Effect of brushing with conventional versus whitening dentifrices on surface roughness and biofilm formation of dental ceramics

The aim of this study was to evaluate the effect of conventional and whitening dentifrices on the weight loss, surface roughness, and early in situ biofilm formation on the surface of dental ceramics. Standardized feldspar ceramic specimens (Vita VM7 and Vita VM13) were submitted to the following experimental conditions: no brushing; brushing without a dentifrice; brushing with a conventional dentifrice; and brushing with a whitening dentifrice. A brushing machine was used to simulate brushing. The mass and surface roughness of all specimens from the test groups were evaluated prior to and after brushing. Ten participants used an oral device for eight hours to evaluate the biofilm formed in situ on the specimens. Scanning electron microscopy was used for qualitative and quantitative analysis of the biofilm. ANOVA and Tukey tests were used to analyze the results of weight loss, surface roughness, and presence of bacteria. A one-way Kruskal-Wallis test was used for bacterial colonization results. For both ceramics, brushing with a whitening dentifrice resulted in weight loss that was significantly greater when compared to brushing without a dentifrice or with a conventional dentifrice. Increased surface roughness was noticed on VM13 ceramic samples with both dentifrices, whereas only conventional dentifrice had a significant effect on the surface roughness of VM7 samples. For both VM7 and VM13, no difference was found between the experimental conditions with regard to the presence or number of bacteria. Cocci and short rods were the predominant microbial morphotypes. Granular or fibrillar acellular material partially covered the specimens. Brushing with a whitening dentifrice resulted in significant weight loss of ceramic restorations, while brushing with both conventional and whitening dentifrices can roughen ceramic surfaces. The increase in roughness was not clinically significant to contribute to increased biofilm formation.

Influence of polishing procedures on the surface roughness of dental ceramics made by different techniques

The aim of this study was to evaluate the influence of 2 different surface polishing procedures - glazing (GZ) and manual polishing (MP) - on the roughness of ceramics processed by computer-aided design/computer-aided manufacturing (CAD/CAM) and conventional systems (stratification technique). Eighty ceramic discs (diameter: 8 mm, thickness: 1 mm) were prepared and divided among 8 groups (n = 10) according to the type of ceramic disc and polishing method: 4 GZ and 4 MP. Specimens were glazed according to each manufacturer's recommendations. Two silicone polishing points were used on the ceramic surface for manual polishing. Roughness was measured using a surface roughness tester. The roughness measurements were made along a distance of 2 mm on the sample surface and the speed of reading was 0.1 mm/s. Three measurements were taken for each sample. The data (μm) were statistically analyzed using analysis of variance (ANOVA) and Tukey's test (α = 0.05). Qualitative analysis was performed using scanning electron microscopy (SEM). The mean (± SD) roughness values obtained for GZ were: 1.1 ± 0.40 μm; 1.0 ± 0.31 μm; 1.6 ± 0.31 μm; and 2.2 ± 0.73 μm. For MP, the mean values were: 0.66 ± 0.13 μm; 0.43 ± 0.14 μm; 1.6 ± 0.55 μm; and 2.0 ± 0.63 μm. The mean roughness values were significantly affected by the ceramic type (P = 0.0001) and polishing technique (P = 0.0047). The SEM images confirmed the roughness data. The manually polished glass CAD/CAM ceramics promoted lower surface roughness than did the glazed feldspathic dental ceramics.

Effect finishing and polishing procedures on the surface roughness of IPS Empress 2 ceramic

Objective. To evaluate the surface roughness of IPS Empress 2 ceramic when treated with different finishing/polishing protocols. Materials and methods. Sixteen specimens of IPS Empress 2 ceramic were made from wax patterns obtained using a stainless steel split mold. The specimens were glazed (Stage 0-S0, control) and divided into two groups. The specimens in Group 1 (G1) were finished/polished with a KG Sorensen diamond point (S1), followed by KG Sorensen siliconized points (S2) and final polishing with diamond polish paste (S3). In Group 2 (G2), the specimens were finished/polished using a Shofu diamond point (S1), as well as Shofu siliconized points (S2) and final polishing was performed using Porcelize paste (S3). After glazing (S0) and following each polishing procedure (S1, S2 or S3), the surface roughness was measured using TALYSURF Series 2. The average surface roughness results were analyzed using ANOVA followed by Tukey post-hoc tests (α = 0.01) Results. All of the polishing procedures yielded higher surface roughness values when compared to the control group (S0). S3 yielded lower surface roughness values when compared to S1 and S2. Conclusions. The proposed treatments negatively affected the surface roughness of the glazed IPS Empress 2 ceramic. © 2013 Informa Healthcare.

