Screening of CO2 Laser (10.6 mu m) Parameters for Prevention of Enamel Erosion

Objective: The aim of this study was to screen CO2 laser (10.6 mu m) parameters to increase enamel resistance to a continuous-flow erosive challenge. Background data: A new clinical CO2 laser providing pulses of hundreds of microseconds, a range known to increase tooth acid-resistance, has been introduced in the market. Methods: Different laser parameters were tested in 12 groups (n = 20) with varying fluences from 0.1 to 0.9 J/cm(2), pulse durations from 80 to 400 mu s and repetition rates from 180 to 700 Hz. Non-lased samples (n = 30) served as controls. All samples were eroded by exposure to hydrochloric acid (pH 2.6) under continuous acid flow (60 mu L/min). Calcium and phosphate release into acid was monitored colorimetrically at 30 sec intervals up to 5 min and at 1 min intervals up to a total erosion time of 15 min. Scanning electron microscopic (SEM) analysis was performed in lased samples (n = 3). Data were statistically analysed by one-way ANOVA (p < 0.05) and Dunnett's post-hoc tests. Results: Calcium and phosphate release were significantly reduced by a maximum of 20% over time in samples irradiated with 0.4 J/cm(2) (200 mu s) at 450 Hz. Short-time reduction of calcium loss (<= 1.5 min) could be also achieved by irradiation with 0.7 J/cm(2) (300 mu s) at 200 and 300 Hz. Both parameters revealed surface modification. Conclusions: A set of CO2 laser parameters was found that could significantly reduce enamel mineral loss (20%) under in vitro erosive conditions. However, as all parameters also caused surface cracking, they are not recommended for clinical use.

Properties of dental resins submitted to pH catalysed hydrolysis

Objectives: This study evaluated the surface microhardness (SM) and roughness (SR) alterations of dental resins submitted to pH catalysed degradation regimens. Methods: Thirty discs of each TPH Spectrum (Dentsply), Z100 (3M-ESPE), or an unfilled experimental bis-GMA/TEGDMA resin were fabricated, totaling 90 specimens. Each specimen was polymerized for 40 s, finished, polished, and individually stored in deionized water at 37 degrees C for 7 days. Specimens were randomly assigned to the following pH solutions: 1.0, 6.9 or 13, and for SM or SR evaluations (n = 5). Baseline Knoop-hardness of each specimen was obtained by the arithmetic mean of five random micro-indentations. For SR, mean baseline values were obtained by five random surface tracings (R-a). Specimens were then soaked in one of the following storage media at 37 degrees C: (1) 0.1 M, pH 1.0 HCl, (2) 0.1 N, pH 13.0 NaOCl, and (3) deionized water (pH 6.9). Solutions were replaced daily. Repeated SM and SR measurements were performed at the 3-, 7- and 14-day storage time intervals. For each test and resin, data were analysed by two-way ANOVA followed by Tukey's test (alpha = 0.05). Results: There was significant decrease in SM and increase in SR values of composites after storage in alkaline medium. TPH and Z100 presented similar behaviour for SM and SR after immersion in the different media, whereas unfilled resin values showed no significant change. Conclusion: Hydrolytic degradation of resin composites seems to begin with the silanized inorganic particles and therefore depend on their composition. Significance: To accelerate composite hydrolysis and produce quick in vitro microstructural damage, alkaline medium appears to be more suitable than acidic medium. Contemporary resin composite properties seem to withstand neutral and acidic oral environments tolerably well. (C) 2012 Elsevier Ltd. All rights reserved.

Impact of different fluoride concentrations and pH of dentifrices on tooth erosion/abrasion in vitro

Background: This in vitro study analysed the effect of different fluoride concentrations in acidic or neutral liquid dentifrices in protecting enamel and dentine from erosive and abrasive wear. Methods: Bovine enamel and dentine specimens (n = 132) were randomly allocated to 11 groups (each n = 12): experimental liquid dentifrices with 550 ppm F, 1100 ppm F, 5000 ppm F or 0 ppm F/placebo (each at pH 4.5 and pH 7.0); and commercial dentifrices with 550 ppm F (Colgate Baby, pH 7.0), 1100 ppm F (Crest, pH 7.0) and 5000 ppm F (Duraphat, pH 7.0). The specimens were subjected to erosion for 90 seconds, 4 times/day, over 7 days. Immediately after the first and last erosion, the specimens were brushed for 15 seconds using one of the dentifrices. Tooth wear was measured profilometrically (lm) and analysed by ANOVA (p < 0.05). Results: All fluoridated liquid dentifrices significantly reduced enamel wear compared to the placebo and commercial dentifrices. Only liquid dentifrices with 1100 and 5000 ppm F significantly reduced dentine wear compared to placebo dentifrice. The pH had no effect, but the consistency had a significant impact on the effect of dentifrices. Conclusions: Liquid dentifrices with high F concentration appear to be a good option to prevent tooth wear

