The influence of cervical finish line, internal relief, and cement type on the cervical adaptation of metal crowns

Objective: the aim of this investigation was to evaluate the cervical adaptation of metal crowns under several conditions, namely (1) variations in the cervical finish line of the preparation, (2) application of internal relief inside the crowns, and (3) cementation using different luting materials. Method and Materials: One hundred eighty stainless-steel master dies were prepared simulating full crown preparations: 60 in chamfer (CH), 60 in 135-degree shoulder (OB), and 60 in rounded shoulder (OR). The finish lines were machined at approximate dimensions of a molar tooth preparation (height: 5.5 mm; cervical diameter: 8 mm; occlusal diameter: 6.4 mm; taper degree: 6; and cervical finish line width: 0.8 mm). One hundred eighty corresponding copings with the same finish lines were fabricated. A 30-mu m internal relief was machined 0.5 mm above the cervical finish line in 90 of these copings. The fit of the die and the coping was measured from all specimens (L0) prior to cementation using an optical microscope. After manipulation of the 3 types of cements (zinc phosphate, glass-ionomer, and resin cement), the coping was luted on the corresponding standard master die under 5-kgf loading for 4 minutes. Vertical discrepancy was again measured (L1), and the difference between L1 and L0 indicated the cervical adaptation. Results: Significant influence of the finish line, cement type, and internal relief was observed on the cervical adaptation (P < .001). The CH type of cervical finish line resulted in the best cervical adaptation of the metal crowns regardless of the cement type either with or without internal relief (36.6 +/- 3 to 100.8 +/- 4 mu m) (3-way analysis of variance and Tukey's test, alpha = .05). The use of glass-ionomer cement resulted in the least cervical discrepancy (36.6 +/- 3 to 115 +/- 4 mu m) than those of other cements (45.2 +/- 4 to 130.3 +/- 2 mu m) in all conditions. Conclusion: the best cervical adaptation was achieved with the chamfer type of finish line. The internal relief improved the marginal adaptation significantly, and the glass-ionomer cement led to the best cervical adaptation, followed by zinc phosphate and resin cement.

Clinical evaluation of abutment teeth of removable partial denture by means of the Periotest method

Prosthodontics should be one of the means of establishing conditions for the maintenance of periodontal health. The forces applied to the abutment teeth and their effects are very important considerations in the design and construction of the removable partial dentures. This 6-month follow-up clinical study evaluated the degree of mobility of abutment teeth of distal extension and tooth supported removable partial dentures by using Periotest. Two types of clasp design were selected for evaluation. In cases with unilateral and bilateral distal-extension, a clasp design including a T clasp of Roach retentive arm, a rigid reciprocal arm and a mesial rest were used. For the abutments of tooth-supported removable partial dentures, a second clasp design with a cast circumferential buccal retentive arm, a rigid reciprocal clasp arm and a rest adjacent to the edentulous ridges was selected. A total of 68 abutment teeth was analysed. Periotest values were made at the time of denture placement (control) and at 1, 3 and 6 months after the denture placement. The statistical analysis was performed using Friedman test. All analysis was performed at a 0.05 level of significance. The results revelled that no significant changes in tooth mobility were observed during the 6-months follow-up (P > 0.05). In conclusion, our findings suggest that adequate oral hygiene instructions, careful prosthetic treatment planning and regular recall appointments play an important role in preventing changes in abutment tooth mobility caused by removable partial denture placement.

Accuracy of Mechanical Torque Devices for Implants Used in Brazilian Dental Offices

The purpose of this study was to determine the accuracy of mechanical torque devices in delivering target torque values in dental offices in Salvador, Brazil. A team of researchers visited 16 dental offices, and the clinicians applied torque values (20 and 32 Ncm) to electronic torque controllers. Five repetitions were completed at each torque value and data were collected. When 20 Ncm of torque was used, 62.5% of measured values were accurate (within 10% of the target value). For 32 Ncm, however, only 37.5% of these values were achieved. Several of the tested mechanical torque devices were inaccurate. Int J Prosthodont 2011;24:38-39.

