Diffractive microlens with a cascade focal plane fabricated by single mask UV-photolithography and common KOH:H2O etching

A diffractive microlens with a cascade focal plane along the main optical axis of the device is fabricated using a low-cost technique mainly including single mask ultraviolet (UV) photolithography and dual-step KOH:H2O etching. Based on the evolutionary behavior of converse pyramid-shaped microholes (CPSMs) preshaped over a {100}-oriented silicon wafer in KOH etchant, the first-step KOH etching is performed to transfer initial square micro-openings in a SiO2 film grown by plasma enhanced chemical vapor deposition (PECVD) and patterned by single mask UV-photolithography, into CPSMs with needed dimension. After completely removing a thinned SiO2 mask, basic annular phase steps with a relatively steep sidewall and scheduled height can be shaped in the overlapped etching region between the neighboring silicon concave-arc microstructures evolved from CPSMs through the second-step KOH etching. Morphological measurements demonstrate a desirable surface of the silicon microlens with a roughness in nanometer scale and the feature height of the phase steps formed in the submicrometer range. Conventional optics measurements of the plastic diffractive microlens obtained by further hot embossing the fine microrelief phase map over the nickel mask made through a common electrochemical method indicate a highly efficient cascaded focusing performance.

Segmented All-Platinum Nanowires with Controlled Morphology through Manipulation of the Local Electrolyte Distribution in Fluidic Nanochannels during Electrodeposition

Synthesis of segmented all-Pt nanowires is achieved by a template-assisted method. The combination of a suitably chosen electrolyte/template system with pulse-reverse electrodeposition allows the formation of well-defined segments linked to nanowires. Manipulation of the morphology is obtained by controlling the electrokinetie effects on the local electrolyte distribution inside the nanochannels during the nanowire growth process, allowing a deviation from the continuously cylindrical geometry given by the nanoporous template. The length of the segments can be adjusted as a function of the cathodic pulse duration. Applying constant pulses leads to segments with homogeneous shape and dimensions along most of the total wire length. X-ray diffraction demonstrates that the preferred crystallite orientation of the polycrystalline wires varies with the average segment length. The results are explained considering transitions in texture formation with increasing thickness of the electrodeposit. A mechanism of segment formation is proposed based on structural characterizations. Nanowires with controlled segmented morphology are of great technological importance, because of the possibility to precisely control their substructure as a means of tuning their electrical, thermal, and optical properties. The concept we present in this work for electrodeposited platinum and track-etched polycarbonate membranes can be applied to other selected materials as well as templates and constitutes a general method to controlled nanostructuring and synthesis of shape controlled nanostructures.

Blends based on sulfonated poly[bis(benzimidazobenzisoquinolinones)] and poly(vinylidene fluoride) for polymer electrolyte membrane fuel cell

A new blend system consisting of an amorphous sulfonated poly[bis(benzimidazobenzisoquinolinones)] (SPBIBI) and the semi-crystalline poly(vinylidene fluoride) (PVDF) was prepared for proton exchange membranes. The miscibility behavior of a series of blends of SPBIBI with PVDF at various weight ratios was studied by WXRD, DSC and FTIR. The properties of the blend membranes were investigated, and it was found that the introduction of PVDF in the SPBIBI matrix altered the morphological structure of the blend membranes, which led to the formation of improved connectivity channels. For instance, the conductivity of the blend membrane containing 10 wt% PVDF displayed the highest proton conductivity (i.e., 0.086 S cm(-1)) at room temperature, a value almost twofold that of the pristine SPBIBI membranes (i.e., 0.054S cm(-1)) under identical conditions.

Synthesis and Electrical Properties of New Solid State Electrolyte Materials Ce6-xHoxMoO15-delta(0.0 <= x <= 1.2)

Ce6-xHoxMoO15-delta(0.0 <= x <= 1.2) was synthesized by modified sol-gel method and characterized by differential X-ray diffraction(XRD), Raman, and X-ray photoelectron spectroscopy(XPS) methods. The oxide ionic conductivity of the samples was investigated by AC impedance spectroscopy. It shows that all the samples are single phase with a cubic fluorite structure. The solid solution Ce6-xHoxMoO15-delta(x=0.6) was detected to be the best conducting phase with the highest conductivity(sigma(t)=1.05x10(-2) S/cm) at 800 degrees C and the lowest activation energy(E-a=1.09 eV). These properties suggest that this kind of material has a potential application in intermediate-low temperature solid oxide fuel cells.

