The influence of cellular source on periodontal regeneration using calcium phosphate coated polycaprolactone scaffold supported cell sheets

Cell-based therapy is considered a promising approach to achieving predictable periodontal regeneration. In this study, the regenerative potential of cell sheets derived from different parts of the periodontium (gingival connective tissue, alveolar bone and periodontal ligament) were investigated in an athymic rat periodontal defect model. Periodontal ligament (PDLC), alveolar bone (ABC) and gingival margin-derived cells (GMC) were obtained from human donors. The osteogenic potential of the primary cultures was demonstrated in vitro. Cell sheets supported by a calcium phosphate coated melt electrospun polycaprolactone (CaP-PCL) scaffold were transplanted to denuded root surfaces in surgically created periodontal defects, and allowed to heal for 1 and 4 weeks. The CaP-PCL scaffold alone was able to promote alveolar bone formation within the defect after 4 weeks. The addition of ABC and PDLC sheets resulted in significant periodontal attachment formation. The GMC sheets did not promote periodontal regeneration on the root surface and inhibited bone formation within the CaP-PCL scaffold. In conclusion, the combination of either PDLC or ABC sheets with a CaP-PCL scaffold could promote periodontal regeneration, but ABC sheets were not as effective as PDLC sheets in promoting new attachment formation.

Clinical outcomes of vitamin D deficiency and supplementation in cancer patients

Results of recent studies suggest that circulating levels of vitamin D may play an important role in cancer-specific outcomes. The present systematic review was undertaken to determine the prevalence of vitamin D deficiency (<25 nmol/L) and insufficiency (25-50 nmol/L) in cancer patients and to evaluate the association between circulating calcidiol (the indicator of vitamin D status) and clinical outcomes. A systematic search of original, peer-reviewed studies on calcidiol at cancer diagnosis, and throughout treatment and survival, was conducted yielding 4,706 studies. A total of 37 studies met the inclusion criteria for this review. Reported mean blood calcidiol levels ranged from 24.7 to 87.4 nmol/L, with up to 31% of patients identified as deficient and 67% as insufficient. The efficacy of cholecalciferol supplementation for raising the concentration of circulating calcidiol is unclear; standard supplement regimens of <1,000 IU D3 /day may not be sufficient to maintain adequate concentrations or prevent decreasing calcidiol. Dose-response studies linking vitamin D status to musculoskeletal and survival outcomes in cancer patients are lacking.

Accounting for volunteer services : a deficiency in accountability

The purpose of this study is to identify the extent to which NFP organisations disclose information on volunteer contributions of services. Design/methodology/approach – The study relies on information disclosed in the websites of NFP organisations. Findings - We find that disclosure was more prevalent on NFP websites compared to digital annual report disclosures. We find that more NFPs provided disclosure on the activities of their volunteers than other items pertaining to volunteers and the quantification and valuation of volunteer contributions were the least likely to be disclosed. Importantly, the findings illustrate an accountability deficiency in the comprehensiveness of disclosure which results in an under-representation of the contribution volunteers provide to organisational sustainability and impact on mission fulfilment. Research limitations/implications – The convenience sample size restricts further interrogation to tease out organisational characteristics that may influence current disclosure practices. Practical implications - The findings contribute to international debate over the inclusion of volunteer contributions in the assessment of a NFP’s accountability over its resources and ultimately the enhancement of its sustainability.

Osteogenic differentiation of bone marrow MSCs by β-tricalcium phosphate stimulating macrophages via BMP2 signalling pathway

Immune reactions play important roles in determining the in vivo fate of bone substitute materials, either in new bone formation or inflammatory fibrous tissue encapsulation. The paradigm for the development of bone substitute materials has been shifted from inert to immunomodulatory materials, emphasizing the importance of immune cells in the material evaluation. Macrophages, the major effector cells in the immune reaction to implants, are indispensable for osteogenesis and their heterogeneity and plasticity render macrophages a primer target for immune system modulation. However, there are very few reports about the effects of macrophages on biomaterial-regulated osteogenesis. In this study, we used b-tricalcium phosphate (b-TCP) as a model biomaterial to investigate the role of macrophages on the material stimulated osteogenesis. The macrophage phenotype switched to M2 extreme in response to b-TCP extracts, which was related to the activation of calcium-sensing receptor (CaSR) pathway. Bone morphogenetic protein 2 (BMP2) was also significantly upregulated by the b-TCP stimulation, indicating that macrophage may participate in the b-TCP stimulated osteogenesis. Interestingly, when macrophageconditioned b-TCP extracts were applied to bone marrow mesenchymal stem cells (BMSCs), the osteogenic differentiation of BMSCs was significantly enhanced, indicating the important role of macrophages in biomaterial-induced osteogenesis. These findings provided valuable insights into the mechanism of material-stimulated osteogenesis, and a strategy to optimize the evaluation system for the in vitro osteogenesis capacity of bone substitute materials.

