Caracterização elementar de ligas metálicas em implantes dentários

An ideal biomaterial for dental implants must have very high biocompatibility, which means that such materials should not provoke any serious adverse tissue response. Also, used metal alloys must have high fatigue resistance due the masticatory force and good corrosion resistance. These properties are rendered by using alpha and beta stabilizers, such as Al, V, Ni, Fe, Cr, Cu, Zn. Commercially pure titanium (TiCP) is used often for dental and orthopedic implants manufacturing. However, sometimes other alloys are employed and consequently it is essential to research the chemical elements present in those alloys that could bring prejudice for the health. Present work investigated TiCP metal alloys used for dental implant manufacturing and evaluated the presence of stabilizing elements within existing limits and standards for such materials. For alloy characterization and identification of stabilizing elements it was used EDXRF technique. This method allows to perform qualitative and quantitative analysis of the materials using the spectra of the characteristic X-rays emitted by the elements present in the metal samples. The experimental setup was based on two X- rays tubes (AMPTEK Mini X model with Ag and Au targets), a X-123SDD detector (AMPTEK) and a 0.5mm Cu collimator, developed due to the sample characteristics. The other experimental setup used as a complementary technique is composed of an X-ray tube with a Mo target, collimator 0.65mm and XFlash (SDD) detector - ARTAX 200 (BRUKER). Other method for elemental characterization by energy dispersive spectroscopy (EDS) applied in present work was based on Scanning Electron Microscopy (SEM) EVO® (Zeeis). This method also was used to evaluate the surface microstructure of the sample. The percentual of Ti obtained in the elementary characterization was among 93.35 ± 0.17% and 95.34 ± 0.19 %. These values are considered below the reference limit of 98.635% to 99.5% for TiCP, established by Association of metals centric materials engineers and scientists Society (ASM). The presence of elements Al and V in all samples also contributed to underpin the fact that are not TiCP implants. The values for Al vary between 6.3 ± 1.3% and 3.7 ± 2.0% and for V, between 0.26 ± 0.09% and 0.112 ± 0.048%. According to the American Society for Testing and Materials (ASTM), these elements should not be present in TiCP and in accordance with the National Institute of Standards and Technology (NIST), the presence of Al should be <0.01% and V should be of 0.009 ± 0.001%. Obtained results showed that implant materials are not exactly TiCP but, were manufactured using Ti-Al-V alloy, which contained Fe, Ni, Cu and Zn. The quantitative analysis and elementary characterization of experimental results shows that the best accuracy and precision were reached with X-Ray tube with Au target and collimator of 0.5 mm. Use of technique of EDS confirmed the results of EDXRF for Ti-Al-V alloy. Evaluating the surface microstructure by SEM of the implants, it was possible to infer that ten of the thirteen studied samples are contemporaneous, rough surface and three with machined surface.

Estudo da hidrogenação para pulverização de ligas à base de terras raras com Nb para eletrodos de hidreto metálico

Tese (Doutorado em Tecnologia Nuclear)

Desarrollo de técnicas de aprendizaje automático para la predicción de resultados de partidos en ligas futbolísiticas

En la actualidad, existen un gran número de investigaciones que usan técnicas de aprendizaje automático basadas en árboles de decisión. Como evolución de dichos trabajos, se han desarrollado métodos que usan Multiclasificadores (Random forest, Boosting, Bagging) que resuelven los mismos problemas abordados con árboles de decisión simples, aumentando el porcentaje de acierto. El ámbito de los problemas resueltos tradicionalmente por dichas técnicas es muy variado aunque destaca la bio-informática. En cualquier caso, la clasificación siempre puede ser consultada a un experto considerándose su respuesta como correcta. Existen problemas donde un experto en la materia no siempre acierta. Un ejemplo, pueden ser las quinielas (1X2). Donde podemos observar que un conocimiento del dominio del problema aumenta el porcentaje de aciertos, sin embargo, predecir un resultado erróneo es muy posible. El motivo es que el número de factores que influyen en un resultado es tan grande que, en muchas ocasiones, convierten la predicción en un acto de azar. En este trabajo pretendemos encontrar un multiclasificador basado en los clasificadores simples más estudiados como pueden ser el Perceptrón Multicapa o Árboles de Decisión con el porcentaje de aciertos más alto posible. Con tal fin, se van a estudiar e implementar una serie de configuraciones de clasificadores propios junto a multiclasificadores desarrollados por terceros. Otra línea de estudio son los propios datos, es decir, el conjunto de entrenamiento. Mediante un estudio del dominio del problema añadiremos nuevos atributos que enriquecen la información que disponemos de cada resultado intentando imitar el conocimiento en el que se basa un experto. Los desarrollos descritos se han realizado en R. Además, se ha realizado una aplicación que permite entrenar un multiclasificador (bien de los propios o bien de los desarrollados por terceros) y como resultado obtenemos la matriz de confusión junto al porcentaje de aciertos. En cuanto a resultados, obtenemos porcentajes de aciertos entre el 50% y el 55%. Por encima del azar y próximos a los resultados de los expertos.

