Structure and catalytic properties of magnesia-supported copper salts of molybdovanadophosphoric acid

The structure and stability of magnesia-supported copper salts of molybdovanadophosphoric acid (Cu2PMo11VO40) were characterized by different techniques. The catalyst was prepared in ethanol by impregnation because this solvent does not hurt texture of the water-sensitive MgO and Cu2PMo11VO40. The Keggin-type structure compound may be degraded partially to form oligomerized polyoxometalate when supported on MgO. However, the oligomers can rebuild as the Keggin structure again after thermal treatment in air or during the reaction. Meanwhile, the V atoms migrate out of the Keggin structure to form a lacunary structure, as observed by Fourier transform IR spectroscopy. Moreover, the presence of Cu2+ as a countercation showed an affirmative influence on the migration of V atoms, and the active sites derived from the lacunary species generated after release of V from the Keggin anion. The electron paramagnetic resonance data imply that V5+ autoreduces to V4+ in the fresh catalyst, and during the catalytic reaction a large number of V4+ ions are produced, which enhance the formation of O2- vacancies around the metal atoms. These oxygen vacancies may also improve the reoxidation function of the catalyst. This behavior is correlated to higher catalytic properties of this catalyst. The oxidative dehydrogenation of hexanol to hexanal was studied over this catalyst.

In(OH)(3) and In2O3 nanorod bundles and spheres: Microemulsion-mediated hydrothermal synthesis and luminescence properties

Indium hydroxide, In(OH)(3), nano-microstructures with two kinds of morphology, nanorod bundles (around 500 nm in length and 200 nm in diameter) and caddice spherelike agglomerates (around 750 - 1000 nm in diameter), were successfully prepared by the cetyltrimethylammonium bromide (CTAB)/water/cyclohexane/n-pentanol microemulsion-mediated hydrothermal process. Calcination of the In(OH)(3) crystals with different morphologies (nanorod bundles and spheres) at 600 degrees C in air yielded In2O3 crystals with the same morphology. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and photoluminescence (PL) spectra as well as kinetic decays were used to characterize the samples. The pH values of microemulsion play an important role in the morphological control of the as-formed In(OH)(3) nano-microstructures from the hydrothermal process. The formation mechanisms for the In( OH) 3 nano- microstructures have been proposed on an aggregation mechanism. In2O3 nanorod bundles and spheres show a similar blue emission peaking around 416 and 439 nm under the 383-nm UV excitation, which is mainly attributed to the oxygen vacancies in the In2O3 nano-microstructures.

Low temperature preparation of ceria solid solutions doubly doped with rare-earth and alkali-earth and their properties as solid oxide fuel cells

A series of solid electrolytes, (Ce(0.8)Ln(0.2))(1 - x)MxO2 - delta(Ln = La, Nd, Sm, Gd, M:Alkali-earth), were prepared by amorphous citrate gel method. XRD patterns indicate that a pure fluorite phase is formed at 800 degreesC. The electrical conductivity and the AC impedance spectra were measured. XPS spectra show that the oxygen vacancies increase owing to the MO doping, which results in the increase of the oxygen ionic transport number and conductivity. The performance of ceria-based solid electrolyte is improved. The effects of rare-earth and alkali-earth ions on the electricity were discussed. The open-circuit voltages and maximum power density of planar solid oxide fuel cell using (Ce0.8Sm0.2)(1 - 0.05)Ca0.05O2 - delta as electrolyte are 0.86 V and 33 mW . cm(-2), respectively.

The role of redox property of La2-x(Sr,Th)(x)CuO4 +/-lambda playing in the reaction of NO decomposition and NO reduction by CO

Two systems of mixed oxides, La2-xSrxCuO4 +/- lambda (0.0 less than or equal to x less than or equal to 1.0) and La(2-x)Tn(x)CuO(4 +/-) (lambda) (0.0 less than or equal to x less than or equal to 0.4), with K2NiF4 structure were prepared. The average valence of Cu ions and oxygen nonstoichiometry (lambda) were determined by means of chemical analysis. Meanwhile, the adsorption and activation of nitrogen monoxide (NO) and the mixture of NO + CO over the mixed oxide catalysts were studied by means of mass spectrometry temperature-programmed desorption (MS-TPD). The catalytic behaviors in the reactions of direct decomposition of NO and its reduction by CO were investigated, and were discussed in relation with average valence of Cu ions, A and the activation and adsorption of reactant molecules. It has been proposed that both reactions proceed by the redox mechanism, in which the oxygen vacancies and the lower-valent Cu ions play important roles in the individual step of the redox cycle. Oxygen vacancy is more significant for NO decomposition than for NO + CO reaction. For the NO + CO reaction, the stronger implication of the lower-valent Cu ions or oxygen vacancy depends on reaction temperature and the catalytic systems (Sr- or Th-substituted). (C) 2000 Elsevier Science B.V. All rights reserved.

