Influence of Remineralizing Gels on Bleached Enamel Microhardness In Different Time Intervals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of surfactants on the effectiveness of bleaching gels

This study evaluated the influence of surfactants on the effectiveness of 35% hydrogen peroxide (HP) and 10% carbamide peroxide (CP) bleaching gels. One hundred and forty bovine teeth were used, which were stained by immersion in a coffee, red wine, and tobacco mixture for 7 days. At the end of this process, the color measurement at baseline was taken with the Vita Easyshade spectrophotometer. The teeth were divided into seven groups: (a) negative control (NC), (b) positive control for HP (PC-35), (c) HP + Tween 20 (T20-35), (d) HP + laurel sodium sulfate (LSS-35), (e) positive control for CP (PC-10), (f) CP + Tween 20 (T20-10), and (g) CP + laurel sodium sulfate (LSS-10). Group NC was kept in artificial saliva for 21 days. Groups PC-35, T20-35, and LSS 35 received three applications of bleaching gel for 10 min; the process was repeated after 7 days. Groups PC-10, T20-10, and LSS-10 received the gel for 8 h per day for 14 days. After the bleaching process, the final color was measured. The analysis of variance and Tukey tests showed statistically significant differences for the parameters of a dagger L, a dagger b, and a dagger E of the HP gels with surfactant and positive control group (PC-35). Within the limits of this in vitro study, the addition of surfactants to HP bleaching gel increased the bleaching effectiveness.

Microhardness change of enamel due to bleaching with in-office bleaching gels of different acidity

Objective. The aim of this study was to assess the enamel microhardness treated with three in-office bleaching agents, containing 35% hydrogen peroxide with different acidity. Materials and methods. Bovine incisors were divided into three groups that received the following bleaching agents: Whiteness HP, Total Bleach and Opalescence Xtra. Three gel applications/10-min each, totaling 30-min of bleaching treatment, were made on the teeth and activated with a blue LED (1000 mW/470 nm) combined to a LASER (120 mW/795 nm) device (Easy Bleach-Clean Line). Vickers hardness (VH) was evaluated at baseline and after the bleaching procedure. The values of Hardness loss [HNL] (% reduction) were calculated. The two-sample t-test was used for comparison of the HNL of the three bleaching products (5% level of significance). Results. The Opalescence Xtra, which had the lowest pH value (pH = 4.30), showed a significant increase of HNL when compared with Total Bleach bleaching agent, which had the highest pH value (pH = 6.62). Conclusions. The 35% hydrogen peroxide bleaching agents resulted in a reduction in surface enamel microhardness and bleaching with the most acid agent resulted in a significant enamel hardness loss compared to the less acid agent (4.30 vs 6.62). Strategies proposed to reduce the enamel loss after bleaching treatment may include the use of daily fluoride therapy, mouth rinsing (fluoride, milk and sodium bicarbonate solution), fluoride/bicarbonate dentifrices without abrasives, do not toothbrush immediately after bleaching, fluorides and calcium add to bleaching agents.

Fractal character of the SAXS correlation volume in poly(ethylene glycol)/silica hybrid wet gels

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Modifications in the correlation function in poly(vinyl alcohol)/silica hybrid wet gels

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Small-angle X-ray scattering from wet gels prepared from co-hydrolysis of tetraethoxysilane and vinyltriethoxysilane

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural characteristics of gels prepared from sonohydrolysis and conventional hydrolysis of TEOS: an emphasis on the mass fractal as determined from the pore size distribution

Silica gels were preparated from fixed proportion mixtures of tetraethoxysilane, water and hydrocloric acid, using either ultrasound stimulation (US) or conventional method (CO) in the hydrolysis step of the process. Wet gets were obtained with the same silica volume concentration and density. According to small-angle X-ray scattering, the structure of the wet gels can be described as mass fractal structures with mass fractal dimension D = 2.20 in a length scale xi = 7.9 nm, in the case of wet gels US, and D = 2.26 in a length scale 6.9 nm, in the case of wet gels CO. The mass fractal characteristics of the wet gels US and CO account for the different structures evolved in the drying of the gels US and CO in the obtaining of xerogels and aerogels. The pore structure of the dried gels was studied by nitrogen adsorption as a function of the temperature. Aerogels (US and CO) present high porosity with pore size distribution (PSD) curves in the mesopore region while xerogels (US and CO) present minor porosity with PSD curves mainly in the micropore region. The dried gels US (aerogels and xerogels) generally present pore volume and specific surface area greater than the dried gels CO. The mass fractal structure of the aerogels has been studied from an approach based on the PSD curves exclusively. (c) 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis and some properties of hybrid gels of titanium oxide containing europium (III)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural properties of silica gels prepared from oxalic-acid-catalyzed tetraethoxysilane sonohydrolysis

