A simple prediction model for asphalt surface texture incorporating mix gradation and air voids

This paper presents the results of a preliminary study that seeks to show how asphalt grading and air voids are related to the texture depth of asphalt. The fiftieth percentile particle size (D50) is shown to be a good predictor of texture depth measurements from a collected database of field and laboratory studies. The D50 is used to normalise collected texture data and this 'relative texture' is shown to correlate with air voids. Regression analyses confirm that air voids should be included along with a measure of gradation in the interpretation of asphalt surface texture.The derived formulae are used to develop correlation charts.

Pothole detection in asphalt pavement images

Pavement condition assessment is essential when developing road network maintenance programs. In practice, the data collection process is to a large extent automated. However, pavement distress detection (cracks, potholes, etc.) is mostly performed manually, which is labor-intensive and time-consuming. Existing methods either rely on complete 3D surface reconstruction, which comes along with high equipment and computation costs, or make use of acceleration data, which can only provide preliminary and rough condition surveys. In this paper we present a method for automated pothole detection in asphalt pavement images. In the proposed method an image is first segmented into defect and non-defect regions using histogram shape-based thresholding. Based on the geometric properties of a defect region the potential pothole shape is approximated utilizing morphological thinning and elliptic regression. Subsequently, the texture inside a potential defect shape is extracted and compared with the texture of the surrounding non-defect pavement in order to determine if the region of interest represents an actual pothole. This methodology has been implemented in a MATLAB prototype, trained and tested on 120 pavement images. The results show that this method can detect potholes in asphalt pavement images with reasonable accuracy.

Fracture mechanics of idealised bituminous mixes

© 2014 Taylor & Francis. The durability of asphalt pavements is strongly impaired by cracks, caused primarily by traffic loads and environmental effects. In this work, fracture behaviour of idealised asphalt mixes is investigated. Experiments on idealised asphalt mixes under pure-tension mode (mode I cracking) were performed and fracture parameters were evaluated. In these three-point bend fracture tests, the test variables were temperature and load rate. The test data were stored in an asphalt materials database and special-purpose tools were implemented to analyse and handle the laboratory data automatically. Fracture mechanism maps were constructed, showing the conditions associated with ductile, brittle and ductile-brittle transition regimes of behaviour. The mechanism maps show the failure response of the material in terms of the stress intensity factor, strain energy release rate and J-integral as a function of the temperature-compensated crack mouth opening strain rate. Fracture behaviour of asphalt mix specimens was simulated by cohesive zone model in conjunction with a novel material constitutive model for asphalt mixes. The finite element model agrees well with the experimental results and provides insights into fracture response of the notched asphalt mix beam specimens.

The effect of construction pattern and unit interlock on the structural behaviour of block pavements

The maintenance or even replacement of cracked pavements requires considerable financial resources and puts a large burden on the budgets of local councils. In addition to these costs, local councils also face liability claims arising from uneven or cracked pedestrian pavements. These currently cost the Manchester City Council and Preston City Council around £6 million a year each. Design procedures are empirical. A better understanding of the interaction between paving blocks, bedding sand and subbase was necessary in order to determine the mode of failure of pavements under load. Increasing applied stress was found to mobilise ‘‘rotational interlock’’, providing increased pavement stiffness and thus increased load dissipation resulting in lower transmitted stress on the subgrade. The indications from the literature
review were that pavements are designed to fail by excessive deformation and that paving blocks remained uncracked at failure. This was confirmed with experimental data which was obtained from tests on segments of pavements that were laid/constructed in a purpose built test frame in the laboratory.