Cover cracking of the reinforced concrete due to rebar corrosion induced by chloride penetration

Este artículo estudia el proceso de fisuración del hormigón por corrosión de la armadura. Se presenta un modelo de transporte de cloruros en el hormigón, que contempla la no-linealidad de los coeficientes de difusión, las isotermas de absorción y el fenómeno de convección. A partir de los resultados de penetración de cloruros, se establece la corrosión de la armadura con la consiguiente expansión radial. La fisuración del hormigón se estudia con un modelo de fisura embebida. Los dos modelos (iniciación y propagación) se incorporan en un programa de elementos finitos. El modelo se contrasta con resultados experimentales, obteniéndose un buen ajuste. Una de las dificultades es establecer el umbral de concentración de cloruros que da lugar al inicio de la corrosión de la armadura.This paper is focused on the chloride-induced corrosion of the rebar in RC. A comprehensive model for the chloride ingress into concrete is presented, with special attention to non-linear diffusion coefficients, chloride binding isotherms and convection phenomena. Based on the results of chloride diffusion, subsequent active corrosion is assumed and the radial expansion of the corroded reinforcement reproduced. For cracking simulation, the Strong Discontinuity Approach is applied. Both models (initiation and propagation corrosion stages) are incorporated in the same finite element program and chained. Comparisons with experimental results are carried out, with reasonably good agreements being obtained, especially for cracking patterns. Major limitations refer to difficulties to establish precise levels of basic data such as the chloride ion content at concrete surface, the chloride threshold concentration that triggers active corrosion, the rate of oxide production or the rust mechanical properties.

Evaluación de parámetros que influyen en el transporte de cloruros en hormigón parcialmente saturado

El deterioro del hormigón debido a la presencia del ion cloruro es causa frecuente de problemas en estructuras localizadas en ambiente marino y alta montaña. Su principal efecto consiste en la despasivación del acero de refuerzo embebido en el hormigón y su consecuente inicio de la corrosión del mismo. El ingreso del ion cloruro al interior del hormigón, está condicionado por una serie de parámetros de origen medioambiental e intrínsecos del hormigón. En función de estos parámetros el ingreso de cloruros en el hormigón puede deberse principalmente a los siguientes mecanismos: difusión y succión capilar. El estudio y evaluación de la resistencia del hormigón frente a cloruros, se ha desarrollado principalmente en condiciones saturadas del hormigón. Lo que ha significado que parámetros de importancia no sean considerados. Debido a esto, distintos procesos que suceden en estructuras reales no han sido identificados y estudiados correctamente. En este trabajo, se diseñó un programa de investigación para evaluar los parámetros que influyen en el transporte cloruros en hormigones no saturados. Para esto se diseñaron tres dosificaciones diferentes de hormigón. En la primera se empleó únicamente cemento portland, para el resto se utilizaron adiciones minerales (humo de sílice y escoria de alto horno). El empleo de adiciones se debió a que tienen un papel importante en la durabilidad de hormigones frente a cloruros. Los hormigones fueron dosificados con una relación agua/material cementício de 0,40 para el hormigón elaborado únicamente con cemento portland y 0,45 para las mezclas con adiciones. Para evaluar las propiedades de los hormigones en estado fresco y endurecido se realizaron ensayos vigentes en las normativas. Con los resultados obtenidos se determinaron parámetros de resistencia mecánica, microestructurales, resistencia al transporte de cloruros e higroscópicos. Una vez caracterizados los hormigones, se diseñó una propuesta experimental para estudiar los principales parámetros presentes en estructuras reales con presencia de cloruros. Tanto la concentración de cloruro como las condiciones ambientales se han variado teniendo como referencia las situaciones reales que podrían producirse en ambientes de alta montaña en la zona centro de España. La propuesta experimental consistió en tratar de evaluar la capacidad de los hormigones al transporte de iones en ambientes de alta montaña con presencia de sales fundentes. Para esto se establecieron 5 fases experimentales donde los principales parámetros ambientales y la presencia de iones agresivos sufrieron variaciones. Al término de cada fase se obtuvieron perfiles de penetración de cloruros en los hormigones y se evaluó la influencia de los parámetros presentes en cada fase. Los resultados experimentales se implementaron en un modelo numérico basado en la teoría de elementos finitos, desarrollado por el grupo de investigación del Departamento de Materiales de Construcción. Para esto fue necesario realizar la calibración y validación del modelo numérico para cada hormigón. El calibrado del modelo precisa de datos químicos y microestructurales de cada hormigón, tales como: capacidad de combinación de cloruros y propiedades difusivas e higroscópicas. Para la validación del modelo numérico se realizaron simulaciones de la propuesta experimental. Los resultados obtenidos se compararon con los valores experimentales. Con el objeto de poder estudiar en mayor profundidad la influencia del grado de saturación del hormigón durante la difusión de cloruros, se llevó a cabo una campaña experimental que consideró distintos grados de saturación en los hormigones. Para esto se establecieron en los hormigones cuatro grados de saturación distintos (50%, 60%, 80% y 100%, aproximadamente), posteriormente se expusieron a cloruro de sodio finamente molido. Una vez transcurrido el tiempo necesario se obtuvieron experimentalmente los perfiles de penetración de cloruros para cada grado de saturación y se calcularon los coeficientes de difusión. Los datos obtenidos durante la campaña experimental han demostrado la influencia positiva que ejercen las adiciones en las mezclas de hormigón. Sus principales ventajas son el refinamiento de la red porosa y el aumento en la capacidad de combinación de cloruros, además de mejorar sus propiedades mecánicas. La porosidad total en las mezclas no presentó grandes cambios, sin embargo, el cambio en la distribución del tamaño de poros es importante en las muestras con adiciones. En especial las fabricadas con humo de sílice. Los coeficientes de difusión y migración de cloruros para las mezclas con adiciones disminuyeron significativamente, igual que los valores de resistividad eléctrica. En los ensayos de penetración del agua bajo presión, fueron las muestras con adiciones las que mostraron las menores penetraciones. Los resultados obtenidos al final de la propuesta experimental permitieron estudiar los distintos parámetros involucrados. Se observó claramente que el proceso de difusión provoca el mayor transporte de cloruros hacia el interior del hormigón. Así mismo se comprobó que el lavado superficial y el secado de las probetas, trasladan cloruros hacia las zonas externas del hormigón. El primero debido a una baja concentración de cloruros externa, mientras que el secado provoca el movimiento de la solución de poro hacia las zonas de secado depositando cloruros en ellas. Las medidas higroscópicas permitieron determinar la existencia de dos zonas distintas en el interior del hormigón. La primera se localizó en el rango de 0-10mm, aproximadamente, en ésta se puso de manifiesto una mayor sensibilidad a los cambios experimentados en el exterior de las probetas. La segunda zona se localizó a una profundidad mayor de 10mm, aproximadamente. Se observó claramente una baja influencia de los cambios externos, siendo la difusión de cloruros el principal mecanismo de transporte presente en ella. En cuanto al estudio de la influencia del grado de saturación en la difusión de cloruros, se observó claramente una marcada diferencia entre los coeficientes de difusión de cloruro obtenidos. Para grados de saturación mayores del 80% el mecanismo de penetración de cloruros por difusión existe de forma significativa. Mientras que para valores inferiores los resultados revelaron que las vías de acceso disminuyen (poros conectado con agua) considerablemente limitando en un alto grado la penetración del agresivo. Para grados de saturación inferiores del 50% los valores del coeficiente de difusión son despreciables. The deterioration of concrete due to chloride ions is a frequent problem identified in structures located in marine and high-mountain environments. After entering the outer layer of the concrete, the chlorides tend to penetrate until they reach and then depassivate the steel bars. Subsequently, this induces the deterioration process of the reinforced concrete. This chloride penetration depends on the environmental conditions and intrinsic parameters of the concrete. Several transport mechanisms, such as diffusion, capillary suction and permeability can be present into the concrete. While recent research into the study and evaluation of concretes with chloride presence has been carried out in saturated concrete, it has not considered certain parameters that can modify this condition. Consequently, at the time of writing several processes that take place in real structures have not been identified and studied. In this work a research programme is designed to evaluate the parameters that influence chloride transport into non-saturated concrete. For this, three concrete mixes were designed by using high-early-strength Portland cement and mineral admixtures (silica fume and blast-slag furnace). The water-cement ratio was 0.40 for the concrete made solely with Portland cement and 0.45 for the concretes that used mineral admixtures as a cement replacement. A set of experimental tests were performed to evaluate the concrete properties both in fresh and hardened state. In addition, an experimental simulation was carried out under laboratory conditions in which the main objective was to assess resistance of concrete to chloride penetration under high-mountain conditions with the presence of de-icing salts. The environmental conditions and surface chloride concentration of the concrete used during the experimental simulation were chosen by considering conditions found in the high-mountain environment in central Spain. For the experimental simulation five phases were designed by varying the environmental parameters and concrete surface concentration. At the end of each phase a chloride profile was obtained with the aim of assessing the influence of the parameters on chloride transport. The experimental results were then used to calibrate and validate a numerical model based on finite element theory developed by the research team from the Construction Materials Department in a previous work. In order to carry out model calibration chemical and microstructural data for the concretes was required, such as binding capacity and the diffusive and hygroscopic properties. The experimental results were compared with the numerical simulations and provided a good fit. With the objective of studying the influence of the degree of concrete saturation on chloride diffusion, an experimental programme was designed. This entailed four saturation degrees (50%, 60%, 80% and 100%) being established in several concrete samples. The samples were then exposed to ground sodium chloride. Once the time required was achieved, the chloride profiles and diffusion coefficients were obtained for each saturation degree. The results obtained from the experimental program revealed a positive influence of the mineral admixtures on the concretes. Their effects were reflected in the pore-network refinement and the increase of chloride binding capacity, together with the improvement of the mechanical properties of the concretes. Total porosity did not reveal any notable change, though the pore-size distribution showed a significant degree of change in the concretes with mineral admixtures, specifically the samples prepared through use of silica fume. The chloride diffusion and migration coefficient, as well as the electrical resistivity values, decreased significantly in the concretes with admixtures. In the water penetration under pressure test, the concretes with admixtures presented the lowest penetration depth. The results obtained in the experimental simulation allowed study of the main parameters involved during the chloride penetration processes in non-saturated concretes in the presence of chlorides. According to the results, the diffusion process was the transport mechanism that transferred the greatest amount of chlorides into the concrete samples. In addition, a chloride movement toward external zones of the concrete, caused by the washing of concrete surface and the drying processes, was identified. The washing occurred when the concrete surface came into contact with a low-chloride concentration solution which initiated the outward movement of chloride diffusion. The drying processes corresponded to a movement of pore solution launched by water evaporation from the outer layer. Furthermore, hygroscopic measurements made in the concrete allowed two areas with distinct behavioural patterns to be identified. The first one, located in the range of approximately 0-10mm, showed a greater degree of influence regarding the changes of the external conditions. The second, situated at depths greater than 10mm, displayed a low influence of external conditions. The main process in this area was diffusion. Study of the influence of the degree of concrete saturation on chloride diffusion showed a clear difference among the chloride diffusion coefficients obtained. For degrees of concrete saturation higher than 80%, chloride penetration by diffusion tends to be significant. However, in the case of extent of saturation of lower than 80%, the results revealed that the access zone through which chlorides can penetrate decreased considerably. For degrees of concrete saturation lower than 50%, the chloride diffusion coefficients were negligible.

