Molecular construction of oriented crystalline NaMnF3 and KMnF3 with perovskite structures at room temperature

In this work. we report the fabrication of high-quality (101)-oriented orthorhombic NaMnF3 and (100)-oriented cubic KMnF3 perovskites via an organic monolayer template at room temperature. The controlled crystallization under the organic monolayer template is explained in terms of the electrostatic interactions and beneficial lattice matching between the organic template and the ions undergoing nucleation. The present study is of great importance in the preparation of oriented perovskite materials as well as in the understanding of the mechanism for organic-template-directed crystallization.

Structural phase transition in the layered perovskite compound BaTb2Mn2O7

A distorted layered perovskite compound BaTb2Mn2O7 was synthesized by the solid state reaction in pure argon. There is a structural phase transition in the BaTb2Mn2O7 compound. The phase transition was characterized by the DSC and high temperature Xray diffraction. The heat capacity of BaTb2Mn2O7 was calculated. The thermal anomaly corresponding to the phase transition was observed at about 740K. The lattice parameters were calculated by the CELL program for BaTb2Mn2O7, It has Tb-type orthorhombic symmetry with a = 0.3908 nm, b = 0.3866 nm, c = 2.0163 nm, and space group Immm at room temperature. With the increase of temperature, the lattice parameters gradually increase until 673K. From 723K to 973K, the compound translates to tetragonal with a = 0.39078 nm, c = 2.0277 nm and S.G. I4/mmm. This result is fairly in accordance with that of heat capacity.

High-pressure and-temperature synthesis and characterization of mixed valence perovskite oxides LaTi1-xMgxO3

Perovskite oxides LaTi1-xMgxO3 (x = 0.25, 0.5) were synthesized using high-pressure and-temperature method. LaTi0.75Mg0.25O3 is a new compound. This new synthesis route has some advantages. XRD analysis showed that the x = 0.25 sample belongs to cubic perovskite-type structure and the a = 0.5 sample belongs to orthorhombic perovskite-type structure. EPR measurement indicated that Ti ions were in mixed valence state of +3 and +4. IR measurement indicated that the vibration frequency and width of BO6 octahedron stretching vibration absorption band decreases with the increasing of x. The valence state of Ti ions can be altered by high-pressure and-temperature. (C) 2000 Elsevier Science S.A. All rights reserved.

Organic template-directed crystallization of the complex fluoride NH4MnF3 with perovskite structure

(100)-oriented NH4MnF3 perovskite with different morphologies have been obtained in situ via an organic template; experimental results can be rationalized in terms of electrostatic interactions and lattice matching between the organic template and the ions undergoing nucleation.

Evaluation of bond covalency and bond valence in Sr-doped perovskite-type compounds

Formulas for decomposing of complex crystals to a sum of binary crystals are described and applied to the study of bond covalency in La1-xSrxFeO3 (0.0 less than or equal to x less than or equal to 0.9) and Ca1-xSrxMnO3 (0.0 less than or equal to x less than or equal to 0.5). The bond valence is treated by bond-valence sums scheme. The results indicate that, for both compounds, with the increasing doping level, the bond covalency and bond valence show the same trend, namely, larger bond covalency corresponds to higher bond valence. For La1-xSrxFeO3, with the increase of doping level, the bond covalency of La-O, Ca-O decreases in the orthorhombic (0.0 less than or equal to x less than or equal to 0.2) and rhombohedral (0.4 less than or equal to x less than or equal to 0.7) systems, then increases slightly for the cubic (0.8 less than or equal to x less than or equal to 0.9) system, but that of Fe-O increases for all crystal systems. A sharp decrease in bond covalency was observed where the crystal changes from orthorhombic to rhombohedral, while a smooth trend was seen for the rhombohedral-to-cubic transition. On the other hand, for orthorhombic Ca1-xSrxMnO3, the bond covalency of Ca-O, Sr-O, and Mn-O (4-coordinate site) decreases with the increasing doping level, that of Mn-O (2-coordinate site) increases.

Layered La-Ba-Cu mixed oxides with perovskite structure as catalyst for NO reduction by CO

The mixed oxides, including LaBa2Cu3O7, LaBaCu2O5, La4BaCu5O12 with perovskite structure, were prepared. The catalysts were characterized by means of chemical analysis, XRD, H-2-TPR. It was found that their structures were layered ABO(3) perovskite structure and they were the active catalysts for the NO reduction by CO. The existence of Cu3+ is an important factor to give the catalysts a high activity for the NO reduction by CO.

Studies on the elimination of NO over the La-Ba-Cu mixed oxide catalysts with perovskite structure

The mixed oxides, including YBa2Cu3O7, LaBa2Cu3O7, LaBaCu2O5, La2BaCu3O7, La4BaCu5O12 with perovskite structure, were prepared. The catalysts were characterized by means of chemical analysis, XRD, TPD and TPR method. It was found that they were the active catalysts for the NO decomposition and NO reduction by CO. The existance of Cu3+ is an important factor to give the catalysts a high activity for the NO reduction by CO.

