Photocatalytic inactivation of Escherischia coli and Pichia pastoris with combustion synthesized titanium dioxide

The photocatalytic inactivation of Escherischia coli and Pichia Pastoris was studied with combustion synthesized titanium dioxide photocatalysts Three different combustion synthesized (CS) catalysts were used viz CS-TiO2 1% Ag substituted in TiO2 and 1% Ag impregnated in TiO2 All the combustion synthesized catalysts showed higher activity as compared to the activity observed with commercial Degussa P-25 TiO2 The effect of various parameters like catalyst loading different catalysts and initial cell concentration was studied At the optimum loading 1% Ag impregnated TiO2 showed the maximum efficiency and complete inactivation of both the microorganisms was observed within an hour of irradiation The morphology of inactivated cells was studied by inverted microscope and SEM From the images obtained it was hypothesized that damage to the cell wall was the main cause of cell inactivation The initial cell concentration had a prominent effect on the inactivation At a low initial cell concentration the complete inactivation of E cob and P pastoris was observed within 10 and 20 min respectively This shows that P pastoris has a stronger resistance towards photocatalytic inactivation than E cols The inactivation reactions were modeled with power law kinetics The order of reaction in case of E colt and P pastoris were determined as 1 20 and 1 08 respectively (C) 2010 Elsevier B V All rights reserved

Combustion Synthesis of Metal Chromite Powders

Fine-particle metal chromites (MCr2O4, where M = Mg, Ca, Mn, Fe, Co, Ni, Cu, and Zn) have been prepared by the combustion of aqueous solutions containing the respective metal nitrate, chromium(III) nitrate, and urea in stoichiometric amounts. The mixtures, when rapidly heated to 350°C, ignite and yield voluminous chromites with surface areas ranging from 5 to 25 m2/g. MgCr2O4, sintered in air at 1500°C for 5 h, has a density of 4.0 g/cm3.

Combustion synthesis of rare earth cuprates

Rare earth cuprates, La2CuO4 Nd2CuO4, La1.8M0.2CuO4 (M=Ca.Sr) and Nd1.85Ce0.15CuO4 have been prepared by the combustion of redox mixtures containing corresponding metal nitrates and maleic hydrazide, C4H4N2O2, at 350°C. The solid combustion products are submicron size amorphous powders which on heat treatment (700°C, 30 minutes) yield crystalline single phase cuprates. Strontium doped lanthanum cuprate, La1.8Sr0.2CuO4, shows an onset of superconductivity at 36K.

Diamond growth in combustion flames

Diamond crystallites were synthesized using various oxygen‐hydrocarbon flames. The flames have been profiled in real time using a nonintrusive diagnostic technique. Optical emission spectra for different zones have been recorded and the active species identified. Diamond growth was observed only in the thermodynamically unequilibriated primary combustion zone of the flames. Carbon‐bearing species, atomic hydrogen, and atomic oxygen, noted to be critical for diamond growth, were observed in the flames. The diamond growth was confirmed by x‐ray diffraction, laser‐Raman analysis, and scanning electron microscopy. The study offers the first insight into the flame spectra in the context of diamond synthesis at atmospheric pressures.

Noble metal ionic sites for catalytic hydrogen combustion: spectroscopic insights

A catalytic hydrogen combustion reaction was carried out over noble metal catalysts substituted in ZrO2 and TiO2 in ionic form. The catalysts were synthesized by the solution combustion technique. The compounds showed high activity and CO tolerance for the reaction. The activity of Pd and Pt ion substituted TiO2 was comparable and was higher than Pd and Pt ion substituted ZrO2. The mechanisms of the reaction over the two supports were proposed by making use of the X-ray photoelectron spectroscopy and FT infrared spectroscopic observations. The reaction over ZrO2 supported catalysts was proposed to take place by the utilization of the surface hydroxyl groups while the reaction over TiO2 supported catalysts was hypothesized to be a hybrid mechanism utilizing surface hydroxyl groups and the lattice oxygen.

