Physical properties of silicate glasses doped with SnO2

The presence of tin in the network of silicate glasses produces changes in several of their physico-chemical properties. Glasses with the composition (mol%) 22Na(2)O (.) 8CaO (.) 70SiO(2) containing up to 5 wt% of SnO2 were analyzed under several experimental techniques. Dilatometric measurements showed an increase of the glass transition temperature with increasing tin content, while the average thermal expansion coefficient is reduced. Vickers microhardness, density, and refractive index also increase with the tin content. Diffuse reflectance spectra in the infrared (DRIFT) showed that the presence of tin, even at low concentrations, is responsible for some structural changes since there is an increase of the bridging oxygen concentration. The doped glasses present a brown color and optical absorption spectra measurements are interpreted as being due to precipitation of tin in the form of colloidal particles during cooling of the melted glass. In the Na+ <-> K+ ion exchange process the presence of tin in the glass network hinders the diffusion of these ions. The diffusion coefficients of those ions were calculated by the Boltzmann-Matano technique, after concentration profiles obtained by EDS measurements. All results obtained present evidences that Sn4+ cation acts as a glass network former. (c) 2005 Elsevier B.V. All rights reserved.

Surface protection of fluoroindate glasses by sol-gel dip-coated SnO2 thin layers

SnO2 coatings were deposited by a sol-gel dip-coating process to shield fluoroindate glasses (40In-F-3:16BaF(2):20SrF(2):20ZnF(2):2NaF:2GaF(3)) against corrosion in aqueous environments. The effect of the number of coating applications and of the withdrawal speed on the thickness, density and roughness of tin oxide films was investigated by X-ray reflectivity. Film thickness increases both with the number of coating applications and the withdrawal speed. The aqueous leaching of uncoated and SnO2-coated fluoroindate glasses was studied by scanning electron microscopy (SEM) and infrared spectroscopy (FTIR), showing that the glass surface was protected against hydrolytic attack. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Efficient energy upconversion emission in Tm3+/Yb3+-codoped TeO2-based optical glasses excited at 1.064 mu m

Efficient energy upconversion of cw radiation at 1.064 mum into blue, red, and near infrared emission in Tm3+-doped Yb3+-sensitized 60TeO(2)-10GeO(2)-10K(2)O-10Li(2)O-10Nb(2)O(5) glasses is reported. Intense blue upconversion luminescence at 485 nm corresponding to the Tm3+ (1)G(4)--> H-3(6) transition with a measured absolute power of 0.1 muW for 800 mW excitation power at room temperature is observed. The experimental results also revealed a sevenfold enhancement in the upconversion efficiency when the sample was heated from room temperature to 235 degreesC yielding 0.7 muW of blue absolute fluorescence power for 800 mW pump power. High brightness emission around 800 nm (F-3(4)--> H-3(6)) in addition to a less intense 655 nm ((1)G(4)--> H-3(4) and F-3(2,3)--> H-3(6)) fluorescence is also recorded. The energy upconversion excitation mechanism for thulium emitting levels is assigned to multiphonon-assisted anti-Stokes excitation of the ytterbium-sensitizer followed by multiphonon-assisted sequential energy-transfer processes. (C) 2001 American Institute of Physics.

The influence of oxygen in the photoexpansion of GaGeS glasses

Irreversible photoexpansion and photobleaching effect has been observed in amorphous Ga10Ge25S65 glass when its surface was exposed to light with energy greater than the band gap, 3.52 eV. The magnitude of the expansion of GaGeS glasses depends on the exposure conditions. Extended X-ray absorption fine structure (EXAFS) spectroscopy and Rutherford backscattering spectrometry (RBS) have been used to identify the chemical nature of the glass samples before and after illumination. The quantitative analysis of the EXAFS data leads to a two-shell model of 0.5 oxygen atoms at 2.01 Angstrom and 3.6 sulfur atoms at a 2.20 Angstrom. RBS technique demonstrated that chemical composition of the glass surface after irradiation is oxygen rich. The existence of Ge-O bonds in the glass after illumination was also confirmed by infrared measurements. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Photoinduced structural changes in antimony polyphosphate based glasses

A photocontraction effect in amorphous films of the binary glass system 0.20 [Sb(PO3)(3)](n)-0.80 Sb2O3 has been observed after UV irradiation using the 350.7 nm Kr+ ion laser line with 5.0 W/cm(2). Good optical quality films up to 4.0 mum were deposited on silica substrates at room temperature in vacuum by electron beam physical vapor deposition (EB-PVD) and characterized using WDX, XRD, optical absorption, infrared reflectance, profilometry and atomic force microscopy (AFM) techniques. Very stable glasses were prepared by the melt quenching technique and used as evaporation source for the production of films. The photoinduced structural change (PSC) was observed as a variation of about 6% in the film thickness and this effect is accompanied by a photobleaching of the irradiated area with a blue shift of the optical absorption edge. Otherwise this photoinduced change in the film thickness is very sensitive to the variations in the shape and intensity of the laser beam; therefore several possibilities in optical recording arise from these results. (C) 2003 Published by Elsevier B.V.