About similar to 2.1 x 10(-3) Mol SiO2 cm(-3) and similar to 88%-volume liquid-phase silica wet gels were prepared from oxalic-acid-catalyzed tetraethoxysilane (TEOS) sonohydrolysis. Aerogels were obtained by supercritical CO2 extraction. The samples were analyzed by thermogravimetry, small-angle X-ray scattering and nitrogen adsorption. Wet gels can be described as mass fractal structures with fractal dimension D similar to 1.94 and structural characteristic length zeta changing between similar to 3.3 to similar to 3.0 nm in the studied range of the catalyst concentration. A fraction of the porosity is apparently eliminated in the supercritical process. The values of the BET specific surface S-BET, the total pore volume V-p and the mean pore size l(p) of the aerogels were found to change almost randomly around the mean values S-BET = 874 m(2) g(-1), V-p = 0.961 cm(3) g(-1) and l(p) = 4.4 nm with catalyst concentration variation. These values were not substantially different from those from an equivalent HCl-catalyzed aerogel. (c) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Rheological Characterization of Hydrophylic Gels

Rheological characteristics of gels were studied, with the focus on their use as a cosmetic base. Some ideal characteristics can be predicted by the rheological characterization, such as the performance, with easy application and without dripping or forming lumps and bubbles. Moreover, it is possible to detect signs of physical instability. The gels were prepared with sodium carboxymethyl cellulose 3% and 5%, with Carbopol 940 (INCI: Carbomer) and with Carbopol Ultrez (INCI: Acrylates/C10-30 alkyl acrylate crosspolymer). The tests performed were yield stress, stress sweep and creep and recovery. The gel with 3% of sodium carboxymethyl cellulose presented the most appropriated behavior and can be indicated as the most suitable cosmetic base.

Influence of Hydrogen Peroxide Bleaching Gels on Color, Opacity, and Fluorescence of Composite Resins

The aim of the present study was to evaluate the effect of 20% and 35% hydrogen peroxide bleaching gels on the color, opacity, and fluorescence of composite resins. Seven composite resin brands were tested and 30 specimens, 3-mm in diameter and 2-mm thick, of each material were fabricated, for a total of 210 specimens. The specimens of each tested material were divided into three subgroups (n=10) according to the bleaching therapy tested: 20% hydrogen peroxide gel, 35% hydroxide peroxide gel, and the control group. The baseline color, opacity, and fluorescence were assessed by spectrophotometry. Four 30-minute bleaching gel applications, two hours in total, were performed. The control group did not receive bleaching treatment and was stored in deionized water. Final assessments were performed, and data were analyzed by two-way analysis of variance and Tukey tests (p<0.05). Color changes were significant for different tested bleaching therapies (p<0.0001), with the greatest color change observed for 35% hydrogen peroxide gel. No difference in opacity was detected for all analyzed parameters. Fluorescence changes were influenced by composite resin brand (p<0.0001) and bleaching therapy (p=0.0016) used. No significant differences in fluorescence between different bleaching gel concentrations were detected by Tukey test. The greatest fluorescence alteration was detected on the brand Z350. It was concluded that 35% hydrogen peroxide bleaching gel generated the greatest color change among all evaluated materials. No statistical opacity changes were detected for all tested variables, and significant fluorescence changes were dependent on the material and bleaching therapy, regardless of the gel concentration.

Formation of SnO2 gels from dispersed sols in aqueous colloidal solutions

Transparent SnO2 gels were obtained from SnCl4 aqueous solution. The sol formation from tin oxihydroxy peptization in different concentrations and by electrolyte addition in solution was measured. It was verified that the residual presence of chloride ions compromises the colloidal system stability. The sol-gel transition was investigated as a function of the quantity of solid particles in the aqueous environment and of aging time at 60°C by infrared spectroscopy and rheological measurements. The transition from plastic to pseudoplastic flow observed with the increase in loading suggests that a continuous and three-dimensional network formation is closely related to hydrogen bridges and/or hydrogen clusters, culminating in the gel formation. © 1990.

Study of SnO2 gels by Eu3+ fluorescence spectroscopy

Eu3+ fluorescence spectroscopy was used as a probe to study the changes in local arrangements of tin oxyhydroxide precipitate → sol → gel → glass conversion. Electronic transition intensities and 5D0 excited state lifetime variations were followed during the entire process. Adsorption of Eu3+ ions on the colloid and changes of chemical interactions occurring in each step are described. © 1992 Elsevier Science Publishers B.V. All rights reserved.