Preparation and characterization of LiNi0.8Co0.2O2/PANI microcomposite electrode materials under assisted ultrasonic irradiation

A preparation method for a new electrode material based on the LiNi0.8Co0.2O2/polyaniline (PANI) composite is reported. This material is prepared by in situ polymerization of aniline in the presence of LiNi0.8Co0.2O2 assisted by ultrasonic irradiation. The materials are characterized by XRD, TG-DTA, FTIR, XPS, SEM-EDX, AFM, nitrogen adsorption (BET surface area) and electrical conductivity measurements. PANI in the emeraldine salt form interacts with metal-oxide particles to assure good connectivity. The dc electrical conductivity measurements at room temperature indicate that conductivity values are one order of magnitude higher in the composite than in the oxide alone. This behavior determines better reversibility for Li-insertion in charge-discharge cycles compared to the pristine mixed oxide when used as electrode of lithium batteries. (c) 2005 Elsevier B.V. All rights reserved.

Effect of ceria content on the sintering of ZrO2 based ceramics synthesized from a polymeric precursor

Zirconia-ceria powders with ceria concentration varying from 0 to 12 mol% were synthesized using a polymeric precursor route based on the Pechini process. Powder characteristics were evaluated with regard to the crystallite size, BET surface area, phase distribution, nitrogen adsorption/desorption behavior, and agglomeration state. Sintering was studied considering the shrinkage rate, densification, grain size, and phase evolution. It was demonstrated that the synthesis method is effective to prepare nanosized powders of tetragonal zirconia single-phase. Sinterability mainly depended on the agglomeration state of powders and the monoclinic phase content, fully tetragonal zirconia ceramic, with grain size of 2.4 mu m, was obtained after addition of at least 9 mol% ceria and sintering at 1500 degrees C for 4 h. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

Investigation of the pore blockage of a Brazilian dolomite during the sulfation reaction

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural changes induced by ultrasound during aging of the boehmite phase

Structural changes induced by ultrasound during the aging of the aluminum monohydroxide (boehmite) were studied by means of X-ray diffraction (XRD) and nitrogen adsorption. The BET surface area and the pore volume of the ultrasound stimulated hydroxide (HU) are about 40% less than those of the non-stimulated one (HS). The mean pore size practically does not change, while the mean crystallite size (L) is about 25% greater in the HU system. The increase of L alone is not enough to account for the surface area diminution, suggesting that the sonication also induces compaction by elimination of some porosity. The sonication of the precursor hydroxide does not seem to play an apparent role in the structural properties of the resulting calcinated γ-alumina. © 1997 Elsevier Science B.V.

'Ti''O IND.2'/'Sn''O IND. 2 modificado com 'Ag IND. 2''O', para obtenção de fotocatalisadores

Pós-graduação em Química - IQ

Síntese e caracterização de argila esmectita Zn-estevensita

Argila do grupo das esmectitas foi obtida com êxito em baixa temperatura de processamento por via hidrotérmica utilizando como precursores metassilicato de sódio, nitrato de zinco e uréia. Durante a etapa de síntese a composição molar da mistura reacional e a temperatura permaneceram constantes, variando-se o tempo de reação. As amostras sintetizadas foram caracterizadas por difração de raios X, microscopia eletrônica de varredura, espectroscopia de refletância difusa no infravermelho com transformada de Fourier, análise térmica diferencial e gravimétrica, análise de adsorção gasosa de nitrogênio pelo método BET e capacidade de troca de cátions. Os resultados evidenciam que com a metodologia empregada obtêm-se Zn-estevensita apresentando uma área superficial total na faixa de 171,6 a 203,4 m²/g e boa cristalinidade; sendo esta a única fase presente no produto sintetizado após reação estática a 90 ºC por um período de 44 a 138 h, indicando ser o aumento no tempo de síntese um parâmetro importante para o processo de cristalização da argila.

An investigation into the influence of zinc precursor on the microstructural, photoluminescence, and gas-sensing properties of ZnO nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

EFFECTS OF ADDING LANTHANUM TO Ni/ZrO2 CATALYSTS ON ETHANOL STEAM REFORMING

EFFECTS OF ADDING LANTHANUM TO Ni/ZrO2 CATALYSTS ON ETHANOL STEAM REFORMING. The catalytic performance of Ni/ZrO2 catalysts loaded with different lanthanum content for steam reforming of ethanol was investigated. Catalysts were characterized by BET surface area, X-ray diffraction, UV-vis spectroscopy, temperature programmed reduction, and X-ray absorption fine structure techniques. Results showed that lanthanum addition led to an increase in the degree of reduction of both NiO and nickel surface species interacting; with the support, due to the higher dispersion effect. The best catalytic performance at 450 degrees C was found for the Ni/2LZ catalyst, which exhibited an effluent gaseous mixture with the highest H-2 yield.