Patients' Expectations of and Satisfaction with Implant-Supported Fixed Partial Dentures and Single Crowns

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Surface Treatments on the Bond Strength between Composite Resin and Acrylic Resin Denture Teeth

Purpose: This investigation studied the effects of 3 surface treatments on the shear bond strength of a light-activated composite resin bonded to acrylic resin denture teeth. Materials and Methods: The occlusal surfaces of 30 acrylic resin denture teeth were ground flat with up to 400-grit silicon carbide paper. Three different surface treatments were evaluated: (1) the flat ground surfaces were primed with methyl methacrylate (MMA) monomer for 180 seconds; (2) light-cured adhesive resin was applied and light polymerized according to the manufacturer's instructions; and (3) treatment 1 followed by treatment 2. The composite resin was packed on the prepared surfaces using a split mold. The interface between tooth and composite was loaded at a cross-head speed of 0.5 mm/min until failure. Results: Analysis of variance indicated significant differences between the surface treatments. Results of mean comparisons using Tukey's test showed that significantly higher shear bond strengths were developed by bonding composite resin to the surfaces that were previously treated with MMA and then with the bonding agent when compared to the other treatments. Conclusion: Combined surface treatment of MMA monomer followed by application of light-cured adhesive resin provided the highest shear bond strength between composite resin and acrylic resin denture teeth.

Effectiveness of Microwave Sterilization on Three Hard Chairside Reline Resins

Purpose: The aim of this study was to evaluate the effectiveness of microwave irradiation sterilization on hard chairside reline resins. Materials and Methods: Specimens of three reline resins (Kooliner, Tokuso Rebase, and Ufi Gel Hard) were fabricated and subjected to ethylene oxide sterilization. The specimens were then individually inoculated (107 cfu/mL) with Tryptic Soy Broth media containing one of the tested microorganisms (C albicans, S aureus, B subtilis, and P aeruginosa). After 48 hours at 37°C, the samples were vortexed for 1 minute and allowed to stand for 9 minutes, followed by a short vortex to resuspend any organisms present. After inoculation, 40 specimens of each material were immersed in 200 mL of water and subjected to microwave irradiation at 650 W for 6 minutes. Forty non-irradiated specimens were used as positive controls. Replicate specimens (25 μL) of suspension were plated at dilutions of 10-3 to 10-6 on plates of selective media appropriate for each organism. All plates were incubated at 37°C for 48 hours. After incubation, colonies were counted, and the data were statistically analyzed by the Kruskal-Wallis test. Twelve specimens of each material were prepared for SEM. Results: All immersed specimens showed consistent sterilization of all the individual organisms after microwave irradiation. SEM examination indicated an alteration in cell morphology after microwave irradiation. Conclusion: Microwave sterilization for 6 minutes at 650 W proved to be effective for the sterilization of hard chairside reline resins.

Cytotoxicity of denture base resins: Effect of water bath and microwave postpolymerization heat treatments

Purpose: This study compared the effect of two postpolymerization heat treatments on the cytotoxicity of three denture base resins on L929 cells using 3H-thymidine incorporation and MTT assays. Materials and Methods: Sample disks of Lucitone 550, QC 20, and Acron MC resins were fabricated under aseptic conditions and stored in distilled water at 37°C for 48 hours. Specimens were then divided into three groups: (1) heat treated in microwave oven for 3 minutes at 500 W; (2) heat treated in water bath at 55°C for 60 minutes; and (3) no heat treatment. Eluates were prepared by placing three disks into a sterile glass vial with 9 mL of Eagle's medium and incubating at 37°C for 24 hours. The cytotoxic effect from the eluates was evaluated using the 3H-thymidine incorporation and MTT assays, which reflect DNA synthesis levels and cell metabolism, respectively. Results: The components leached from the resins were cytotoxic to L929 cells when 3H- thymidine incorporation assay was employed. In contrast, eluates from all resins revealed noncytotoxic effects as measured by MTT assay. For both MTT assay and 3H-thymidine incorporation, the heat treatments did not decrease the cytotoxicity of the materials tested. Conclusion: Resins were graded by 3H-thymidine incorporation assay as slightly cytotoxic and by MTT assay as noncytotoxic. Cytotoxicity of the denture base materials was not influenced by microwave or water bath heat treatment.

