Corrosion of the component phases presents in high copper dental amalgams. Application of electrochemical impedance spectroscopy and electrochemical noise analysis

The corrosion resistance of three of the constituent phases in high copper dental amalgams has been investigated by electrochemical methods in 0.9% NaCl solution. Polarization curves show corrosion potentials most positive for gamma(1)-Ag2Hg3, followed by Ag-Cu, and gamma-Ag3Sn in agreement with the order of corrosion resistance deduced from the corrosion currents. Complex plane impedance plots at the open circuit potential showed distorted semicircles with diffusional components at low frequency for Ag-Hg and Ag-Cu, while for gamma-Ag3Sn a layer of corrosion products is formed, partially or completely covering the surface of the electrode. Impedance and noise spectra have been compared in the frequency domain, and show good agreement. (C) 2004 Elsevier Ltd. All rights reserved.

Corrosion of dental amalgams: electrochemical study of Ag-Hg, Ag-Sn and Sn-Hg phases

Dental amalgams, formed by reaction of mercury with a powder alloy containing mainly Ag, Sn, Cu and Zn, have a complex metallurgical structure which can contain up to six phases. Their observed corrosion is thus a complex process, which involves contributions from each of the phases present as well as intergranular corrosion. It is thus of interest to investigate the corrosion of individual phases present in dental amalgams. In this work the corrosion behaviour in 0.9% NaCl solution of Ag-Hg, Ag-Sn and Sn-Hg phase components of dental amalgams was investigated by electrochemical methods. The corrosion resistance was found to decrease in the order gamma (1)-Ag2\Hg3, gamma -Ag3Sn and gamma (2)-Sn7Hg. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Electrochemical stability and corrosion resistance of Ti-Mo alloys for biomedical applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of corrosion resistance of laser welded Au-Pd-Ag-In alloy using electrochemical.

The aim of this work was to evaluate the corrosion resistance of AuPdAgIn alloy, submitted to laser beam welding, in 0.9% NaCl solution, using electrochemical techniques. Measures of the open circuit potential (OCP) versus time were applied to electrochemical experiments, as well as potentiodynamic direct scanning (PDS) and electrochemical impedance spectroscopy (EIS) on AuPdAgIn alloy, submitted to laser beam welding in 0.9% NaCl solution. Some differences observed in the microstructure can explain the results obtained for corrosion potential, Ecorr, and corrosion resistance, Rp. EIS spectra have been characterized by distorted capacitive components, presenting linear impedance at low frequencies, including a non-uniform diffusion. The area of the laser weld presented corrosion potential slightly superior when compared to the one of the base metal. The impedance results suggest the best resistant corrosion behavior for laser weld than base metal region. This welding process is a promising alternative to dental prostheses casting.

Electrochemical behavior and corrosion resistance of Ti-15Mo alloy in naturally-aerated solutions, containing chloride and fluoride ions

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efficiency of a conductive cement-based anodic system for the application of cathodic protection, cathodic prevention and electrochemical chloride extraction to control corrosion in reinforced concrete structures

This article describes the research carried out regarding the application of cathodic protection (CP) and cathodic prevention (CPrev), in some cases with a pre-treatment of electrochemical chloride extraction (ECE), on representative specimens of reinforced concrete structures, using an anodic system consisting of a graphite-cement paste applied as a coating on the surface. The aim of this research is to find out the competence of this anode for the aforementioned electrochemical treatments. The efficiency of this anode has been clearly demonstrated, as well as its capability to apply a combined process of ECE and after CP.

Electrochemical study of UNS S32550 super duplex stainless steel corrosion in turbulent seawater using the rotating cylinder electrode

The cathodic and anodic characteristics of freshly polished and pre-reduced UNS S32550 (ASTM A479) super duplex stainless steel in a filtered and conductivity-adjusted seawater have been investigated under controlled flow conditions. A rotating cylinder electrode was used together with both steady and non-steady-state voltammetry and a potential step current transient technique to investigate the electrode reactions in the fully characterized electrolyte. Both oxygen reduction and hydrogen evolution were highly irreversible and the material exhibited excellent passivation and repassivation kinetics. Relative corrosion rates were derived and the corrosion mechanism of the alloy was found to be completely independent of the mass-transfer effects, which can contribute to flow-induced corrosion.

Electrochemical chloride extraction to halt corrosion of reinforcement

This thesis presents results of experiments designed to study the effect of applying electrochemical chloride extraction (ECE) to a range of different hardened cement pastes. Rectangular prism specimens of hydrated cement paste containing sodium chloride at different concentrations were subjected to electrolysis between the embedded steel cathodes and external anodes of activated titanium mesh. The cathodic current density used was in the range of 1 to 5 A/m2 with treatment periods of 4 to 12 weeks. After treatment, the specimens were cut into sections which were subjected to pore-solution expression and analysis in order to determine changes in the distribution of free and total ionic species. The effect of the ECE treatment on the physical and microstructural properties of the cements was studied by using microhardness and MIP techniques. XRD was employed to look at the possibility of ettringite redistribution as a result of the accumulation of soluble sulphate ions in the cement matrix near the cathode during ECE. Remigration of chloride which remains after the ECE treatment and distribution of other ions were studied by analysing specimens which had been stored for several months, after undergoing ECE treatment. The potentials of the steel cathodes were also monitored over the period to detect any changes in their corrosion state. The main findings of this research were as follows: 1, ECE, as applied in this investigation, was capable of removing both free and bound chloride. The removal process occurred relatively quickly and an equilibrium between free and bound chlorides in the specimens was maintained throughout. At the same time, alkali concentrations in the pore solution near the steel cathode increased. The soluble sulphate ionic concentration near the cathode also increased due to the local increase in the pH of the pore solution. 2, ECE caused some changes in physical and microstructural of the cement matrix. However these changes were minimal and in the case of microhardness, the results were highly scattered. Ettringite in the bulk material well away from the cathode was found not to increase significantly with the increase in charge passed.3, Remigration of chloride and other ionic species occurred slowly after cessation of ECE with a resultant gradual increase in the Cl-/OH- ratio around the steel.4, The removal of chloride from blended cements was slower than that from OPC.