Análise mecânica e microestrutural das ligas de cobalto-cromo de uso odontológico após sucessivas refundições

The cobalt-chromium alloy is extensively used in the Odontology for the confection of metallic scaffolding in partial removable denture. During the last few years, it has been reported an increasing number of premature imperfections, with a few months of prosthesis use. The manufacture of these components is made in prosthetic laboratories and normally involves recasting, using parts of casting alloy and parts of virgin alloy. Therefore, the objective of the present study was to analyze the mechanical properties of a commercial cobalt-chromium alloy of odontological use after successive recasting, searching information to guide the dental prosthesis laboratories in the correct manipulation of the cobalt-chromium alloy in the process of casting and the possible limits of recasting in the mechanical properties of this material. Seven sample groups were confectioned, each one containing five test bodies, divided in the following way: G1: casting only with virgin alloy; G2: casting with 50% of the alloy of the G1 + 50% of virgin alloy; G3: casting with 50% of the alloy of the G2 + 50% of virgin alloy; G4: casting with 50% of the alloy of the G3 + 50% of virgin alloy; G5: 50% of alloy of the G4 + 50% of virgin alloy; G6: 50% of alloy of the G5 + 50% of virgin alloy and finally the G7, only with recasting alloy. The modifications in the mechanical behavior of the alloy were evaluated. Moreover, it was carried the micro structural characterization of the material by optic and electronic scanning microscopy, and X ray diffraction.and fluorescence looking into the correlatation of the mechanical alterations with structural modifications of the material caused by successive recasting process. Generally the results showed alterations in the fracture energy of the alloy after successive recasting, resulting mainly of the increasing presence of pores and large voids, characteristic of the casting material. Thus, the interpretation of the results showed that the material did not reveal significant differences with respect to the tensile strength or elastic limit, as a function of successive recasting. The elastic modulus increased from the third recasting cycle on, indicating that the material can be recast only twice. The fracture energy of the material decreased, as the number of recasting cycles increased. With respect to the microhardness, the statistical analyses showedno significant differences. Electronic scanning microscopy revealed the presence of imperfections and defects, resulting of the recasting process. X ray diffraction and fluorescence did not show alterations in the composition of the alloy or the formation of crystalline phases between the analyzed groups. The optical micrographs showed an increasing number of voids and porosity as the material was recast. Therefore, the general conclusion of this study is that the successive recasting of of Co-Cr alloys affects the mechanical properties of the material, consequently leading to the failure of the prosthetic work. Based on the results, the best recommendadition is that the use of the material should be limited to two recasting cycles

Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita

Nickel alloys are frequently used in applications that require resistance at high temperatures associated with resistance to corrosion. Alloys of Ni-Si-C can be obtained by means of powder metallurgy in which powder mixtures are made of metallic nickel powders with additions of various alloying carriers for such were used in this study SiC, Si3N4 or Si metal with graphite. Carbonyl Ni powder with mean particle size of 11 mM were mixed with 3 wt% of SiC powders with an average particle size of 15, 30 and 50 μm and further samples were obtained containing 4 to 5% by mass of SiC with average particle size of 15 μm. Samples were also obtained by varying the carrier alloy, these being Si3N4 powder with graphite, with average particle size of 1.5 and 5 μm, respectively. As a metallic Si graphite with average particle size of 12.5 and 5 μm, respectively. The reference material used was nickel carbonyl sintered without adding carriers. Microstructural characterization of the alloys was made by optical microscopy and scanning electron microscopy with semi-quantitative chemical analysis. We determined the densities of the samples and measurement of microhardness. We studied the dissociation of carriers alloy after sintering at 1200 ° C for 60 minutes. Was evaluated also in the same sintering conditions, the influence of the variation of average particle size of the SiC carrier to the proportion of 3% by mass. Finally, we studied the influence of variation of the temperatures of sintering at 950, 1080 and 1200 ° C without landing and also with heights of 30, 60, 120 and 240 minutes for sintering where the temperature was 950 °C. Dilatometry curves showed that the SiC sintered Ni favors more effectively than other carriers alloy analyzed. SiC with average particle size of 15 μm active sintering the alloy more effectively than other SiC used. However, with the chemical and morphological analyzes for all leagues, it was observed that there was dissociation of SiC and Si3N4, as well as diffusion of Si in Ni matrix and carbon cluster and dispersed in the matrix, which also occurred for the alloys with Si carriers and metallic graphite. So the league that was presented better results containing Si Ni with graphite metallic alloy as carriers, since this had dispersed graphite best in the league, reaching the microstructural model proposed, which is necessary for material characteristic of solid lubricant, so how we got the best results when the density and hardness of the alloy

