Blue cooperative luminescence properties in Yb3+ doped GeO2-PbO-Bi2O3 vitreous system for the production of thin films

Germanate glasses are of interest for optoelectronic applications because they combine high mechanical strength, high chemical durability and temperature stability with a large transmission window (400 to 4500 nm) and high refractive index (2.0). GeO2-PbO-Bi2O3 glasses doped with Y-b(3+) were fabricated by melting powders in a crucible and then pouring them in a brass mold. Energy Dispersive Spectroscopy showed that the glass composition has a high spatial uniformity and that the Yb concentration in the solid sample is proportional to the Yb concentration in the melt, what was confirmed by absorption measurements. Intense blue emission at 507 nm was observed, corresponding to half of the wavelength of the near infrared region (NIR) emission; besides, a decay lifetime of 0.25 ms was measured and this corresponds to half of the decay lifetime in the infrared region; these are very strong indications of the presence of blue cooperative luminescence. Larger targets have been produced to be sputtered, resulting in thin films for three dimensional (3D) display and waveguide applications. (c) 2006 Elsevier B.V. All rights reserved.

Preparation and thermal behavior of mixture of basic carbonate and 4-dimethylaminocinnamylidenepyruvate with lanthanides (III) and yttrium (III) in the solid state

Solid Ln-OKCO3-DMCP compounds, where Ln represents lanthanides (III) and yttrium (III) ions and DMCP is the anion 4-dimethyiaminocinnamylidenepyruvate, have been prepared. Thermogravimetry, derivative thermogravimetry (TG, DTG), differential scanning calorimetry (DSC), X-ray diffraction powder patterns and elemental analysis have been used to characterize the compounds. The thermal stability as well as the thermal decomposition of these compounds were studied using an alumina crucible in an air atmosphere.

Hydrodynamic aspects of the amorphous alloy ribbon fabrication

Conditions for as-quenched amorphous ribbon fabrication by a single roll-casting method are analyzed from a hydrodynamic standpoint. The analysis is based on the investigation of the processing conditions for Fe 4 0Ni 40P 14B 6 amorphous ribbons. It is shown that the dependence of ribbon thickness on the ejection pressure for different roll angular velocities and different dimensions of crucible and orifice can be obtained from general considerations on the melt flow regime.

Preparation and characterization of glass-ceramic materials in the BaO-Li2O-ZrO2-SiO2 system and their dependence on treatment temperatures

The preparation and characterization of transparent glass-ceramics in the composition of 30Li2O:5ZrO2:xBaO:(100-x) SiO2 with x = 0, 5, 10, 15, and 20 mol% are described. Glasses were melted in a platinum crucible at 1100°C for 2 h and then heat-treated at 900°C for 3 h. The characterizations were performed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman and infrared spectroscopy, and scanning electron microscopy (SEM). The experimental results indicate that there was a structural change in the glass-ceramics as the BaO concentration in the mixture increased. In the XRD patterns of samples without heat treatment, only the halo was observed. After heat treatment, the appearance of the materials was verified by X-ray diffraction peaks. The reorganization of the amorphous solid was confirmed by Raman and IR spectroscopy along with XPS and SEM, with a more homogeneous phase formation being observed.

Urbach energy parameter of flash evaporated amorphous gallium arsenide films

The dependence of the optical absorption edge on the deposition crucible temperature is used to investigate the electronic states in As-rich a-GaAs flash evaporated films. The Urbach energy parameter, determined from photothermal deflection spectroscopy (PDS), presents large correlated variations with crucible temperature. The optical and electrical results are consistent with the As under coordinated sites being the more important defect in the material. © 2002 Elsevier Science B.V. All rights reserved.

Fabrication and characterization of GeO2-PbO optical waveguides

This work presents studies of GeO2-PbO thin films deposited by RF Sputtering for fabrication of rib-waveguide. GeO2-PbO vitreous targets were prepared melting the reagents in alumina crucible. Thin films were deposited at room temperature using pure Ar plasma, at 5 mTorr pressure and RF power of 40 W on substrates of (100) silicon wafers. Rutherford Backscattering Spectroscopy (RBS) analyses were employed for the determination of the chemical elements present in the GeO2-PbO film. Geometry and sidewall of the waveguides were investigated by Scanning Electron Microscopy (SEM). The mode propagation in the waveguide structure of GeO2-PbO thin films was analyzed using an integrated optic simulation software to obtain a monomode propagation. © The Electrochemical Society.

Thermal behavior of coffee oil (Robusta and Arabica species)

Coffee seeds are a source for obtaining oil which is used in the candy, soluble coffee, and cosmetics industries. The main purpose of this study was the investigation of the lipid profile and thermal behavior of the roasted and in nature coffee oil of Arabica and Robusta species, using thermogravimetry, differential thermal analysis, derivative thermogravimetry, differential scanning calorimetry (DSC), and modulated DSC. Details concerning the thermal decomposition as well as data of the kinetic parameters have been described here. The kinetic studies were evaluated from several heating rates with a sample mass of 10 mg in open crucible under nitrogen atmospheres. The obtained data were evaluated with the isoconversional kinetic method, where the values of activation energy (Ea/kJ mol-1) were evaluated in function of the conversion degree (α). In addition, this oil was evaluated by modulated DSC from 25 to -60 °C, where the transition phase behavior was verified. © 2013 Akadémiai Kiadó, Budapest, Hungary.