Effect of surface treatments on the resin bond to zirconium-based ceramic

Purpose: This study tested the hypothesis that the tribochemical silica coating on ceramic surfaces increases the bond strength of resin cement to a glass-infiltrated zirconium-based ceramic. Materials and Methods: Fifteen blocks of In-Ceram Zirconia from CEREC InLab (5 per group) and 15 composite blocks (Z-250) 5 mm x 5 mm x 4 mm were made. The ceramic surfaces were polished, and the blocks were divided into three groups: (1) airborne abrasion with 110-μm aluminum oxide particles; (2) Rocatec system, tribochemical silica coating; and (3) CoJet system, tribochemical silica coating. The ceramic blocks were cemented to the composite blocks using Panavia F according to the manufacturer's specifications. All samples were stored in 37°C distilled water for 7 days and later sectioned in two axes using a diamond disk under cooling to obtain specimens with a cross-sectional area of approximately 1 mm2 (n = 45). Each specimen was then attached with cyanoacrylate glue to an adapted device for the microtensile test, which was carried out on a universal testing machine. Results: The results were subjected to ANOVA and Tukey's test. Group 2 (23.0 ± 6.7 MPa) and group 3 (26.8 ± 7.4 MPa) showed greater bond strength than group 1 (15.1 ± 5.3 MPa). There was no significant difference between groups 2 and 3. All failures were in the adhesive zone. Conclusion: The hypothesis was confirmed - the tribochemical systems increased the bond strength between Panavia F and In-Ceram Zirconia.

Intercommissural width in 4 racial groups as a guide for the selection of maxillary anterior teeth in complete dentures

Purpose: To determine whether intercommissural width is a reliable guide for the selection of maxillary denture teeth width. Materials and Methods: Casts were made of 160 subjects from 4 different racial groups. Locations of intercommissural width landmarks (the corners of the mouth) were made on the subjects and transferred to the casts. The distances between the corners of the mouth and the distal of the canines were measured on the casts and compared. Results: A weak correlation was found between the distal of the canines and the distance between the corners of the mouth in the 4 racial groups. Conclusion: The use of the corners of the mouth for the selection of artificial teeth is generally inaccurate.

Effect of silica coating on flexural strength of fiber posts

Purpose: Fiber-reinforced composite (FRC) posts can be air-abraded to obtain good attachment to the resin cement. This study tested the effect of silica coating on the flexural strength of carbon, opaque, and translucent quartz FRC posts. Materials and Methods: Six experimental groups of FRC posts (n = 10 per group) were tested, either as received from the manufacturer or after chairside silica coating (30-μm CoJet-Sand). Results: There was no significant difference in the flexural strength of nonconditioned (504 to 525 MPa) and silica-coated (514 to 565 MPa) specimens (P > .05) (analysis of variance). The type of post did have a significant effect on flexural strength (P < .05). Conclusion: Chairside silica coating did not affect the flexural strength of both carbon and quartz FRC posts.

Cytotoxicity of hard chairside reline resins: Effect of microwave irradiation and water bath postpolymerization treatments

Purpose: To evaluate the influence of water bath and microwave postpolymerization treatments on the cytotoxicity of 6 hard reline acrylic resins. Materials and Methods: The materials tested were Tokuso Rebase Fast (TR), Ufi Gel Hard (UGH), Duraliner II (D), Kooliner (K), New Truliner (NT), and Light Liner (LL). LL resin was additionally tested with an air-barrier coating (LLABC). Nine disks of each material (10 × 1 mm) were made and divided into 3 groups: group 1 (no postpolymerization treatment); group 2 (postpolymerization in microwave oven); group 3 (postpolymerization in water bath at 55°C for 10 minutes). L929 cells were cultured in 96-well plates and incubated for 24 hours in Eagle's medium. Eluates prepared from the disks or medium without disks (control) replaced the medium. Cytotoxicity was assessed by both dehydrogenase succinic activity (MTT) assay and incorporation of radioactive 3H-thymidine assay. Tests were carried out in quadruplicate and repeated twice. Differences between groups were determined by analysis of variance with Tukey multiple-comparison intervals (α = .05). Results: For MTT assay, the postpolymerization treatments had no effect on the cytotoxicity of all materials (P > .05). For 3H-thymidine assay, the postpolymerization treatments significantly decreased the cytotoxicity of UGH (P < .05). The cytotoxicity of K, NT, LL, and LLABC increased after microwave irradiation (P < .05). TR, NT, and LLABC showed an increase in cytotoxicity after water bath (P < .05). Conclusion: When assessed by MTT assay, the cytotoxicity of the materials was not affected by postpolymerization treatments. 3H-Thymidine assay showed that the cytotoxicity of the resins was not improved by the postpolymerization treatments, with the exception of UGH.

