Size effects of polycrystalline lanthanum modified Bi4Ti3O12 thin films

The film thickness dependence on the ferroelectric properties of lanthanum modified bismuth titanate Bi3.25La0.75Ti3O12 was investigated. Films with thicknesses ranging from 230 to 404 nut were grown on platinum-coated silicon substrates by the polymeric precursor method. The internal strain is strongly influenced by the film thickness. The morphology of the film changes as the number of layers increases indicating a thickness dependent grain size. The leakage current, remanent polarization and drive voltage were also affected by the film thickness. (c) 2007 Elsevier Ltd. All rights reserved.

Rietveld analysys and electrical properties of lanthanum doped BiFeO3 ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lanthanum doped BiFeO3 powders: Syntheses and characterization

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure and crystallization of lanthanum fluorozirconate glasses

Glasses with compositions (1-x)ZrF4-xLnF(3), 0.2 less than or equal to x less than or equal to 0.4 and Ln = La or La, Eu have been synthesized and investigated using differential scanning calorimetry, X-ray diffraction, Raman scattering and Eu3+ optical spectroscopy. Single-phase polycrystalline lanthanum fluorozirconates with Zr/Ln ratio equal to 1, 2 and 3 have been investigated using the same techniques for comparison. The crystalline phases LnZrF(7), LnZr(2)F(11), LT-LnZr(3)F(15) (orthorhombic) and HT-LnZr(3)F(15) (trigonal) have been characterized in the recrystallized glasses and in samples spontaneously crystallized from the melt. Another phase has also been observed but remains undefined, the Raman scattering spectra of the vitreous samples are related to the vibration modes of [ZrF6] isolated octahedra, and of [ZrF7] and [ZrF8] structural units with bridging fluorine ions. The Eu3+ fluorescence data are related to a predominant local environment of the lanthanide ions in the glasses similar to that of the lanthanide in LnZrF(7).

Biosotption of lanthanum using Sargassum fluitans in batch system

Separation and purification of lanthanum from other rare-earth (RE) elements are highly complex processes comprising several steps of extraction using organic solvents or ion-exchange resins at high costs. In order to study the biosorption process as an alternative for conventional lanthanum recovery, this work investigated some basic aspects of lanthanum-Sargassum biomass interactions in batch equilibrium contact. The dynamics of biosorption, influence of pH, and the desorption of this RE were investigated. Maximum biosorption coefficient (q(max)) increased from 0.05 at pH 2 to 0.53 mmol g(-1) at pH 5 for lanthanum sulfate. When lanthanum chloride was used, a higher q(max) at pH 5 (0.73 mmol g(-1)) was observed as compared to the sulfate salt (q(max) = 0.53 mmol g(-1)) at the same pH. Adsorption and desorption curves pointed out a complete recovery of metal adsorbed in the Sargassum fluitans biomass, showing a reversibility of this process and indicating the potential of biosorption for lanthanum removal and recovery. (C) 2002 Elsevier B.V. B.V. All rights reserved.

The influence of crystallization route on the properties of lanthanum-doped Bi4Ti3O12 thin films prepared from polymeric precursors

Pure and lanthanum-doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. The spin-coated films were specular and crack-free and crystalline after annealing at 700 degreesC for 2 h. Crystallinity and morphological evaluation were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Multilayered films obtained using the intermediate-crystalline layer route present a dense microstructure with spherical grains. Films obtained using the intermediate-amorphous layer, present elongated grains around 250 nm in size. The dielectric and ferroelectric properties of the lanthanum-doped Bi4Ti3O12 films are strongly affected by the crystallization route. The hysteresis loops are fully saturated with a remnant polarization and drive voltage of the films, heat-treated by the intermediate-crystalline (P-r = 20.2 muC/cm(2) and V = 1.35 V) and for the film heat-treated by amorphous route (P-r = 22.4 muC/cm(2) and V = 2.99 V). (C) 2004 Elsevier B.V. All rights reserved.

Luminescence in semi-crystalline zirconium titanate doped with lanthanum

This paper aims to describe the synthesis of the semi-crystalline and crystalline powder of lanthanum doped with zirconium titanate (65/35), LZT through Pechini method. The analysis done by Raman demonstrated that semi-crystalline phase at 550 degrees C and crystalline phase after 600 degrees C were formed. The XRD pattern shows the ZrTiO4 phase formation demonstrating that La substitutions into the lattice take place. The calcined powder at different temperatures shows a semi-crystalline phase presenting photoluminescence effect when processed at low temperatures. From 300 to 400 degrees C a broadband is observed at 563 nm and 568 nm, respectively. Defects creation such as: Zr3+ center dot Vo(center dot center dot) and Ti3+ - V-O(center dot center dot), Zr and Ti replaced by La with vacancy formation, impurities and imperfections contributed to the photoluminescence effect. However, the main emission is due to a reverse Ti4+ -> O2- or/and Zr4+ -> O2- transition that occur within a regular titanate or zirconate eight-fold coordination [BO8-delta], B = Zr4+, Ti4+. (c) 2006 Elsevier B.V. All rights reserved.

