Novel Bi-doped glasses for broadband optical amplification

Broadband infrared luminescence is observed in various Bi-doped oxide glasses prepared by conventional melting-quenching technique. The absorption spectrum of the Bi-doped germanium oxide glass consists of five broad peaks at below 370, 500, 700, 800 and 1000 nm. The fluorescence spectrum exhibits a broad peak at about 1300 nm with full width at half maximum (FWHM) of more than 300 nm when excited by an 808 nm laser diode. The fluorescence lifetime at room temperature decreases with increasing Bi2O3 concentration. Influence of the glass composition and melting atmosphere on the fluorescence lifetime and luminescent intensity is investigated. The mechanism of the broadband infrared luminescence is suggested. The product of stimulated emission cross-section and lifetime of the Bi-doped aluminophosphate glass is about 5.0 X 10(-24) cm(2) s. The glasses might be promising for applications in broadband optical fiber amplifiers and tunable lasers. (c) 2007 Elsevier B.V. All rights reserved.

用于波导放大器的Er^3＋／Yb^3＋共掺磷酸盐玻璃的性能研究

通过优化熔融条件和玻璃组份，成功开发出一种新的Er^3+／Yb^3+共掺磷酸盐玻璃，其在沸水和熔盐中均表现出很好的化学稳定性。通过分析室温下Er^3+／Yb^3+共掺磷酸盐玻璃的吸收光谱，计算得到了Er^3+离子在波长1533nm处的峰值发射截面和杜得-奥菲而特强度参数；其中Er^3+离子在波长1533nm处的峰值发射截面为0．72×10^20cm^2，大于Schott的IOG1玻璃中Er^3+离子的峰值发射截面0．67×10^-20cm^2。通过改变离子交换的条件，获得了1．55μm单模光波导的制作条件

不同退火气氛下γ-LiAlO2形貌和结构研究

研究了温度梯度法生长的γ-LiAlO2晶体在1100℃下富Li气氛和空气中退火处理后的表面形貌、表面结构以及吸收光谱。发现γ-LiAlO2晶体的抛光面在1100℃空气中退火后变为粗糙面，X射线衍射(XRD)分析表明此粗糙面为单相的LiAl5O8。而γ-LiAlO2晶体的抛光面在1100℃富Li气氛中处理后几乎没有变化。同时对不同气氛下热处理的γ-LiAlO2晶体进行了光谱分析，确认了晶片中196nm的吸收峰是由Li空位引起的。

新型衬底材料γ-LiAlO2热稳定性研究

研究了温度梯度法生长的γ-LiAlO2晶体在1100℃不同气氛处理的热稳定性。借助扫描电子显微镜和X射线衍射分析发现：1100℃／10h真空和空气处理后的样品表面分别形成了均匀微孔状和岛状LiAl5O8多晶；而富Li气氛处理后样品表面仍然光滑且仍为LiAlO2。用Leitz大视场显微镜观察重新抛光后样品内部宏观缺陷，发现空气和真空处理后样品缺陷增多，分别为岛状和条纹状缺陷；而富Li气氛处理后样品中缺陷明显减少。对比不同气氛处理的4块样品吸收光谱，确认了真空和空气处理产生的196nm吸收峰可能是Li空位吸收

Optical spectroscopy of Yb3Al5O12 single crystal

Yb3Al5O12 single crystal has been grown by Czochralski (CZ) method. The absorption spectrum was investigated at low temperature and the electronic energy levels for F-2(5/2) multiplet of Yb3+ in YbAG was proposed. The up-conversion emission of the crystal under 940 nm diode pumping and the X-ray excited luminescence (XEL) features of the crystal were also studied. (c) 2005 Elsevier B.V. All rights reserved.

Cr^3＋：Al2O3透明多晶陶瓷光谱特性分析

对透光性良好的Cr^3＋：Al2O3透明多晶陶瓷的光谱性能进行了研究，其吸收光谱中吸收峰与单晶红宝石相一致，按吸收光谱和Tanabe-Sugano能级图，算出其晶场强度参数Dq及Racah参数B分别为1792cm^-1，689cm^-1，Dq／B=2．6，陶瓷中Cr^3＋离子所处格位的晶体场强比单晶弱一些，但Cr^3＋：Al2O3透明陶瓷仍属于强场晶体材料；当Cr^3＋掺杂浓度到达0．8wt％时，陶瓷的发射谱仍保持较好的R线发射；随Cr^3＋掺杂浓度的增大，激发峰位发生“红移”．在Cr^3＋：Al2O3透

Luminescence studies of Ce : YAG using vacuum ultraviolet synchrotron radiation

Photoluminescence spectrum of Ce:YAG single crystal was studied employing vacuum ultraviolet (VUV) synchrotron radiation. Intrinsic absorption edge at about 52,000 cm(-1) was observed in the absorption spectrum. From the VUV excitation spectrum, the energy of the highest d-component of 53,191 cm(-1) (188 nm) for the Ce3+ ions in YAG was obtained at 300 K. The disappearance of the third 5d level at 37,735 cm(-1) (265 nm) in absorption and excitation spectra in our samples may be due to the impurity Fe3+ ions absorption. (C) 2006 Elsevier Ltd. All rights reserved.

Characteristics of large-sized ruby crystal grown by temperature gradient technique

Large ruby with the size of circle divide75 x 45 mm was grown by temperature gradient technique for the first time. Absorption spectrum was carried out in the range of 190-800 nm by spectrophotometer, and the concentration spatial distribution of Cr3+ in ruby was calculated from the absorption coefficient that based on the Beer-Lambert's Law. Cr3+ ions gradually increase alone both the growth axis and the radial direction. The shape and ingredient of the inclusions were measured by means of Leitz ride field microscopy and scanning electron microscopy. Lane photos and X-ray omega scan show the good quality of as grown ruby. The optimized growth conditions were pointed out based on the observation. (C) 2004 Elsevier B.V. All rights reserved.