Experimental and numerical study of cracking of concrete due to reinforcement corrosion

La corrosión del acero es una de las patologías más importantes que afectan a las estructuras de hormigón armado que están expuestas a ambientes marinos o al ataque de sales fundentes. Cuando se produce corrosión, se genera una capa de óxido alrededor de la superficie de las armaduras, que ocupa un volumen mayor que el acero inicial; como consecuencia, el óxido ejerce presiones internas en el hormigón circundante, que lleva a la fisuración y, ocasionalmente, al desprendimiento del recubrimiento de hormigón. Durante los últimos años, numerosos estudios han contribuido a ampliar el conocimiento sobre el proceso de fisuración; sin embargo, aún existen muchas incertidumbres respecto al comportamiento mecánico de la capa de óxido, que es fundamental para predecir la fisuración. Por ello, en esta tesis se ha desarrollado y aplicado una metodología, para mejorar el conocimiento respecto al comportamiento del sistema acero-óxido-hormigón, combinando experimentos y simulaciones numéricas. Se han realizado ensayos de corrosión acelerada en condiciones de laboratorio, utilizando la técnica de corriente impresa. Con el objetivo de obtener información cercana a la capa de acero, como muestras se seleccionaron prismas de hormigón con un tubo de acero liso como armadura, que se diseñaron para conseguir la formación de una única fisura principal en el recubrimiento. Durante los ensayos, las muestras se equiparon con instrumentos especialmente diseñados para medir la variación de diámetro y volumen interior de los tubos, y se midió la apertura de la fisura principal utilizando un extensómetro comercial, adaptado a la geometría de las muestras. Las condiciones de contorno se diseñaron cuidadosamente para que los campos de corriente y deformación fuesen planos durante los ensayos, resultando en corrosión uniforme a lo largo del tubo, para poder reproducir los ensayos en simulaciones numéricas. Se ensayaron series con varias densidades de corriente y varias profundidades de corrosión. De manera complementaria, el comportamiento en fractura del hormigón se caracterizó en ensayos independientes, y se midió la pérdida gravimétrica de los tubos siguiendo procedimientos estándar. En todos los ensayos, la fisura principal creció muy despacio durante las primeras micras de profundidad de corrosión, pero después de una cierta profundidad crítica, la fisura se desarrolló completamente, con un aumento rápido de su apertura; la densidad de corriente influye en la profundidad de corrosión crítica. Las variaciones de diámetro interior y de volumen interior de los tubos mostraron tendencias diferentes entre sí, lo que indica que la deformación del tubo no fue uniforme. Después de la corrosión acelerada, las muestras se cortaron en rebanadas, que se utilizaron en ensayos post-corrosión. El patrón de fisuración se estudió a lo largo del tubo, en rebanadas que se impregnaron en vacío con resina y fluoresceína para mejorar la visibilidad de las fisuras bajo luz ultravioleta, y se estudió la presencia de óxido dentro de las grietas. En todas las muestras, se formó una fisura principal en el recubrimiento, infiltrada con óxido, y varias fisuras secundarias finas alrededor del tubo; el número de fisuras varió con la profundidad de corrosión de las muestras. Para muestras con la misma corrosión, el número de fisuras y su posición fue diferente entre muestras y entre secciones de una misma muestra, debido a la heterogeneidad del hormigón. Finalmente, se investigó la adherencia entre el acero y el hormigón, utilizando un dispositivo diseñado para empujar el tubo en el hormigón. Las curvas de tensión frente a desplazamiento del tubo presentaron un pico marcado, seguido de un descenso constante; la profundidad de corrosión y la apertura de fisura de las muestras influyeron notablemente en la tensión residual del ensayo. Para simular la fisuración del hormigón causada por la corrosión de las armaduras, se programó un modelo numérico. Éste combina elementos finitos con fisura embebida adaptable que reproducen la fractura del hormigón conforme al modelo de fisura cohesiva estándar, y elementos de interfaz llamados elementos junta expansiva, que se programaron específicamente para reproducir la expansión volumétrica del óxido y que incorporan su comportamiento mecánico. En el elemento junta expansiva se implementó un fenómeno de despegue, concretamente de deslizamiento y separación, que resultó fundamental para obtener localización de fisuras adecuada, y que se consiguió con una fuerte reducción de la rigidez tangencial y la rigidez en tracción del óxido. Con este modelo, se realizaron simulaciones de los ensayos, utilizando modelos bidimensionales de las muestras con elementos finitos. Como datos para el comportamiento en fractura del hormigón, se utilizaron las propiedades determinadas en experimentos. Para el óxido, inicialmente se supuso un comportamiento fluido, con deslizamiento y separación casi perfectos. Después, se realizó un ajuste de los parámetros del elemento junta expansiva para reproducir los resultados experimentales. Se observó que variaciones en la rigidez normal del óxido apenas afectaban a los resultados, y que los demás parámetros apenas afectaban a la apertura de fisura; sin embargo, la deformación del tubo resultó ser muy sensible a variaciones en los parámetros del óxido, debido a la flexibilidad de la pared de los tubos, lo que resultó fundamental para determinar indirectamente los valores de los parámetros constitutivos del óxido. Finalmente, se realizaron simulaciones definitivas de los ensayos. El modelo reprodujo la profundidad de corrosión crítica y el comportamiento final de las curvas experimentales; se comprobó que la variación de diámetro interior de los tubos está fuertemente influenciada por su posición relativa respecto a la fisura principal, en concordancia con los resultados experimentales. De la comparación de los resultados experimentales y numéricos, se pudo extraer información sobre las propiedades del óxido que de otra manera no habría podido obtenerse. Corrosion of steel is one of the main pathologies affecting reinforced concrete structures exposed to marine environments or to molten salt. When corrosion occurs, an oxide layer develops around the reinforcement surface, which occupies a greater volume than the initial steel; thus, it induces internal pressure on the surrounding concrete that leads to cracking and, eventually, to full-spalling of the concrete cover. During the last years much effort has been devoted to understand the process of cracking; however, there is still a lack of knowledge regarding the mechanical behavior of the oxide layer, which is essential in the prediction of cracking. Thus, a methodology has been developed and applied in this thesis to gain further understanding of the behavior of the steel-oxide-concrete system, combining experiments and numerical simulations. Accelerated corrosion tests were carried out in laboratory conditions, using the impressed current technique. To get experimental information close to the oxide layer, concrete prisms with a smooth steel tube as reinforcement were selected as specimens, which were designed to get a single main crack across the cover. During the tests, the specimens were equipped with instruments that were specially designed to measure the variation of inner diameter and volume of the tubes, and the width of the main crack was recorded using a commercial extensometer that was adapted to the geometry of the specimens. The boundary conditions were carefully designed so that plane current and strain fields were expected during the tests, resulting in nearly uniform corrosion along the length of the tube, so that the tests could be reproduced in numerical simulations. Series of tests were carried out with various current densities and corrosion depths. Complementarily, the fracture behavior of concrete was characterized in independent tests, and the gravimetric loss of the steel tubes was determined by standard means. In all the tests, the main crack grew very slowly during the first microns of corrosion depth, but after a critical corrosion depth it fully developed and opened faster; the current density influenced the critical corrosion depth. The variation of inner diameter and inner volume of the tubes had different trends, which indicates that the deformation of the tube was not uniform. After accelerated corrosion, the specimens were cut into slices, which were used in post-corrosion tests. The pattern of cracking along the reinforcement was investigated in slices that were impregnated under vacuum with resin containing fluorescein to enhance the visibility of cracks under ultraviolet lightening and a study was carried out to assess the presence of oxide into the cracks. In all the specimens, a main crack developed through the concrete cover, which was infiltrated with oxide, and several thin secondary cracks around the reinforcement; the number of cracks diminished with the corrosion depth of the specimen. For specimens with the same corrosion, the number of cracks and their position varied from one specimen to another and between cross-sections of a given specimen, due to the heterogeneity of concrete. Finally, the bond between the steel and the concrete was investigated, using a device designed to push the tubes of steel in the concrete. The curves of stress versus displacement of the tube presented a marked peak, followed by a steady descent, with notably influence of the corrosion depth and the crack width on the residual stress. To simulate cracking of concrete due to corrosion of the reinforcement, a numerical model was implemented. It combines finite elements with an embedded adaptable crack that reproduces cracking of concrete according to the basic cohesive model, and interface elements so-called expansive joint elements, which were specially designed to reproduce the volumetric expansion of oxide and incorporate its mechanical behavior. In the expansive joint element, a debonding effect was implemented consisting of sliding and separation, which was proved to be essential to achieve proper localization of cracks, and was achieved by strongly reducing the shear and the tensile stiffnesses of the oxide. With that model, simulations of the accelerated corrosion tests were carried out on 2- dimensional finite element models of the specimens. For the fracture behavior of concrete, the properties experimentally determined were used as input. For the oxide, initially a fluidlike behavior was assumed with nearly perfect sliding and separation; then the parameters of the expansive joint element were modified to fit the experimental results. Changes in the bulk modulus of the oxide barely affected the results and changes in the remaining parameters had a moderate effect on the predicted crack width; however, the deformation of the tube was very sensitive to variations in the parameters of oxide, due to the flexibility of the tube wall, which was crucial for indirect determination of the constitutive parameters of oxide. Finally, definitive simulations of the tests were carried out. The model reproduced the critical corrosion depth and the final behavior of the experimental curves; it was assessed that the variation of inner diameter of the tubes is highly influenced by its relative position with respect to the main crack, in accordance with the experimental observations. From the comparison of the experimental and numerical results, some properties of the mechanical behavior of the oxide were disclosed that otherwise could not have been measured.

Aplicaciones basadas en las propiedades eléctricas y térmicas de recubrimientos de sílice-cb obtenidos por el método sol-gel

En los últimos años el interés en los recubrimientos obtenidos por sol-gel ha aumentado mucho en aplicaciones de protección y refuerzo de superficies contra la corrosión. Asimismo, el uso de polimorfos de carbono (nanofibras de carbono, grafeno, grafito...) para mejorar las propiedades mecánicas y conferirle propiedades conductoras a algunos materiales, también se ha desarrollado mucho en los últimos años. En trabajos previos se prepararon y estudiaron recubrimientos híbridos de sílice-CB obtenidos por el método sol-gel. Mediante el estudio de la microestructura y composición de estos recubrimientos (SEM, Raman, ATD-TG, y FT-IR) y de las propiedades eléctricas se obtuvo que en función la temperatura de sinterización de los recubrimientos, se podía controlar la respuesta eléctrica de los composites. Esto permite abrir enormemente el campo de aplicaciones, ya que para temperaturas de sinterización por debajo de 400ºC se consiguen resistividades del orden de 10-4Ωm, apropiadas para aplicaciones en dispositivos electrónicos, electrodos, apantallamiento de interferencias electromagnéticas y radiofreciencia, etc; mientras que para temperaturas de sinterización por encima de 400ºC, obtenemos recubrimientos más resistivos que pueden aplicarse como dispositivos calefactores, anticongelantes. Por tanto, el objetivo de este trabajo es desarrollar más profundamente estas aplicaciones, así como diseñar experimentos que demuestren las múltiples posibilidades que estos recubrimientos conductores obtenidos por sol-gel pueden aportar.

Protección catódica en estructuras sumergidas. Aplicación al proyecto de boyas y tuberías de un terminal portuario de descarga de crudo.

