Thermo-reversible sol-gel transition of TiO2 nanoparticles with surface modified by p-toluene sulfonic acid

In this paper an unprecedent thermo-reversible sol-gel transition for titania nanoparticles dispersed in a solution of p-toluene sulfonic acid (PTSH) in isopropanol is reported. The sol formed by the thermo-hydrolysis at 60 degrees C of titanium tetraisopropoxide (Ti((OPr)-Pr-i)(4)) reversibly changes into a turbid gel upon cooling to room temperature. Turbidimetric measurements performed for samples containing different nominal acidity ratios (A = [PTSH]/[Ti]) have evidenced that the gel transformation temperature increases from 20 to 35 degrees C as the [PTSH]/[Ti] ratio increases from 0.2 to 2.0. SAXS results indicate that the thermo-reversible gelation is associated to a reversible aggregation of a monodisperse set of titania nanoparticles with average gyration radius of approximate to 2 nm. From the different PTSH species evidenced by Raman spectroscopy and TG/DTA of dried gels we proposed that the then-no-reversible gelation in this systems is induced by the formation of a supramolecular network, in which the protonated surface of nanoparticles is interconnected through cooperative hydrogen bonds between -SO3 groups of p-toluene sulfonic acid. (C) 2009 Elsevier Ltd. All rights reserved.

Formation of SnO2 gels from dispersed sols in aqueous colloidal solutions

Transparent SnO2 gels were obtained from SnCl4 aqueous solution. The sol formation from tin oxihydroxy peptization in different concentrations and by electrolyte addition in solution was measured. It was verified that the residual presence of chloride ions compromises the colloidal system stability. The sol-gel transition was investigated as a function of the quantity of solid particles in the aqueous environment and of aging time at 60°C by infrared spectroscopy and rheological measurements. The transition from plastic to pseudoplastic flow observed with the increase in loading suggests that a continuous and three-dimensional network formation is closely related to hydrogen bridges and/or hydrogen clusters, culminating in the gel formation. © 1990.

Structural characterization of a tin oxyhydroxide gel and its precursor sol

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Study of SnO2 gels by Eu3+ fluorescence spectroscopy

Eu3+ fluorescence spectroscopy was used as a probe to study the changes in local arrangements of tin oxyhydroxide precipitate → sol → gel → glass conversion. Electronic transition intensities and 5D0 excited state lifetime variations were followed during the entire process. Adsorption of Eu3+ ions on the colloid and changes of chemical interactions occurring in each step are described. © 1992 Elsevier Science Publishers B.V. All rights reserved.

Spectroscopic characterization of SnO2 gels - Code: CP11

Excitation and dynamic emission spectra of Eu3+ ions were simultaneously used with FTIR and Raman spectroscopy to study the structural evolution during SnO2 sol → gel → xerogel conversion. Results make evident an increase of the surroundings symmetry for the Eu3+ ions dissolved in SnO2 matrix and a decrease of the amount of hydroxo groups (Sn-OH) during drying. These phenomena were associated to the pursuit of the condensation reaction after gelation. © 1994 Kluwer Academic Publishers.

Anisotropy of crystallite growth during sintering of SnO2 xerogels

The crytallite and pore-size evolution during isothermal sintering (400 ≤ T ≤ 700°C) of SnO2 xerogels was studied by X-ray line broadening and nitrogen adsorption-desorption isotherms. The experimental results show a strong anisotropy of crystallite growth between [110] and [101] directions. The preferential growth at [101] is followed by an increase in the mean pore size, reduction of the specific surface area and invariance of total pore volume. This behaviour is typical of grain coalescence sintering. The kinetic analysis of experimental results suggests that the crystallite coalescence at [101] is governed by lattice diffusion. The strong anisotropy of the growth causes pore-size distribution broadening, hindering the macroscopic shrinkage of the compact during sintering. © 1996 Chapman & Hall.