Corrosion of silicon carbide ceramics using conventional and electrochemical methods

Silicon carbide ceramics are candidate materials for use in aggressive environments, including those where aqueous acids are present. Standard corrosion testing methods such as immersion testing are not always sufficiently sensitive for these ceramics owing to the very low, almost unobservable, corrosion rates encountered. Using electrochemical methods the corrosion processes can be assisted, leading to higher rates and thus the elucidation of reaction mechanisms. The behaviour of a sintered and a reaction bonded silicon carbide has been investigated in aqueous HCl, HF, HNO3, and H2SO4, using standard immersion and new electrochemical methods. Both materials were passive in HCl, HNO3, and H2SO4 because of the formation of a surface silica film, and were active in HF. In HF, corrosion of sintered silicon carbide was slight and the residual silicon was removed from reaction bonded specimens.

Electrochemical methods for monitoring localized corrosion under cathodic protection

This research proposes two new electrochemical methods for measuring corrosion rates and their distribution under cathodic protection (CP). These methods were incorporated into a corrosion monitoring sensor that grow a great interest in the Australian energy pipeline industry.

Corrosion studies on the plasma-sprayed nanostructured titanium dioxide coating

Purpose: The purpose of this paper is to report the resistance of plasma-sprayed titanium dioxide (TiO2) nanostructured coatings in a corrosive environment.----- Design/methodology/approach: Weight loss studies are performed according to ASTM G31 specifications in 3.5?wt% NaCl. Electrochemical polarization resistance measurements are made according to ASTM G59-91 specifications. Corrosion resistance in a humid and corrosive environment is determined by exposing the samples in a salt spray chamber for 100?h. Microstructural studies are carried out using an atomic force microscope and scanning electron microscope.----- Findings: The nanostructured TiO2 coatings offer good resistance to corrosion, as shown by the results of immersion, electrochemical and salt spray studies. The corrosion resistance of the coating is dictated primarily by the geometry of splat lamellae, density of unmelted nanoparticles, magnitude of porosity and surface homogeneity.----- Practical implications: The TiO2 nanostructured coatings show promising potential for use as abrasion, wear-resistant and thermal barrier coatings for service in harsh environments.----- Originality/value: The paper relates the corrosion resistance of nanostructured TiO2 coatings to their structure and surface morphology.

Novel corrosion sensor based on carbon nanotube composites for structural health monitoring

Bridges are important infrastructures of all nations and are required for transportation of goods as well as human. A catastrophic failure can result in loss of lives and enormous financial hardship to the nation. Hence, there is an urgent need to monitor our infrastructures to prolong their life span, at the same time catering for heavier and faster moving traffics. Although various kinds of sensors are now available to monitor the health of the structures due to corrosion, they do not provide permanent and long term measurements. This paper investigates the fabrication of Carbon Nanotube (CNT) based composite sensors for structural health monitoring. The CNTs, a key material in nanotechnology has aroused great interest in the research community due to their remarkable mechanical, electrochemical, piezoresistive and other physical properties. Multi-wall CNT (MWCNT)/Nafion composite sensors were fabricated to evaluate their electrical properties when subjected to chemical solutions, to simulate a chemical reaction due to corrosion and real life corrosion experimental tests. The electrical resistance of the sensor electrode was dramatically changed due to corrosion. The novel sensor is expected to effectively detect corrosion in structures based on the measurement of electrical impedances of the CNT composite.

Cathodic corrosion of Cu substrates as a route to nanostructured Cu/M (M = Ag, Au, Pd) surfaces

The electrochemical formation of nanostructured materials is generally achieved by reduction of a metal salt onto a substrate that does not influence the composition of the deposit. In this work we report that Ag, Au and Pd electrodeposited onto Cu under conditions where galvanic replacement is not viable and hydrogen gas is evolved results in the formation of nanostructured surfaces that unexpectedly incorporate a high concentration of Cu in the final material. Under cathodic polarization conditions the electrodissolution/corrosion of Cu occurs which provides a source of ionic copper that is reduced at the surface-electrolyte interface. The nanostructured Cu/M (M = Ag, Au and Pd) surfaces are investigated for their catalytic activity for the reduction of 4 nitrophenol by NaBH4 where Cu/Ag was found to be extremely active. This work indicates that a substrate electrode can be utilized in an interesting manner t make bimetallic nanostructures with enhanced catalytic activity.