Structure effect on the oxygen permeation properties of barium bismuth iron oxide membranes

In this work, we investigated the oxygen permeation properties of barium bismuth iron oxide within the family of [Ba_2−3xBi_3x−1][Fe_2xBi_1−2x]O_2+3x/2 for x = 0.17–0.60. The structure changed progressively from cubic to tetragonal and then to hexagonal as function of x in accordance with the different relative amounts of bismuth on A-site and B-site of ABO_3−δ perovskite lattices. We found that the oxygen flux and electrical conductivity correlated strongly, and it was prevalent for the cubic structure (x = 0.33–0.40) which conferred the highest oxygen flux of 0.59 ml min⁻¹ cm⁻² at 950 °C for a disk membrane x = 0.33 with a thickness of 1.2 mm. By reducing the thickness of the disk membrane to 0.8 mm, the oxygen flux increased to 0.77 ml min⁻¹ cm⁻², suggesting both surface kinetics and ion diffusion controlled oxygen flux, though the former was more prominent at higher temperatures. For disk membranes x = 0.45–0.60, the perovskite structure changed to tetragonal and hexagonal, and the oxygen flux was insignificant below 900 °C, clearly indicating electron conduction properties only. However, for two compositions with relatively high bismuth content, e.g. x = 0.55 and 0.60, there was a sudden and significant rise of oxygen permeability above 900 °C, by more than one order of magnitude. These materials changed conduction behavior from metallic to semiconductor at around 900 °C. These results suggest the advent of mixed ionic electronic conducting properties caused by the structure transition as bismuth ions changed their valence states to compensate for the oxygen vacancies formed within the perovskite lattices.

Graphene oxide nanoparticles as a nonbleaching optical probe for two-photon luminescence imaging and cell therapy

Lasting glow: Under femtosecond laser irradiation, graphene oxide nanoparticles (GONs) give strong two-photon luminescence (TPL; see picture). The presence of GONs also induces microbubbling, which causes cell death at an order of magnitude lower laser power than when cells are not labeled. The results show that GONs can be used for TPL-based imaging and photothermal cancer therapy.

Biocompatibility of transition metal-substituted cobalt ferrite nanoparticles

Transition metals of copper, zinc, manganese, and nickel were substituted into cobalt ferrite nanoparticles via a sol-gel route using citric acid as a chelating agent. The microstructure and elemental compositions of the nanoparticles were characterized using scanning electron microscopy combined with energy dispersive X-ray spectroscopy. The particle size of the nanoparticles was investigated using particle size analyzer, and the zeta potentials were measured using zeta potential analyzer. The phase components of the synthesized transition metal-substituted cobalt ferrite nanoparticles were studied using Raman spectroscopy. The biocompatibility of the nanoparticles was assessed using osteoblast-like cells. Results indicated that the substitution of transition metals strongly influences the physical, chemical properties, and biocompatibility of the cobalt ferrite nanoparticles. © 2014 Springer Science+Business Media.

Nanomedicine based nanoparticles for neurological disorders

Human health is severely hampered by a majority of the neurological disorders such as the brain tumors, degenerative Alzheimer's disease, Parkinson's disease and those involving inflammatory component. Owing to the stringent protection offered by the blood brain barrier, conventional therapeutics gain limited access and therefore, are therapeutically suboptimal. Hence, research has now focused to develop the novel drug delivery systems with a prime motto of maintaining therapeutic drug levels inside the brain, avoiding non-specific tissue distribution. The introduction of nanotechnology has addressed few of these objectives and opened up new avenues for even more improvization. To some extent, nanodelivery systems were successful in crossing the blood brain barrier and accessing the remote areas of the brain. They also have shown tremendous potential in delivering the therapeutic and diagnostic aids following systemic administration. What revolutionised the nano applications is the development of "smart" nanosystems, whose surface is tailor made for the effective theranostic delivery. However, a detailed understanding of the long term nanoformulation toxicities, along with the neuropathology, is the critical future question to be addressed. In this review, a brief introduction of the prominent neurological disorders and detailed applications of nanotechnology are discussed.