A randomised, concentration-controlled, comparison of standard (5-day) vs. prolonged (15-day) infusions of etoposide phosphate in small-cell lung cancer

Purpose: This randomised trial was designed to investigate the activity and toxicity of continuous infusion etoposide phosphate (EP), targeting a plasma etoposide concentration of either 3 μg/ml for five days (5d) or 1 μg/ml for 15 days (15d), in previously untreated SCLC patients with extensive disease. Patients and methods: EP was used as a single agent. Plasma etoposide concentration was monitored on days 2 and 4 in patients receiving 5d EP and on days 2, 5, 8 and 11 in patients receiving 15d EP, with infusion modification to ensure target concentrations were achieved. Treatment was repeated every 21 days for up to six cycles, with a 25% reduction in target concentration in patients with toxicity. Results: The study has closed early after entry of 29 patients (14 with 5d EP, 15 with 15d EP). Objective responses were seen in seven of 12 (58%, confidence interval (CI): 27%-85%) evaluable patients after 5d EP, and two of 14 (14%, CI: 4%42%) evaluable patients after 15d EP (P = 0.038). Grade 3 or 4 neutropenia or leucopenia during the first cycle of treatment was observed in six of 12 patients after 5d EP and 0/14 patients after 15d EP (P = 0.004), with median nadir WBC count of 2.6 x 109/1 after 5d and 5.0 x 109/1 after 15d EP (P = 0.017). Only one of 49 cycles of 15d EP was associated with grade 3 or worse haematological toxicity, compared to 14 of 61 cycles of 5d EP. Conclusions: Although the number of patients entered into this trial was small, the low activity seen at 1 μg/ml in the 15d arm suggests that this concentration is below the therapeutic window in this setting. Further concentration- controlled studies with prolonged EP infusions are required.

Vibrational spectroscopic characterization of the phosphate mineral althausite Mg2(PO4)(OH,F,O) – implications for the molecular structure

Natural single-crystal specimens of althausite from Brazil, with general formula Mg2(PO4)(OH,F,O) were investigated by Raman and infrared spectroscopy. The mineral occurs as a secondary product in granitic pegmatites. The Raman spectrum of althausite is characterized by bands at 1020, 1033 and 1044 cm-1, assigned to ν1 symmetric stretching modes of the HOPO33- and PO43- units. Raman bands at around 1067, 1083 and 1138 cm-1 are attributed to both the HOP and PO antisymmetric stretching vibrations. The set of Raman bands observed at 575, 589 and 606 cm-1 are assigned to the ν4 out of plane bending modes of the PO4 and H2PO4 units. Raman bands at 439, 461, 475 and 503 cm-1 are attributed to the ν2 PO4 and H2PO4 bending modes. Strong Raman bands observed at 312, 346 cm-1 with shoulder bands at 361, 381 and 398 cm-1 are assigned to MgO stretching vibrations. No bands which are attributable to water were found. Vibrational spectroscopy enables aspects of the molecular structure of althausite to be assessed.

A study of the phosphate mineral kapundaite NaCa(Fe3+)4(PO4)4(OH)3⋅5(H2O) using SEM/EDX and vibrational spectroscopic methods

Vibrational spectroscopy enables subtle details of the molecular structure of kapundaite to be determined. Single crystals of a pure phase from a Brazilian pegmatite were used. Kapundaite is the Fe3+ member of the wardite group. The infrared and Raman spectroscopy were applied to compare the structure of kapundaite with wardite. The Raman spectrum of kapundaite in the 800–1400 cm−1 spectral range shows two intense bands at 1089 and 1114 cm−1 assigned to the ν1PO43- symmetric stretching vibrations. The observation of two bands provides evidence for the non-equivalence of the phosphate units in the kapundaite structure. The infrared spectrum of kapundaite in the 500–1300 cm−1 shows much greater complexity than the Raman spectrum. Strong infrared bands are found at 966, 1003 and 1036 cm−1 and are attributed to the ν1PO43- symmetric stretching mode and ν3PO43- antisymmetric stretching mode. Raman bands in the ν4 out of plane bending modes of the PO43- unit support the concept of non-equivalent phosphate units in the kapundaite structure. In the 2600–3800 cm−1 spectral range, Raman bands for kapundaite are found at 2905, 3151, 3311, 3449 and 3530 cm−1. These bands are broad and are assigned to OH stretching vibrations. Broad infrared bands are also found at 2904, 3105, 3307, 3453 and 3523 cm−1 and are attributed to water. Raman spectroscopy complimented with infrared spectroscopy has enabled aspects of the structure of kapundaite to be ascertained and compared with that of other phosphate minerals.