Perovskite-like mixed oxides La2-x(Sr,Th)(x)CuO4+/-lambda

Two groups of mixed oxides La2-xThxCuO4+/-lambda (0.0 less than or equal to x less than or equal to 0.4) and La2-xSrxCuO4+/-lambda (0.0 less than or equal to x less than or equal to 1.0) were prepared. Their crystal structures were studied with XRD and IR spectra, etc. Meanwhile, the average valence of Cu ions and nonstoichiometric oxygen (lambda) was measured through chemical analyses. Catalysis of the abovementioned mixed oxides was investigated in phenol hydroxylation, good results were obtained for some mixed oxides, and found that the catalysis of these mixed oxides have close relation with their defect structure and composition. A radical substitution mechanism was also proposed for this catalytic reaction.

Luminescence properties of Ce3+ in KMF3(M=Mg, Ca, Sr, Ba) hosts with perovskite structure

KMF3(M = Mg, Ca, Sr, Ba) compounds were synthesized by solid state reaction under argon atmosphere. Their structures were determined by X-ray diffraction. It belongs to cubic system with perovskite structure. The excitation and emission spectra of KMF3:Ce3+ were measured. According to the characteristics of spectral structures, the occupation site of Ce3+ is discussed.

Hydrothermal synthesis and lanthanide doping of complex fluorides, LiYF4, KYF4 and BaBeF4 under mild conditions

The complex fluorides LiYF4, KYF4, BaBeF4 and AYF(4)Eu(x) (A = Li, K) are hydrothermally synthesized at 140-240 degrees C and characterized by powder X-ray diffraction, thermogravimetric analysis, IR spectroscopy, scanning electron microscopy and luminescence measurements.

Preparation, physico-chemical behavior and catalytic property for ammonia oxidation of perovskite like mixed oxides La2-xSrxCuO4-lambda

A series of Sr2+ doped perovskite like oxides La2-xSrxCuO4-lambda (x = 0 similar to 1) were prepared, the structure, lattice parameters, content of Cu3+, oxygen vacancies created by Sr2+ substitution and composition of these complex oxides were studied by XRD and iodic titration method. The redox ability,active oxygen species and surface image were evaluated and analyzed with TPD, TG, XPS and SEM measurements. The catalytic activity for ammonia oxidation over these oxides was tested, and the relationship among the catalytic properties, structure, nonstoichiometric oxygen,redox ability and surface behavior were correlated and some information on the mechanism of ammonia oxidation was obtained.

Comparative study of Nickel-based perovskite-like mixed oxide catalysts for direct decomposition of NO

The mixed oxides LaNiO3, La0.1Sr0.9NiO3, La2NiO4 and LaSrNiO4 were prepared and used as catalysts for the direct decomposition of NO. The catalysts were characterized by means of XRD, XPS, O-2-TPD, NO-TPD and chemical analysis. By comparing the physico-chemical properties and catalytic activity for NO decomposition, a conclusion could be drawn as follows. The direct decomposition of NO over perovskite and related mixed oxide catalysts follows a redox mechanism. The lower valent metal ions Ni2+ and disordered oxygen vacancies seem to be the active sites in the redox process. The oxygen vacancy plays an important role favorable for the adsorption and activation of NO molecules on one hand and on the other hand for increasing the mobility of lattice oxygen which is beneficial to the reproduction of active sites. The presence of oxygen vacancies is one of the indispensable factors to give the mixed oxides a steady activity for NO decomposition.

Studies on the adsorption property of NO on the Ni-based mixed oxide catalysts with Perovskite-like (ABO(3) and A(2)BO(4)) structure

The mixed oxides LaNiO3, La0.1Sr0.9NiO3, La2NiO4 and LaSrNiO4 with perovskite (ABO(3)) and related(A(2)BO(4)) structures were prepared and the adsorption property for NO and the catalytic activity for NO decomposition over these oxidse were also tested. The catalysts were characterized by means of BET surface measurement, chemical analysis, NO-TPD etc.. It was shown that the adsorption amount of NO is correlated with the concentration of oxygen vacancy formed and the adsorption type and strength of NO are related to the valence of metallic ion. Generally there are three kinds of adsorption species, NO-, NO+ and NO on the mixed oxides, among them the negative adsorpion species (NO-) are active for NO decomposition. The weaker the adsorption of oxygen on the catalyst is, the faster the mobility of oxygen is and the easier the redox process takes place in reproducing the active sites in which the oxygen species (O-, O2-) would participate.

ELECTRON-TRANSFER BETWEEN EU AND TB IN COMPLEX FLUORIDES

Europium (II) and europium (III) have been observed in MMgF(4):xEu, yTb (M=Ca, Sr, Ba) phosphors using their typical photoluminescence spectra when are synthesized in Ar or an Ar/H-2 stream. The valence state of Eu is influenced by terbium. It is notable that the intensities of the electron spin resonance peaks corresponding to Eu2+ change in a regular way when terbium ions are incorporated which can be explained by an electron transfer mechanism.