Effect of beverages on bovine dental enamel subjected to erosive challenge with hydrochloric acid

This study evaluated by an in vitro model the effect of beverages on dental enamel previously subjected to erosive challenge with hydrochloric acid. The factor under study was the type of beverage, in five levels: Sprite® Zero Low-calorie Soda Lime (positive control), Parmalat® ultra high temperature (UHT) milk, Ades® Original soymilk, Leão® Ice Tea Zero ready-to-drink low-calorie peach-flavored black teaand Prata® natural mineral water (negative control). Seventy-five bovine enamel specimens were distributed among the five types of beverages (n=15), according to a randomized complete block design. For the formation of erosive wear lesions, the specimens were immersed in 10 mL aqueous solution of hydrochloric acid 0.01 M for 2 min. Subsequently, the specimens were immersed in 20 mL of the beverages for 1 min, twice daily for 2 days at room temperature. In between, the specimens were kept in 20 mL of artificial saliva at 37ºC. The response variable was the quantitative enamel microhardness. ANOVA and Tukey's test showed highly significant differences (p<0.00001) in the enamel exposed to hydrochloric acid and beverages. The soft drink caused a significantly higher decrease in microhardness compared with the other beverages. The black tea caused a significantly higher reduction in microhardness than the mineral water, UHT milk and soymilk, but lower than the soft drink. Among the analyzed beverages, the soft drink and the black tea caused the most deleterious effects on dental enamel microhardness.

Tooth wear and erosion: methodological issues in epidemiological and public health research and the future research agenda

This paper addresses methodological issues in the field of tooth wear and erosion research including the epidemiological indices, and identifies future work that is needed to improve knowledge about tooth wear and erosion.

Methods for the measurement and characterization of erosion in enamel and dentine

The advantages, limitations and potential applications of available methods for studying erosion of enamel and dentine are reviewed. Special emphasis is placed on the influence of histological differences between the dental hard tissue and the stage of the erosive lesion. No method is suitable for all stages of the lesion. Factors determining the applicability of the methods are: surface condition of the specimen, type of the experimental model, nature of the lesion, need for longitudinal measurements and type of outcome. The most suitable and most widely used methods are: chemical analyses of mineral release and enamel surface hardness for early erosion, and surface profilometry and microradiography for advanced erosion. Morphological changes in eroded dental tissue have usually been characterised by scanning electron microscopy. Novel methods have also been used, but little is known of their potential and limitations. Therefore, there is a need for their further development, evaluation, consolidation and, in particular, validation.

Effects of buffering properties and undissociated acid concentration on dissolution of dental enamel in relation to pH and acid type

To quantify the relationships between buffering properties and acid erosion and hence improve models of erosive potential of acidic drinks, a pH-stat was used to measure the rate of enamel dissolution in solutions of citric, malic and lactic acids, with pH 2.4-3.6 and with acid concentrations adjusted to give buffer capacities (β) of 2-40 (mmol·l(-1))·pH(-1) for each pH. The corresponding undissociated acid concentrations, [HA], and titratable acidity to pH 5.5 (TA5.5) were calculated. In relation to β, the dissolution rate and the strength of response to β varied with acid type (lactic > malic ≥ citric) and decreased as pH increased. The patterns of variation of the dissolution rate with TA5.5 were qualitatively similar to those for β, except that increasing pH above 2.8 had less effect on dissolution in citric and malic acids and none on dissolution in lactic acid. Variations of the dissolution rate with [HA] showed no systematic dependence on acid type but some dependence on pH. The results suggest that [HA], rather than buffering per se, is a major rate-controlling factor, probably owing to the importance of undissociated acid as a readily diffusible source of H(+) ions in maintaining near-surface dissolution within the softened layer of enamel. TA5.5 was more closely correlated with [HA] than was β, and seems to be the preferred practical measure of buffering. The relationship between [HA] and TA5.5 differs between mono- and polybasic acids, so a separate analysis of products according to predominant acid type could improve multivariate models of erosive potential.