A vibrational spectroscopic study of the phosphate mineral minyulite KAl2(OH,F)(PO4)2⋅4(H2O) and in comparison with wardite

Vibrational spectroscopy enables subtle details of the molecular structure of minyulite KAl2(OH,F)(PO4)2⋅4(H2O). Single crystals of a pure phase from a Brazilian pegmatite were used. Minyulite belongs to the orthorhombic crystal system. This indicates that it has three axes of unequal length, yet all are perpendicular to each other. The infrared and Raman spectroscopy were applied to compare the structure of minyulite with wardite. The reason for the comparison is that both are Al containing phosphate minerals. The Raman spectrum of minyulite shows an intense band at 1012 cm−1 assigned to the ν1PO43- symmetric stretching vibrations. A series of low intensity Raman bands at 1047, 1077, 1091 and 1105 cm−1 are assigned to the ν3PO43- antisymmetric stretching modes. The Raman bands at 1136, 1155, 1176 and 1190 cm−1 are assigned to AlOH deformation modes. The infrared band at 1014 cm−1 is ascribed to the PO43- ν1 symmetric stretching vibrational mode. The infrared bands at 1049, 1071, 1091 and 1123 cm−1 are attributed to the PO43- ν3 antisymmetric stretching vibrations. The infrared bands at 1123, 1146 and 1157 cm−1 are attributed to AlOH deformation modes. Raman bands at 575, 592, 606 and 628 cm−1 are assigned to the ν4 out of plane bending modes of the PO43- unit. In the 2600–3800 cm−1 spectral range, Raman bands for minyulite are found at 3661, 3669 and 3692 cm−1 are assigned to AlOH/AlF stretching vibrations. Broad infrared bands are also found at 2904, 3105, 3307, 3453 and 3523 cm−1. Raman bands at 3225, 3324 cm−1 are assigned to water stretching vibrations. A comparison is made with the vibrational spectra of wardite. Raman spectroscopy complimented with infrared spectroscopy has enabled aspects of the structure of minyulite to be ascertained and compared with that of other phosphate minerals.

A vibrational spectroscopic study of the phosphate mineral whiteite CaMn++Mg2Al2(PO4)4(OH)2·8(H2O)

Vibrational spectroscopy enables subtle details of the molecular structure of whiteite to be determined. Single crystals of a pure phase from a Brazilian pegmatite were used. The infrared and Raman spectroscopy were applied to compare the molecular structure of whiteite with that of other phosphate minerals. The Raman spectrum of whiteite shows an intense band at 972 cm-1 assigned to the m1 PO3- 4 symmetric stretching vibrations. The low intensity Raman bands at 1076 and 1173 cm-1 are assigned to the m3 PO3- 4 antisymmetric stretching modes. The Raman bands at 1266, 1334 and 1368 cm-1 are assigned to AlOH deformation modes. The infrared band at 967 cm-1 is ascribed to the PO3- 4 m1 symmetric stretching vibrational mode. The infrared bands at 1024, 1072, 1089 and 1126 cm-1 are attributed to the PO3-4 m3 antisymmetric stretching vibrations. Raman bands at 553, 571 and 586 cm-1 are assigned to the m4 out of plane bending modes of the PO3- 4 unit. Raman bands at 432, 457, 479 and 500 cm-1 are attributed to the m2 PO4 and H2PO4 bending modes. In the 2600 to 3800 cm-1 spectral range, Raman bands for whiteite are found 3426, 3496 and 3552 cm-1 are assigned to AlOH stretching vibrations. Broad infrared bands are also found at 3186 cm-1. Raman bands at 2939 and 3220 cm-1 are assigned to water stretching vibrations. Raman spectroscopy complimented with infrared spectroscopy has enabled aspects of the structure of whiteite to be ascertained and compared with that of other phosphate minerals.

Strong and bioactive tri-calcium phosphate scaffolds with tube-like macropores

Calcium phosphate ceramic scaffolds have been widely investigated for bone tissue engineering due to their excellent biocompatibility and biodegradation. Unfortunately, they have the shortcoming of low mechanical properties. In order to provide strong, bioactive, and biodegradable scaffolds, a new approach of infiltrating the macro-tube ABS (acrylontrile butadiene styrene) templates with a hydroxyapatite/bioactive glass mixed slurry was developed to fabricate porous Si-doped TCP (tri-calcium phosphate) scaffolds. The porous Si-doped TCP ceramics with a high porosity (~65%) and with interconnected macrotubes (~0.8mm in diameter) and micropores (5-100 m) had a high compressive strength (up to 14.68+0.2MPa), which was comparable to that of a trabecular bone and was much higher than those of pure TCP scaffolds. Additional cell attachment study and MTT cytotoxicity assay proved the bioactivity and biocompatibility of the new scaffolds. Thus a potential bioceramic material and a new approach to make the potential scaffolds were developed for bone tissue engineering.