Tunable dual-stimuli response of a microgel composite consisting of reduced graphene oxide nanoparticles and poly(N-isopropylacrylamide) hydrogel microspheres

A type of photo- and thermo-responsive composite microsphere composed of reduced graphene oxide nanoparticles and poly(N-isopropylacrylamide) (rGO@pNIPAM) is successfully fabricated by a facile solution mixing method. Due to the high optical absorbance and thermal conduction of rGO, the composite microspheres are endowed with the new property of photo-response, in addition to the intrinsic thermally sensitive property of pNIPAM. This new ability undoubtedly enlarges the scope of applications of the microgel spheres. Furthermore, through controlling the rGO content in the composite, the photo- and thermo-sensitivity of the composite can be effectively modulated. That is, with a lower rGO content (≤32% by weight), the composite microspheres perform only thermally induced changes, such as volume contraction (by ∼45% in diameter) and drug release, when crossing the lower critical solution temperature of pNIPAM. With a higher rGO content (∼47.5%), both temperature and light irradiation can trigger changes in the composite. However, when the rGO content is increased to around 64.5%, the thermo-responsivity of the composite disappears, and the spheres exhibit only photo-induced drug release. With a further increase in rGO content, the environmentally responsive ability of the microspheres vanishes. This journal is © the Partner Organisations 2014.

Small angle X-ray scattering study of surface modified tin oxide nanoparticles prepared by sol-gel route

The surface properties of SnO2 nanoparticles were modified by grafting ionic (Tiron (R). (OH)(2)C6H2(SO3Na)(2)(H2O)-H-.) or non-ionic (Catechol (R). C6H4-1,2-(OH)(2)) capping Molecules during aqueous sol-gel processing to improve the redispersibility of powdered xerogel. The effect of the amount of grafted organic molecules on the redispersibility of powders in aqueous solution at several basic pH values was Studied. The nanostructural features of the colloidal suspensions were analyzed by small angle X-ray scattering (SAXS) measurements. Irrespective of the nature and amount of grafted molecules, complete redispersion was obtained in aqueous solution at pH = 13. The redispersion at pH = 11 results in a mixture of dispersed primary particles and aggregates. The proportion of well dispersed nanoparticles and aggregates (and their average size) can be tuned by the quantity of grafted ionic molecules.

SAXS study of formation and growth of tin oxide nanoparticles in the presence of complexing ligands

The effect of acetylacetone (acac) complexing ligand on the formation and growth of tin oxide-based nanoparticles during thermohydrolysis at 70 degreesC of a tin precursor SnCl4-n(acac)(n) (0 less than or equal to n less than or equal to 2) solution was analyzed by in situ small-angle X-ray scattering. A. transparent and stable sol was obtained after 2 h of thermohydrolysis at 70 degreesC, allowing the quantitative determination of the particle volume distribution function and its variation with the reaction time. The number of colloidal particles for equivalent thermohydrolysis temperature and time decreases as the [acac]/[Sn] ratio in initial solution increases from 0.5 to 6. Instead, the amount of soluble species remaining in solution increases for increasing [acac]/[Sn] ratio within the same range. This indicates that increasing amounts of Sn-acetylacetone complexes partially prevent the hydrolysis and consequent formation of colloidal particles. The N-2 adsorption isotherm characterization of freeze-dried powders demonstrates that the average pore size is approximately equal to the average size (approximate to9 Angstrom) of the colloidal primary particles in the sol, and that the porosity and surface area (approximate to200 m(2) g(-1)) are independent of the acac content in the initial solution.