Preparation, physico-chemical behavior and catalytic property for ammonia oxidation of perovskite like mixed oxides La2-xSrxCuO4-lambda

A series of Sr2+ doped perovskite like oxides La2-xSrxCuO4-lambda (x = 0 similar to 1) were prepared, the structure, lattice parameters, content of Cu3+, oxygen vacancies created by Sr2+ substitution and composition of these complex oxides were studied by XRD and iodic titration method. The redox ability,active oxygen species and surface image were evaluated and analyzed with TPD, TG, XPS and SEM measurements. The catalytic activity for ammonia oxidation over these oxides was tested, and the relationship among the catalytic properties, structure, nonstoichiometric oxygen,redox ability and surface behavior were correlated and some information on the mechanism of ammonia oxidation was obtained.

Study on the microstructure and properties of nanosized stannic oxide powders

Stannic oxide xerogel was prepared by a forced hydrolysis method using SnCl4 as the precursor. The average grain sizes of the nanosized stannic oxide powders varied with the sintering temperatures. The powders were characterized by several different physico-chemical techniques. TEM was employed for the direct observation on grain sizes, shape and state of aggregation of the particles. XRD technique was used for the determination of the crystalline structure. Microstructural parameters of average crystallite size () and mean-square root microstrain (epsilon(2)>(1/2)) for the samples were calculated from the broadened values of the half-peak intensity of XRD. The atomic ratio between oxygen and tin in the surface region of the particles was estimated through the analysis of XPS. Attributing to lots of oxygen vacancies in the surface region of the nanoparticulates and the 'trapped electrons' in the vacancies, an ESR signal was observed in the sample sintered at 300 degrees C for 2 h. FTIR of the powders showed that intensity of the transverse optical mode of Sn-O stretching vibration increased with the sintering temperature while the bending vibration of O-Sn-O showed a blue shift. For Raman spectra, very important spectral characteristics such as variations of intensity and width of the bands were observed. A new Raman vibrational band located at 572 cm(-1) was identified in the samples of nanosized stannic oxide powders. Variation of these spectroscopic properties were strongly affected by grain size, shape and state of aggregation of the nanosized particulates.

Comparative study of Nickel-based perovskite-like mixed oxide catalysts for direct decomposition of NO

The mixed oxides LaNiO3, La0.1Sr0.9NiO3, La2NiO4 and LaSrNiO4 were prepared and used as catalysts for the direct decomposition of NO. The catalysts were characterized by means of XRD, XPS, O-2-TPD, NO-TPD and chemical analysis. By comparing the physico-chemical properties and catalytic activity for NO decomposition, a conclusion could be drawn as follows. The direct decomposition of NO over perovskite and related mixed oxide catalysts follows a redox mechanism. The lower valent metal ions Ni2+ and disordered oxygen vacancies seem to be the active sites in the redox process. The oxygen vacancy plays an important role favorable for the adsorption and activation of NO molecules on one hand and on the other hand for increasing the mobility of lattice oxygen which is beneficial to the reproduction of active sites. The presence of oxygen vacancies is one of the indispensable factors to give the mixed oxides a steady activity for NO decomposition.

Relationship between the structure and catalytic activity of La2-xSrxNiO4-lambda(0<=x<=1) mixed oxides for NH3 oxidation