Estudo da molhabilidade de ligas de adição à base de prata sobre insertos cerâmicos para aplicação em brocas perfuração de poços de petróleo

Metal-ceramic interfaces are present in tricone drill bits with hard ceramic inserts for oil well drilling operations. The combination of actions of cutting, crushing and breaking up of rocks results in the degradation of tricone drill bits by wear, total or partial rupture of the drill bit body or the ceramic inserts, thermal shock and corrosion. Also the improper pressfitting of the ceramic inserts on the bit body may cause its total detachment, and promote serious damages to the drill bit. The improvement on the production process of metal-ceramic interfaces can eliminate or minimize some of above-mentioned failures presented in tricone drill bits, optimizing their lifetime and so reducing drilling metric cost. Brazing is a widely established technique to join metal-ceramic materials, and may be an excellent alternative to the common mechanical press fitting process of hard ceramic inserts on the steel bit body for tricone drill bit. Wetting phenomena plays an essential role in the production of metal/ceramic interfaces when a liquid phase is present in the process. In this work, 72Silver-28Copper eutectic based brazing alloys were melted onto zirconia, silicon nitride and tungsten carbide/Co substrates under high vacuum. Contact angle evolution was measured and graphically plotted, and the interfaces produced were analysed by SEM-EDX. The AgCu eutectic alloy did not wet any ceramic substrates, showing high contact angles, and so without chemical interaction between the materials. Better results were found for the systemns containing 3%wt of titanium in the AgCu alloy. The presence os titanium as a solute in the alloy produces wettable cand termodinamically stable compounds, increasing the ceramics wetting beahviour

Aplicação de Ligas com Memória de Forma como Dispositivos de Segurança

As ligas com memória de forma Ni-Ti apresentam diversas características bastante úteis, das quais podemos realçar a sua elevada resistência à corrosão, às vibrações e geração de forças superiores quando comparadas com outros atuadores. Estas ligas apresentam diversas áreas de aplicabilidade em diferentes aéreas de pesquisa, como a metalomecânica, a robótica, aplicações espaciais, sendo mais relevante para este trabalho a sua aplicação em mecanismos de segurança para portas e acessos. Com este trabalho, pretendemos contribuir para uma forma eficaz de combate e contenção de incêndios em navios, através da apresentação de um mecanismo que vai permitir o corte de ventilação e isolamento no local do incêndio, permitindo criar uma fronteira de fumos que levará ao combate do incêndio por asfixia. O trabalho descreve um mecanismo idealizado com a utilização de ligas com memória de forma, que vai proceder à libertação de um flap, para isolamento da ventilação, na presença de temperatura proveniente do incêndio. Descreve também ensaios termomecânicos realizados, para determinação das características das molas e seu comportamento em determinadas situações chave. Para isto, irão ser utilizadas duas molas com diferentes gamas de temperatura, com o intuito de demonstrar a eficácia na utilização de diversos atuadores de ligas com memória de forma. Todos os testes foram feitos na presença de gamas de temperatura que se assemelham aos valores de atuação dos sistemas automáticos de extinção por água, pelo que os resultados obtidos, ilustram a verdadeira eficácia e utilidade do mecanismo, em casos reais.

Modelagem e análise de um dispositivo mitigador de flecha para linhas de transmissão de energia elétrica baseado em ligas com memória de forma

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2016.