Reply to the comments on “A study of the phosphate mineral kapundaite NaCa(Fe3+)4(PO4)4(OH)3·5(H2O) using SEM/EDX and vibrational spectroscopic methods” by Frost et al. (2014)

"The authors agree with the statements made by Mills and Christy on the study of kapundaite [1]. These authors are correct and have removed any confusion about the origin of the sample kapundaite. The authors (Frost et al.) confirm the sample of kapundaite studied in this work is from the Tom‘s quarry, Australia and can be considered a type material. The authors do not accept the statements by Mills and Christy on “type minerals”. The sample of kapundaite from the Australian source is from the collection of the Geology Department of the Federal University of Ouro Preto, Minas Gerais, Brazil with sample code SAC-111. At least if our mineral sample is not a co-type mineral, our sample is from the same origin as the type mineral. Samples..."--publisher website.

A vibrational spectroscopic study of a hydrated hydroxy-phosphate mineral fluellite, Al2(PO4)F2(OH)·7H2O

Raman and infrared spectra of two well-defined fluellite samples, Al2(PO4)F2(OH)�7H2O, from the Krásno near Horní Slavkov (Czech Republic) and Kapunda, South Australia (Australia) were studied and tentatively interpreted. Observed bands were assigned to the stretching and bending vibrations of phosphate tetrahedra, aluminum oxide/hydroxide/fluoride octahedra, water molecules and hydroxyl ions. Approximate O–H���O hydrogen bond lengths were inferred from the Raman and infrared spectra.

A vibrational spectroscopic study of the phosphate mineral lulzacite Sr2Fe2+(Fe2+,Mg)2Al4(PO4)4(OH)10

The mineral lulzacite from Saint-Aubin des Chateaux mine, France, with theoretical formula Sr2Fe2+(Fe2+,Mg)2Al4(PO4)4(OH)10 has been studied using a combination of electron microscopy with EDX and vibrational spectroscopic techniques. Chemical analysis shows a Sr, Fe, Al phosphate with minor amounts of Ga, Ba and Mg. Raman spectroscopy identifies an intense band at 990 cm�1 with an additional band at 1011 cm�1. These bands are attributed to the PO3� 4 m1 symmetric stretching mode. The m3 antisymmetric stretching modes are observed by a large number of Raman bands. The Raman bands at 1034, 1051, 1058, 1069 and 1084 together with the Raman bands at 1098, 1116, 1133, 1155 and 1174 cm�1 are assigned to the m3 antisymmetric stretching vibrations of PO3� 4 and the HOPO2� 3 units. The observation of these multiple Raman bands in the symmetric and antisymmetric stretching region gives credence to the concept that both phosphate and hydrogen phosphate units exist in the structure of lulzacite. The series of Raman bands at 567, 582, 601, 644, 661, 673 and 687 cm�1 are assigned to the PO3� 4 m2 bending modes. The series of Raman bands at 437, 468, 478, 491, 503 cm�1 are attributed to the PO3� 4 and HOPO2� 3 m4 bending modes. No Raman bands of lulzacite which could be attributed to the hydroxyl stretching unit were observed. Infrared bands at 3511 and 3359 cm�1 are ascribed to the OH stretching vibration of the OH units. Very broad bands at 3022 and 3299 cm�1 are attributed to the OH stretching vibrations of water. Vibrational spectroscopy offers insights into the molecular structure of the phosphate mineral lulzacite.

A vibrational spectroscopic study of the phosphate mineral churchite (REE)(PO4)⋅2H2O

Vibrational spectroscopy has been used to study the rare earth mineral churchite of formula (REE)(PO4)-⋅2H2O. The mineral contains a range of rare earth metals including yttrium depending on the locality. The Raman spectra of churchite-(REE) are characterized by an intense sharp band at 984 cm-1 assigned to the v1 (PO¾-) symmetric stretching mode. A lower intensity band observed at around 1067 cm-1 is attributed to the v3 (PO¾-) antisymmetric stretching mode. The (PO¾-) bending modes are observed at 497 cm-1 (v2) and 565 cm-1(v4). Raman bands at 649 and 681 cm-1 are assigned to water librational modes. Vibrational spectroscopy enables aspects of the structure of churchite to be ascertained.