Este proyecto tiene por objeto el diseño de la protección catódica contra la corrosión de las boyas y las tuberías sumergidas en agua de mar de un terminal portuario de descarga de crudo. La protección catódica consiste en la igualación de los potenciales de las áreas anódicas y catódicas del material por el flujo de electrones suministrado. En el proyecto se han empleado los métodos de ánodos de sacrificio y de corriente impresa para analizar la protección catódica más adecuada de cada componente. Para los cálculos de los ánodos necesarios para la protección catódica se utilizó el procedimiento de la masa, seleccionando así el método, ánodos de sacrificio o corriente impresa, y los ánodos más apropiados para la protección catódica de las boyas y de las tuberías. ABSTRACT The aim of this project was to design the cathodic protection against corrosion of a crude oil unloading port terminal’s buoys and under sea water pipelines. The cathodic protection consists in the equating of anodic and cathodic material areas by the electrons flow supplied. In this project, sacrificial anodes and impressed current methods were used for analyze the most suitable cathodic protection for each component. For the cathodic protection required anodes calculations, the weight procedure was used, thereby selecting the method, sacrificial anodes or impressed current, and the most appropriate anodes, for the cathodic protection of the buoys and pipelines

Desarrollo de métodos para la caracterización predictiva acoplada de tensiones y deformaciones en procesos de tratamiento superficial mediante ondas de choque generadas por láser

En ingeniería los materiales están sujetos a un proceso de degradación desde el mismo momento en el que concluye su proceso de fabricación. Cargas mecánicas, térmicas y agresiones químicas dañan las piezas a lo largo de su vida útil. El daño generado por procesos de fatiga, corrosión y desgaste son unos pocos ejemplos de posible deterioro. Este deterioro de las piezas se combate mediante la prevención en la etapa de diseño, a través de reparaciones periódicas y mediante la sustitución de piezas en servicio. La mayor parte de los tipos de daño que pueden sufrir los materiales durante su vida útil se originan en la superficie. Por esta razón, el objetivo de los tratamientos superficiales es inhibir el daño a través de la mejora de las propiedades superficiales del material, intentando no generar sobrecostes inasumibles en el proceso productivo ni efectos colaterales notablemente perjudiciales. En general, se ha de llegar a una solución óptima entre el coste del tratamiento superficial y el beneficio generado por el aumento de la vida útil del material. En esta tesis se estudian los efectos del tratamiento superficial de aleaciones metálicas mediante ondas de choque generadas por láser. Su denominación internacional más empleada "Láser Shock Processing" hace que se emplee la denominación de procesos de LSP para referirse a los mismos. También se emplea la denominación de "Láser Peening" por semejanza al tratamiento superficial conocido como "Shot Peening", aunque su uso sólo está generalizado en el ámbito industrial. El tratamiento LSP es una alternativa eficaz a los tratamientos tradicionales de mejora de propiedades superficiales, mejorando la resistencia a la fatiga, a la corrosión y al desgaste. El tratamiento LSP se basa en la aplicación de uno o varios pulsos láser de elevada intensidad (superior a 1 GW/cm2) y con duración en el dominio de los nanosegundos sobre la superficie de la pieza metálica a tratar. Esta, bien se recubre con una fina capa de medio confinante (generalmente una fina capa de agua) transparente a la radiación láser, bien se sumerge en el medio confinante (también se usa agua). El pulso láser atraviesa el medio confinante hasta llegar a la superficie de la pieza. Es entonces cuando la superficie inmediatamente se vaporiza y se ioniza, pasando a estado de plasma. Como el plasma generado es confinado por el medio confinante, su expansión se limita y su presión crece. De este modo, el plasma alcanza presiones de varios GPa y crea dos ondas de choque: una de las cuales se dirige hacia el medio confinante y la otra se dirige hacia la pieza. Esta última produce un cráter microscópico por aplastamiento mecánico, generándose deformación plástica y un campo de tensiones residuales de compresión que mejoran las propiedades superficiales del material. La capacidad de los procesos LSP para mejorar las propiedades de materiales metálicos es indiscutible. En la bibliografía está reflejado el trabajo experimental y de simulación que se ha llevado a cabo a lo largo de los años en orden a optimizar el proceso. Sin embargo, hay pocos estudios que hayan tratado exhaustivamente la física del proceso. Esto es debido a la gran complejidad de la fenomenología física involucrada en los procesos LSP, con comportamientos no lineales tanto en la generación y dinámica del plasma como en la propagación de las ondas de choque en el material. Además, el elevado coste de los experimentos y su duración, así como el gran coste computacional que debían asumir los antiguos modelos numéricos, dificultó el proceso de optimización. No obstante, los nuevos sistemas de cálculo son cada vez más rápidos y, además, los programas de análisis de problemas no lineales por elementos finitos son cada vez más sofisticados, por lo que a día de hoy es posible desarrollar un modelo exhaustivo que no solo permita simular el proceso en situaciones simplificadas, sino que pueda ser empleado para optimizar los parámetros del tratamiento en casos reales y sobre áreas extensas. Por esta razón, en esta tesis se desarrolla y se valida un modelo numérico capaz de simular de manera sistemática tratamientos LSP en piezas reales, teniendo en cuenta la física involucrada en los mismos. En este sentido, cabe destacar la problemática del tratamiento LSP en placas delgadas. La capacidad del LSP para inducir tensiones residuales de compresión bajo la superficie de materiales con un espesor relativamente grueso (> 6 mm) con objeto de mejorar la vida en fatiga ha sido ampliamente demostrada. Sin embargo, el tratamiento LSP en especímenes delgados (típicamente < 6 mm, pero también mayores si es muy alta la intensidad del tratamiento) conlleva el efecto adicional del doblado de la pieza tratada, un hecho que puede ser aprovechado para procesos de conformado láser. Este efecto de doblado trae consigo una nueva clase de problemas en lo referente a los perfiles específicos de tensiones residuales en las piezas tratadas, ya que al equilibrarse las tensiones tras la retirada de su sujeción puede afectar considerablemente el perfil de tensiones residuales obtenido, lo que posiblemente puede derivar en la obtención de un perfil de tensiones residuales no deseado y, lo que puede ser aún más crítico, una deformación indeseable de la pieza en cuestión. Haciendo uso del modelo numérico desarrollado en esta Tesis, el análisis del problema del tratamiento LSP para la inducción de campos de tensiones residuales y la consecuente mejora de la vida en fatiga en piezas de pequeño espesor en un modo compatible con una deformación asumible se aborda de forma específica. La tesis está estructurada del siguiente modo: i) El capítulo 1 contiene una introducción al LSP, en la que se definen los procesos de tratamiento de materiales mediante ondas de choque generadas por láser. A continuación se expone una visión panorámica de las aplicaciones industriales de la tecnología LSP y, por último, se realiza una comparativa entre la tecnología LSP y otras tecnologías en competencia en el ámbito industrial: Shot Peening, Low Plasticity Burnishing y Waterjet Peening. ii) El capítulo 2 se divide en dos partes: fundamentos físicos característicos del tratamiento LSP y estado del arte de la modelización de procesos LSP. En cuanto a la primera parte, fundamentos físicos característicos del tratamiento LSP, en primer lugar se describe la física del tratamiento y los principales fenómenos que tienen lugar. A continuación se detalla la física de la interacción confinada en agua y la generación del pulso de presión asociado a la onda de choque. También se describe el proceso de saturación de la presión máxima por ruptura dieléctrica del agua y, por último, se describe la propagación de las ondas de choque y sus efectos en el material. En cuanto a la segunda parte, el estado del arte de la modelización de procesos LSP, recoge el conocimiento preexistente al desarrollo de la propia Tesis en los siguientes campos: modelización de la generación del plasma y su expansión, modelización de la ruptura dieléctrica del medio confinante, modelización del pulso de presión aplicado al material y la respuesta del mismo: inducción de tensiones residuales y deformaciones. iii) El capítulo 3 describe el desarrollo de un modelo propio para la simulación de las tensiones residuales y las deformaciones generadas por procesos LSP. En él se detalla la simulación de la propagación del pulso de presión en el material, los pormenores de su puesta en práctica mediante el método de los elementos finitos, la determinación de parámetros realistas de aplicación y se establece un procedimiento de validación de los resultados. iv) El capítulo 4 contiene los resultados de la aplicación del modelo a distintas configuraciones de interés en tratamientos LSP. En él se recoge un estudio del tratamiento LSP sobre áreas extensas que incluye un análisis de las tensiones residuales inducidas y un análisis sobre la influencia de la secuencia de barrido de los pulsos en las tensiones residuales y en las deformaciones. También se presenta un estudio específico de la problemática del tratamiento LSP en piezas de pequeño espesor y se detallan dos casos prácticos abordados en el CLUPM de gran interés tecnológico en función de las aplicaciones reales en las que se ha venido trabajando en los últimos años. v) En el capítulo 5 se presentan las conclusiones derivadas de los resultados obtenidos en la tesis. Concretamente, se destaca que el modelo desarrollado permite reproducir las condiciones experimentales de los procesos de LSP reales y predecir los efectos mecánicos inducidos por los mismos. Los anexos incluidos como parte accesoria contienen información importante que se ha utilizado en el desarrollo de la Tesis y que se desea incluir para hacer el volumen autoconsistente: i) En el anexo A se presenta una revisión de conceptos básicos sobre el comportamiento de los sólidos sometidos a ondas de choque [Morales04]. ii) El anexo B contiene la resolución analítica de la ecuación de ritmo utilizada en el código DRUPT [Morales04]. iii) El anexo C contiene la descripción de los procedimientos de uso del modelo de simulación desarrollado en la Tesis y el código fuente de la subrutina OVERLAP desarrollada para programar el solapamiento de pulsos en tratamientos LSP sobre áreas extensas. iv) El anexo D contiene un resumen de las principales técnicas para la medición de las tensiones residuales en los materiales [PorrolO] y [Gill2]. v) El anexo E contiene una descripción de las instalaciones experimentales del CLUPM en el que se han desarrollado los procesos LSP utilizados en la validación del modelo desarrollado [PorrolO].

