Lithium-lanthanum double chromates

Synthesis and crystallographic data are reported for low and high temperature forms of LiLa(CrO4)2. The compounds are closely related to lamellar rare earth phosphates and arsenates of sodium and to RbLu(CrO4)2. Lattice parameters of the orthorhombic (low temperature) and monoclinic (high temperature) forms are given. The low temperature form is moisture sensitive and Li+ ions are easily displaced by protons. Thermal decomposition takes place at 250 °C and results in the formation of LiCrO2, LaCrO4, LaCrO3 and Cr2O3. © 1993.

Phonons in binary BCC lithium-sodium alloys

The dispersion relations along the principal symmetry directions in BCC lithium-sodium alloys are calculated using second-order perturbation theory. The local modified Hoshino-Youngmodel potential was used for the lithium and the local Harrison model potential for sodium. The phonon density of states, the root mean square displacements and (Θ-T) curves are also calculated. In the absence of experimental data, just the theoretical predictions are presented here.

Lanthanum-lithium-sodium double chromates as ionic conductors

Lanthanum-lithium-sodium double chromates Li1-xNaxLa(CrO4)2 were prepared and analysed by means of admittance spectroscopy. Their a.c. conductivity parameters are correlated with structural details of high and low temperature forms of pure lanthanum-lithium double chromates. Lithium compounds show the lowest conductivity values and the highest activation energy for ion motion, while the sample Li0.5Na0.5La(CrO4)2 exhibits the highest conductivity 10-5 S cm-1 and the lowest activation energy 0.58 eV.

Scandium fluorides

A new modification of scandium fluoride has been synthesised. The compound is deficient in fluorine, with the composition ScF2.76. It belongs to the tetragonal system, lattice parameters being a = 3.792 and c = 6.740 Å and may be obtained at low temperatures by the decomposition of the precursor NH4ScF4. The reaction is topotactic, tetragonal parameters of the precursor are a = 4.021 and c = 6.744 Å. Structural relationships with various fluorides and ammonium aminofluorides are discussed. This synthesis route with IR-assisted decomposition should be considered as a soft-chemistry approach. © 1997 Elsevier Science S.A.

S-, P-, and D-wave resonances in positronium-lithium-atom scattering

We investigate ortho-positronium-lithium-atom (Ps-Li) scattering using static-exchange and three-Ps-state coupled-channel calculations. The present three-PS-state scheme, while closely agreeing with the resonance and binding energies in the Ps-H system, predicts S-, P-, and D-wave resonances at 4.25 eV, 4.9 eV, and, 5.25 eV. respectively, in the electronic spin-singlet channel of Ps-Li scattering. The present calculation also yields a Ps-Li binding in this attractive singlet channel with an approximate binding energy of 0.218 eV, which is in adherence with the recent findings of a chemically stable PsLi system using stocastic variational and quantum Monte Carlo calculations. We further report elastic, Ps(2s)-, and Ps(2p)-excitation cross sections at low to medium energies (0.068-30 eV).

Solid-state NMR, ionic conductivity, and thermal studies of lithium-doped siloxane-poly(propylene glycol) organic-inorganic nanocomposites

Hybrid organic-inorganic ionic conductors, also called ormolytes (organically modified electrolytes), were obtained by dissolution of LiClO 4 in siloxane-poly(propylene glycol) matrixes. The dynamic features of these nanocomposites were studied and correlated to their electrical properties. Solid-state nuclear magnetic resonance (NMR) spectroscopy was used to probe the effects of the temperature and nanocomposite composition on the dynamic behaviors of both the ionic species ( 7Li) and the polymer chains ( 13C). NMR, dc ionic conductivity, and DSC results demonstrate that the Li + mobility is strongly assisted by the segmental motion of the polymer chain above its glass transition temperature. The ac ionic conductivity in such composites is explained by use of the random free energy barrier (RFEB) model, which is agreement with their disordered and heterogenous structures. These solid ormolytes are transparent and flexible, and they exhibit good ionic conductivity at room temperature (up to 10 -4 S/cm). Consequently, they are very promising candidates for use in several applications such as batteries, sensors, and electrochromic and photoelectro-chemical devices.

X-ray-induced conductivity in iron-doped lithium niobate crystals

Illumination of photorefractive, iron-doped lithium niobate crystals (LiNbO 3:Fe) with x-rays generates a conductivity that we determine from the speed of hologram erasure. The doping levels of the crystals and the acceleration voltage of our x-ray tube are varied. A theoretical model is presented, which describes the obtained results. A decrease of the conductivity with increasing Fe 2+ concentration can be explained by assuming that holes are the dominant charge carriers for this short-wavelength illumination.

Effect of lithium doping on the evolution of rheological and structural properties during gelation of siloxane-poly(oxypropylene) nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Measurement of orthovoltage X-ray intensity with a lithium niobate transducer

A microcontrolled instrument for measuring the energy fluence rate (or intensity) of X-ray pulses in the orthovoltage range of 120 to 300 kV is described. The prototype instrument consists of a pyroelectric sensor, a low-noise highsensitivity current-to-voltage converter, a microcontroller and a digital display. The response of the instrument is nonlinear with the intensity of the radiation. The precision is better than 3%. The equipment is inexpensive, rugged, simple to construct and has good long-term stability. © 2009 Springer-Verlag.