Combustion synthesis and properties of fine-particle rare-earth-metal zirconates, Ln2Zr2O7

Fine-particle rare-earth-metal zirconates, Ln2Zr2O7, where Ln = La, Ce, Pr, Nd, Sm, Gd and Dy having the pyrochlore structure have been prepared using a novel combustion process. The process employs aqueous solutions of the corresponding rare-earth-metal nitrate, zirconium nitrate and carbohydrazide/urea in the required molar ratio. When the solution is rapidly heated to 350–500 °C it boils, foams and burns autocatalytically to yield voluminous oxides. The formation of single-phase Ln2Zr2O7 has been confirmed by powder X-ray diffraction, infrared and fluorescence spectroscopy. The solid combustion products are fine, having surface areas in the range 6–20 m2 g–1. The cold-pressed Pr2Zr2O7 compact when sintered at 1500 °C, 4 h in air, achieved 99% theoretical density.

Combustion Synthesis and Properties of Fine Particle Spinel Manganites

Fine particle spinel manganites have been prepared by thermal decomposition of the precursors N2H5M1/3Mn2/3(N2H3COO)3 · H2O (M = Co and Ni) and M1/3 Mn2/3(N2H3COO)2 · 2H2O (M = Mg and Zn), as well as by the combustion of redox mixtures containing M(II) nitrate (M = Mg, Co, Ni, Cu, and Zn), Mn(II) nitrate, and maleic hydrazide (MH) in the required molar ratio. Both the precursor and redox mixtures undergo self-propagating, gas-producing, exothermic reactions once ignited at 250-375°C to yield corresponding manganites in less than 5 min. Formation of single phase products was confirmed by X-ray powder diffraction patterns. The manganites are of submicrometer size and have surface area in the range 20-76 m2/g.

Synthesis of A1PO4, LaPO4 and KTiOPO4 by flash combustion

Fine particle AlPO4, LaPO4 and KTiOPO4 have been prepared by the flash combustion of aqueous solutions containing metal nitrate, ammonium hydrogen phosphate, ammonium nitrate or ammonium perchlorate and carbohydrazide or tetraformal trisazine. When rapidly heated at 400 °C, the solution containing the redox mixtures ignites to undergo self-propagating, gas-producing, exothermic reactions. Formation of crystalline phosphates was confirmed by powder X-ray diffraction patterns and IR spectra. The metal phosphates formed are fine and have 20�78 m2 g?1 surface area.

Combustion synthesis and properties of Ln3Fe5O12 and yttrium aluminium garnets

The rare earth iron garnets Ln3Fe5O12 and Y3AlxFe5-xO12, where x=1.0-5.0, and Y1.5Gd1.5Al0.2Fe4.8O12 have been prepared by the combustion of redox mixtures containing corresponding metal nitrates and oxalyl dihydrazide, i.e. C2H6N4O2 at 350-degrees-C. The solid combustion products are amorphous, submicrometre-sized powders which, on heating at 750-degrees-C for 3 h, yield crystalline single-phase garnets. The particle size of the garnets is below 1 mum and the surface area ranges from 16 to 90 m2 g-1. Yttrium iron garnet could be sintered to a density of more than 95% at 1200-degrees-C for 3 h, giving an average grain size of 3-5 mum.

Combustion synthesis of oxide materials for nuclear waste immobilization

Oxide materials like perovskite, zirconolite, hollandite, pyrochlore, NASICON and sphene which are used for nuclear waste immobilization have been prepared by a solution combustion process. The process involves the combustion of stoichiometric amount of corresponding metal nitrates and carbohydrazide/tetraformyl trisazine/diformyl hydrazide at 450 degrees C. The combustion products have been characterized using powder X-ray diffraction, infrared spectroscopy, and Si-29 MAS-NMR. The fine particle nature of the combustion derived powders has been studied using density, particle size, BET surface area measurements and scanning electron microscopy. Sintering of combustion derived powder yields 85-95% dense ceramics in the temperature range 1000 degrees-1300 degrees C.

Controlled combustion synthesis and properties of fine-particle NASICON materials

Fine-particle NASICON materials, Na1+xZr2P3-xSixO12 (where x = 0.0, 0.5, 1.0, 1.5, 2.0 and 2.5), have been prepared by controlled combustion of an aqueous solution containing stoicthiometric amounts of sodium nitrate, zirconyl nitrate, ammonium perchlorate, diammonium hydrogen phosphate, fumed silica and carbonohydrazide. Formation of NASICON has been confirmed by powder XRD, Si-29 NMR and IR spectroscopy. These NASICON powders are fine (average agglomerate size 5-12 mum) with a surface area varying from 8 to 30 m2 g-1. NASICON powders pelletized and sintered at 1100-1200-degrees-C for 5 h achieved 90-95% theoretical density and show fine-grain microstructure. The coefficient of thermal expansion of sintered NASICON compact was measured up to 500-degrees-C and changes f rom -3.4 x 10(-6) to 4.1 x 10(-6) K-1. The conductivity of Sintered Na3Zr2PSi2O12 compact at 300-degrees-C is 0.236 OMEGA-1 cm-1.