Ferroelectric and dielectric properties of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration of 0.75 was grown on Pt/Ti/SiO2/Si substrates by using the polymeric precursor solution and spin-coating method. The scanning electron microscopy (SEM) showed rounded grains, which is not typical for these system. The BLT films showed well-saturated polarization-electric field curve which 2P(r) = 41.4 muC/cm(2) and V-c = 0.99 V. The capacitance dependence on the voltage is strongly nonlinear, confirming the ferroelectric properties of the film resulting from the domains switching. These properties make BLT a promising material for FERAM applications.

Electrical characterization of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration ranging from 0 to 0.75 were grown on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution and spin-coating method. The scanning electron microscopy shows a change of morphology with increasing the lanthanum concentration. The BLT films show well-saturated polarization-electric field curves whit remnant polarizations of 14.7, 20.5, 21.5, and 20.4 muC/cm(2) for x = 0, 0.25, 0.50 and 0.75, respectively. The dielectric constant of BLT (x = 0.75 mol% La) is equal to 158 while dielectric loss remain low (tandelta = 0.0018).

The effect of microwave annealing on the electrical characteristics of lanthanum doped bismuth titanate films obtained by the polymeric precursor method

Lanthanum doped bismuth titanate thin films (Bi3.25La0.75Ti3O12-BLT) were produced by the polymeric precursor method and crystallized in a domestic microwave oven and in conventional furnace. Using platinum coated silicon substrates configuration, ferroelectric properties of the films were determined with remanent polarization P-r and a coercive field E-c of 3.9 mu C/cm(2) and 70 kV/cm for the film annealed in the microwave oven and 20 mu C/cm(2) and 52 kV/cm for the film annealed in conventional furnace, respectively. The films annealed in conventional furnace exhibited excellent retention-free characteristics at low infant periods indicating that BLT thin films can be a promise material for use in nonvolatile memories. on the other hand, the pinning of domains wall causes a strong decay at low infant periods for the films annealed in the microwave furnace which makes undesireable the application for future FeRAMS memories. (c) 2005 Elsevier B.V. All rights reserved.

a-b axis-oriented lanthanum doped Bi4Ti3O12 thin films grown on a TiO2 buffer layer

a-b axis-oriented, lanthanum doped Bi4Ti3O12 (BLT) thin films with a TiO2 rutile buffer layer deposited on Pt/Ti/SiO2/Si substrates were grown by the soft chemical method. Butterfly dielectric behavior has been achieved and can be ascribed to the ferroelectric domain switching. The remanent polarization and the coercive voltage for the film deposited on TiO2 buffer layer were 22.2 mu C/cm(2) and 1.8 V, respectively. Random-oriented BLT films showed a reduction in switching polarization when compared to the a-b axis-oriented films. Due to the excellent physical properties, these films are a promising candidate for use in lead-free applications in ferroelectric devices. (c) 2006 American Institute of Physics.

Nucleation and growth of mullite whiskers from lanthanum-doped aluminosilicate melts

Nucleation and growth of mullite whiskers in the La2O3-Al2O3-SiO2 system were investigated in the 1500degrees-1700degreesC temperature range. A differential thermal analysis (DTA) showed that the mullitization temperature decreases from 1350degreesC to 1240degreesC as a result of lanthania doping. In the temperature range of 1250-1500degreesC, most of the mullite grains have an Al2O3/SiO2 = 1.5 composition throughout the ceramic body; however, from 1400degreesC upward, the number of anisotropic grains with the Al2O3/SiO2 = 1.3 composition begins to increase. The concentration of alumina in the composition of the grain-boundary phase decreases as firing temperatures increase. At temperatures > 1500degreesC, alumina grains and whiskers grow on the internal and external surfaces of the ceramic body with the characteristic Al2O3/SiO2 = 1.3 composition. Removal of the mullite whisker layer by acid attack revealed an alumina-rich, rosace-like patterned microstructure correlated with the process of whisker nucleation and growth. In the early stages, whisker growth rates were found to be near 60 mum/h. Experimental evidence pointed to nucleation inside the thin glass layer on the external surface.

Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystal structure refinement of Co-doped lanthanum chromites

Results of crystal structure refinements and phase quantification for samples of Co-doped lanthanum chromites with nominal composition LaCr(1-x)Co(x)O(3), for x=0.00, 0.10, 0.20, and 0.30, prepared by combustion synthesis are presented. The resulting powders were characterized by scanning electron microscopy and X-ray diffraction (XRD). The XRD patterns were obtained with Cu K alpha radiation for non-doped lanthanum chromite sample and additionally with Cr K alpha radiation for Co-doped lanthanum chromites samples, in order to enhance the signal from scattering. Rietveld analysis of XRD data showed that the studied samples presented the lanthanum chromite with an orthorhombic structure (Pnma), except for the composition with x=0.30, in which the space group was found to be R (3) over barc. (C) 2008 International Centre for Diffraction Data.