm/min). Data were analyzed using ANOVA and a Tukey test (α = 0.05). The surface treatments significantly affected the results (P < 0.05); no difference was observed between the composites (P > 0.05). The bond strength means (MPa) were as follows: Group 1a = 29.6; Group 1b = 33.7; Group 2a = 28.9; Group 2b = 27.1; Group 3a = 13.8; Group 3b = 14.9; Group 4a = 18.6; Group 4b = 19.4; Group 5a = 15.3; Group 5b = 16.5; Group 6a = 11; Group 6b = 18; Groups 7a to 10b = 0. While the use of primers alone was not sufficient for adequate bond strengths to feldspathic ceramic, HF etching followed by any silane delivered higher bond strength.

Development of silicon carbide substrates for aerospace applications

Payload and high-tech are important characteristics when the goals are aerospace applications. The development of the technologies associated to these applications has interests that transcend national boundaries and are of strategic importance to the nations. Ultra lightweight mirrors, supports and structures for optical systems are important part of this subject. This paper reports the development of SiC substrates, obtained by pressing, to be applied on embedded precision reflective optics. Different SiC granulometries, having YAG as sintering additive, were processed by: ball milling, drying and deagglomeration, sift, uniaxial and isostatic pressing, and, finally, argon atmosphere sintering at 1900°C. Different porosities were obtained according to the amount of organic material added. Into one side of the samples pellets of organic material were introduced to generate voids to reduce the weight of samples as a whole. The substrates were grinding and polished, looking for a SiC surface having low porosity, as porosity is directly related to light scattering that should be avoided on optical surfaces. Laser surface treatments were applied (using or not SiC barbotine) as a method to improve the surface quality. The samples were characterized by optical and laser confocal microscopy, roughness measurements and mechanical tests. The results are very promissory for future applications. © 2012 Materials Research Society.

Growth of TiO2 nanotubes by anodization of Ti-7.5Mo in NH 4F solutions

Titanium and its alloys are widely used as biomaterials due to their mechanical, chemical and biological properties. To enhance the biocompatibility of titanium alloys, various surface treatments have been proposed. In particular, the formation of titanium oxide nanotubes layers has been extensively examined. According to the literature, it is possible to induce the growth of TiO2 on the surface of titanium, employing the aqueous anodizing electrolyte. This Ti-7.5Mo alloy was anodized in glycerol electrolytes containg 0.25 wt% of NH4F, with variations in time, voltage and calcinations temperature. After anodization, the sample surfaces were analyzed with a field emission scanning electron microscopy, DRX and contact angle measurements. It was possible to observe the formation of TiO2 on the surface and these findings represent a simple surface treatment for Ti alloys that has high potential for biomedical applications. Copyright © 2013 American Scientific Publishers. All rights reserved.

Growth of calcium phosphate coating on Ti-7.5Mo alloy after anodic oxidation

Titanium and its alloys are widely used as biomaterials due to their mechanical, chemical and biological properties. To enhance the biocompatibility of titanium alloys, various surface treatments have been proposed. In particular, the formation of titanium oxide nanotubes layers has been extensively examined. Among the various materials for implants, calcium phosphates and hydroxyapatite are widely used clinically. In this work, titanium nanotubes were fabricated on the surface of Ti-7.5Mo alloy by anodization. The samples were anodized for 20 V in an electrolyte containing glycerol in combination with ammonium fluoride (NH4F, 0.25%), and the anodization time was 24 h. After being anodized, specimens were heat treated at 450 °C and 600°C for 1 h to crystallize the amorphous TiO2 nanotubes and then treated with NaOH solution to make them bioactive, to induce growth of calcium phosphate in a simulated body fluid. Surface morphology and coating chemistry were obtained respectively using, field-emission scanning electron microscopy (FEG-SEM), AFM and X-ray diffraction (XRD). It was shown that the presence of titanium nanotubes induces the growth of a sodium titanate nanolayer. During the subsequent invitro immersion in a simulated body fluid, the sodium titanate nanolayer induced the nucleation and growth of nano-dimensioned calcium phosphate. It was possible to observe the formation of TiO2 nanotubes on the surface of Ti-7.5Mo. Calcium phosphate coating was greater in the samples with larger nanotube diameter. These findings represent a simple surface treatment for Ti-7.5Mo alloy that has high potential for biomedical applications. © (2013) Trans Tech Publications, Switzerland.

Resistência adesiva de reparos em resina composta: tratamento da superfície com ponta diamantada, jato de óxido de alumínio e laser de Er:YAG

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Avaliação da resistência de união de diferentes sistemas adesivos à dentina bovina: influência de agentes dessensibilizantes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência ao cisalhamento de reparos de resina: interface tratada com laser de Er Yag, ponta diamantada e jato abrasivo com óxido de alumínio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação in vitro da resistência de união do cerômero ao sistema de cimentação adesiva, através do teste de micro-tração. Efeito de diferentes tratamentos de superfície

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estudo dos procedimentos utilizados para obtenção de microrretenções na superfície interna da porcelana: avaliação por meio de testes de rugosimetria e microscopia eletrônica de varredura

Pós-graduação em Ciências Odontológicas - FOAR

Estudo da eficiência de inibidores voláteis de corrosão para o aço Galvannealed

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)