Comportamiento frente a la durabilidad de morteros de reparación de cemento modificados con polímeros

El auge que ha surgido en los últimos años por la reparación de edificios y estructuras construidas con hormigón ha llevado al desarrollo de morteros de reparación cada vez más tecnológicos. En el desarrollo de estos morteros por parte de los fabricantes, surge la disyuntiva en el uso de los polímeros en sus formulaciones, por no encontrarse justificado en ocasiones el trinomio prestaciones/precio/aplicación. En esta tesis se ha realizado un estudio exhaustivo para la justificación de la utilización de estos morteros como morteros de reparación estructural como respuesta a la demanda actual disponiéndolo en tres partes: En la primera parte se realizó un estudio del arte de los morteros y sus constituyentes. El uso de los morteros se remonta a la antigüedad, utilizándose como componentes yeso y cal fundamentalmente. Los griegos y romanos desarrollaron el concepto de morteros de cal, introduciendo componentes como las puzolanas, cales hidraúlicas y áridos de polvo de mármol dando origen a morteros muy parecidos a los hormigones actuales. En la edad media y renacimiento se perdió la tecnología desarrollada por los romanos debido al extenso uso de la piedra en las construcciones civiles, defensivas y religiosas. Hubo que esperar hasta el siglo XIX para que J. Aspdin descubriese el actual cemento como el principal compuesto hidraúlico. Por último y ya en el siglo XX con la aparición de moléculas tales como estireno, melanina, cloruro de vinilo y poliésteres se comenzó a desarrollar la industria de los polímeros que se añadieron a los morteros dando lugar a los “composites”. El uso de polímeros en matrices cementantes dotan al mortero de propiedades tales como: adherencia, flexibilidad y trabajabilidad, como ya se tiene constancia desde los años 30 con el uso de caucho naturales. En la actualidad el uso de polímeros de síntesis (polivinialacetato, estireno-butadieno, viniacrílico y resinas epoxi) hacen que principalmente el mortero tenga mayor resistencia al ataque del agua y por lo tanto aumente su durabilidad ya que se minimizan todas las reacciones de deterioro (hielo, humedad, ataque biológico,…). En el presente estudio el polímero que se utilizó fue en estado polvo: polímero redispersable. Estos polímeros están encapsulados y cuando se ponen en contacto con el agua se liberan de la cápsula formando de nuevo el gel. En los morteros de reparación el único compuesto hidraúlico que hay es el cemento y es el principal constituyente hoy en día de los materiales de construcción. El cemento se obtiene por molienda conjunta de Clínker y yeso. El Clínker se obtiene por cocción de una mezcla de arcillas y calizas hasta una temperatura de 1450-1500º C por reacción en estado fundente. Para esta reacción se deben premachacar y homogeneizar las materias primas extraídas de la cantera. Son dosificadas en el horno con unas proporciones tales que cumplan con unas relación de óxidos tales que permitan formar las fases anhidras del Clínker C3S, C2S, C3A y C4AF. De la hidratación de las fases se obtiene el gel CSH que es el que proporciona al cemento de sus propiedades. Existe una norma (UNE-EN 197-1) que establece la composición, especificaciones y tipos de cementos que se fabrican en España. La tendencia actual en la fabricación del cemento pasa por el uso de cementos con mayores contenidos de adiciones (cal, puzolana, cenizas volantes, humo de sílice,…) con el objeto de obtener cementos más sostenibles. Otros componentes que influyen en las características de los morteros son: - Áridos. En el desarrollo de los morteros se suelen usar naturales, bien calizos o silícicos. Hacen la función de relleno y de cohesionantes de la matriz cementante. Deben ser inertes - Aditivos. Son aquellos componentes del mortero que son dosificados en una proporción menor al 5%. Los más usados son los superplastificantes por su acción de reductores de agua que revierte en una mayor durabilidad del mortero. Una vez analizada la composición de los morteros, la mejora tecnológica de los mismos está orientada al aumento de la durabilidad de su vida en obra. La durabilidad se define como la capacidad que éste tiene de resistir a la acción del ambiente, ataques químicos, físicos, biológicos o cualquier proceso que tienda a su destrucción. Estos procesos dependen de factores tales como la porosidad del hormigón y de la exposición al ambiente. En cuanto a la porosidad hay que tener en cuenta la distribución de macroporos, mesoporos y microporos de la estructura del hormigón, ya que no todos son susceptibles de que se produzca el transporte de agentes deteriorantes, provocando tensiones internas en las paredes de los mismos y destruyendo la matriz cementante Por otro lado los procesos de deterioro están relacionados con la acción del agua bien como agente directo o como vehículo de transporte del agente deteriorante. Un ambiente que resulta muy agresivo para los hormigones es el marino. En este caso los procesos de deterioro están relacionados con la presencia de cloruros y de sulfatos tanto en el agua de mar como en la atmosfera que en combinación con el CO2 y O2 forman la sal de Friedel. El deterioro de las estructuras en ambientes marinos se produce por la debilitación de la matriz cementante y posterior corrosión de las armaduras que provocan un aumento de volumen en el interior y rotura de la matriz cementante por tensiones capilares. Otras reacciones que pueden producir estos efectos son árido-álcali y difusión de iones cloruro. La durabilidad de un hormigón también depende del tipo de cemento y su composición química (cementos con altos contenidos de adición son más resistentes), relación agua/cemento y contenido de cemento. La Norma UNE-EN 1504 que consta de 10 partes, define los productos para la protección y reparación de estructuras de hormigón, el control de calidad de los productos, propiedades físico-químicas y durables que deben cumplir. En esta Norma se referencian otras 65 normas que ofrecen los métodos de ensayo para la evaluación de los sistemas de reparación. En la segunda parte de esta Tesis se hizo un diseño de experimentos con diferentes morteros poliméricos (con concentraciones de polímero entre 0 y 25%), tomando como referencia un mortero control sin polímero, y se estudiaron sus propiedades físico-químicas, mecánicas y durables. Para mortero con baja proporción de polímero se recurre a sistemas monocomponentes y para concentraciones altas bicomponentes en la que el polímero está en dispersión acuosa. Las propiedades mecánicas medidas fueron: resistencia a compresión, resistencia a flexión, módulo de elasticidad, adherencia por tracción directa y expansión-retracción, todas ellas bajo normas UNE. Como ensayos de caracterización de la durabilidad: absorción capilar, resistencia a carbonatación y adherencia a tracción después de ciclos hielo-deshielo. El objeto de este estudio es seleccionar el mortero con mejor resultado general para posteriormente hacer una comparativa entre un mortero con polímero (cantidad optimizada) y un mortero sin polímero. Para seleccionar esa cantidad óptima de polímero a usar se han tenido en cuenta los siguientes criterios: el mortero debe tener una clasificación R4 en cuanto a prestaciones mecánicas al igual que para evaluar sus propiedades durables frente a los ciclos realizados, siempre teniendo en cuenta que la adición de polímero no puede ser elevada para hacer el mortero competitivo. De este estudio se obtuvieron las siguientes conclusiones generales: - Un mortero normalizado no cumple con propiedades para ser clasificado como R3 o R4. - Sin necesidad de polímero se puede obtener un mortero que cumpliría con R4 para gran parte de las características medidas - Es necesario usar relaciones a:c< 0.5 para conseguir morteros R4, - La adición de polímero mejora siempre la adherencia, abrasión, absorción capilar y resistencia a carbonatación - Las diferentes proporciones de polímero usadas siempre suponen una mejora tecnológica en propiedades mecánicas y de durabilidad. - El polímero no influye sobre la expansión y retracción del mortero. - La adherencia se mejora notablemente con el uso del polímero. - La presencia de polímero en los morteros mejoran las propiedades relacionadas con la acción del agua, por aumento del poder cementante y por lo tanto de la cohesión. El poder cementante disminuye la porosidad. Como consecuencia final de este estudio se determinó que la cantidad óptima de polímero para la segunda parte del estudio es 2.0-3.5%. La tercera parte consistió en el estudio comparativo de dos morteros: uno sin polímero (mortero A) y otro con la cantidad optimizada de polímero, concluida en la parte anterior (mortero B). Una vez definido el porcentaje de polímeros que mejor se adapta a los resultados, se plantea un nuevo esqueleto granular mejorado, tomando una nueva dosificación de tamaños de áridos, tanto para el mortero de referencia, como para el mortero con polímeros, y se procede a realizar los ensayos para su caracterización física, microestructural y de durabilidad, realizándose, además de los ensayos de la parte 1, mediciones de las propiedades microestructurales que se estudiaron a través de las técnicas de porosimetría de mercurio y microscopia electrónica de barrido (SEM); así como propiedades del mortero en estado fresco (consistencia, contenido de aire ocluido y tiempo final de fraguado). El uso del polímero frente a la no incorporación en la formulación del mortero, proporcionó al mismo de las siguientes ventajas: - Respecto a sus propiedades en estado fresco: El mortero B presentó mayor consistencia y menor cantidad de aire ocluido lo cual hace un mortero más trabajable y más dúctil al igual que más resistente porque al endurecer dejará menos huecos en su estructura interna y aumentará su durabilidad. Al tener también mayor tiempo de fraguado, pero no excesivo permite que la manejabilidad para puesta en obra sea mayor, - Respecto a sus propiedades mecánicas: Destacar la mejora en la adherencia. Es una de las principales propiedades que confiere el polímero a los morteros. Esta mayor adherencia revierte en una mejora de la adherencia al soporte, minimización de las posibles reacciones en la interfase hormigón-mortero y por lo tanto un aumento en la durabilidad de la reparación ejecutada con el mortero y por consecuencia del hormigón. - Respecto a propiedades microestructurales: la porosidad del mortero con polímero es menor y menor tamaño de poro critico susceptible de ser atacado por agentes externos causantes de deterioro. De los datos obtenidos por SEM no se observaron grandes diferencias - En cuanto a abrasión y absorción capilar el mortero B presentó mejor comportamiento como consecuencia de su menor porosidad y su estructura microscópica. - Por último el comportamiento frente al ataque de sulfatos y agua de mar, así como al frente de carbonatación, fue más resistente en el mortero con polímero por su menor permeabilidad y su menor porosidad. Para completar el estudio de esta tesis, y debido a la gran importancia que están tomando en la actualidad factores como la sostenibilidad se ha realizado un análisis de ciclo de vida de los dos morteros objeto de estudio de la segunda parte experimental.In recent years, the extended use of repair materials for buildings and structures made the development of repair mortars more and more technical. In the development of these mortars by producers, the use of polymers in the formulations is a key point, because sometimes this use is not justified when looking to the performance/price/application as a whole. This thesis is an exhaustive study to justify the use of these mortars as a response to the current growing demand for structural repair. The thesis is classified in three parts:The first part is the study of the state of the art of mortars and their constituents.In ancient times, widely used mortars were based on lime and gypsum. The Greeks and Romans developed the concept of lime mortars, introducing components such as pozzolans, hydraulic limes and marble dust as aggregates, giving very similar concrete mortars to the ones used currently. In the middle Age and Renaissance, the technology developed by the Romans was lost, due to the extensive use of stone in the civil, religious and defensive constructions. It was not until the 19th century, when J. Aspdin discovered the current cement as the main hydraulic compound. Finally in the 20th century, with the appearance of molecules such as styrene, melanin, vinyl chloride and polyester, the industry began to develop polymers which were added to the binder to form special "composites".The use of polymers in cementitious matrixes give properties to the mortar such as adhesion, Currently, the result of the polymer synthesis (polivynilacetate, styrene-butadiene, vynilacrylic and epoxy resins) is that mortars have increased resistance to water attack and therefore, they increase their durability since all reactions of deterioration are minimised (ice, humidity, biological attack,...). In the present study the polymer used was redispersible polymer powder. These polymers are encapsulated and when in contact with water, they are released from the capsule forming a gel.In the repair mortars, the only hydraulic compound is the cement and nowadays, this is the main constituent of building materials. The current trend is centered in the use of higher contents of additions (lime, pozzolana, fly ash, silica, silica fume...) in order to obtain more sustainable cements. Once the composition of mortars is analyzed, the technological improvement is centred in increasing the durability of the working life. Durability is defined as the ability to resist the action of the environment, chemical, physical, and biological attacks or any process that tends to its destruction. These processes depend on factors such as the concrete porosity and the environmental exposure. In terms of porosity, it be considered, the distribution of Macropores and mesopores and pores of the concrete structure, since not all of them are capable of causing the transportation of damaging agents, causing internal stresses on the same walls and destroying the cementing matrix.In general, deterioration processes are related to the action of water, either as direct agent or as a transport vehicle. Concrete durability also depends on the type of cement and its chemical composition (cement with high addition amounts are more resistant), water/cement ratio and cement content. The standard UNE-EN 1504 consists of 10 parts and defines the products for the protection and repair of concrete, the quality control of products, physical-chemical properties and durability. Other 65 standards that provide the test methods for the evaluation of repair systems are referenced in this standard. In the second part of this thesis there is a design of experiments with different polymer mortars (with concentrations of polymer between 0 and 25%), taking a control mortar without polymer as a reference and its physico-chemical, mechanical and durable properties were studied. For mortars with low proportion of polymer, 1 component systems are used (powder polymer) and for high polymer concentrations, water dispersion polymers are used. The mechanical properties measured were: compressive strength, flexural strength, modulus of elasticity, adhesion by direct traction and expansion-shrinkage, all of them under standards UNE. As a characterization of the durability, following tests are carried out: capillary absorption, resistance to carbonation and pull out adhesion after freeze-thaw cycles. The target of this study is to select the best mortar to make a comparison between mortars with polymer (optimized amount) and mortars without polymer. To select the optimum amount of polymer the following criteria have been considered: the mortar must have a classification R4 in terms of mechanical performance as well as in durability properties against the performed cycles, always bearing in mind that the addition of polymer cannot be too high to make the mortar competitive in price. The following general conclusions were obtained from this study: - A standard mortar does not fulfill the properties to be classified as R3 or R4 - Without polymer, a mortar may fulfill R4 for most of the measured characteristics. - It is necessary to use relations w/c ratio < 0.5 to get R4 mortars - The addition of polymer always improves adhesion, abrasion, capillary absorption and carbonation resistance - The different proportions of polymer used always improve the mechanical properties and durability. - The polymer has no influence on the expansion and shrinkage of the mortar - Adhesion is improved significantly with the use of polymer. - The presence of polymer in mortars improves the properties related to the action of the water, by the increase of the cement power and therefore the cohesion. The cementitious properties decrease the porosity. As final result of this study, it was determined that the optimum amount of polymer for the second part of the study is 2.0 - 3.5%. The third part is the comparative study between two mortars: one without polymer (A mortar) and another with the optimized amount of polymer, completed in the previous part (mortar B). Once the percentage of polymer is defined, a new granular skeleton is defined, with a new dosing of aggregate sizes, for both the reference mortar, the mortar with polymers, and the tests for physical, microstructural characterization and durability, are performed, as well as trials of part 1, measurements of the microstructural properties that were studied by scanning electron microscopy (SEM) and mercury porosimetry techniques; as well as properties of the mortar in fresh State (consistency, content of entrained air and final setting time). The use of polymer versus non polymer mortar, provided the following advantages: - In fresh state: mortar with polymer presented higher consistency and least amount of entrained air, which makes a mortar more workable and more ductile as well as more resistant because hardening will leave fewer gaps in its internal structure and increase its durability. Also allow it allows a better workability because of the longer (not excessive) setting time. - Regarding the mechanical properties: improvement in adhesion. It is one of the main properties which give the polymer to mortars. This higher adhesion results in an improvement of adhesion to the substrate, minimization of possible reactions at the concrete-mortar interface and therefore an increase in the durability of the repair carried out with mortar and concrete. - Respect to microstructural properties: the porosity of mortar with polymer is less and with smaller pore size, critical to be attacked by external agents causing deterioration. No major differences were observed from the data obtained by SEM - In terms of abrasion and capillary absorption, polymer mortar presented better performance as a result of its lower porosity and its microscopic structure. - Finally behavior against attack by sulfates and seawater, as well as to carbonation, was better in the mortar with polymer because of its lower permeability and its lower porosity. To complete the study, due to the great importance of sustainability for future market facts, the life cycle of the two mortars studied was analysed.