Structural and magnetic transformation of monodispersed iron oxide particles in a reducing atmosphere

Uniform metal iron ellipsoidal particles of around 200 nm in length were obtained by reduction and passivation of alumina-coated alpha-Fe2O3 (hematite) particles under different conditions of temperature and hydrogen flow rate. The monodispersed hematite particles were prepared by the controlled hydrolysis of ferric sulfate and further coated with a homogeneous thin layer of Al2O3 by careful selection of the experimental conditions, mainly pH and aluminum salt concentration. The reduction mechanism of alpha-Fe2O3 into alpha-Fe was followed by x-ray and electron diffraction, and also by the measurements of the irreversible magnetic susceptibility. The transformation was found to be topotactic with the [001] direction of hematite particles, which lies along the long axis of the particles, becoming the [111] direction of magnetite and finally the [111] direction of metal iron. Temperature and hydrogen flow rate during the reduction have been found to be important parameters, which determine not only the degree of reduction but also the crystallite size of the final particles. Magnetic characterization of the samples shows that the only parameters affected by the crystallite size are the saturation magnetization and magnetic time-dependence effect, i.e., activation volume. (C) 2002 American Institute of Physics.

Preparation of ceramic membranes from surface modified tin oxide nanoparticles

The preparation of crack-free SnO2 supported membranes requires the development of new strategies of synthesis capable to allow controlled changes of surface chemistry and to improve the processability of supported layers. In this way, the controlled modification of the SnO2 nanoparticle surface by adding capping molecules like Tiron(R) ((OH)(2)C6H2(SO3Na)(2)) during the sol-gel process was studied, aiming to obtain high performance membranes. Colloidal suspensions were prepared by hydrolyzing SnCl4.5H(2)O aqueous solution with NH4OH in presence of Tiron(R). The effect of the amount of Tiro(R) (from I to 20 wt.%) on the structural features of nanoparticles, powder redispersability and particle-solution interface properties was investigated by X-ray powder diffraction (XRPD), extended X-ray absorption fine structure (EXAFS), quasi-elastic light scattering and electrophoretic mobility measurements. XRPD and EXAFS results showed that the addition of Tiron(R) up to 20 wt.% to colloidal suspensions does not affect the crystallite size of SnO2 primary particles, determined around 2-3 nm. This value is comparable to the hydrodynamic size measured after redispersion of powder prepared with amount of Tiro(R) higher than 7.5 wt.%, indicating the absence of condensation reactions between primary particles after the initial precipitation step. As a consequence the powder with amount of Tiron(R) > 7.5 wt.%, can be fully redispersed in aqueous solution at pH greater than or equal to I I until a nanoparticle concentration of 6 vol.%. The electrophoresis measurements showed a decrease of the isoelectric point by increasing the amount of grafted Tiron(R) at the SnO2 nanoparticle surface, resulting in negatively charged particle-solution interface in all the studied pH range (2-11). These features govern the gelation process favoring the preparation of crack-free SnO2 supported membranes. The control exercised by Tiron(R) modifying agent in the aggregation process allows the fine-tuning of the porosity, from 0.124 to 0.065 cm(3) g(-1), and mean pore size, from 6.4 to 1.9 nm, as the amount of grafted molecules increases from 0 to 10 wt.%. In consequence, the membrane cut-off determined by filtration of polyethylene glycol standard solutions can be screened from 1500 to 3500 g mol(-1). (C) 2002 Elsevier B.V. B.V. All rights reserved.

Polyol-mediated synthesis of ultrafine tin oxide nanoparticles for reversible Li-ion storage

A simple, cheap and versatile, polyol-mediated fabrication method has been extended to the synthesis of tin oxide nanoparticles on a large scale. Ultrafine SnO2 nanoparticles with crystallite sizes of less than 5 nm were realized by refluxing SnCl2 . 2H(2)O in ethylene glycol at 195 degrees C for 4 h under vigorous stirring in air. The as-prepared SnO2 nanoparticles exhibited enhanced Li-ion storage capability and cyclability, demonstrating a specific capacity of 400 mAh g(-1) beyond 100 cycles. (c) 2006 Elsevier B.V. All rights reserved.

Development of metal oxide nanoparticles by soft chemical method