Inhibition of enamel erosion by stannous fluoride containing rinsing solutions

This in vitro study investigated the erosion-inhibiting properties of dental rinses during erosion in the presence of the salivary pellicle. The erosion inhibition by a Sn/F containing dental rinse (800 ppm Sn2+, 500 ppm F –, pH = 4.5) was compared with a fluoridated solution (500 ppm F –, pH = 4.5) and water(control). Calcium release and enamel softening were significantly reduced among enamel samples exposed to the Sn/F rinse (group SF)compared to those treated with the fluoride solution (group F) and the control (p 0.05). SEM showed slightly etched enamel interfaces in group SF, whereas the erosion was more pronounced in group F and even more severe in the control group. In conclusion, the Sn/F combination provided the best inhibition of erosion among tested solutions. This study demonstrates the application of different analytical tools for comparative erosion quantification.A strong correlation (r2 ≥ 0.783) was shown between calcium release and enamel softening during demineralization.

Erosion in relation to nutrition and the environment.

When considering the erosive potential of a food or drink, a number of factors must be taken into account. pH is arguably the single most important parameter in determining the rate of erosive tissue dissolution. There is no clear-cut critical pH for erosion as there is for caries. At low pH, it is possible that other factors are sufficiently protective to prevent erosion, but equally erosion can progress in acid of a relatively high pH in the absence of mitigating factors. Calcium and phosphate concentration, in combination with pH, determine the degree of saturation with respect to tooth minerals. Solutions supersaturated with respect to enamel or dentine will not cause them to dissolve, meaning that given sufficient common ion concentrations erosion will not proceed, even if the pH is low. Interestingly, the addition of calcium is more effective than phosphate at reducing erosion in acid solutions. Today, several calcium-enriched soft drinks are on the market, and acidic products with high concentrations of calcium and phosphorus are available (such as yoghurt), which do not soften the dental hard tissues. The greater the buffering capacity of the drink or food, the longer it will take for the saliva to neutralize the acid. A higher buffer capacity of a drink or foodstuff will enhance the processes of dissolution because more release of ions from the tooth mineral is required to render the acid inactive for further demineralization. Temperature is also a significant physical factor; for a given acidic solution, erosion proceeds more rapidly the higher the temperature of that solution. In recent years, a number of interesting potentially erosion-reducing drink and food additives have been investigated.

The histological features and physical properties of eroded dental hard tissues.

Erosive demineralisation causes characteristic histological features. In enamel, mineral is dissolved from the surface, resulting in a roughened structure similar to an etching pattern. If the acid impact continues, the initial surface mineral loss turns into bulk tissue loss and with time a visible defect can develop. The microhardness of the remaining surface is reduced, increasing the susceptibility to physical wear. The histology of eroded dentine is much more complex because the mineral component of the tissue is dissolved by acids whereas the organic part is remaining. At least in experimental erosion, a distinct zone of demineralised organic material develops, the thickness of which depends on the acid impact. This structure is of importance for many aspects, e.g. the progression rate or the interaction with active agents and physical impacts, and needs to be considered when quantifying mineral loss. The histology of experimental erosion is increasingly well understood, but there is lack of knowledge about the histology of in vivo lesions. For enamel erosion, it is reasonable to assume that the principal features may be similar, but the fate of the demineralised dentine matrix in the oral cavity is unclear. As dentine lesions normally appear hard clinically, it can be assumed that it is degraded by the variety of enzymes present in the oral cavity. Erosive tooth wear may lead to the formation of reactionary or reparative dentine.

The future of fluorides and other protective agents in erosion prevention

The effectiveness of fluoride in caries prevention has been convincingly proven. In recent years, researchers have investigated the preventive effects of different fluoride formulations on erosive tooth wear with positive results, but their action on caries and erosion prevention must be based on different requirements, because there is no sheltered area in the erosive process as there is in the subsurface carious lesions. Thus, any protective mechanism from fluoride concerning erosion is limited to the surface or the near surface layer of enamel. However, reports on other protective agents show superior preventive results. The mechanism of action of tin-containing products is related to tin deposition onto the tooth surface, as well as the incorporation of tin into the near-surface layer of enamel. These tin-rich deposits are less susceptible to dissolution and may result in enhanced protection of the underlying tooth. Titanium tetrafluoride forms a protective layer on the tooth surface. It is believed that this layer is made up of hydrated hydrogen titanium phosphate. Products containing phosphates and/or proteins may adsorb either to the pellicle, rendering it more protective against demineralization, or directly to the dental hard tissue, probably competing with H(+) at specific sites on the tooth surface. Other substances may further enhance precipitation of calcium phosphates on the enamel surface, protecting it from additional acid impacts. Hence, the future of fluoride alone in erosion prevention looks grim, but the combination of fluoride with protective agents, such as polyvalent metal ions and some polymers, has much brighter prospects.