Short Range Order Evolution in the Preparation of SnO2 Based Materials

The evolution of Eu3+ doped SnO2 xerogels to the cassiterite structure observed during sintering was studied by means of Eu3+ spectroscopy, XRD and EXAFS at the Sn K-edge. Eu3+ ions adsorbed at the surface of colloidal particles present a broad distribution of sites, typical of oxide glasses. With sintering at 300°C, this distribution is still broadened. Crystallization is clearly observed by the three techniques with increasing sintering temperature. It is found that the addition of Eu3+ limits the crystallite growth.

Structural study of aged saturated silica gels obtained from tetramethoxysilane sonohydrolysis with different water/tetramethoxysilane molar ratio

The structural characteristics of saturated silica sonogels were studied by means of small-angle x-ray scattering (SAXS) and thermogravimetric analysis (TG), after a long time of aging in saturated conditions. The sonogels were obtained by a sol-gel routine from ultrasound stimulated tetramethoxysilane (TMOS) hydrolysis carried out with the initial water/TMOS molar ratio (r) ranging from 2 to 10. The saturated sonogel structure can be described as composed by mass fractal-like aggregates (clusters) of primary silica particles, all imbibed in a liquid phase. The values of the mass fractal dimension (D) of the clusters was found all around 2.5, while the characteristic size of the clusters (ξ) was found generally increasing with r, going from approximately 2.3 nm (r = 2) to 4.5 nm (r = 10). The volume fraction of the clusters was estimated from the SAXS data. The results were compared to the values of weight loss fraction at the inflection point that has been found in the derivative of the TG curve, which should accounts for the instant in which the meniscus of the liquid phase penetrates into the clusters under a rapid evaporation process as in a TG test.

Modifications induced by acetylacetone in properties of sol-gel derived Y3Al5O12:Tb3+ - I: Structural and morphological organizations

Acetylacetone has been used as a chemical modifier for the synthesis of undoped and Tb3+-doped Y3Al5O12 powders. A systematic investigation concerning its influence on the structural and morphological properties of amorphous and crystallized samples has been carried out. These properties have been comparatively studied by means of X-ray diffraction, infrared spectroscopy, SEM, XAS and SAXS. 27Al NMR and EPR experiments have been performed to complete the study. The combined results have evidenced that acetylacetone promotes organic groups departure during calcination, entailing a better structural organization at lower temperatures compared with unmodified powders. Structuration has been proven to occur at short-scale range until a 600°C heating treatment before being extended by coalescence at higher temperatures. Finally, the presence of acac ligands on the alkoxides leads to a monomer-cluster aggregation process, and thus to a more open network. © 2010 The Royal Society of Chemistry.

Efeito fotocrômico em Ormosil's dopados com molibdênio preparados por síntese de Sol-Gel

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudos de absorção e emissão de UV/Vis em xerogéis de sílica dopados com cromo obtidos por processo Sol-Gel

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Propriedades estruturais de géis obtidos a partir de sono-hidrólise de TEOS e troca de fase líquida por acetona

Pós-graduação em Física - IGCE

Espumas cerâmicas produzidas pela conjugação dos processos sol-gel, aeração e emulsificação

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparação pelo processo sol-gel de pós redispersáveis, filmes finos densos e materiais mesoporosos de óxido de titânio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Dye incorporation in polyphosphate gels: synthesis and theoretical calculations

ABSTRACT: In this work we described theoretical calculations on the electronic structure and optical properties of the dyes crystal violet and malachite green based in semiempirical methods (Parametric Method 3 and Intermediate Neglect of Differential Overlap / Spectroscopic - Configuration Interaction) and the synthesis of a new hybrid material based upon the incorporation of these dyes in an aluminum polyphosphate gel network. The samples are nearly transparent, free-standing thick films. The optical properties of the entrapped dyes are sensitive to chemical changes within the matrix caused either by gel aging or external stimulli such as exposition to acidic and basic vapors that can percolate within the matrix. Our theoretical modeling is in good agreement with the experimental results for the dyes.