Surface Roughness of Acrylic and Silicone-Based Soft Liners: In Vivo Study in a Rat Model

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SURFACE ROUGHNESS AND CANDIDA ALBICANS BIOFILM FORMATION ON A RELINE RESIN AFTER LONG-TERM CHEMICAL DISINFECTION AND TOOTHBRUSHING

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Incorporation of chlorhexidine gluconate or diacetate into a glass-ionomer cement: porosity, surface roughness, and anti-biofilm activity

To evaluate the porosity, surface roughness and anti-biofilm activity of a glass-ionomer cement (GIC) after incorporation of different concentrations of chlorhexidine (CHX) gluconate or diacetate. Methods: For the porosity and surface roughness tests, 10 test specimens were fabricated of the GIC Ketac Molar Easy Mix (KM) and divided into the following groups: Control, GIC and 0.5% CHX diacetate; GIC and 1.0% CHX diacetate; GIC and 2.0% CHX diacetate; GIC and 0.5% CHX gluconate; GIC and 1.0% CHX gluconate; GIC and 2.0% CHX gluconate. To evaluate porosity, the test specimens were fractured. The fragments were photographed by scanning electron microscopy (SEM), and the images analyzed with the aid of the software program Image J. The surface roughness (Ra) was obtained by the mean value of three readouts performed on the surface of each specimen, always through the center. To analyze the anti-biofilm activity, strains of S. mutans ATCC 35688 were used, and the groups control and GIC +CHX diacetate 1% were divided as follows: GIC (1 day); GIC (7 days), GIC (14 days), GIC (21 days); GIC+CHX (1 day), GIC+CHX (7 days), GIC+CHX (14 days), GIC+CHX (21 days); GIC+ CHX (1 day), GIC+ CHX (7 days), GIC+ CHX (14 days) and GIC+ CHX (21 days) using 10 test specimens per group. For biofilm growth, the specimens were placed in a vertical position in 24-well plates and incubated overnight 10 times. The culture medium was renewed every 24 hours. The suspension was diluted and seeded on BHI agar for quantification of the bacteria present. For evaluation of all the tests the two-way ANOVA was used, and if necessary, the Tukey test was applied, with a level of significance of 5%. Results: Regarding GIC porosity, the ANOVA showed that the presence of CHX increased the porosity (P< 0.001) proportionally to the increase in concentrations (P= 0.001), without however, presenting interaction between material and concentration (P= 0.705). Regarding the number of pores, a significant increase in pores was observed with the increase in CHX concentration (P= 0.003). The surface roughness test demonstrated no statistically significant effect as to increase or reduction in roughness at any of the CHX concentrations used (P> 0.05). Anti-biofilm activity analysis pointed out a significant effect of the factors material (P= 0.006) and time (P< 0.001), with CHX diacetate CHX presenting greater effectiveness in reducing microorganisms.

Effect of surface roughness on the hydrophobicity of a denture-base acrylic resin and Candida albicans colonization

Aim The aim of the present study was to evaluate the effect of surface roughness (roughness average [Ra] μm) on the hydrophobicity of a denture-base acrylic resin and the initial adherence and biofilm formation of Candida albicans (C. albicans). Methods Disk-shaped specimens were divided into six groups: Ra 0.05, Ra 0.2, Ra 0.4, Ra 0.8, Ra 1.5, and Ra 3.0. Water contact angles (WCA) were measured, and the specimens incubated with C. albicans for 90 min (initial adherence, n = 108) or 48 h (biofilm formation, n = 108). Adhered and biofilm cells were evaluated by c.f.u./mL and 2,3-bis-(2-methoxy-4-nitro-5-sulfophenyl)-2H-tetrazolium-5-carboxanilide (XTT), and the correlation between the two methods was evaluated. The surface of the specimens and cells (adhered and biofilm) were also analyzed by scanning electron microscopy (SEM). Results Groups Ra 0.05 and 3.0 exhibited the lowest (~75°) and the highest (~100°) WCA mean values, respectively. For both initial adherence and biofilm formation, no statistically-significant differences were observed among all groups, as determined by c.f.u./mL and XTT. A positive correlation between these two methods was found. SEM analysis showed the presence of scratches and valleys on the acrylic specimens and densely-packed yeast cells covering the entire surface. Conclusions Roughness significantly increased hydrophobicity (WCA), but had no effect on the number and metabolic activity of adherent and biofilm cells of C. albicans.