Estudio de la adherencia de armaduras corroídas y su influencia en la capacidad resistente de elementos de hormigón armado

La verificación de la seguridad estructural, tanto de estructuras que permitan un cierto grado de deterioro en su dimensionado como de estructuras existentes deterioradas, necesita disponer de modelos de resistencia que tengan en cuenta los efectos del deterioro. En el caso de la corrosión de las armaduras en las estructuras de hormigón armado, la resistencia depende de múltiples factores tales como la sección del acero corroído, el diagrama tensión-deformación del acero corroído, la adherencia hormigón-acero corroído, la fisuración o desprendimiento del hormigón debido a la expansión de los productos de corrosión. En este sentido, la transferencia de las fuerzas a través de la superficie de contacto entre el hormigón y el acero, la adherencia, es uno de los aspectos más importantes a considerar y es la base del comportamiento del hormigón armado como elemento estructural. La adherencia debe asegurar el anclaje de las armaduras y transmitir la tensión tangencial que aparece en las mismas como consecuencia de la variación de las solicitaciones a lo largo de un elemento estructural. Como consecuencia de la corrosión de las armaduras, el desarrollo de la adherencia se altera y, por tanto, la transferencia de la tensión longitudinal. Esta Tesis Doctoral aborda el comportamiento en estado límite último de la adherencia en el hormigón estructural con armaduras corroídas. El objetivo principal es la obtención de un modelo suficientemente realista y fiable para la evaluación de la adherencia con armaduras corroídas en el marco de la verificación de la seguridad estructural de elementos de hormigón armado con armaduras corroídas. Para ello se ha llevado a cabo un programa experimental de ensayos tipo pull-out excéntricos, con diferentes probetas, unas sin corrosión y otras sometidas tanto a procesos de corrosión natural como a procesos de corrosión acelerada, con diferentes grados de deterioro. Este tipo de ensayo de adherencia representa de forma realista y fiable realista los esfuerzos de adherencia en la zona de anclaje. Por otra parte, para la realización de estos ensayos se ha puesto a punto, además del procedimiento de ensayo, un sistema de adquisición de datos entre los que se incluye el empleo de sensores de tipo fibra óptica con redes de Bragg embebidos en la armadura para determinar los parámetros representativos de la adherencia en el hormigón estructural con armaduras corroídas. Por otra parte, la recopilación de los datos de los estudios de adherencia con armaduras corroídas procedentes de la literatura científica, además de los resultados de la presente investigación, junto con la identificación de las variables relevantes en el comportamiento de la adherencia con armaduras sanas y corroídas ha servido para la obtención de una formulación realista y fiable para la evaluación conjunta de la adherencia con armaduras sanas y corroídas a partir de modelos de regresión múltiple. La formulación propuesta ha sido validada mediante criterios estadísticos y comparada con otras formulaciones propuestas en la literatura científica. Además se ha realizado un análisis de las variables influyentes de la formulación propuesta. También se ha obtenido un modelo numérico simple y eficiente, validado con alguno de los ensayos realizados en esta tesis, para simular la adherencia con armaduras sanas y corroídas. Finalmente, se presenta un procedimiento para realizar la evaluación de vigas deterioradas por corrosión mediante el método de los campos de tensiones que incluye la evaluación de la adherencia mediante la formulación sugerida en esta Tesis Doctoral. Las conclusiones alcanzadas en este trabajo han permitido evaluar la adherencia con armaduras corroídas de forma realista y fiable. Asimismo, se ha podido incluir la evaluación de la adherencia en el marco de la verificación de la seguridad estructural en elementos de hormigón armado deteriorados por corrosión. ABSTRACT Structural safety verification of both structures allowing a certain degree of deterioration in design and deteriorated existing structures needs strength models that factor in the effects of deterioration. In case of corrosion of steel bars in reinforced concrete structures, the resistance depends on many things such as the remaining cross-section of the corroded reinforcement bars, the stress-strain diagrams of steel, the concrete-reinforcement bond and corrosion-induced concrete cracking or spalling. Accordingly, the force transfer through the contact surface between concrete and reinforcement, bond, is one of the most important aspects to consider and it is the basis of the structural performance of reinforced concrete. Bond must assure anchorage of reinforcement and transmit shear stresses as a consequence of the different stresses along a structural element As a consequence of corrosion, the bond development may be affected and hence the transfer of longitudinal stresses. This PhD Thesis deals with ultimate limit state bond behaviour in structural concrete with corrode steel bars. The main objective is to obtain a realistic and reliable model for the assessment of bond within the context of structural safety verifications of reinforced concrete members with corroded steel bars. In that context, an experimental programme of eccentric pull-out tests were conducted, with different specimens, ones without corrosion and others subjected to accelerated or natural corrosion with different corrosion degrees. This type of bond test reproduces in a realistic and reliable way bond stresses in the anchorage zone. Moreover, for conducting these tests it was necessary to develop both a test procedure and also a data acquisition system including the use of an embedded fibre-optic sensing system with fibre Bragg grating sensors to obtain the representative parameters of bond strength in structural concrete with corroded steel bars. Furthermore, the compilation of data from bond studies with corroded steel bars from scientific literature, including tests conducted in the present study, along with the identification of the relevant variables influencing bond behaviour for both corroded and non-corroded steel bars was used to obtain a realistic and reliable formulation for bond assessment in corroded and non-corroded steel bars by multiple linear regression analysis. The proposed formulation was validated with a number of statistical criteria and compared to other models from scientific literature. Moreover, an analysis of the influencing variables of the proposed formulation has been performed. Also, a simplified and efficient numerical model has been obtained and validated with several tests performed in this PhD Thesis for simulating the bond in corroded and non-corroded steel bars. Finally, a proposal for the assessment of corrosion-damaged beams with stress field models including bond assessment with the proposed formulation is presented. The conclusions raised in this work have allowed a realistic and reliable bond assessment in corroded steel bars. Furthermore, bond assessment has been included within the context of structural safety verifications in corrosion-damaged reinforced concrete elements.

Evaluación de efectos de biocidas contenidos en recubrimientos “antifouling “(AF coatings) en ecosistemas marinos

De entre los diversos grupos de contaminantes que pueden ser dañinos para ecosistemas acuáticos, sobresalen en los últimos años los biocidas utilizados como principio activo en recubrimientos antifouling ó pinturas anti-incrustantes para cascos de barcos y todo tipo de equipamiento sumergido ó en contacto con agua. Estos recubrimientos se aplican como sistema de protección para combatir la formación y asentamiento de comunidades bioincrustantes (fouling) frente a superficies expuestas al agua, también tienen como finalidad proteger frente a la corrosión de tipo químico y biológico. Normalmente estas pinturas anti-incrustantes son aplicadas en embarcaciones comerciales y de recreo, plataformas petrolíferas, tuberías submarinas, compuertas de presas, instalaciones destinadas a acuicultura, entre otro equipamiento. La utilización de biocidas en la formulación de pinturas anti-incrustantes para barcos ha sido propuesta por muchos investigadores como la aplicación de más impacto para los ecosistemas marinos, debido al intenso tráfico marítimo mundial que provoca la difusión de biocidas contaminantes en los mares, sobre todo en zonas costeras, bahías y puertos que es donde se magnifica el problema. Los llamados recubrimientos antifouling de segunda generación fueron los primeros que emplearon el tributilestaño (TBT) como principio activo en su formulación, a pesar de su gran eficacia y amplia utilización, al cabo del tiempo se ha demostrado su alta toxicidad y persistencia; por lo que existe una gran actividad investigadora en la búsqueda de alternativas asimismo eficientes pero más respetuosas con el medio marino. En este trabajo se pretende comparar los efectos para ecosistemas marinos del TBT y cinco biocidas como son dibutilestaño dicloruro, diuron (diclorofenil dimetil urea), piritionato de Zn ó Zn omadine, óxido de cobre (I) y DCOIT (Dicloro-2-n-octil-4-isotiazol-3-ona). Estos biocidas se han seleccionado en función de su naturaleza química diferenciada, distintas solubilidades en agua, eficacia, ecotoxicidad, persistencia y bioacumulación fundamentalmente. Para proceder a la clasificación del riesgo para ecosistema marino de los biocidas mencionados, nos valdremos de dos metodologías, una será la evaluación de unos índices de riesgo de biocidas para ecosistemas acuáticos con el fin de realizar una clasificación prospectiva de los mismos, basada en criterios PBT (Persistencia, Bioacumulación y Toxicidad para organismos acuáticos) y otra será una evaluación de la razón de la EXPOSICIÓN, valorada como PEC (Predictive Environmental Concentration) con relación a los EFECTOS originados, valorados como PNEC (Predicted No-Effect Concentration). Para cuantificar PEC nos valdremos de modelizaciones para ecosistemas marinos como MAMPEC (Marine Antifoulant Model to Predict Environmental Concentrations). Para cuantificar PNEC se hace uso de bioensayos a corto o largo plazo en organismos acuáticos. De esta manera podremos agrupar los biocidas en diversas categorías de riesgo y así poder decidir cuando su impacto medioambiental es asumible ó no asumible, alternativas posibles y en todo caso que decisiones se deben tomar al respecto.