铝酸镧单晶体中Ce^3＋的能级结构和荧光特性

采用提拉法成功生长了纯LaAlO3和掺铈的LaAlO3单晶体，测试了它们的远红外吸收谱，紫外吸收谱，荧光谱，根据吸收光谱确定了晶体中Ce^3+的能级结构，利用这一能级结构模型较好地解释了Ce：LaAlO3晶体的荧光光谱。

Effect of air annealing on the spectral properties of Ce : Y3Al5O12 single crystals grown by the temperature gradient technique

Five absorption hands, at 227, 300 340, 370 and 457nm, were observed in the optical absorption spectrum of Ce:Y3Al5O12 (Ce:YAG) crystals grown by the temperature gradient technique (TGT). The absorption bands at 227, 340, and 457 nm were identified Lis belonging to the Ce3+ -ion in the YAG crystal. A near UV optical emission band at 398nm was observed. with an excitation spectrum containing two bands, at 235 and 370nm. No fluorescence was detected under 300 nm excitation. The pair of absorption bands at 235 and 370 nm and the absorption band at 300 nm were attributed to the F- and F+-type color centers, respectively. The color centers model was also applied to explain the spectral changes in the Ce:YAG (TGT) crystal, including the reduction in the Ce 31 -ion absorption intensity, after annealing in an oxidizing atmosphere (air). (C) 2004 Elsevier B.V. All rights reserved.

Characteristics and optical spectra of V : YAG crystal grown in reducing atmosphere

A V:YAG single crystal was grown by the temperature gradient technique (TGT) with graphite-heating elements. The as-grown crystal has different colorations of light green and yellow brown in different parts. Distribution of vanadium in three samples with different colorations was determined by inductively coupled plasma-mass spectrometry. From the absorption spectrum of the yellow-brown part with peaks at 370, 820 and 1320nm, we can deduce that the reducing atmosphere of carbon diffused from the heating elements can increase the concentration of tetrahedral V3+ ions and induce F color centers. All three samples exhibited light-green color after annealing in vacuum or H-2 atmospheres. In the vacuum annealing process, the V3+ ions in tetrahedral positions were enhanced through two methods: one method is the exchanging of octahedral V3+ and tetrahedral Al3+ ions in neighboring sites under thermal excitation, the other is that F color centers were thoroughly eliminated and the escaped free electrons could be captured by V ions with higher valance states to further improve the concentration of tetrahedral V3+ ions. Besides the two mechanisms, the H-2 annealing process greatly improved the V-tetra(3+) ions through the reduction effect of H-2. (c) 2006 Elsevier B.V. All rights reserved.

Co^2＋，Er^3＋：Y3Al5O12晶体的生长及其吸收特性

应用中频感应提拉法成功生长出新型的Co^2＋，Er^3＋：Y3Al5O12晶体。研究了室温下晶体的吸收光谱性能。结合Er^3＋：Y3Al5O12晶体的光谱，并利用调Q判据对Co^2＋，Er^3＋：Y3Al5O12晶体调Q特性进行了简单的分析。结果表明Co^2＋，Er^3＋：YAG晶体是一种很有潜力的白调Q激光晶体。

氧化铝透明陶瓷中Cr3+的发光性能

采用传统无压烧结工艺制备出透明性良好的掺Cr3+氧化铝陶瓷;测定了陶瓷的吸收光谱、发射光谱和激发光谱。结果表明,氧化铝陶瓷吸收峰与红宝石单晶一致,吸收截面大小与单晶相近;陶瓷中Cr3+离子所处格位的晶体场强较单晶弱,但其发射谱仍有较好的锐线发射;陶瓷中微量添加剂以及晶界的存在使得Al2O3晶胞发生畸变,造成其发射峰宽化。

Infrared to visible upconversion fluorescence in Yb,Tm : YAG single crystal

Absorption spectrum from 400 to 2000 run and upconversion fluorescence spectra under 940 nm pumping of YAG single crystal codoped with 5 at.% Yb3+ and 4 at.% Tm3+ were studied at room temperature. The blue upconversion emission centered at 483 nm corresponds to the transition (1)G(4) -> H-3(6), the emission band around 646 nm corresponds to the transition (1)G(4) -> F-3(4) of Tm3+. Energy transfer from Yb3+ to Tm3+ is mainly nonradiative and the transfer efficiency was experimentally assessed. The line strengths, transition probabilities and radiative lifetimes of (1)G(4) level were calculated by using Judd-Ofelt theory. Gain coefficient calculated from spectra shows that the upconversion corresponding with transitions (1)G(4) -> H-3(6) in YAG doped with Yb3+ and Tm3+ is potentially useful for blue light Output. (c) 2006 Elsevier B.V. All rights reserved.

Growth and spectral properties of Yb : FAP single crystal

In this paper, single crystal of ytterbium (Yb) doped Ca-5(PO4)(3)F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982 nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (sigma(abs)) is 5.117 x 10(-20) cm(2) with an FWHM of 4 nm at 982 nm. The emission cross-section is (sigma(em)) 3.678 x 10(-20) cm(2) at 1042 nm. Favorable values of the absorption cross-section at about 982 nm are promising candidates for laser diode (LD) pumping. (c) 2005 Elsevier B.V. All rights reserved.