A series of samples having the composition of La2-xSrxNiO4(0 less than or equal to x less than or equal to 1) were prepared and used as catalysts for NH3 oxidation. It was found that the La and oxygen vacancies exist in the La2-xSrxNiO4-lambda(0 less than or equal to x less than or equal to 1). The unit cell volume decreases with the increase of x. For bath c and a parameters there appeared a turning point at x = 0.5. Doping with a lower valence cation Sr2+ in the case of La2NiO4 resulted in an increase of Ni3+, consequently the formation of oxygen vacancies, the increase of reducing ability and the increase of catalytic activity. In the oxygen TPD of La2-xSrxNiO4(0 less than or equal to x less than or equal to 1) appeared three peaks, the alpha' peak at about 400K was attributed to the surplus oxygen desorption, the a peak at 700K which approaches to a maxium at x = 0.6 was attributed to the oxygen adsorbed at oxygen vacancies. The beta peak at about 1000K which depends closely on the x and favors the catalytic activity was attributed to the reduction of Ni3+. The catalytic activity of La-2-x SrxNiO4 mixed oxides in the NH3 oxidation in general could be attributed to the extent of the redox reaction: 2Ni(2+) + O-2 + V-0(..) reversible arrow 2Ni(3+) + 20(-) where V-0(..) representes the oxygen vacancies and O- the oxygen species adsorbed at the vacancies.

PREPARATION AND MICROSTRUCTURAL CHARACTERIZATION OF SURFACE-MODIFIED NANOSIZED SNO2 PARTICLES

Nanosized stannic oxide particles modified with a layer of DBS were successfully prepared through the colloidal chemical method and their microstructures were characterized. FTIR and XPS were used for the determination of the main components. It can be proved that the nanosized SnO2 particles were capped by DBS. The sizes of particle were determined by TEM and XRD. By the investigation of XPS, we can conclude that there are a lot of oxygen vacancies in the surface of the nanoparticulates. Based on this conclusion, the ESR signal of the sample can be explained.

STUDIES ON THE PEROVSKITE-TYPE MIXED CATALYSTS OF TITANIUM SYSTEM FOR OXIDATIVE COUPLING OF METHANE - THE INFLUENCE OF CALCINATION TEMPERATURE

The correlations of the calcination temperature, structure and catalytic activity for the oxidative coupling of methane on the LiLa0.5Ti0.5O2+lambda catalysts whose main phase and major active phase is Perovskite-type ternary complex oxide LaTi1-yLiyO3-lambda have been studied. The surface and bulk structures of the catalysts were characterized by means of XRD, XPS, IR, BET and so on, The results cleary indicated that the effect of calcination temperature on the activity for the oxidative coupling of methane is twofold. On one hand, it is favorable for Li+ substitution for Ti3+ to enter into the lattice of LaTiO3 and produce more oxygen vacancies in which active oxygens are formed; however, excessively high calcination temperature make the amount of Li+ substitution for Ti3+ lower, due to a little change of structure or phases for the catalyst. On the other hand, the conversion of CH4 drops because of the decrease of surface area, when the calcination temperature is raised.

STUDY ON THE NON-STIOCHIOMETRIC SNO2-X NANOCRYSTALLINE MATERIAL BY XRD, XPS AND ESR

Nonstiochiometric SnO2-x nanocrystalline material were successfully prepared through Sol-Gel process using anhydrous stannic chloride and iso-propyl alcohol. TEM observation shows that the mean diameter of the powder sintered at 700 degrees C for 2 hours is about 20 nm. By the investigation of XRD and ESR, we can conclude that the sample sintered at 300 degrees C for 2 hours was amorphous and it grew into nanocrystalline with the oxygen vacancies and defects when sintered at 700 degrees C for 2 hours. Using these conclusion, the ESR signals and the difference between the two SnO2-x samples are explained.

SOLID DEFECT STRUCTURE AND CATALYTIC ACTIVITY OF PEROVSKITE-TYPE CATALYSTS LA1-XSRXNIO3-LAMBDA AND LA1-1.333XTHXNIO3-LAMBDA

Two series of La1-xSrxNiO3-lambda and La1-1.333xThxNiO3-lambda catalysts have been prepared, and the relationships between the solid defect structure and catalytic activity for NH3 oxidation were measured. The results showed that in the range of x < 0.3, the samples possessed single perovskite-type structure, and as the content of Sr2+ decreased and that of Th4+ increased the catalytic activity increased which was paralleled with the Ni3+ concentration within the catalysts. The active oxygen species (O- or O2(2-)) were present not only on the surface but also in the bulk of the samples. The synergistic effect of transition metal ions with higher oxidation states and randomly distributed oxygen vacancies was the key factor determining catalytic activity of perovskite-type oxides. A redox mechanism for NH3 oxidation over ABO3 is proposed.