Influence of standard load micro and nanopatterned in surface roughness of bleached teeth and submitted to different surface treatments?

The aim of this study was evaluate the dental enamel after whitening treatment with Opalescence Boost PF® 38%, correlating the structural alterations in the surface of the enamel with its respective pH and verify if whitened teeth submitted to different finishing and polishing techniques show similar surface texture to healthy teeth (control group). Sixty premolars were divided in 6 groups (n = 10), which had been immersed in artificial saliva during all the experiment. Protocol whitening was performed according to the manufacturer recommendations, and then the specimens were submitted to different polishing technique with Sof-Lex Pop On® disks, Flex Diamond® felt disks using two different micrometric polishing pastes (Enamelize® and Diamond Polish®) and two nanometric polishing pastes (Lummina-E Diamond and Lummina-E Alumina), according to the groups. Representative specimens were analyzed in scanning electronic microscopy (SEM). Whitening gel used in this experiment had modified the morphologic aspect of the enamel surface. It was found that two nanometric polishing pastes (G5 and G6) promoted a less rough surface compared to control group even after the whitening process.

Surface roughness analysis of dental ceramics treated with hydrofl uoric acid and aluminum oxide jet

The aim of this study was to evaluate the surface roughness of 5 indirect restorative materials treated with hydrofluoric acid to 10%, with aluminum oxide jet and a combination of both. The specimens was prepared with 10 mm in diameter and 2 mm thickness, divided into fi ve groups: (1) Ceromer (CeseadII-Kuraray), (2) Leucite crystals ceramics (IPS EmpressIIIvoclarforcasket), (3) glass ceramic with fluorapatite (IPS D. Sign-Ivoclar), (4) lithium disilicate ceramic (IPS Empress II-Ivoclar restorations), (5) ceramics (Cergogold-Degussa). For all groups were performed the controls, and the surfaces with the 3 types of treatment. For testing roughness used the rugosimeter Taylor/Hobson-Precision, model form tracerSV-C525 high sensitivity. After confi rmation of variance analysis with a signifi cance level of 1% (p < 0.01), there was equality between the average roughness of materials from groups 1, 3 and 5, and the group 2 was different from the others. It was also found that the ceramics of the group 5 behaved similar to group 4. However the lowest average roughness was observed in group 2 ceramic. In the evaluation between the types of treatment, the aluminum oxide jet and associations and blasting with hydrofl uoric acid were similar, and different isolated hydrofl uoric acid, and 3 types of treatment signifi cantly higher than the control group. All treatments promoted superfi cial alterations in all tested materials.

Influence of light source and immersion media in surface roughness and hardness of a nanofilled composite resin

The study evaluated the influence of light curing units and immersion media on superficial roughness and microhardness of the nanofilled composite resin Supreme XT (3M/ESPE). Light curing units used were: XL 3000 (3M/ESPE), Jet Lite 4000 Plus (JMorita) and Ultralume Led 5 (Ultradent) and immersion media were artificial saliva, Coke®, tea and coffee, totaling 12 experimental groups. Specimens (10mm x 2mm) were immersed in each respective solution for 5 seconds, three times a day, during 60 days and so, were submitted to measure of superficial roughness (Ra) and Vickers hardness. Data were subjected to two-way ANOVA test (p<0.05). Results showed that only the light source factor showed statistically difference for hardness. It was observed that the hardness of the composite resin Filtek Supreme XT (3M/ESPE) was influenced by the light source (p<0.01) independently of the immersion media (p= 0.35) and the Jet Lite 4000 Plus (JMorita) was the light curing unit that presented lower values. In relation to surface roughness, it was noted no-significant statistical difference for light source (p=0.84), when specimens were immersed in different beverages (p=0.35).

