Evaluation of degree of conversion and hardness of dental composites photoactivated with different light guide tips

Objective: The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Methods: Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm-1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm-1. The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey's test, with a significance level set at 5%. Results: The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). Conclusions: The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness.

Effect of Beverages and Mouthwashes on the Hardness of Polymers Used in Intraoral Prostheses

PurposeThe mechanical properties of acrylic resins used in intraoral prostheses may be altered by frequent exposure to liquids such as beverages and mouthwashes. This study aimed to evaluate the effect of thermocycling and liquid immersion on the hardness of four brands of acrylic resins commonly used in removable prostheses (Onda Cryl, QC-20, Classico, Lucitone).Materials and MethodsFor each brand of resin, seven specimens were immersed in each of six solutions (coffee, cola, red wine, Plax-Colgate, Listerine [LI], Oral B), and seven more were placed in artificial saliva (control). The hardness was tested using a microhardness tester before and after 5000 thermocycles and after 1, 3, 24, 48, and 96 hours of immersion. The results were analyzed using three-way repeated-measures ANOVA and Tukey's test (p < 0.05).ResultsThe hardness of the resins decreased following thermocycling and immersion in the solutions. Specimens immersed in cola and wine exhibited significant decreases in hardness after immersion for 96 hours, although the greatest significant decrease in hardness occurred in specimens immersed in LI. However, according to American Dental Association specification 12, the Knoop hardness of acrylic resins for intraoral prostheses should not be below 15. Thus, the median values of superficial hardness observed in most of the acrylic resins in this study are considered clinically acceptable.ConclusionsThe microhardness of polymers used for intraoral prostheses decreases following thermocycling. Among specimens immersed in beverages, those immersed in cola or wine experienced the greatest decrease in microhardness. Immersion of acrylic resins in LI significantly decreased the microhardness in relation to the initial value. Among the resins assessed, QC-20 exhibited the lowest initial hardness.

Influence of heat treatment and mechanical cycling on hardness and fracture analysis of Ti35Nb5Zr casting alloy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of different light-curing techniques on hardness of a microhybrid dental composite resin

Coordenação de Aperfeicoamento de Pessoal de Nivel Superior (CAPES)

Influence of light source and immersion media in surface roughness and hardness of a nanofilled composite resin

The study evaluated the influence of light curing units and immersion media on superficial roughness and microhardness of the nanofilled composite resin Supreme XT (3M/ESPE). Light curing units used were: XL 3000 (3M/ESPE), Jet Lite 4000 Plus (JMorita) and Ultralume Led 5 (Ultradent) and immersion media were artificial saliva, Coke®, tea and coffee, totaling 12 experimental groups. Specimens (10mm x 2mm) were immersed in each respective solution for 5 seconds, three times a day, during 60 days and so, were submitted to measure of superficial roughness (Ra) and Vickers hardness. Data were subjected to two-way ANOVA test (p<0.05). Results showed that only the light source factor showed statistically difference for hardness. It was observed that the hardness of the composite resin Filtek Supreme XT (3M/ESPE) was influenced by the light source (p<0.01) independently of the immersion media (p= 0.35) and the Jet Lite 4000 Plus (JMorita) was the light curing unit that presented lower values. In relation to surface roughness, it was noted no-significant statistical difference for light source (p=0.84), when specimens were immersed in different beverages (p=0.35).

Effect of thermal and mechanical cycles on the hardness and roughness of artificial teeth

In this study the effects of thermal and mechanical cycles on the hardness and roughness of artificial teeth were evaluated. Materials and Methods:Specimens were prepared and stored in distilled water at 37ºC for 48 hours (n=10).The hardness and roughness readings were made in the following time intervals, according to each group:G1: after specimen storage in distilled water at 37°C for 48 hours; G2: after 600.000 constant mechanical cycles; G3: after 1.200.000 constant mechanical cycles; G4: after 2.500 thermalcycling baths, alternated between hot water (55°C) and cold water (5°C) and G5: after 5.000 thermalcycling baths, alternated between hot water (55°C) and cold water (5°C). After cycling and storage procedures, the specimens of each group were submittedto surface roughness and hardness readouts. Statistical evaluation was performed by three-way analysis of variance, complemented by the Tukey multiple comparisons of means test. The level of significance adopted was 5%. There was no significant difference between G1, G4 and G5 as regards mean roughness of different brands of artificial teeth. Groups G2 and G3 showed higher mean roughness values, and generally equivalent values in all time intervals, except for Trilux (G3> G2). Significant differences in hardness values were observed in different brands of artificial teeth, and differences in values after thermal and mechanical cycling. In conclusion, our findings suggest that thermal cyclingdid not change the roughness of the artificial teeth tested, but after the mechanical cycling the roughness values increased. Thermal and mechanical cycling influenced the hardness of the artificial teeth tested.