High power beam dump project for the accelerator prototype LIPAc: Cooling design and analysis

En el campo de la fusión nuclear y desarrollándose en paralelo a ITER (International Thermonuclear Experimental Reactor), el proyecto IFMIF (International Fusion Material Irradiation Facility) se enmarca dentro de las actividades complementarias encaminadas a solucionar las barreras tecnológicas que aún plantea la fusión. En concreto IFMIF es una instalación de irradiación cuya misión es caracterizar materiales resistentes a condiciones extremas como las esperadas en los futuros reactores de fusión como DEMO (DEMOnstration power plant). Consiste de dos aceleradores de deuterones que proporcionan un haz de 125 mA y 40 MeV cada uno, que al colisionar con un blanco de litio producen un flujo neutrónico intenso (1017 neutrones/s) con un espectro similar al de los neutrones de fusión [1], [2]. Dicho flujo neutrónico es empleado para irradiar los diferentes materiales candidatos a ser empleados en reactores de fusión, y las muestras son posteriormente examinadas en la llamada instalación de post-irradiación. Como primer paso en tan ambicioso proyecto, una fase de validación y diseño llamada IFMIFEVEDA (Engineering Validation and Engineering Design Activities) se encuentra actualmente en desarrollo. Una de las actividades contempladas en esta fase es la construcción y operación de una acelarador prototipo llamado LIPAc (Linear IFMIF Prototype Accelerator). Se trata de un acelerador de deuterones de alta intensidad idéntico a la parte de baja energía de los aceleradores de IFMIF. Los componentes del LIPAc, que será instalado en Japón, son suministrados por diferentes países europeos. El acelerador proporcionará un haz continuo de deuterones de 9 MeV con una potencia de 1.125 MW que tras ser caracterizado con diversos instrumentos deberá pararse de forma segura. Para ello se requiere un sistema denominado bloque de parada (Beam Dump en inglés) que absorba la energía del haz y la transfiera a un sumidero de calor. España tiene el compromiso de suministrar este componente y CIEMAT (Centro de Investigaciones Energéticas Medioambientales y Tecnológicas) es responsable de dicha tarea. La pieza central del bloque de parada, donde se para el haz de iones, es un cono de cobre con un ángulo de 3.5o, 2.5 m de longitud y 5 mm de espesor. Dicha pieza está refrigerada por agua que fluye en su superficie externa por el canal que se forma entre el cono de cobre y otra pieza concéntrica con éste. Este es el marco en que se desarrolla la presente tesis, cuyo objeto es el diseño del sistema de refrigeración del bloque de parada del LIPAc. El diseño se ha realizado utilizando un modelo simplificado unidimensional. Se han obtenido los parámetros del agua (presión, caudal, pérdida de carga) y la geometría requerida en el canal de refrigeración (anchura, rugosidad) para garantizar la correcta refrigeración del bloque de parada. Se ha comprobado que el diseño permite variaciones del haz respecto a la situación nominal siendo el flujo crítico calorífico al menos 2 veces superior al nominal. Se han realizado asimismo simulaciones fluidodinámicas 3D con ANSYS-CFX en aquellas zonas del canal de refrigeración que lo requieren. El bloque de parada se activará como consecuencia de la interacción del haz de partículas lo que impide cualquier cambio o reparación una vez comenzada la operación del acelerador. Por ello el diseño ha de ser muy robusto y todas las hipótesis utilizadas en la realización de éste deben ser cuidadosamente comprobadas. Gran parte del esfuerzo de la tesis se centra en la estimación del coeficiente de transferencia de calor que es determinante en los resultados obtenidos, y que se emplea además como condición de contorno en los cálculos mecánicos. Para ello por un lado se han buscado correlaciones cuyo rango de aplicabilidad sea adecuado para las condiciones del bloque de parada (canal anular, diferencias de temperatura agua-pared de decenas de grados). En un segundo paso se han comparado los coeficientes de película obtenidos a partir de la correlación seleccionada (Petukhov-Gnielinski) con los que se deducen de simulaciones fluidodinámicas, obteniendo resultados satisfactorios. Por último se ha realizado una validación experimental utilizando un prototipo y un circuito hidráulico que proporciona un flujo de agua con los parámetros requeridos en el bloque de parada. Tras varios intentos y mejoras en el experimento se han obtenido los coeficientes de película para distintos caudales y potencias de calentamiento. Teniendo en cuenta la incertidumbre de las medidas, los valores experimentales concuerdan razonablemente bien (en el rango de 15%) con los deducidos de las correlaciones. Por motivos radiológicos es necesario controlar la calidad del agua de refrigeración y minimizar la corrosión del cobre. Tras un estudio bibliográfico se identificaron los parámetros del agua más adecuados (conductividad, pH y concentración de oxígeno disuelto). Como parte de la tesis se ha realizado asimismo un estudio de la corrosión del circuito de refrigeración del bloque de parada con el doble fin de determinar si puede poner en riesgo la integridad del componente, y de obtener una estimación de la velocidad de corrosión para dimensionar el sistema de purificación del agua. Se ha utilizado el código TRACT (TRansport and ACTivation code) adaptándalo al caso del bloque de parada, para lo cual se trabajó con el responsable (Panos Karditsas) del código en Culham (UKAEA). Los resultados confirman que la corrosión del cobre en las condiciones seleccionadas no supone un problema. La Tesis se encuentra estructurada de la siguiente manera: En el primer capítulo se realiza una introducción de los proyectos IFMIF y LIPAc dentro de los cuales se enmarca esta Tesis. Además se describe el bloque de parada, siendo el diseño del sistema de rerigeración de éste el principal objetivo de la Tesis. En el segundo y tercer capítulo se realiza un resumen de la base teórica así como de las diferentes herramientas empleadas en el diseño del sistema de refrigeración. El capítulo cuarto presenta los resultados del relativos al sistema de refrigeración. Tanto los obtenidos del estudio unidimensional, como los obtenidos de las simulaciones fluidodinámicas 3D mediante el empleo del código ANSYS-CFX. En el quinto capítulo se presentan los resultados referentes al análisis de corrosión del circuito de refrigeración del bloque de parada. El capítulo seis se centra en la descripción del montaje experimental para la obtención de los valores de pérdida de carga y coeficiente de transferencia del calor. Asimismo se presentan los resultados obtenidos en dichos experimentos. Finalmente encontramos un capítulo de apéndices en el que se describen una serie de experimentos llevados a cabo como pasos intermedios en la obtención del resultado experimental del coeficiente de película. También se presenta el código informático empleado para el análisis unidimensional del sistema de refrigeración del bloque de parada llamado CHICA (Cooling and Heating Interaction and Corrosion Analysis). ABSTRACT In the nuclear fusion field running in parallel to ITER (International Thermonuclear Experimental Reactor) as one of the complementary activities headed towards solving the technological barriers, IFMIF (International Fusion Material Irradiation Facility) project aims to provide an irradiation facility to qualify advanced materials resistant to extreme conditions like the ones expected in future fusion reactors like DEMO (DEMOnstration Power Plant). IFMIF consists of two constant wave deuteron accelerators delivering a 125 mA and 40 MeV beam each that will collide on a lithium target producing an intense neutron fluence (1017 neutrons/s) with a similar spectra to that of fusion neutrons [1], [2]. This neutron flux is employed to irradiate the different material candidates to be employed in the future fusion reactors, and the samples examined after irradiation at the so called post-irradiative facilities. As a first step in such an ambitious project, an engineering validation and engineering design activity phase called IFMIF-EVEDA (Engineering Validation and Engineering Design Activities) is presently going on. One of the activities consists on the construction and operation of an accelerator prototype named LIPAc (Linear IFMIF Prototype Accelerator). It is a high intensity deuteron accelerator identical to the low energy part of the IFMIF accelerators. The LIPAc components, which will be installed in Japan, are delivered by different european countries. The accelerator supplies a 9 MeV constant wave beam of deuterons with a power of 1.125 MW, which after being characterized by different instruments has to be stopped safely. For such task a beam dump to absorb the beam energy and take it to a heat sink is needed. Spain has the compromise of delivering such device and CIEMAT (Centro de Investigaciones Energéticas Medioambientales y Tecnológicas) is responsible for such task. The central piece of the beam dump, where the ion beam is stopped, is a copper cone with an angle of 3.5o, 2.5 m long and 5 mm width. This part is cooled by water flowing on its external surface through the channel formed between the copper cone and a concentric piece with the latter. The thesis is developed in this realm, and its objective is designing the LIPAc beam dump cooling system. The design has been performed employing a simplified one dimensional model. The water parameters (pressure, flow, pressure loss) and the required annular channel geometry (width, rugoisty) have been obtained guaranteeing the correct cooling of the beam dump. It has been checked that the cooling design allows variations of the the beam with respect to the nominal position, being the CHF (Critical Heat Flux) at least twice times higher than the nominal deposited heat flux. 3D fluid dynamic simulations employing ANSYS-CFX code in the beam dump cooling channel sections which require a more thorough study have also been performed. The beam dump will activateasaconsequenceofthe deuteron beam interaction, making impossible any change or maintenance task once the accelerator operation has started. Hence the design has to be very robust and all the hypotheses employed in the design mustbecarefully checked. Most of the work in the thesis is concentrated in estimating the heat transfer coefficient which is decisive in the obtained results, and is also employed as boundary condition in the mechanical analysis. For such task, correlations which applicability range is the adequate for the beam dump conditions (annular channel, water-surface temperature differences of tens of degrees) have been compiled. In a second step the heat transfer coefficients obtained from the selected correlation (Petukhov- Gnielinski) have been compared with the ones deduced from the 3D fluid dynamic simulations, obtaining satisfactory results. Finally an experimental validation has been performed employing a prototype and a hydraulic circuit that supplies a flow with the requested parameters in the beam dump. After several tries and improvements in the experiment, the heat transfer coefficients for different flows and heating powers have been obtained. Considering the uncertainty in the measurements the experimental values agree reasonably well (in the order of 15%) with the ones obtained from the correlations. Due to radiological reasons the quality of the cooling water must be controlled, hence minimizing the copper corrosion. After performing a bibligraphic study the most adequate water parameters were identified (conductivity, pH and dissolved oxygen concentration). As part of this thesis a corrosion study of the beam dump cooling circuit has been performed with the double aim of determining if corrosion can pose a risk for the copper beam dump , and obtaining an estimation of the corrosion velocitytodimension the water purification system. TRACT code(TRansport and ACTivation) has been employed for such study adapting the code for the beam dump case. For such study a collaboration with the code responsible (Panos Karditsas) at Culham (UKAEA) was established. The work developed in this thesis has supposed the publication of three articles in JCR journals (”Journal of Nuclear Materials” y ”Fusion Engineering and Design”), as well as presentations in more than four conferences and relevant meetings.