Low-temperature oxidation of CO over Pd/CeO2-TiO2 catalysts with different pretreatments

A comprehensive study of the low-temperature oxidation of CO was conducted over Pd/TiO2, Pd/CeO2, and Pd/CeO2-TiO2 pretreated by a series of calcination and reduction processes. The catalysts were characterized by N-2 adsorption, XRD, H-2 chemisorption, and diffuse-reflectance infrared Fourier transform spectroscopy. The results indicated that Pd/CeO2-TiO2 has the highest activity among these catalysts, whether in the calcined state or in the reduced state. The activity of all of the catalysts can be improved significantly by the pre-reduction, and it seems that the reduction at low temperature (LTR. 150 degrees C) is more effective than that at high temperature (HTR, 500 degrees C), especially for Pd/CeO2 and Pd/TiO2. The catalysts with various supports and pretreatments are also different in the reaction mechanisms for CO oxidation at low temperature. Over Pd/TiO2, the reaction may proceed through a surface reaction between the weakly adsorbed CO and oxygen (Langmuir-Hinshelwood). For Ce-containing catalysts, however, an alteration of reaction mechanism with temperature and the involvement of the oxygen activation at different sites were observed, and the light-off profiles of the calcined Pd/CeO2 and Pd/CeOi-TiO2 show a distortion before CO conversion achieves 100%. At low temperature, CO oxidation proceeds mainly via the reaction between the adsorbed CO on Pd-0 sites and the lattice oxygen of surface CeO2 at the Pd-Ce interface, whereas at high temperature it proceeds via the reaction between the adsorbed CO and oxygen. The high activity of Pd/CeO2-TiO2 for the low-temperature CO oxidation was probably due to the enhancements of both CO activation, caused by the facilitated reduction of Pd2+ to Pd-0, and oxygen activation, through the improvement of the surface oxygen supply and the oxygen vacancies formation. The reduction pretreatment enhances metal-support interactions and oxygen vacancy formation and hence improves the activity of CO oxidation. (c) 2005 Elsevier Inc. All rights reserved.

Reactivity of sub 1 nm supported clusters: (TiO2)(n) clusters supported on rutile TiO2 (110)

Metal oxide clusters of sub-nm dimensions dispersed on a metal oxide support are an important class of catalytic materials for a number of key chemical reactions, showing enhanced reactivity over the corresponding bulk oxide. In this paper we present the results of a density functional theory study of small sub-nm TiO2 clusters, Ti2O4, Ti3O6 and Ti4O8 supported on the rutile (110) surface. We find that all three clusters adsorb strongly with adsorption energies ranging from -3 eV to -4.5 eV. The more stable adsorption structures show a larger number of new Ti-O bonds formed between the cluster and the surface. These new bonds increase the coordination of cluster Ti and O as well as surface oxygen, so that each has more neighbours. The electronic structure shows that the top of the valence band is made up of cluster derived states, while the conduction band is made up of Ti 3d states from the surface, resulting in a reduction of the effective band gap and spatial separation of electrons and holes after photon absorption, which shows their potential utility in photocatalysis. To examine reactivity, we study the formation of oxygen vacancies in the cluster-support system. The most stable oxygen vacancy sites on the cluster show formation energies that are significantly lower than in bulk TiO2, demonstrating the usefulness of this composite system for redox catalysis.

SrTiO3(001)(2x1) reconstructions: First-principles calculations of surface energy and atomic structure compared with scanning tunneling microscopy images

(1x1) and (2x1) reconstructions of the (001) SrTiO3 surface were studied using the first-principles full-potential linear muffin-tin orbital method. Surface energies were calculated as a function of TiO2 chemical potential, oxygen partial pressure and temperature. The (1x1) unreconstructed surfaces were found to be energetically stable for many of the conditions considered. Under conditions of very low oxygen partial pressure the (2x1) Ti2O3 reconstruction [Martin R. Castell, Surf. Sci. 505, 1 (2002)] is stable. The question as to why STM images of the (1x1) surfaces have not been obtained was addressed by calculating charge densities for each surface. These suggest that the (2x1) reconstructions would be easier to image than the (1x1) surfaces. The possibility that the presence of oxygen vacancies would destabilise the (1x1) surfaces was also investigated. If the (1x1) surfaces are unstable then there exists the further possibility that the (2x1) DL-TiO2 reconstruction [Natasha Erdman Nature (London) 419, 55 (2002)] is stable in a TiO2-rich environment and for p(O2)>10(-18) atm.