Weight loss and surface roughness of hard chairside reline resins after toothbrushing: Influence of postpolymerization treatments

Purpose: To evaluate the effect of 2 postpolymerization treatments on toothbrushing wear (weight loss) and surface roughness of 3 autopolymerized reline resins-Duraliner II (D) (Reliance Dental), Kooliner (K) (Coe Laboratories), and Tokuso Rebase Fast (T) (Tokuyama Dental)-and 1 heat-polymerized resin, Lucitone 550 (L) (Dentsply International). Materials and Methods: Specimens (40 x 10 x 2mm) of each material (n = 24) were prepared and divided into 3 groups: control (no postpolymerization treatment); water bath (immersion in water at 55°C); and microwave (microwave irradiation). Specimens were dried until constant weight was achieved and the surface roughness (Ra) was measured. Tests were performed in a toothbrush machine using 20,000 strokes of brushing at a weight of 200 g, with the specimens immersed in 1:1 dentifrice/water slurry. Specimens were reconditioned to constant weight and the weight loss (mg) and surface roughness were evaluated. Data were analyzed by 2-way analysis of variance and followed by Tukey test (α = .05). Results: In the control group, the weight loss of materials D and T was lower (P < .05) than that of L. No differences among materials were found after postpolymerization treatments (P > .05). The weight loss of material T (control = 0.5 mg) was significantly increased (P < .05) after postpolymerization treatments (water bath = 1.9 mg; microwave = 1.8 mg). For materials K and T, the toothbrushed surface roughness was higher (P < .05) after microwave and waterbath postpolymerization treatments. Material L showed increased surface roughness after microwave postpolymerization treatment. Conclusion: The toothbrushing wear resistance of L was not superior to the reline resins. The postpolymerization treatments did not improve the toothbrushing wear resistance of the materials and produced an increased surface roughness for materials L, K, and T.

Effectiveness of microwave irradiation on the disinfection of complete dentures

Purpose: The purpose of this study was to evaluate the effectiveness of microwave irradiation on the disinfection of simulated complete dentures. Materials and Methods: Eighty dentures were fabricated in a standardized procedure and subjected to ethylene oxide sterilization. The dentures were individually inoculated (10 7 cfu/mL) with tryptic soy broth (TSB) media containing one of the tested microorganisms (Candida albicans, Streptoccus aureus, Bacillus subtilis, and Pseudomonas aeruginosa). After 48 hours of incubation at 37°C, 40 dentures were individually immersed in 200 mL of water and submitted to microwave irradiation at 650 W for 6 minutes. Forty nonirradiated dentures were used as positive controls. Replicate aliquots (25 μL) of suspensions were plated at dilutions of 10 -3 to 10 -6 on plates of selective media appropriate for each organism. All plates were incubated at 37°C for 48 hours. TSB beakers with the microwaved dentures were incubated at 37°C for 7 more days. After incubation, the number of colony-forming units was counted and the data were statistically analyzed by Kruskal-Wallis test (α = .05). Results: No evidence of growth was observed at 48 hours for S aureus, B subtilis, and C albicans. Dentures contaminated with P aeruginosa showed small growth on 2 plates. After 7 days incubation at 37°C, no growth was visible in the TSB beakers of S aureus and C albicans. Turbidity was observed in 3 broth beakers, 2 from P aeruginosa and 1 from B subtilis. Conclusion: Microwave irradiation for 6 minutes at 650 W produced sterilization of complete dentures contaminated with S aureus and C albicans and disinfection of those contaminated with P aeruginosa and B subtilis.