Optimización de la gasificación de lodos de estaciones depuradoras de aguas residuales urbanas para minimizar la formación de alquitranes

La gasificación de lodos de depuración es una alternativa atractiva para generar gases combustibles como H2 y CO. A su vez, estos gases pueden emplearse como materias primas para la obtención de productos químicos orgánicos y combustibles líquidos. Sin embargo, la gasificación no está exenta de problemas como el ligado a la generación de residuos sólidos y alquitrán. El alquitrán en el gas puede ser un inconveniente para emplear el gas como combustible por las obstrucciones y corrosión en los equipos. Dado que las condiciones de gasificación influyen en la producción de alquitrán, este trabajo de investigación se ha centrado en analizar la influencia de parámetros como la temperatura, la carga de alimentación, el tamaño de partícula, el agente gasificante y la utilización de catalizadores en la gasificación en lecho fluidizado de lodos de depuración. Adicionalmente a la medición del efecto de los anteriores parámetros en la producción y composición del alquitrán, también se ha cuantificado su influencia en la producción y composición del gas y en producción del residuo carbonoso. Los resultados muestran que el incremento de la carga de alimentación (kg/h.m2) provoca el descenso de la producción de gas combustible y el incremento del residuo carbonoso y del alquitrán debido a la reducción del tiempo de residencia del gas lo que supone un menor tiempo disponible para las reacciones gas-gas y gas-sólido ligadas a la conversión del alquitrán y del residuo carbonoso en gases combustibles. También se ha comprobado que, el aumento del tamaño de partícula, al incrementar el tiempo de calentamiento de ésta, tiene un efecto similar en los productos de la gasificación que el derivado del incremento en la carga de alimentación. La utilización de una temperatura de gasificación alta (850 ºC), el empleo de aire-vapor como agente gasificante y/o catalizadores primarios como la dolomía consiguen reducir la producción de alquitrán. ABSTRACT Gasification of sewage sludge is an attractive alternative for generating of fuel gases such as H2 and CO. These gases, in turn, can be used as raw materials for the production of organic chemicals and liquid fuel. However, gasification is not without problems as the linked ones to production of char and tar. The tar in the gas can be an inconvenience for to use it as fuel by the problems of blockage and corrosion in the equipments. Since the gasification conditions affect the production of tar, this research has focused on analysing the influence of parameters such as temperature, throughput, the particle size, the gasifying agent and the use of catalysts in the fluidized bed gasification of sewage sludge. In addition to measuring the effect of the above parameters on the production and composition of the tar, it has also been quantified their influence on the yield and composition of the gas and char production. The results show that higher throughput (kg/h.m2) leads to a reduction of fuel gas production and an increase in the production of char and tar, this owes to a lower of gas residence time or what is the same thing less time available for gas-solid and gas-gas reactions attached to the conversion of tar and char to fuel gases. There has also been proven that the rising in particle size, by the increasing heating time of it, has a similar effect in the products of gasification that the results by the rise in the throughput. The applications a high gasification temperature (850 ° C), the use of air-steam as gasifying agent and/or dolomite as primary catalysts are able to reduce the production of tar.

Representación tridimensional de vainas de bala de la batalla del Jarama de la Guerra Civil Española, mediante utilización de tecnología escáner láser 3D.

El objetivo del presente Proyecto Fin de Carrera (PFC) consiste en obtener la representación tridimensional de vainas de bala de la batalla del Jarama de la Guerra Civil Española, mediante la utilización de tecnología escáner láser 3D. Se plantea en segundo lugar el análisis del comportamiento del escáner y de la modelización 3D en relación al material de las vainas y la corrosión que se ha producido en ellas. Se realizaron ensayos con vainas y puntas de balas de materiales metálicos de mayor o menor complejidad y se concluye con el estudio de las diversas vainas de bala de la Batalla del Jarama de la Guerra Civil Española seleccionadas para este trabajo. El modelo se obtendrá con una precisión interna de ± 1 mm.

Recubrimientos autolubricantes cuasicristalinos tipo composite depositados mediante proyección térmica para aplicaciones espaciales y de alta temperatura

Los recubrimientos lubricantes sólidos son requeridos para reducir la fricción y prevenir el desgaste en componentes que operan a altas temperaturas o en vacío (vehículos espaciales, industria química, motores diésel, turbinas aeronáuticas y de generación de energía…). Los lubricantes líquidos pierden sus características cuando las condiciones de presión, temperatura o ambientales son severas (oxidación, inestabilidad térmica, volatilidad,…), por ejemplo los aceites minerales convencionales se descomponen a temperaturas próximas a 200 ºC. Por tanto, la única manera de poder conseguir una adecuada lubricación a temperaturas extremas es por medio de sólidos, que cada vez más, se aplican en forma de recubrimientos. Estos recubrimientos podrían ser empleados en componentes de vehículos espaciales reutilizables, donde se pueden alcanzar, en la reentrada en la atmósfera, temperaturas de 700 ºC (bisagras, rodamientos, articulaciones y zonas de sellado en las superficies de control, y rodamientos de las turbobombas y las cajas de engranajes). Dichos recubrimientos también deberían ser capaces de proporcionar una lubricación efectiva a bajas temperaturas para las operaciones en tierra, para las operaciones de arranque en frío, incluso en el espacio. El conjunto de requisitos que tendrían que satisfacer las capas tribológicas relacionadas con estas condiciones extremas es muy diverso, lo que hace que el concepto de capas tipo composite (aquéllas constituidas por varios componentes) sea, en principio, muy adecuado para estas aplicaciones. Recubrimientos composite proyectados térmicamente constituidos por una matriz dura y conteniendo lubricantes sólidos pueden ser una buena solución desde el punto de vista tribológico. El “Lewis Research Centre” de la NASA ha estado desarrollando recubrimientos autolubricantes tipo composite, constituidos por la combinación de materiales duros como el carburo de cromo, junto con lubricantes sólidos como plata o la eutéctica de fluoruros de calcio y bario, en una matriz de NiCr, para su uso en aplicaciones terrestres a alta temperatura. Estos recubrimientos han sido aplicados mediante proyección térmica, siendo denominados como series PS100, PS200, PS300 y PS400, reduciendo de forma significativa el coeficiente de fricción y mejorando la resistencia al desgaste en un amplio margen de temperaturas. Otra nueva familia de materiales con comportamiento tribológico prometedor son las aleaciones cuasicristalinas (QC). Presentan características muy atractivas: alta dureza, baja fricción, alto límite elástico de compresión... Son muy frágiles como materiales másicos, por lo que se intentan aplicar en forma de recubrimientos. Se pueden depositar mediante proyección térmica. Algunos de estos materiales cuasicristalinos, como AlCoFeCr, poseen coeficientes de dilatación próximos al de los materiales metálicos, alta estabilidad térmica, baja conductividad térmica y una elevada resistencia a la oxidación y a la corrosión en caliente. En esta tesis se han desarrollado recubrimientos tipo composite conteniendo cuasicristales como componente antidesgaste, NiCr como componente tenaz, y Ag y la eutéctica de BaF2-CaF2, como lubricantes sólidos. Estos recubrimientos han sido depositados con diferentes composiciones (denominadas TH100, TH103, TH200, TH400, TH600…) mediante distintos procesos de proyección térmica: plasma en aire (PS), plasma en baja presión (LPPS) y combustión a alta velocidad (HVOF). Los recubrimientos se han generado sobre el sustrato X-750, una superaleación base níquel, endurecible por precipitación, con muy buena resistencia mecánica y a la oxidación hasta temperaturas de 870 ºC y, además, es empleada en aplicaciones aeroespaciales e industriales. Los recubrimientos han sido caracterizados microestructuralmente en INTA (Instituto Nacional de Técnica Aeroespacial), mediante SEM-EDS (Scanning Electronic Microscopy-Energy Dispersive Spectroscopy) y XRD (X-Ray Diffraction), y tribológicamente mediante medidas de microdureza y ensayos en tribómetro POD (Pin On Disc) para determinar los coeficientes de fricción y de desgaste. Los recubrimientos han sido ensayados tribológicamente a alta temperatura en INTA y en vacío en AMTTARC (Aerospace and Space Materials Technology Testhouse – Austrian Research Centres), en Seibersdorf (Austria). Se ha estudiado la influencia de la carga normal aplicada, la velocidad lineal y el material del pin. De entre las diferentes series de recubrimientos cuasicristalinos tipo composite desarrolladas, dos de ellas, TH100 y TH103 han presentado una excelente calidad microestructural (baja porosidad, distribución uniforme de fases…) y se han mostrado como excelentes recubrimientos antidesgaste. Sin embargo, estas capas presentan un pobre comportamiento como autolubricantes a temperatura ambiente, aunque mejoran mucho a alta temperatura o en vacío. Los resultados del trabajo presentado en esta tesis han proporcionado nuevo conocimiento respecto al comportamiento tribológico de recubrimientos autolubricantes cuasicristalinos tipo composite depositados por proyección térmica. Sin embargo, dichos resultados, aunque son muy prometedores, no han puesto de manifiesto el adecuado comportamiento autolubricante que se pretendía y, además, como ocurre en cualquier trabajo de investigación, durante el desarrollo del mismo siempre aparecen nuevas dudas por resolver. Se proponen nuevas líneas de trabajo futuro que complementen los resultados obtenidos y que puedan encaminar hacia la obtención de un recubrimiento que mejore su comportamiento autolubricante. ABSTRACT Solid lubricant coatings are required to reduce friction and prevent wear in components that operate at high temperatures or under vacuum (space vehicles, chemical industry, diesel engines, power generation turbines and aeronautical turbines, for instance). In these cases neither greases nor liquid lubricants can be employed and the only practicable approach to lubrication in such conditions is by means of solids. These are increasingly applied in the form of coatings which should exhibit low shear strength, whilst maintaining their chemical stability at extremes temperatures and in the space environment. In the space field, these coatings would be employed in re-usable space plane applications, such as elevon hinges, where temperatures of 700 ºC are reached during re-entry into the Earth’s atmosphere. These coatings should also be capable of providing effective lubrication at lower temperatures since “cold start” operation may be necessary, even in the space environment. The diverse and sometimes conflictive requirements in high temperature and space-related tribological coatings make the concept of composite coatings highly suitable for these applications. Thermal-sprayed composites containing solid lubricants in a hard matrix perform well tribologically. NASA‘s Lewis Research Centre had developed self-lubricating composite coatings for terrestrial use, comprising hard materials like chromium carbide as well as solid lubricant additives such as silver and BaF2-CaF2 eutectic on a Ni-Cr matrix. These coatings series, named PS100, PS200, PS300 and PS400, are applied by thermal spray and significantly reduce friction coefficients, improving wear resistance over a wide temperature range. Quasicrystalline alloys (QC) constitute a new family of materials with promising tribological behaviour. Some QC materials exhibit a combination of adequate antifriction properties: low friction coefficient, high hardness and high yield strength under compression, and can be easily produced as coatings on top of metallic and non-metallic materials. Among these QC alloys, AlCoFeCr has high hardness (700 HV0.1), a thermal expansion coefficient close to that of metals, high thermal stability, low thermal conductivity and good oxidation and hot corrosion resistance. However most QC materials have the disadvantage of being very brittle. In order to take advantage of the excellent tribological properties of QCs, thick composite lubricant coatings were prepared containing them as the hard phase for wear resistance, Ag and BaF2-CaF2 eutectic as lubricating materials and NiCr as the tough component. These coatings were deposited in different composition mixtures (named TH100, TH103, TH200, TH400, TH600…) by different thermal spray processes: air plasma spray (PS), low pressure plasma spray (LPPS) and high velocity oxy-fuel (HVOF), on X-750 substrates. X-750 is an age-hardenable nickel-base superalloy with very good strength and a good resistance to oxidising combustion gas environments at temperatures up to about 870 ºC and it is widely used in aerospace and industrial applications. Coatings have been characterized microstructurally, at INTA (National Institute for Aerospace Technology), by means of SEM-EDS (Scanning Electronic Microscopy- Energy Dispersive Spectroscopy) and XRD (X-Ray Diffraction), and tribologically by microhardness measurements and pin-on-disc testing to determine friction coefficients as well as wear resistance. The coatings were tested tribologically at high temperature at INTA and under vacuum at AMTT-ARC (Aerospace and Space Materials Technology Testhouse – Austrian Research Centres), in Seibersdorf (Austria). Different loads, linear speeds and pin materials were studied. TH100 and TH103 QC alloy matrix composite coatings were deposited by HVOF with excellent microstructural quality (low porosity, uniform phase distribution) and showed to be excellent wear resistant coatings. However these QC alloy matrix composite coatings are poor as a self-lubricant at room temperature but much better at high temperature or in vacuum. The results from the work performed within the scope of this thesis have provided new knowledge concerning the tribological behavior of self-lubricating quasicrystalline composite coatings deposited by thermal spraying. Although these results are very promising, they have not shown an adequate self-lubricating behavior as was intended, and also, as in any research, the results have in addition raised new questions. Future work is suggested to complement the results of this thesis in order to improve the selflubricating behaviour of the coatings.