Enhanced electrochemical properties of nanocomposite polymer electrolyte based on copolymer with exfoliated clays

In this present work, a polymer electrolyte based on polymer/clay nanocomposite has been developed. Montmorillonite (MMT) clay was used as the filler. due to its special size in length and thickness, and its sandwich type structure. The obtained gel polymer electrolytes have high ionic conductivity up to 2.5 mS cm(-1) with high cationic transference number (about 0.64) at room temperature. The influences of the filler on the membrane morphology. the solvent uptake, the ionic conductivity, and the cation transport number were investigated, and thus the significant contribution from the exfoliated organophilic MMT was identified.

Organic/inorganic nanocomposite polymer electrolyte

The organic/inorganic nanocomposites polymer electrolytes were designed and synthesized. The organic/inorganic nanocomposites membrane materials and their lithium salt complexes have been found thermally stable below 200 degrees C. The conductivity of the organic/inorganic nanocomposites polymer electrolytes prepared at room temperature was at magnitude range of 10(-6) S/cm. (c) 2007 Li Qi. Published by Elsevier B.V. on behalf of Chinese Chemical Society. All rights reserved.

Synthesis and electrical properties of new solid state. Electrolyte materials Ce5.2RE0.8MoO15-delta

A series of solid state electrolytes, Ce-5.2 RE0.8 MoO15-delta (RE = Y, La, Sm, Gd, Dy, Ho, Er), were synthesized by sol-gel method. Their structures and electrical conductivities were characterized by X-ray Diffraction (XRD), Raman and X-ray Photoelectron Spectroscopy (XPS) and AC impedance spectroscopy, respectively. The results show that the concentrations of oxygen vacancy increased with increasing x and their conductivity were improved. And the cell parameters increase as the radius of RE3+ increases. Because the ionic radius of doped Dy3+ (0.0908 nm) is closed to that of Ce4+ (0.0920 nm), their oxide has minimal cell elastic straining between RE3+ and oxygen vacancy, and the system has the least association enthalpy, thus the oxide Ce-5.2 Dy-0.8 MoO15-delta exhibits a higher conductivity (7.02 x 10(-3) S/cm) and lower activation energy (1.056 eV) compared to the other doped compounds.

Synthesis, characterization and electrical properties of solid state electrolyte materials La2-xCaxMo1.7W0.3O9-delta (0 <= x <= 0.2)

The new compounds La2-xCaxMo1.7W0.3O9-delta (0 <= x <= 0.2) in which La3+ substituted with Ca2+ were synthesized by dry-chemistry techniques based on the oxygen Ionic conductor La2Mo1.7W0.3O9. The new series were characterized by X-ray Diffraction (XRD), Raman and X-ray Photoelectron Spectroscopy (XPS) and the electrical conductivity of samples were investigated by AC impedance spectroscopy. The lattice parameters were reduced due to the smaller atomic radius of the Ca2+ compared with that of the La3+. Furthermore, Additional oxygen vacancies were introduced into La2Mo1.7W0.3O9 lattice by substitution, and then the oxygen ionic conductivity was increased. At 550 degrees C, the conductivity increased 89.9%, that is, from 0.79 x 10(-4) S center dot cm(-1) (x=0) to 1.5 X 10(-4)S center dot cm(-1) (x=0.16, 0.2).

Polyelectrolyte-functionalized ionic liquid for electrochemistry in supporting electrolyte-free aqueous solutions and application in amperometric flow injection analysis

As a green process, electrochemistry in aqueous solution without a supporting electrolyte has been described based on a simple polyelectrolyte-functionalized ionic liquid (PFIL)-modified electrode. The studied PFIL material combines features of ionic liquids and traditional polyelectrolytes. The ionic liquid part provides a high ionic conductivity and affinity to many different compounds. The polyelectrolyte part has a good stability in aqueous solution and a capability of being immobilized on different substrates. The electrochemical properties of such a PFIL-modified electrode assembly in a supporting electrolyte-free solution have been investigated by using an electrically neutral electroactive species, hydroquinone ( HQ) as the model compound. The partition coefficient and diffusion coefficient of HQ in the PFIL film were calculated to be 0.346 and 4.74 X 10(-6) cm(2) s(-1), respectively. Electrochemistry in PFIL is similar to electrochemistry in a solution of traditional supporting electrolytes, except that the electrochemical reaction takes place in a thin film on the surface of the electrode. PFILs are easily immobilized on solid substrates, are inexpensive and electrochemically stable. A PFIL-modified electrode assembly is successfully used in the flow analysis of HQ by amperometric detection in solution without a supporting electrolyte.