Surface roughness and hardness of yttria stabilized zirconia (Y-TZP) after 10 years of simulated brushing

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Characterization of Soil Surface Roughness Effects on Runoff and Soil Erosion Rates under Simulated Rainfall

This study aims at identifying the influence of soil surface roughness from small to large aggregates (random roughness) on runoff and soil loss and to investigate the interaction with soil surface seal formation. Bulk samples of a silty clay loam soil were sieved to four aggregate-size classes of 3 to 12, 12 to 20, 20 to 45, 45 to 100 mm, and packed in soil trays set at a 5% slope. Rainfall simulations using an oscillating nozzle simulator were conducted for 90 min at an average rainfall intensity of 50.2 mm h(-1). Soil surface roughness was measured using an instantaneous profile laser scanner and surface sealing was studied by macroscopic analysis of epoxy impregnated soil samples. The rainfall simulations revealed longer times to initiate runoff with increasing soil surface roughness. For random roughness levels up to 6 mm, a decrease in final runoff rate with increasing roughness was observed. This can be attributed to a decreased breakdown of the larger roughness elements on rougher surfaces, thus keeping infiltration rate high. For a random roughness larger than 6 mm, a greater final runoff rate was observed. This was caused by the creation of a thick depositional seal in the concentrated flow areas, thus lowering the infiltration rates. Analysis of impregnated soil sample blocks confirmed the formation of a structural surface seal on smooth surfaces, whereas thick depositional seals were visible in the depressional areas of rougher surfaces. Therefore, from our observations it can be learned that soil surface roughness as formed by the presence of different aggregate sizes reduces runoff but that its effect diminishes due to aggregate breakdown and the formation of thick depositional seals in the case of rough soil surfaces. Sediment concentration increased with increasing soil surface roughness, due to runoff concentration in flow paths. Nevertheless, final soil loss rates were comparable for all soil roughness categories, indicating that random roughness is only important in influencing runoff rates and the time to initiate runoff, but not in influencing sediment export through soil loss rates.

Influence of CAD-CAM diamond bur deterioration on surface roughness and maximum failure load of Y-TZP-based restorations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Color stability, surface roughness and microhardness of composites submitted to mouthrinsing action

Objective: The purpose of this study was to evaluate the effect of mouth rinse solutions Lion color stability, surface roughness and microhardness of two composite resins. Material and Methods: Fifty test specimens of each composite (Filtek Z250 and Z350; 3M ESPE) were made using a teflon matrix (12x2 mm). Color, surface roughness and Knoop microhardness baseline measurements of each specimen were made and specimens (n=10) were immersed in 5 mouth rinse solutions: G1: distilled water (control), G2: Plax Classic, G3: Plax alcohol-free; G4: Periogard, and G5: Listerine. Final measurements of color, roughness and microhardness were performed and the results submitted to statistical analysis (2-way ANOVA, Bonferroni's test; p<0.05). Results: The most significant color change was observed for Z250 when immersed in Listerine (p<0.05). Z350 showed greater color change when immersed in Plax alcohol-free (p<0.05), but with no significant difference for Listerine (p>0.05). With regard to roughness, both composites showed significant changes when immersed in Listerine in comparison with Plax alcohol-free (p<0.05). Microhardness of Z350 was shown to be significantly changed when the composite was immersed in Plax alcohol-free (p<0.05). Conclusion: Composite changes depended on the material itself rather than the mouth rinse solution used.

The influence of mouthrinses and simulated toothbrushing on the surface roughness of a nanofilled composite resin

The aim of this study was to determine the influence of mouthrinses on the surface roughness of a nanofilled composite resin after toothbrushing. One hundred nanofilled composite resin specimens were prepared and randomly distributed into two groups-brushed and non-brushed-and then assigned to five subgroups, according to the mouthrinse solutions (n = 10): Colgate Plax Fresh Mint, Oral B, Cepacol, Colgate Plax, and artificial saliva. Each sample was immersed in 20 mL of the mouthrinses for 1 minute, 5 days per week, twice a day, for a 3-week period. The control group used in the study was one in which the specimens were not subjected to brushing and remained only in artificial saliva. Toothbrushing was performed once a week for 1 minute, for 3 weeks. Surface roughness measurements (Ra) were performed after the immersion period and toothbrushing, by means of a profilometer. Data were analyzed by two-way ANOVA and Tukey's test. Analysis revealed that the association between toothbrushing and Colgate Plax Fresh Mint produced the lowest surface roughness (p < 0.05). All other groups tested (Oral B, Cepacol, Colgate Plax, artificial saliva) exhibited no statistically significant differences between surfaces, whether subjected to toothbrushing or not (p < 0.05). It was concluded that the surface roughness of the nanofilled composite resin tested can be influenced by the mouthrinse associated with toothbrushing.