Precipitation hardening of Cu-Fe-Cr alloys - Part II - Microstructural characterisation

This research is part of a project whose scope was to investigate the engineering properties of new non-commercial alloy formulations based on the Cu rich corner of the Cu-Fe-Cr ternary system with the primary aim of exploring the development of a new cost-effective high-strength, high-conductivity copper alloy. Promising properties have been measured for the following alloys: Cu-0.7wt%Cr-0.3wt%Fe and Cu-0.7wt%Cr-2.0wt%Fe. This paper reports on the microstructural characterisation of these alloys and discusses the mechanical and electrical properties of these alloys in terms of their microstructure, particularly the formation of precipitates. These alloys have evinced properties that warrant further investigation. Cost modelling has shown that Cu-0.7wt%Cr-0.3wt%Fe is approximately 25% cheaper to produce than commercial Cu-1%Cr. It has also been shown to be more cost efficient on a yield stress and % IACS per dollar basis. The reason for the cost saving is that the Cu-0.7%Cr-0.3%Fe alloy can be made with low carbon ferro-chrome additions as the source of chromium rather than the more expensive Cu-Cr master-alloy. For applications in which cost is one of the primary materials selection criteria, it is envisaged that there would be numerous applications in both cast and wrought form, where the Cu-0.7%Cr-0.3%Fe alloy would be more suitable than Cu-1%Cr. (C) 2001 Kluwer Academic Publishers.

Quaternary Cu-0.7%Cr-0.3%Fe-X alloys

This research is part of a project whose scope was to investigate the engineering properties of new non-commercial alloy formulations based on the Cu rich corner of the Cu-Fe-Cr ternary system with the primary aim of exploring the development of a new cost-effective high-strength, high-conductivity copper alloy. The aim of the present work was to increase the electrical conductivity and strength of the Cu-0.7wt%Cr-0.3wt%Fe alloy through selective minor additions (less than or equal to0.15 wt%) of elements expected to promote precipitation of dissolved Fe: Ti, B, P, Ni & Y. Such quaternary alloys with reduced Fe in solid solution would be expected to have properties equivalent to or better than those of the Cu-1%Cr reference alloy (Alloy Z). The investigation showed that none of the trace element additions significantly improved the size of the age hardening response or the peak aged electrical conductivity of Alloy A, although further work is required on the influence of Ti. Additions of P and B were detrimental. Other trace additions had little or no effect apart from causing some slight changes to the precipitation kinetics. The mechanical properties of the Cu-0.7%Cr-0.3%Fe alloy made with less expensive high carbon ferrochrome were found to be inferior to those of the equivalent alloy made with low carbon ferrochrome. (C) 2001 Kluwer Academic Publishers.

Cold worked Cu-Fe-Cr alloys

The aim of this project was to investigate the properties of copper rich Cu-Fe-Cr alloys for the purpose of developing a new cost effective, high-strength, high-conductivity copper alloy. This paper reports on the influence of cold work. The age hardening response of the Cu-0.7%Cr-2.0%Fe alloy was minimal, but the resistance to softening was superior to that reported for any commercial high-strength, high-conductivity (HSHC) copper alloy with comparable mechanical and electrical properties. For example, an excess of 85% of the original hardness of the 40% cold worked alloy is retained after holding at 700 degreesC for 1 hour, whereas commercial HSHC Cu-Fe-P alloys have been reported to soften significantly after 1 hours exposure at less than 500 degreesC. The Cu-0.7Cr-2.0Fe alloy would therefore be expected to be more suitable for applications with a significant risk of exposure to elevated temperatures. Optical microscope examination of cold worked and aged microstructures confirmed the high resistance to recrystallization for Cu-0.7%Cr-2.0%Fe. The Zener-Smith drag term, predicting the pinning effect of second phase particles on dislocations in cold worked microstructures, was calculated using the precipitate characteristics obtained from TEM, WDS and resistivity measurements. The pinning effect of the precipitate dispersions in the peak-aged condition was determined to be essentially equivalent for the Cu-0.7%Cr-0.3%Fe and Cu-0.7%Cr-2.0%Fe alloys. A lower recrystallisation temperature in the Cu-0.7%Cr-0.3%Fe alloy was therefore attributed to faster coarsening kinetics of the secondary precipitates resulting from a higher Cr concentration in the precipitates at lower iron content. (C) 2001 Kluwer Academic Publishers.