Surface roughness and hardness of yttria stabilized zirconia (Y-TZP) after 10 years of simulated brushing

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of the Atibaia River water quality using Lecane bulla as a test organism

In view of the diversity of environments found in the Brazilian territory, it is understandable that the use of native species can provide more relevant information for ecotoxicological studies. The purpose of this work was to evaluate the quality of water samples from the Atibaia River in an area that is under the influence of petroleum refinery using a native test-organism and submitting the data to PCA statistical analysis. Therefore, acute toxicity assays with Lecane bulla (Rotifera) were performed in four locations of the river, as well as physical-chemical analyses. Sampling was drawn in the dry and rainy seasons. The bioassays were static and lasted 48 hours; dead organisms were quantified at the end of the tests. Toxicological differences among the samples/per location and control were compared by means of the Analysis of Variance. Physical-chemical and mortality variables were simultaneously analyzed by multivariate analysis of the principal components and the Pearson correlation coefficient. Water samples from the exit of the refinery stabilization pond (location S.1) were toxic to L. bulla in both seasons, with significant differences in relation to the control and between the seasons. The statistical treatment of data showed that mortality was strong and positively correlated with total hardness, chlorides and EC, which together with pH presented higher values in location S.1, in the dry and in the rainy seasons. Due to its sensibility to the quality of the Atibaia river water samples, the potential use of L. bulla for ecotoxicological studies as an alternative test organism could be demonstrated.

Effect of the addition of antimicrobial agents on shore a hardness and roughness of soft lining materials

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of short-term immersion and brushing with different denture cleansers on the roughness, hardness, and color of two types of acrylic resin

Purpose: To investigate the cumulative effects of brushing (B) or immersion (I), using different cleansing agents, on the surface roughness, hardness and color stability of a heat-polymerized denture resin, Lucitone 550 (L), and a hard chairside reline resin, Tokuyama Rebase Fast II (T). Methods: A total of 316 specimens (10 x 2 mm) were fabricated. The specimens (n= 9) were divided into brushing or immersion groups according to the following agents: dentifrice/distilled water (D), 1% sodium hypochlorite (Na0C1), Corega Tabs (Pb), 1% chlorhexidine gluconate (Chx), and 0.2% peracetic acid (Ac). Brushing and immersion were tested independently. Assays were performed after 1, 3, 21, 45 and 90 blushing cycles or immersion of 10 seconds each. Data were evaluated statistically by repeated measures ANOVA. Tukey's honestly significant difference (HSD) post-hoc test was used to determine differences between means (a= 0.05). Results: For L there was no statistically significant difference in roughness, except a significant decrease in roughness by brushing with D. T showed a significant effect on the roughness after 90 immersions with Ac. Hardness values decreased for L when specimens were immersed or brushed in Na0C1 and Pb. The hardness of T decreased with increases in the repetitions (immersion or brushing), regardless of the cleaning method. Values of color stability for L resin showed significant color change after brushing with and immersion in Ac and Pb. Brushing with D exhibited a higher incidence of color change. For T there were no significant differences between cleaning agents and repetitions in immersion. A color change was noted after three brushings with the Ac, Chx, and D. Brushing with dentifrice decreased roughness of L. Immersion in or brushing with Na0C1 and Pb decreased the hardness of L. For T, hardness decreased with increases in immersions or brushing. Color changes after the immersion in or brushing with cleaning agents were clinically acceptable according to National Bureau of Standards parameters for both resins.

Effect of different solutions on knoop hardness of indirect composite

Introduction: Indirect dental composites may have adequate clinical performance. However, the literature is scarce regarding indirect composite resins and these solutions should be considered to maintain their properties. The aim of the study was to evaluate the influence of beverages, mouthwashes and bleaching agents on the hardness of indirect composite resins. Methods: Five different brands of indirect composite resins were evaluated: Adoro, Resilab, Cristobal, Sinfony and Epricord. Ten specimens of each brand were immersed in eleven different solutions: four mouthwashes (Listerine, Oral-B, Plax, Periogard), four beverages (coke soft drink, red wine, coffee, orange juice), three dental bleaching agents (16% peroxide of carbamide, 7.5% and 38% peroxide of hydrogen) and artificial saliva (control group). The Knoop hardness was measured before (baseline) and after 12, 24, 36 and 60 hours of immersion in mouthwashes; after 7, 14 and 21 days of immersion in beverages and after 7 and 14 days of immersion in dental bleaching agents. The results were analyzed using 3-way repeated measures ANOVA and Tukey’s test (p<0.05). Results: All resins presented significant decrease on hardness values after immersion process whereas this reduction was higher for Resilab and Sinfony. The latter exhibited the lowest initial values of hardness while Cristobol resin presented the highest hardness values. The mouthwashes promoted a significant decrease in the hardness of specimens.