Estudo da dilatometria do titânio e das expansões de presa e térmica de revestimentos fosfatados

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização térmica de sacarose de cana-de-açúcar: amostras de padrão de referência, comercial e purificada

Pós-graduação em Química - IBILCE

Síntese, caracterização e estudo do comportamento térmico dos 3-metoxibenzoatos de Mn(II), Co(II), Ni(II), Cu(II) e Zn(II), no estado sólido

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Vitrocerâmicas de alta resistência mecânica obtidas a partir da cristalização do sistema SiO2-Al2O3-MgO-Li2O com adição de ZrO2 e B2O3

Pós-graduação em Engenharia Mecânica - FEG

Preparação e estudo termoanalítico dos 4-Clorobenzalpiruvatos de lantanídeos (III) e de ítrio (III) no estado sólido

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characteristics of PbO-BiO1.5-GaO1.5 glasses melted in SnO2 crucibles

PbO-BiO 1.5-GaO 1.5-based glasses are good candidates for optical applications, because of some of their interesting characteristics, such as high refraction indices and high transmission in the ultraviolet (UV), visible (VIS), and infrared (IR) regions. A limited stage in the processing of these glasses is the corrosion that is caused by the melt in all currently used conventional crucibles, such as noble metals (platinum or gold) and Al 2O 3. The absorption of crucible material by the glass composition may reduce the transmission level, the cutoff in the UV-VIS, and IR regions, and the thermal stability. In this study, a SnO 2 crucible has been tested for PbO-BiO 1.5-GaO 1.5 molten glass. Optical and thermal analyses show, in some cases, advantages over the use of platinum and Al 2O 3 crucibles. A visible cutoff value of 474 nm has been measured, and a longer melting time (850°C for 4 h) results in a significant reduction of the O-H absorption band at 3.2 μm.

Microstructural characterization of as-cast hf-b alloys

An accurate knowledge of several metal-boron phase diagrams is important to evaluation of higher order systems such as metal-silicon-boron ternaries. The refinement and reassessment of phase diagram data is a continuous work, thus the reevaluation of metal-boron systems provides the possibility to confirm previous data from an investigation using higher purity materials and better analytical techniques. This work presents results of rigorous microstructural characterization of as-cast hafnium-boron alloys which are significant to assess the liquid composition associated to most of the invariant reactions of this system. Alloys were prepared by arc melting high purity hafnium (minimum 99.8%) and boron (minimum 99.5%) slices under argon atmosphere in water-cooled copper crucible with non consumable tungsten electrode and titanium getter. The phases were identified by scanning electron microscopy, using back-scattered electron image mode and X-ray diffraction. In general, a good agreement was found between our data and those from the currently accepted Hafnium-Boron phase diagram. The phases identified are αHfSS and B-RhomSS, the intermediate compounds HfB and HfB2 and the liquide L. The reactions are the eutectic L ⇔ αHfSS + HfB and L ⇔ HfB2 + B-Rhom, the peritectic L + HfB2 ⇔ HfB and the congruent formation of HfB2.

Preparation and characterisation of refractory whiskers and selected alumina composites

A whisker is a common name of single crystalline inorganic fibre of small dimensions, typically 0.5-1 μm in diameter and 20-50 μm in length. Whiskers are mainly used as reinforcement of ceramics. This work describes the synthesis and characterisation of new whisker types. Ti0.33Ta0.33Nb0.33CxN1-x, TiB2, B4C, and LaxCe1-xB6 have been prepared by carbothermal vapour–liquid–solid (CTR-VLS) growth mechanisms in the temperature range 900-1800°C, in argon or nitrogen. Generally, carbon and different suitable oxides were used as whisker precursors. The oxides reacted via a carbothermal reduction process. A halogenide salt was added to form gaseous metal halogenides or oxohalogenides and small amount of a transition metal was added to catalyse the whisker growth. In this mechanism, the whisker constituents are dissolved into the catalyst, in liquid phase, which becomes supersaturated. Then a whisker could nucleate and grow out under continuous feed of constituents. The syntheses of TiC, TiB2, and B4C were followed at ordinary synthesis conditions by means of mass spectrometry (MS), thermogravimetry (TG), differential thermal analysis (DTA) and quenching. The main reaction starting temperatures and reaction time for the different mixtures was revealed, and it was found that the temperature inside the crucible during the reactions was up to 100°C below the furnace set-point, due to endothermic nature of the reactions. Quench experiments showed that whiskers were formed already when reaching the temperature plateau, but the yield increased fast with the holding time and reached a maximum after about 20-30 minutes. Growth models for whisker formation have been proposed. Alumina based composites reinforced by (2-5 vol.%) TiCnano and TiNnano and 25 vol.% of carbide, and boride phases (whiskers and particulates of TiC, TiN, TaC, NbC, (Ti,Ta)C, (Ti,Ta,Nb)C, SiC, TiB2 and B4C) have been prepared by a developed aqueous colloidal processing route followed by hot pressing for 90 min at 1700°C, 28 MPa or SPS sintering for 5 minutes at 1200-1600°C and 75 MPa. Vickers indentation measurements showed that the lowest possible sintering temperature is to prefer from mechanical properties point of view. In the TiNnano composites the fracture mode was typically intergranular, while it was transgranular in the SiCnano composites. The whisker and particulate composites have been compared in terms of e.g. microstructure and mechanical properties. Generally, additions of whiskers yielded higher fracture toughness compared to particulates. Composites of commercially available SiC whiskers showed best mechanical properties with a low spread but all the other whisker phases, especially TiB2, exhibited a great potential as reinforcement materials.