Columnar to equiaxed transition of eutectic in hypoeutectic aluminium-silicon alloys

Directional solidification of unmodified and strontium modified binary, high-purity aluminium-7 wt% silicon and commercial A356 alloys has been carried out to investigate the mechanism of eutectic solidification. The microstructure of the eutectic growth inter-face was investigated with optical microscopy and Electron Backscattering Diffraction (EBSD). In the commercial alloys, the eutectic solidification inter-face extends in the growth direction and creates a eutectic mushy zone. A planar eutectic growth front is observed in the high-purity alloys. The eutectic aluminium has mainly the same crystallographic orientation as the dendrites in the unmodified alloys and the strontium modified high-purity alloy. A more complex eutectic grain structure is found in the strontium modified commercial alloy. A mechanism involving constitutional undercooling and a columnar to equiaxed transition explains the differences between pure and commercial alloys. It is probably caused by the segregation of iron and magnesium and the activation of nucleants in the commercial alloy. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

An age hardening model for Al-7Si-Mg casting alloys

Yield strength (YS) ageing curves have been modelled for A356 and A357 aluminium casting alloys below the solvus temperature of the main hardening precipitate. Predictions are based on the Shercliff and Ashby methodology (Acta MetaH. Mater. 38 (1990) 1789) for wrought alloys. Differences between strengthening in wrought and cast Al-Si-Mg alloys are considered. A Brinell hardness to YS conversion incorporating strain hardening has been established to enable YS ageing curves to be predicted with reduced experimental effort. (C) 2002 Elsevier Science B.V. All rights reserved.

Characteristic zirconium-rich coring structures in Mg-Zr alloys

The most characteristic feature of the microstructure of a magnesium alloy that contains more than a few tenths per cent soluble zirconium is the zirconium-rich cores that exist in most grains. The morphology, distribution and composition of cores observed in a Mg-0.56%Zr alloy and the small particles present in them were investigated. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Chiral resolution of hexaamine cobalt(III) cages: Substituent effects on chiral discrimination

Chiral resolution of the cobalt cage complexes [Co(diNOsar)](3+) and [Co(diAMsarH(2))](5+) have been achieved by selective crystallization with the anion bis-mu-(R),(R)-tartratodiantimonate(III) ([Sb-2(R,R-tart)(2)](2-)) and also by column chromatography with Na-2[Sb-2(R, R-tart)(2)] as eluent. The X-ray crystal structures of Lambda-[ Co(diNOsar)][Sb-2(R, R-tart)(2)] Cl . 7H(2)O and Delta-[Co(diAMsarH(2))][Sb-2(R, R-tart)(2)](2)Cl . 14H(2)O are reported, which reveal an unexpected reversal of chiral discrimination when the cage substituent is changed from nitro (Lambda-enantiomer) to ammonio (Delta-enantiomer) and shows that the ammonio- substituted cage is capable of forming a three-point hydrogen-bonding interaction with each complex anion, whereas the nitro analogue can only form two hydrogen bonds with each [Sb-2(R, R-tart)(2)](2-) anion. During cation exchange chromatography of the racemic cobalt cage complexes with Na-2[Sb-2(R, R-tart)(2)] as eluent, Lambda-[Co(diNOsar)](3+) elutes first, which implies a tighter ion pairing interaction than for the Delta-enantiomer. On the other hand, Delta-[Co(diAMsarH(2))](5+) elutes first during chromatography under identical conditions, which is also consistent with a preferred outer-sphere complex formed between Delta-[Co(diAMsarH(2))](5+) and [Sb-2(R, R-tart)(2)](2-) relative to Lambda-[Co(diAMsarH(2))](5+) and [Sb-2(R,R-tart)(2)](2-).

Geometric isomers of chloro(6-methyl-1,4,8,11-tetraazacyclotetradecane-6-amine)cobalt(III) tetrachlorozincate(II)

The crystal structures of a pair of cis and trans isomers of the macrocyclic chloropentaamine title complex, as their tetrachlorozincate(II) salts, [CoCl(C11H27N5)][ZnCl4], are reported. The two distinct isomeric forms lead to significant variations in the Co-N bond lengths and, furthermore, hydrogen bonding between the complex ions is influenced by the folded (cis) or planar (trans) conformations of the coordinated ligand.