Effect of different light sources on degree of conversion, hardness and plasticization of a composite

Clinical performance of composite resins depends largely on their mechanical properties,and those are influenced by several factors,such as the light-curing mode. The purpose of this study was to evaluate the influence of different light sources on degree of conversion(DC), Knoop hardness(KHN) and plasticization(P) of a composite resin. Disc-shaped specimens (5 x 2 mm) of Esthet-X(Dentsply) methacrylate-based microhybrid composite were light-cured using quartz-tungsten-halogen (QTH) Optilight Plus(Gnatus) or light-emitting diode(LED) Ultraled(Dabi Atlante) curing units at 400 and 340 mW/cm2 of irradiance, respectively. After 24 h, absorption spectra of composite were obtained using Nexus 670(Nicolet)FT-IR spectrometer in order to calculate the DC.The KHN was measured in the HMV-2000(Shimadzu) microhardness tester under 50 g loads for 15 s, and P was evaluated by percentage reductio of hardness after 24 h of alcohol storage. Data were subjected to t-Student test(alpha=0.05).QTH device showed lower P and higher KHN$ than LED (p<0.05), and no difference between the light-curing units was found for DC (p>0.05). The halogen-curing unit with higher irradiance promoted higher KHN and lower softening in alcohol than LED.

Effects of curing protocol and storage time on the micro-hardness of resin cements used to lute fiber-reinforced resin posts

Objectives: To determine the micro-hardness profile of two dual cure resin cements (RelyX - U100 (R), 3M-ESPE and Panavia F 2.0 (R), Kuraray) used for cementing fiber-reinforced resin posts (Fibrekor (R) - Jeneric Pentron) under three different curing protocols and two water storage times. Material and methods: Sixty 16mm long bovine incisor roots were endodontically treated and prepared for cementation of the Fibrekor posts. The cements were mixed as instructed, dispensed in the canal, the posts were seated and the curing performed as follows: a) no light activation; b) light-activation immediately after seating the post, and; c) light-activation delayed 5 minutes after seating the post. The teeth were stored in water and retrieved for analysis after 7 days and 3 months. The roots were longitudinally sectioned and the microhardness was determined at the cervical, middle and apical regions along the cement line. The data was analyzed by the three-way ANOVA test (curing mode, storage time and thirds) for each cement. The Tukey test was used for the post-hoc analysis. Results: Light-activation resulted in a significant increase in the microhardness. This was more evident for the cervical region and for the Panavia cement. Storage in water for 3 months caused a reduction of the micro-hardness for both cements. The U100 cement showed less variation in the micro-hardness regardless of the curing protocol and storage time. Conclusions: The micro-hardness of the cements was affected by the curing and storage variables and were material-dependent.

Evaluation of Vickers hardness of different types of acrylic denture base resins with and without glass fibre reinforcement

Objective: To evaluate the Vickers hardness of different acrylic resins for denture bases with and without the addition of glass fibres. Background: It has been suggested that different polymerisation methods, as well as the addition of glass fibre (FV) might improve the hardness of acrylic. Materials and methods: Five types of acrylic resin were tested: Vipi Wave (VW), microwave polymerisation; Vipi Flash (VF), auto-polymerisation; Lucitone (LT), QC20 (QC) and Vipi Cril (VC), conventional heat-polymerisation, all with or without glass fibre reinforcement (GFR) and distributed into 10 groups (n = 12). Specimens were then submitted to Vickers hardness testing with a 25-g load for 30 s. All data were submitted to ANOVA and Tukey's HSD test. Results: A significant statistical difference was observed with regard to the polymerisation method and the GFR (p < 0.05). Without the GFR, the acrylic resin VC presented the highest hardness values, and VF and LT presented the lowest. In the presence of GFR, VC resin still presented the highest Vickers hardness values, and VF and QC presented the lowest. Conclusions: The acrylic resin VC and VW presented higher hardness values than VF and QC resins. Moreover, GFR increased the Vickers hardness of resins VW, VC and LT.

Influence of ultrasound or halogen light on microleakage and hardness of enamel adjacent to glass ionomer cement

Background. The use of external sources of energy may accelerate the setting rate of glass ionomer cements (GICs) allowing better initial mechanical properties. Aim. To investigate the influence of ultrasound and halogen light on the microleakage and hardness of enamel adjacent to GIC restorations, after artificial caries challenge. Design. Cavities were prepared in 60 primary canines, restored with GIC, and randomly distributed into three groups: control group (CG), light group (LG) - irradiation with a halogen lightcuring unit for 60 s, and ultrasonic group (UG) application of ultrasonic scaler device for 15 s. All specimens were then submitted to a cariogenic challenge in a pH cycling model. Half of sample in each group were immersed in methylene blue for 4 h and sectioned for dye penetration analysis. The remaining specimens were submitted to Knoop cross-sectional microhardness assessments, and mineral changes were calculated for adjacent enamel. Results. Data were compared using Kruskal-Wallis test and two- way ANOVA with 5% significance. Higher dye penetration was observed for the UG (P < 0.01). No significant mineral changes were observed between groups (P = 0.844). Conclusion. The use of halogen light- curing unit does not seem to interfere with the properties of GICs, whereas the use of ultrasound can affect its marginal sealing.