New insights into ancient environments using dental characters in Australian Cenozoic lungfish

Environmentally-related wear conditions and pathologies affecting the dentition of fossil lungfish from freshwater deposits in Australia have been analysed and compared with similar changes in the dentition of the living Australian lungfish, Neoceratodus forsteri. Fossil populations from the Namba, Etadunna, Wipajiri and Katipiri formations in central Australia, and the Carl Creek Limestone and the Camfield beds in northern Australia were assessed. Tooth plates from populations of living lungfish from the Brisbane River and Enoggera Reservoir in southeast Queensland were analysed for comparison. Tooth plates were measured to determine the numbers of different age groups in each population. They were assessed for abrasion, attrition, spur and step wear, erosion and caries, and for trauma and pathological conditions such as malocclusion, hyperplasia, abscesses, osteopenia and parasitic damage. All of these conditions are related to the environment where the fish lived, are found in living members of the group, and can be compared directly with those of fossil relatives. The results suggest that some of the fossil populations were at risk before climatic changes late in the Cainozoic destroyed their habitats. Some fossil lungfish populations, such as those of the Wipajiri Formation, exhibit active spawning and recruitment, good growth rates and a low incidence of disease and environmentally related damage to the tooth plates. Others, like those of the Katipiri and Namba Formations, include no young, and the adult fish were ageing and show environmentally-related damage to the dentition. Etadunna lungfish had active recruitment, but the tooth plates show a high incidence of attrition and caries. Riversleigh lungfish were actively spawning but did not grow large. Tooth plates from this latter deposit have a high incidence of pathological conditions. Fish from the Camfield Beds, where food was severely limiting, had little serious pathology but high levels of caries. Pathologies among living lungfish are common, but fossil fish were comparatively healthy, with few serious dental problems. Information from studies of fossil lungfish confirms that conservation of the few living species of lungfish depends on the maintenance of clean environments that provide adequate supplies of food and suitable sites for spawning and for the growth of young fish.

Springboards into design : exploring multiple representations of interaction in a dental surgery

This paper demonstrates that in order to understand and design for interactions in complex work environments, a variety of representational artefacts must be developed and employed. A study was undertaken to explore the design of better interaction technologies to support patient record keeping in a dental surgery. The domain chosen is a challenging real context that exhibits problems that could potentially be solved by ubiquitous computing and multi-modal interaction technologies. Both transient and durable representations were used to develop design understandings. We describe the representations, the kinds of insights developed from the representations and the way that the multiple representations interact and carry forward in the design process.

A participatory design agenda for ubiquitous computing : a case study in dental practice

This paper reflects upon our attempts to bring a participatory design approach to design research into interfaces that better support dental practice. The project brought together design researchers, general and specialist dental practitioners, the CEO of a dental software company and, to a limited extent, dental patients. We explored the potential for deployment of speech and gesture technologies in the challenging and authentic context of dental practices. The paper describes the various motivations behind the project, the negotiation of access and the development of the participant relationships as seen from the researchers' perspectives. Conducting participatory design sessions with busy professionals demands preparation, improvisation, and clarity of purpose. The paper describes how we identified what went well and when to shift tactics. The contribution of the paper is in its description of what we learned in bringing participatory design principles to a project that spanned technical research interests, commercial objectives and placing demands upon the time of skilled professionals.

Maintaining human agency in the design on context-aware systems : Design games in a dental surgery

This paper describes a series of design games, specifically aimed at exploring shifts in human agency in order to inform the design of context-aware applications. The games focused on understanding information handling issues in dental practice with participants from a university dental school playing an active role in the activities. Participatory design activities help participants to reveal potential implicit technical resources that can be presented explicitly in technologies in order to assist humans in managing their interactions with and amidst technical systems gracefully.