Fluoride release/recharge from restorative materials: effect of fluoride gels and time

This study examined the differences in fluoride release and recharge among four restorative materials following treatment with APF or neutral fluoride gel for one or four minutes. Specimens were immersed in 2 mL of deionized water, while fluoride release was measured at 24-hour intervals for 15 days using an ion-selective electrode and analyzer. The materials were then treated with the fluoride gels. The fluoride release was measured for 15 days. ANOVA (p<0.05) showed higher fluoride release for Ketac-Fil before fluoride application and for Vitremer and Fuji 11 LC after application of APF gel. APF gel yielded higher fluoride release when compared to neutral gel, regardless of the material. Fluoride recharge and release was greater after the four-minute APF gel application, with no difference between the times of application for the neutral gel (p>0.05), except for Ketac-Fil. The pattern of release before and after application of the gels was similar and was higher at day 16 compared to day one for the APF gel for resin materials, with higher release at day 15 compared to the initial for Fuji 11 LC and Vitremer. Et was concluded that RM-GICs were the most effective materials with regards to fluoride release after application of APF gel for four minutes.

Effect of prolonged erosive pH cycling on different restorative materials

This in vitro study evaluated the effect of a prolonged erosive pH cycling on the superficial microhardness change (SMHC) and the erosive wear of different restorative materials. Eighty enamel specimens with prepared cavities of 1.5 x 1.5 mm were randomly divided into eight groups according to the restorative materials used for the fillings (RMGI - resin-modified glass-ionomer, CGI - conventional glass-ionomer, CR- composite resin, A - amalgam) and immersion media used (ERO - erosive medium or SAL - artificial saliva). During 35 days, half of the specimens were immersed in a cola drink (ERO), for 5 min, three times a day, and they remained in SAL between the erosive cycles. The other half of the specimens was immersed in SAL only, for the entire experimental period (control). Data were tested for significant differences by anova and Tukey's tests (P < 0.05). Scanning electron microscopy images were made to illustrate the enamel erosive wear and restorative materials alterations. The mean SMHC (%) and mean erosive wear (mu m) of the materials were: RMGI-ERO (30/0.5); CGI-ERO (37/0.5); CR-ERO (-0.3/0.3); A-ERO (-4/0.3); RMGI-SAL (4/0.4); CGI-SAL (-6/0.4); CR-SAL (-3/0.2) and A-SAL (2/0.4). Scanning electron microscopy images showed pronounced enamel erosive wear on groups submitted to erosive pH cycling when compared with groups maintained in saliva. In conclusion, the prolonged pH cycling promoted significantly higher alterations (SMHC and erosive wear) on the glass-ionomer cements than the CR and amalgam.

In situ effect of an erosive challenge on different restorative materials and on enamel adjacent to these materials

Objectives: This in situ study evaluated the effect of an erosive challenge on different restorative materials and on enamel restored with these materials, as well as the ability of these materials to protect the adjacent enamel against erosion.Methods: Ten volunteers wore palatal devices with eight bovine enamel blocks, randomly selected and distributed into two vertical rows, corresponding to the following groups: GI/GV, resin-modified glass ionomer; GII/GVI, conventional glass ionomer; GIII/GVII, composite resin; GIV/GVIII, amalgam. one row (corresponding to groups I-IV) was immersed in a cola drink and the other row (corresponding to groups V-VIII) was subjected to saliva only. The palatal device was continuously worn for 7 days and only half of the appliance (groups I-IV) was immersed in the soft drink (Coca-Cola (R), 150 mL) for 5 min, three times a day. The study variables comprised the wear (profilometry, mu m) and the percentage of surface microhardness change (%SMHC). Data were tested for significant differences by two-way ANOVA and Tukey's tests (p < 0.05).Results: Considering the restorative materials, for %SMHC and wear, there were no differences among the materials and between the saliva and the erosive challenge. For enamel analyses, the erosive challenge promoted a higher wear and %SMHC of the enamel than did the saliva. There were no significant differences in wear and %SMHC of the enamel adjacent to the different restorative materials.Conclusion: This research data suggest that there is little %SMHC and wear of the studied restorative materials and none of them had a preventive effect against erosion on adjacent enamel, which showed a pronounced wear. (c) 2007 Elsevier Ltd. All rights reserved.

Effect of erosive pH cycling on different restorative materials and on enamel restored with these materials

This in vitro study evaluated the effect of erosive pH cycling on the percentage of surface micro-hardness change (%SMHC) and wear of different restorative materials and bovine enamel restored with these materials. Eighty enamel specimens were randomly divided into eight groups according to the restorative materials and immersion media used: GI/GV-resin-modifled glass-ionomer, GII/GVI-conventional glass-ionomer, GIII/GVII-resin composite and GIV/GVIII-amalgam. Over a period of seven days, groups GI to GIV were immersed in a cola drink (ERO) for 5 minutes, 3x/day and kept in artificial saliva between erosive cycles. Groups GV to GVIII were immersed in artificial saliva (SAL) throughout the entire experimental period (control). Data were tested for significant differences using ANOVA and Tukey's tests (p < 0.05). For %SMHC, considering the restorative materials, no significant differences were detected among the materials and immersion media. Mean wear was higher for the resin modified glass ionomer cement when compared to conventional cement, but those materials did not significantly differ from the others. For enamel analyses, erosive pH cycling promoted higher wear and %SMHC compared to saliva. There were no significant differences in wear and %SMHC of enamel around the different restorative materials, regardless of the distance from the restorative material (50, 150 or 300 mu m). In conclusion, there were only subtle differences among the materials, and these differences were not able to protect the surrounding enamel from erosion.