Study of fluorine losses in oxyfluoride glasses

Glasses in PbGeO3-PbF-CdF2 and GeO2-PbO-PbF2-CdF2 systems were studied and the fluorine losses during synthesis were investigated. Samples were characterized by differential scanning calorimetry (DSC), X-ray diffraction, Fourier transform infrared spectroscopy (FTIR) and Raman scattering spectroscopy. The use of stoichiometric germanate glass, PbGeO3, instead of introducing individual oxides (GeO2 + PbO) lead to decreasing fluorine losses, as detected by a fluorine ion selective electrode. The main structural features obtained from vibrational spectroscopy could be described by a metagermanate basic structure permeating fluorine rich regions. (c) 2005 Elsevier B.V. All rights reserved.

Structural studies of NaPO3-MoO3 glasses by solid-state nuclear magnetic resonance and raman spectroscopy

Vitreous samples were prepared in the (100 - x)% NaPO3-x% MoO3 (0 <= x <= 70) glass-forming system by a modified melt method that allowed good optical quality samples to be obtained. The structural evolution of the vitreous network was monitored as a function of composition by differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FT-IR), Raman scattering, and solid-state nuclear magnetic resonance (NMR) for P-31, Na-23, and Mo-95 nuclei. Addition of MoO3 to the NaPO3 glass melt leads to a pronounced increase in the glass transition temperatures up to x = 45, suggesting a significant increase in network connectivity. For this same composition range, vibrational spectra suggest that the Mo6+ ions are bonded to some nonbridging oxygen atoms (Mo-O- or Mo=O bonded species). Mo-O-Mo bond formation occurs only at MoO3 contents exceeding x = 45. P-31 magic-angle spinning (MAS) NMR spectra, supported by two-dimensional J-resolved spectroscopy, allow a clear distinction between species having two, one, and zero P-O-P linkages. These sites are denoted as Q(2Mo)((2)), Q(1Mo)((2)), and Q(0Mo)((2)), respectively. For x < 0.45, the populations of these sites can be described along the lines of a binary model, according to which each unit of MoO3 converts two Q(nMo)((2)) sites into two Q((n+1)Mo)((2)) sites (n = 0, 1). This structural model is consistent with the presence of tetrahedral Mo(=O)(2)(O-1/2)(2) environments. Indeed, Mo-95 NMR data suggest that the majority of the molybdenum species are four-coordinated. However, the presence of additional six-coordinate molybdenum in the MAS NMR spectra indicates that the structure of these glasses may be more complicated and may additionally involve sharing of network modifier oxide between the network formers phosphorus and molybdenum. This latter hypothesis is further supported by Na-23{P-31} rotational echo double resonance (REDOR) data, which clearly reveal that the magnetic dipole-dipole interactions between P-31 and Na-23 are increasingly diminished with increasing molybdenum content. The partial transfer of modifier from the phosphate to the molybdate network former implies a partial repolymerization of the phosphate species, resulting in the formation of Q(nMo)((3)) species and accounting for the observed increase in the glass transition temperature with increasing MoO3 content that is observed in the composition range 0 <= x <= 45. Glasses with MoO3 contents beyond x = 45 show decreased thermal and crystallization stability. Their structure is characterized by isolated phosphate species [most likely of the P(OMo)(4) type] and molybdenum oxide clusters with a large extent of Mo-O-Mo connectivity.

New glasses in the system InF3-BaF2-ErPO4

New glasses have been obtained in the system InF3-BaF2-ErPO4. Glass compositions with up to 30% mol Er3+ were shown to exist and characterized by thermal analysis, x-ray: diffraction, IR absorption and electronic spectroscopy. The systems with high Er3+ content were studied recording IR and visible emission spectral characteristics. A specially elaborated technique allowed the preparation of a high purity phosphate precursor ErPO4. X-ray identification of the crystalline phases appearing during thermal treatment have been carried out and parameters of a mixed fluoride Ba4In3-nErnF17 calculated.