Aplicação de técnicas eletroquímicas na determinação do potencial de corrosividade de ligas de alumínio em água produzida

The resistance of aluminum and their alloys, to the corrosion phenomenon, in aqueous solutions, is a result of the oxide layer formed. However, the corrosion process in the aluminum alloy is associated with the presence a second phase of particles or the presence of chloride ions which promote the disruption of the oxide layer located producing the corrosion process. On the other hand, the term water produced is used to describe the water after the separation of the oil and gas in API separators. The volumes of produced water arrive around 5 more times to the volume of oil produced. The greatest feature of the water is the presence of numerous pollutants. Due to the increased volume of waste around the world in the current decade, the outcome and the effect of the discharge of produced water on the environment has recently become an important issue of environmental concern where numerous treatments are aimed at reducing these contaminants before disposal. Then, this study aims to investigate the electrochemical corrosion behavior of aluminum alloy 6060 in presence of water produced and the influence of organic components as well as chloride ions, by using the electrochemical techniques of linear polarization. The modification of the passive layer and the likely breakpoints were observed by atomic force microscopy (AFM). In the pit formation potential around -0.4 to -0.8 V/EAg/AgCl was observed that the diffusion of chloride ions occurs via the layer formed with the probable formation of pits. Whereas, at temperatures above 65 °C, it was observed that the range of potential for thepit formation was -0.4 to -0.5 V/EAg/AgCl. In all reactions, the concentration of Al(OH)3 in the form of a gel was observed

DAS LIGAS AO MST: LUTA PELA TERRA E A TERRITORIALIDADE CAMPONESA

Diversos são os movimentos de luta pela terra e na terra no Brasil, com diferentes estratégias de atuação, princípios políticos e formas de surgimento. No interior desses movimentos, camponeses e trabalhadores desempregados enxergam a possibilidade de ter a terra para trabalhar e manter, de forma mínina, as condições necessárias para sua sobrevivência e reprodução social. As primeiras lutas camponesas organizadas, com proporção nacional ocorreram nas décadas de 1950/60 com as Ligas Camponesas formadas no Nordeste brasileiro. Até 1964 as Ligas atuaram em 14 estados brasileiros, reunindo e organizando milhares de camponeses. As Ligas estavam prestes a se transformar em uma organização política mais forte, conseqüente e com um programa que extrapolava a questão agrária, até que veio o golpe militar e elas foram destroçadas. Porém a luta pela terra não cessou e a garra, a determinação dos camponeses integrantes das Ligas estão presentes hoje no Movimento dos Trabalhadores Rurais Sem Terra, que se considera herdeiro natural daquela histórica organização. Pretendemos, portanto, analisar o sentido da luta pela terra desde as Ligas até o Movimento dos Trabalhadores Rurais Sem Terra. A análise de documentos históricos e material bibliográfico constituem-se na metodologia da pesquisa.

Avaliação da corrosão microbiológica do aço carbono 1020 em água do mar sintética na presença de bactérias redutoras de sulfato

Bactérias redutoras de sulfato (BRS) possuem um papel importante na corrosão de ligas metálicas expostas em hábitats marinhos, óleos e solos úmidos. A redução do sulfato por estas bactérias resulta na produção de H2S, podendo influenciar os processos anódico e catódico na corrosão de materiais. Neste trabalho, o comportamento da corrosão microbiológica no aço carbono AISI 1020 foi avaliada em meio Postgate C, na presença e na ausência de BRS, as quais foram isoladas da camada de ferrugem presente numa tubulação submersa da Baía de Guanabara RJ. A taxa de corrosão e o comportamento eletroquímico do aço nas duas condições foram investigados através dos métodos de perda de massa e de polarização potenciodinâmica. A formação do biofilme e dos produtos de corrosão na superfície do aço foram observados por microscopia eletrônica de varredura (MEV) e por espectroscopia de energia dispersiva (EDS). Em complementação, foi realizada a quantificação das BRS (planctônicas e sésseis) pelo método do número mais provável (NMP). A presença de BRS no meio ocasionou o deslocamento do potencial de corrosão para valores mais negativos em todos os tempos de ensaio estudados, indicando um aumento no processo corrosivo. Nos ensaios de perda de massa, a taxa de corrosão do aço carbono foi maior na ausência de BRS, provavelmente devido à formação de um biofilme na superfície do metal nos ensaios com inóculo, e a uma menor tendência de haver corrosão generalizada neste tipo de meio. As micrografias de MEV revelaram a presença de agregado celular na superfície do aço carbono durante o experimento, e a presença de pites profundos após remoção do biofilme, mostrando prevalência deste tipo de corrosão. Com 35 dias de ensaio, a densidade de corrente de corrosão aumentou na presença de BRS