Effect of hydrofluoric acid etching duration on the roughness and flexural strength of a lithium disilicate-based glass ceramic

The aim of this study was to examine the effect of different acid etching times on the surface roughness and flexural strength of a lithium disilicate-based glass ceramic. Ceramic bar-shaped specimens (16 mm x 2 mm x 2 mm) were produced from ceramic blocks. All specimens were polished and sonically cleaned in distilled water. Specimens were randomly divided into 5 groups (n=15). Group A (control) no treatment. Groups B-E were etched with 4.9% hydrofluoric acid (HF) for 4 different etching periods: 20 s, 60 s, 90 s and 180 s, respectively. Etched surfaces were observed under scanning electron microscopy. Surface profilometry was used to examine the roughness of the etched ceramic surfaces, and the specimens were loaded to failure using a 3-point bending test to determine the flexural strength. Data were analyzed using one-way ANOVA and Tukey's test (α=0.05). All etching periods produced significantly rougher surfaces than the control group (p<0.05). Roughness values increased with the increase of the etching time. The mean flexural strength values were (MPa): A=417 ± 55; B=367 ± 68; C=363 ± 84; D=329 ± 70; and E=314 ± 62. HF etching significantly reduced the mean flexural strength as the etching time increased (p=0.003). In conclusion, the findings of this study showed that the increase of HF etching time affected the surface roughness and the flexural strength of a lithium disilicate-based glass ceramic, confirming the study hypothesis.

Topical use of fluorides for caries control

Since the early findings on the protective effects of fluoride present in drinking water upon caries incidence and prevalence, intensive research has been conducted in order to determine the benefits, safety, as well as the cost-effectiveness of other modalities of fluoride delivery. The present chapter reviews the various forms of topical fluoride use - professionally and self-applied - with special emphasis on clinical efficacy and possible side effects. The most widely used forms of fluoride delivery have been subject of several systematic reviews, providing strong evidence supporting the use of dentifrices, gels, varnishes and mouth rinses for the control of caries progression. Dentifrices with fluoride concentrations of 1,000 ppm and above have been shown to be clinically effective in caries prevention when compared to a placebo treatment, but the evidence regarding formulations with 450-550 ppm is still subject of debate. Therefore, the recommendation for low-fluoride dentifrice use must take into account both risks and benefits. The evidence for the combined use of two modalities of fluoride application in comparison to a single modality is still inconsistent, implying that more studies with adequate methodology are needed to determine the real benefits of each method. Considering the currently available evidence and risk-benefit aspects, it seems justifiable to recommend the use of fluoridated dentifrices to individuals of all ages, and additional fluoride therapy should also be targeted towards individuals at high caries risk. © 2011 S. Karger AG, Basel.

Stress distribution in ceramic restorations over natural tooth using finite element analysis. lithium disilicate x aluminum oxide material

Background: Data on stress distribution in tooth-restoration interface with different ceramic restorative materials are limited. The aim of this chapter was to assess the stress distribution in the interface of ceramic restorations with laminate veneer or full-coverage crown with two different materials (lithium dissilicate and densely sintered aluminum oxide) under different loading areas through finite element analysis. Materials and Methods: Six two-dimensional finite element models were fabricated with different restorations on natural tooth: laminate veneer (IPS Empress, IPS Empress Esthetic and Procera AllCeram) or full-coverage crown (IPS e.max Press and Procera AllCeram). Two different loading areas (L) (50N) were also determined: palatal surface at 45° in relation to the long axis of tooth (L1) and perpendicular to the incisal edge (L2). A model with higid natural tooth was used as control. von Mises equivalent stress (σ vM) and maximum principal stress (σ max) were obtained on Ansys software. Results: The presence of ceramic restoration increased σ vM and σ max in the adhesive interface, mainly for the aluminum oxide (Procera AllCeram system) restorations. The full-coverage crowns generated higher stress in the adhesive interface under L1 while the same result was observed for the laminate veneers under L2. Conclusions: Lithium dissilicate and densely sintered aluminum oxide restorations exhibit different behavior due to different mechanical properties and loading conditions. © 2011 Nova Science Publishers, Inc.

Governance of strategic minerals in Latin America: the case of Lithium

The objectives of this report are twofold: The first is to provide an integrated overview of the governance of strategic minerals in the Latin American and Caribbean region, focused on sharing the economic-resource rent. The second objective is to provide a context for the policy proposal of the Chilean National Lithium Commission (NLC. The collected data, and information, on the various fiscal regimes can be used as a reference for further research. The objectives in this report are met by analyzing distinct aspects of strategic mineral governance, in three different parts. The lithium-industry serves as a case study for this report, as an example of a strategic mineral.

Effect of Resin Cement Type on the Microtensile Bond Strength to Lithium Disilicate Ceramic and Dentin Using Different Test Assemblies

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microwave-assisted hydrothermal synthesis of magnetite nanoparticles with potential use as anode in lithium ion batteries

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)