Effect of disinfectants on the hardness and roughness of reline acrylic resins

Purpose: Potential effects on hardness and roughness of a necessary and effective disinfecting regimen (1% sodium hypocholorite and 4% chlorhexidine) were investigated for two hard chairside reline resins versus a heat-polymerizing denture base acrylic resin. Materials and Methods: Two standard hard chairside reliners (Kooliner and Duraliner II), one heat-treated chairside reliner (Duraliner II +10 minutes in water at 55°C), and one standard denture base material (Lucitone 550) were exposed to two disinfecting solutions (1% sodium hypochlorite; 4% chlorhexidine gluconate), and tested for two surface properties [Vickers hardness number (VHN, kg/mm2); Roughness (Ra, μm)] for different times and conditions (1 hour after production, after 48 hours at 37 ± 2°C in water, after two disinfection cycles, after 7 days in disinfection solutions, after 7 days in water only). For each experimental condition, eight specimens were made from each material. Data were analyzed by analysis of variance followed by Tukey's test, and Student's t-test (p= 0.05). Results: For Kooliner (from 6.2 ± 0.3 to 6.5 ± 0.5 VHN) and Lucitone 550 (from 16.5 ± 0.4 to 18.4 ± 1.7 VHN), no significant changes in hardness were observed either after the disinfection or after 7 days of immersion, regardless of the disinfectant solution used. For Duraliner II (from 4.0 ± 0.1 to 4.2 ± 0.1 VHN), with and without heat treatment, a small but significant increase in hardness was observed for the specimens immersed in the disinfectant solutions for 7 days (from 4.3 ± 0.2 to 4.8 ± 0.5 VHN). All materials showed no significant change in roughness (Kooliner: from 0.13 ± 0.05 to 0.48 ± 0.24 μm; Duraliner II, with and without heat treatment: from 0.15 ± 0.04 to 0.29 ± 0.07 μm; Lucitone 550: from 0.44 ± 0.19 to 0.49 ± 0.15 μm) after disinfection and after storage in water for 7 days. Conclusions: The disinfectant solutions, 1% sodium hypochlorite and 4% chlorhexidine gluconate, caused no apparent damage on hardness and roughness of the materials evaluated. Copyright © 2006 by The American College of Prosthodontists.

Effect of the association of nystatin with a tissue conditioner on its ultimate tensile strength

Purpose: This study evaluated the ultimate tensile strength of a tissue conditioner without nystatin incorporation (GI - control group) and the same tissue conditioner modified by the addition of nystatin in two concentrations: GII - 500,000 International Units (U) and GIII - 1,000,000 U, in which each milligram of the medicament corresponded to 6079 U. Materials and Methods: Dumbbell-shaped specimens (N = 7) with a central cross-sectional area of 33 × 6 × 3 mm were produced for the three experimental groups. After polymerization following manufacturer's instructions, specimens were immersed in distilled water at 37°C for either 24 hours or 7 days and then tested in tension in the MTS 810 at 40 mm/minute. Data were analyzed by two-way ANOVA followed by Tukey's test, at 95% level of confidence. Results: The means (force-grams (gf) ± standard deviation) of the ultimate tensile strength were: GI - 634.29 ± 122.80; GII - 561.92 ± 133.56; and GIII - 547.30 ± 73.47 for 24-hour storage, and GI - 536.68 ± 54.71; GII - 467.50 ± 143.51; and GIII - 500.62 ± 159.76 for 7-day storage. There were no statistically significant differences among the three experimental groups (p > 0.05). The ultimate tensile strength means of all experimental groups after 7 days were significantly lower than those observed after 24 hours (p = 0.04). Conclusions: The results of this study suggest that the addition of nystatin into the tissue conditioner investigated in concentrations below 1,000,000 U did not affect its ultimate tensile strength. Copyright © 2006 by The American College of Prosthodontists.