Antibacterial activity of four glass ionomer cements used in atraumatic restorative treatment

The in vitro antibacterial activity of four glass ionomer cements ( Fuji IX, Ketac Molar, Vidrion R and Vitromolar) indicated for Atraumatic Restorative Treatment ( ART) was studied against strains of bacteria involved in the development of oral diseases, Streptococcus mutans, Streptococcus sobrinus, Lactobacillus acidophilus and Actinomyces viscosus. The agar plate diffusion test was used for the cultures, which included chlorhexidine as a positive control. The results demonstrated that all the cements evaluated presented antibacterial activity. Based on the results of this study, it can be concluded that Fuji IX and Ketac Molar presented the most effective antibacterial activity considering the ART approach.

Effects of light-curing time on the cytotoxicity of a restorative composite resin on odontoblast-like cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Combined periodontal, orthodontic, and restorative treatment of pathologic migration of anterior teeth: A case report

Pathologic tooth migration related to periodontal disease is a common chief complaint of periodontal patients. This paper describes the treatment of a case of severe periodontal disease and disfiguring pathologic migration of maxillary central incisors, which required a multidisciplinary approach. After conventional pert. odontal treatment was performed, the anterior diastema was closed using a combination of orthodontic therapy and restorative treatment. A 6-month follow-up examination of this case revealed resolution of the anterior pathologic migration, with gains in clinical attachment levels and a successful esthetic and functional final result.

Ability of different restorative materials to prevent in situ secondary caries: analysis by polarized light-microscopy and energy-dispersive X-ray

Secondary caries is the main cause of direct restoration replacement. The purpose of this study was to analyze enamel adjacent to different restorative materials after in situ cariogenic challenge using polarized-light microscopy (PLM), scanning electron microscopy (SEM) and energy-dispersive X-ray analysis (EDS). Twelve volunteers, with a low level of dental plaque, a low level of mutans streptococci, and normal salivary flow, wore removable palatal acrylic appliances containing enamel specimens restored with Z250 composite, Freedom composite, Fuji IX glass-ionomer cement, or Vitremer resin-modified glass-ionomer for 14 days. Volunteers dripped one drop of 20% sucrose solution (n = 10) or distilled water (control group) onto each specimen 8 times per day. Specimens were removed from the appliances and submitted to PLM for examination of the lesion area (in mm(2)), followed by dehydration, gold-sputtering, and submission to SEM and EDS. The calcium (Ca) and phosphorus (P) contents were evaluated in weight per cent (%wt). Differences were found between Z250 and Vitremer, and between Z250 and FujiIX, when analyzed using PLM. Energy-dispersive X-ray analysis results showed differences between the studied materials regarding Ca %wt. In conclusion, enamel adjacent to glass-ionomer cement presented a higher Ca %wt, but this material did not completely prevent enamel secondary caries under in situ cariogenic challenge.

Effects of Resinous Monomers Used in Restorative Dental Modeling on the Cohesive Strength of Composite Resin

Purpose: The purpose of this study was to evaluate the cohesive strength of the composite using different resinous monomers to lubricate instruments used in the Restorative Dental Modeling Insertion Technique (RDMIT).Materials and Methods: The composite specimens were made by using a prefabricated Teflon device. Different resinous monomers were used at the interface to lubricate the instruments, for a total of 72 specimens divided into 6 groups: 1. control group, no resinous monomer was used; 2. Composite Wetting Resin; 3. C & B Liquid; 4. Scotchbond Multi-Purpose Adhesive; 4. Adper Single Bond Adhesive; 6. Prime & Bond NT. Specimens were submitted to the circular area tensile test to evaluate the cohesive strength at the composite interfaces. Data were analyzed using ANOVA and Tukey's test (alpha = 0.05).Results: ANOVA showed a value of p < 0.0001, which indicated that there were significant differences among the groups. The means (SD) for the different groups were: Adper Single Bond Adhesive: 26 (12) a; control group: 28 (3) ab; Prime & Bond NT: 32 (12) ab; Composite Wetting Resin: 36 (9) abc; C&B Liquid: 38 (7) bc; Scotchbond Multi-Purpose Adhesive: 46 (10) c. Groups denoted with the same letters were not significantly different. Only Scotchbond Multi-Purpose Adhesive, used for direct restorations, had a statistically significantly higher bond strength than the control group, Adper Single Bond Adhesive, and Prime & Bond NT. Adper Single Bond with Adhesive showed a statistically significantly lower mean value than C & B Liquid.Conclusion: The results of this study indicate that the resinous monomers used for lubricating the instruments in the RDMIT did not alter the mechanical properties of the composite, and therefore did not reduce the cohesive bond strength at the composite interfaces.