Modelado de fractura dúctil sobre aceros modificados superficialmente 545-A

Históricamente la fractura ha sido considerada siempre como un efecto indeseado entre los materiales, dado que su aparición supone un cese del material en servicio, puesto que un material fracturado carece de importancia desde el punto de vista comercial. Consecuentemente, la Mecánica de Fractura ha experimentado un desarrollo importante en las últimas décadas como no lo hizo en toda la historia de los materiales. El desarrollo de nuevos campos a nivel científico y técnico han estado de la mano con el desarrollo de nuevos materiales que satisfagan las necesidades particulares de cada sector o aplicación. Este requerimiento se ve acentuado cuando se incorpora el aspecto económico, dado que, así como se necesitan materiales con mayor resistencia a la fractura, corrosión etc, también se necesita que su precio en el mercado sea accesible y que permita una aplicación rentable. En los últimos 70 años, desde los requerimientos de nuevos materiales resistentes a la fractura con los buques Liberty hasta el boom petrolero, pasando por las aplicaciones aeroespaciales se han desarrollado diversas teorías que explican el comportamiento de los materiales, en cuando a la tenacidad a la fractura en distintas temperaturas, composiciones químicas, materiales compuestos etc. Uno de los sectores que más ha demandado un desarrollo, por su amplitud en cuanto a requerimientos y consumo global, así como su impacto en la economía mundial, es el sector de gas, petróleo y petroquímica. Muchos de los proyectos que se intentaron desarrollar hasta hace menos de 25 años eran inviables por su elevado coste de ejecución y su bajo retorno de inversión debido a la caída de los precios del petróleo. Con una demanda creciente a nivel mundial y unos precios que apuntan hacia la estabilización o alza moderada, nuevos sistemas de trasporte por tuberías han sido necesarios desarrollar, desde el punto de vista de ingeniería, con el menos coste posible y de un modo seguro. Muchas de estas aplicaciones se vieron incrementadas cuando nuevos requerimientos en cuanto a resistencia a la corrosión fueron necesarios: demanda de materiales que no se corroan, con prestaciones seguras a nivel mecánico y un bajo coste. Esta nueva etapa se conoce como Aleaciones Resistentes a la Corrosión (CRA´s por sus siglas en inglés) en las cuales uno de los factores de diseño seguro recaían indiscutiblemente en la mecánica de fractura. Por estas razones era necesario entender como influía en la resistencia a la fractura las aportaciones que podrían hacerse sobre una superficie metálica. Al realizar el presente estudio se comenzó analizando la influencia que tenían modificaciones en el rango iónico sobre aceros al carbono. Estudios previos sobre láminas de acero ferrítico usadas en reactores de fisión nuclear demostraron que aportes de iones, en este particular el Helio, influían en el comportamiento de la tenacidad a la fractura en función de la temperatura. De este modo, un primer análisis fue hecho sobre la influencia de iones de nitrógeno aportados sobre superficies de acero al carbono y como modificaban su tenacidad a la fractura. Este primer análisis sirvió para comprobar el impacto que tenían pequeñas dosis de iones de nitrógeno en la tenacidad a la fractura. Otro desarrollo con una mayor aplicación industrial fue hecho sobre superficies de acero al carbono con aporte por soldadura de los materiales más usados para evitar la corrosión. El análisis se centró fundamentalmente en la influencia que tenían distintos materiales aportados como el MONEL 400, DUPLEX 928, INCONEL 625 y STAINLESS-STEEL 316 en referencia a características de diseño como la tensión elástica y la tensión a la rotura. Este análisis permitió conocer el impacto de los materiales aportados en los ensayos de tracción en probetas de acero al carbono. Una explicación acerca del comportamiento fue soportada por el análisis macrofractográfico de los perfiles fracturados y las macro deformaciones en la superficie de las probetas. Un posterior desarrollo teórico permitió modelar matemáticamente la fractura de las probetas aportadas por soldadura en la región elástica por medio de la Ley de Hooke, así como la teoría de Plasticidad de Hill para la región de deformación plástica. ABSTRACT Fracture mechanics has been extensively studied in the last 70 years by the constant requirements of new materials with low costs. These requirements have allowed surface modified welded materials in which it is necessary to know the influence of design fundamentals with the material surface welded. Several specimens have been studied for ductile fracture in longitudinal tensile tests for carbon steel surface-modified by weld overlay MONEL 400, DUPLEX 928, INCONEL 625 and STAINLESS-STEEL 316. Similarly of macro photographic analyzes to level the fractured surfaces that explain the behavior curves obtained in Tensile – displacement charts. The contribution of weld overlay material shows a significant impact on the yield and tensile stress of the specimens which was modeled according to Hooke's law for elastic area and Hill´s theory of plasticity to the plastic one.

Desarrollo de métodos para la evaluación integrada de propiedades mecánicas y superficiales inducidas en materiales metálicos mediante tratamiento superficial por ondas de choque generadas por láser

El tratamiento superficial por ondas de choque generadas por láser, LSP, es una técnica cuyo principal objetivo es el de la modificación del estado tensional de las primeras micras en profundidad de materiales metálicos. En sus comienzos está técnica fue empleada para inducir tensiones residuales de compresión en superficie, pero mientras se avanzaba en su desarrollo se empezaron a observar otros efectos. Profundizando en ellos se llega a la conclusión de que existe una fuerte relación entre todos, pero dependiendo de la aplicación a la que se vea sometido un componente tratado con LSP será necesario una serie de características que bien pueden ser ajustadas “a priori”. Para ello se ha de tener una buena caracterización del proceso láser y de las modificaciones que produce en las propiedades de un material determinado. Y es en este punto donde surge el problema: las modificaciones introducidas por el tratamiento láser son dependientes de la interacción de la energía del pulso láser con el material, es decir, para cada material es necesaria una caracterización previa de cómo sus propiedades son modificadas con las diferentes configuraciones del tratamiento LSP, encontrando para cada material un óptimo en los parámetros láser. En esta Tesis se pretende desarrollar una metodología para evaluar las modificaciones en las propiedades mecánicas y superficiales inducidas en materiales metálicos debido al tratamiento superficial por ondas de choque. De esta manera y avanzando de una manera lógica con la línea de investigación del grupo, se ha querido aplicar todo el conocimiento adquirido de la técnica para desarrollar esa metodología sobre un caso práctico: el empleo de dos configuraciones de tratamiento LSP sobre el acero inoxidable AISI 316L. Estas dos configuraciones elegidas se hacen en base a estudios previos, por parte del grupo de investigación, donde se han optimizados los parámetros para obtener el óptimo en lo que a perfil de tensiones residuales en profundidad se refiere. El material elegido como caso característico para llevar acabo la evaluación integrada del tratamiento LSP, de acuerdo con el propósito de esta Tesis, ha sido el acero inoxidable AISI 316L, debido a que este tipo de acero tiene una excelente resistencia a la corrosión en un amplio rango de atmosferas corrosivas, y es conocido como el grado estándar para un importante número de aplicaciones tecnológicas. La resistencia a la oxidación es buena incluso a altas temperaturas de servicio y la soldabilidad es excelente. Los aceros austeníticos son empleados en aplicaciones que soportan condiciones de alta temperatura y medios altamente corrosivos, como en reactores nucleares. Estos aceros resisten la corrosión en el agua de un reactor y procesos químicos en plantas que operan a temperaturas superiores a los 900 ˚C. En concreto el acero 316L se utiliza en la industria de equipamiento alimentario, en ambientes donde haya presencia de cloruros, en aplicaciones farmacéuticas, en la industria naval, en arquitectura, sector energético, centrales nucleares y en implantes médicos. Es decir, es un material ampliamente implantado en la industria, tanto en industrias tradicionales, como en industrias emergentes como la biomédica. El objetivo marcado para el desarrollo de la presente Tesis es caracterizar de forma precisa cómo el tratamiento superficial por ondas de choque generadas por láser es capaz de mejorar las propiedades de los materiales y cómo de estables son estas con la temperatura. Este punto es importante puesto que a la hora de introducir el proceso LSP en la industria no solo se tiene que tener en cuenta que las propiedades del material sean mejoradas, sino que también es necesario comprobar si esas mejoras se mantienen después de ser sometido el material a un tratamiento térmico ya que las condiciones de servicio de los materiales y componentes empleados no tienen por qué trabajar a temperatura ambiente. Para lograr el objetivo mencionado, el trabajo experimental realizado en la aleación seleccionada bajo todas las condiciones a estudio (material según fue recibido de fábrica, tratado con las dos configuraciones LSP y después de haber sido sometido al tratamiento térmico) ha consistido en lo siguiente: i) Estudios microestructural, morfológico y de composición química. ii) Medida de las tensiones residuales introducidas. iii) Caracterización superficial del material. iv) Estudio de las propiedades mecánicas: ensayos de tracción, ensayos de dureza, cálculo de la densidad de dislocaciones y ensayos de fatiga. v) Caracterización tribológica: ensayos de fricción y cálculo de la tasa de desgaste y volumen eliminado. vi) Caracterización electro-química para el material base y tratado con las dos configuraciones LSP. Se realizan medidas a circuito abierto, curvas de polarización (OCP), ensayos potenciostáticos y espectroscopia de impedancia electroquímica (EIS). El trabajo se ha llevado a cabo en los laboratorios del Centro Láser de la Universidad Politécnica de Madrid.