Effect of Li+-ion on enhancement of photoluminescence in Gd2O3:Eu3+ nanophosphors prepared by combustion technique

Gd2O3:Eu3+ (4 mol%) nanophosphor co-doped with Li+ ions have been synthesized by low-temperature solution combustion technique in a short time. Powder X-ray diffractometer (PXRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), UV-VIS and photoluminescence (PL) techniques have been employed to characterize the synthesized nanoparticles. It is found that the lattice of Gd2O3:Eu3+ phosphor transforms from monoclinic to cubic as the Li+-ions are doped. Upon 254 nm excitation, the phosphor showed characteristic luminescence D-5(0) -> F-7(J) (J= 0-4) of the Eu3+ ions. The electronic transition located at 626 nm (D-5(0) -> F-7(2)) of Eu3+ ions was stronger than the magnetic dipole transition located at 595 nm (D-5(0) -> F-7(1)). Furthermore, the effects of the Li+ co-doping as well as calcinations temperature on the PL properties have been studied. The results show that incorporation of Li+ ions in Gd2O3:Eu3+ lattice could induce a remarkable improvement of their PL intensity. The emission intensity was observed to be enhanced four times than that of with out Li+-doped Gd2O3:Eu3+. (C) 2010 Elsevier B.V. All rights reserved,

Role of lattice defects and crystallite morphology in the UV and visible-light-induced photo-catalytic properties of combustion-prepared TiO2

The physico-chemical, photo-physical and micro-structural properties responsible for the strikingly different photocatalytic behavior of combustion-prepared TiO2 (c.TiO2) and Degussa P25 (d.TiO2) samples are elucidated in this study. Electron microscopy and selected area electron diffraction micrographs revealed that the two samples exhibited different morphologies. The grains of c.TiO2 were spherical and comprised of 5-6 nm size primary particle. On the other hand, d.TiO2 consisted of large (0.5-3.0 mu m) size and irregular shape aggregates having primary particles of 15-40 nm cross-sectional diameter. The ESR study revealed that the presence of certain defect states in c.TiO2 helped in stabilization of O-. and Ti3+-OH type species during room-temperature UV-irradiation. No such paramagnetic species were however formed over d.TiO2 under similar conditions. C1s and Ti 2p XPS spectra provide evidence for the presence of some lattice vacancies in c.TiO2 and also for the bulk Ti4+ -> Ti3+ conversion during its UV-irradiation. Compared to d.TiO2, c.TiO2 displayed considerably higher activity for discoloration of methyl orange but very poor activity for splitting of water, both under UV and visible light radiations. This is attributed to enhanced surface adsorption of dye molecules over c.TiO2, because of its textural features and also the presence of photo-active ion-radicals. On the other hand, the poor activity of c.TiO2 for water splitting is related to certain defect-induced inter-band charge trapping states in the close vicinity of valence and conduction bands of c.TiO2, as revealed by thermoluminescence spectroscopy. Further, the dispersion of nanosize gold particles gave rise to augmented activity of both the catalysts, particularly for water splitting. This is explained by the promotional role of Au-0 or Au-0/TiO2 interfacial sites in the adsorption and charge-adsorbate interaction processes. (C) 2011 Elsevier B.V. All rights reserved.

Photocatalytic Activity of Combustion Synthesized Nanocrystalline CeAlO3

The photocatalytic activity of combustion synthesized nanocrystalline CeAlO3 was determined for the degradation of four anionic and four cationic dyes. The perovskite oxide showed high-photocatalytic activity and a complete degradation of all the dyes was possible within 2 h. The photocatalytic activity of the compound was comparable with the activity of the commercial Degussa P-25 TiO2 catalyst. The degradation of dyes was found to follow first order kinetics and the first order degradation rate constants were determined.