Spectroscopic properties of Yb3+ doped PbO-Bi2O3-Ga2O3 glasses for IR laser applications

PbO-Bi2O3-Ga2O3 glasses doped with different concentrations of Yb3+ are presented. The spectroscopic properties and laser parameters are calculated and a comparison between different results obtained when calculating the Yb3+ emission cross-section with the reciprocity method and with the Fuchtbauer-Ladenburg formula is presented. The behavior of the near-infrared luminescence is described theoretically by a rate equation and compared with the experimental results. This host doped with Yb3+ is a promising material for laser action at 1019 nm, with properties similar to other known glasses used as active laser media; the emission cross-section of 1.1 x 10(-20) cm(2), the high absorption cross-section (of 2.0 x 10(-20) cm(2)) and a minimum pump intensity of 2.4 kW/cm(2) are interesting properties for short pulse generation. (C) 2005 Elsevier B.V. All rights reserved.

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Er(3+) doped phosphoniobate glasses and planar waveguides: structural and optical properties

Phosphoniobate glasses with composition (mol%) (100-x) NaPO(3)-xNb(2)O(5) ( x varying from 11 to 33) were prepared and characterized by means of thermal analysis, Fourier transform infrared spectroscopy, Raman scattering and (31)P nuclear magnetic resonance. The addition of Nb(2)O(5) to the polyphosphate base glass leads to depolymerization of the metaphosphate structure. Different colors were observed and assigned as indicating the presence of Nb(4+) ions, as confirmed by electron paramagnetic resonance measurements. The color was observed to depend on the glass composition and melting temperature as well. Er(3+) containing samples were also prepared. Strong emission in the 1550 nm region was observed. The Er(3+4)I(15/2) emission quantum efficiency was observed to be 90% and the quenching concentration was observed to be 1.1 mol%( 1.45 x 10(20) ions cm(-3)). Planar waveguides were prepared by Na(+)-K(+)-Ag(+) ion exchange with Er(3+) containing samples. Optical parameters of the waveguides were measured at 632.8, 543.5 and 1550 nm by the prism coupling technique as a function of the ion exchange time and Ag(+) concentration. The optimized planar waveguides show a diffusion depth of 5.9 mu m and one propagating mode at 1550 nm.

Frequency upconversion properties of Tm3+ doped TeO2-ZnO glasses containing silver nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of the heat treatment on the nucleation of silver nanoparticles in Tm3+ doped PbO-GeO2 glasses

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of the temperature on the nucleation of silver nanoparticles in Tm3+/Yb3+ codoped PbO-GeO2 glasses

The influence of the temperature on the nucleation of silver nanoparticles (NPs) in Tm3+/Yb3+ codoped PbO-GeO2 glasses was studied in this work. The infrared-to-visible frequency upconversion (UC) luminescence of Tm3+ ions was used to probe the NPs nucleation and the results were correlated with the increase of the heat-treatment temperature. Emission spectra in the blue-red region were measured by exciting the samples with a cw 980 nm diode laser in resonance with the Yb3+ transition (F-2(7/2) -> F-2(5/2)). The results were correlated with transmission electron microscopy measurements and revealed the different behavior of the nucleation process as a function of temperature.The enhanced UC emission in the visible region is attributed to the increased local field in the proximity of the silver NPs combined with the Yb3+ -> Tm3+ energy transfer. (C) 2010 Elsevier B.V. All rights reserved.

Frequency upconversion luminescence from Yb+3-Tm+3 codoped PbO-GeO2 glasses containing silver nanoparticles

Infrared-to-visible and infrared-to-infrared frequency upconversion processes in Yb3+-Tm3+ doped PbO-GeO2 glasses containing silver nanoparticles (NPs) were investigated. The experiments were performed by exciting the samples with a diode laser operating at 980 nm (in resonance with the Yb3+ transition F-2(7/2)-> F-2(5/2)) and observing the photoluminescence (PL) in the visible and infrared regions due to energy transfer from Yb3+ to Tm3+ ions followed by excited state absorption in the Tm3+ ions. The intensified local field in the vicinity of the metallic NPs contributes for enhancement in the PL intensity at 480 nm (Tm3+ :(1)G(4)-> H-3(6)) and at 800 nm (Tm3+ : H-3(4) -> H-3(6)). (C) 2009 American Institute of Physics. [doi:10.1063/1.3211300]