CuO-CeO2 catalysts synthesized in one-step: Characterization and PROX performance

PEM fuel cells seem to be the most affordable and commercially viable hydrogen-based cells, the biggest challenge being to obtain CO-free H-2 (<100 ppm) as the fuel. In this study, the use of CuO-CeO2 catalysts in preferential oxidation of CO to obtain CO-free H-2 (PROX reaction) was investigated. Ce1-xCuxO2 catalysts, with x (mol%) = 0, 0.01, 0.03, 0.05 and 0.10, were synthesized in one-step by the polymeric precursor method, to obtain a very fine dispersion and strong metal-support interaction, to favor active copper species and a preference for the PROX reaction. The results obtained from catalyzed reactions and characterization of the catalysts by XRD, Rietveld refinement, BET surface area, UV-Vis and TPR, suggest that this one-step synthesis method gives rise to catalysts with copper species selective for the PROX reaction, which reaches a maximum rate on Ce0.97Cu0.03O2 catalyst. Copyright (C) 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Investigation of the pore blockage of a Brazilian dolomite during the sulfation reaction

The influence of the temperature and reaction time on the sulfation process of a dolomite is investigated in this paper. The sulfation effectiveness was evaluated and correlated with changes in the physical characteristics of a Brazilian dolomite during the reactive process. Calcination and sulfation experiments were performed under isothermal conditions for dolomite samples with average particle sizes of 545 mu m at temperatures of 750 degrees C, 850 degrees C and 950 degrees C at different times of sulfation. Thermogravimetric tests were applied to establish the reactivity variation of the dolomite in function of the time in the sulfation reaction and evaluate the methodology of the samples preparation. Porosimetry tests were performed to study the pore blockage of dolomite during the sulfation reaction. The highest values of BET surface area were 25.55 m(2)/g, 29.55 m(2)/g and 12.62 m(2)/g for calcined samples and after their sulfation processes, conversions of 51.5%, 61.9% and 42.8% were obtained at 750 degrees C, 850 degrees C and 950 degrees C, respectively. Considering the process as a whole, the best fit was provided by a first-order exponential decay equation. Moreover, the results have shown that it is possible to quantify the decreasing in the dolomite reactivity for sulfur dioxide sorption and understand the changes in the behavior of the sulfation process of limestones when applied to technologies, as fluidized bed combustor, in which sulfur dioxide is present. (C) 2011 Elsevier B. V. All rights reserved.

Efeito da adição de lantânio em catalisadores de Ni/ZrO2 aplicados na reação de reforma a vapor de etanol

The catalytic performance of Ni/ZrO2 catalysts loaded with different lanthanum content for steam reforming of ethanol was investigated. Catalysts were characterized by BET surface area, X-ray diffraction, UV-vis spectroscopy, temperature programmed reduction, and X-ray absorption fine structure techniques. Results showed that lanthanum addition led to an increase in the degree of reduction of both NiO and nickel surface species interacting with the support, due to the higher dispersion effect. The best catalytic performance at 450 ºC was found for the Ni/12LZ catalyst, which exhibited an effluent gaseous mixture with the highest H2 yield.

Effects of synthesis conditions on the nanostructre of CexZr1-xO2 mesoporous ceramics.

CexZr1-xO2 (0.5 ≤ x ≤ 0.9) were synthesized with Zr and Ce chloride precursors, using the triblock copolymer Pluronic P123 and HCl (2 mol/L). The pH adjustment was performed in two ways: synthesis A used 11.4 mL of a NH4OH solution added at once to the initial mixture, composed by metal precursors and template in HCl; synthesis B was done by dripping slowly until the change of pH value (between 3 and 6). In this work, CexZr1-xO2 samples synthesized by these two processes are compared. The effects of pH values in materials characteristics were also evaluated. These samples were analysed by X-Ray Diffraction (XRD) with Rietveld refinement, and Nitrogen Adsorption/Desorption. In both processes, the studied materials presented two crystalline phases of CexZr1-xO2 solid solution: cubic and tetragonal. The synthesis A also presented a tetragonal phase of ZrO2. The average crystallite size and the Brunauer- Emmett-Teller (BET) surface area are bigger in process A. Both processes give samples with a mesoporous structure.

Photocatalytic degradation of phenolic compounds with new TiO2 catalysts

[EN] New TiO2 catalysts have been synthesised by means of a sol–gel method in which aggregates have been selected before thermal treatment. Sieving and calcination temperature have been proved to be key factors in obtaining catalysts with greater photoactivity than that of Degussa P-25. These new catalysts have been characterized by means of transmission electron microscopy (TEM), BET surface area, diffuse reflectance spectroscopy (DRS), UV–vis spectroscopy, Fourier transformed infrared (FTIR) and X-ray diffraction (XRD). The different parameters studied were compared to those obtained from two commercial catalysts (Degussa P-25 and Hombikat-UV100). The photocatalytic efficiency of the new catalysts was evaluated by the degradation of various phenolic compounds using UV light (maximum around 365 nm, 9mW). The catalyst sieved and calcinated at 1023 K, ECT-1023t, showed phenol degradation rates 2.7 times higher than those of Degussa P-25. Also in the degradation of different phenolic compounds, this catalyst showed a higher activity than that of the commercial one. The high photoactivity of this new catalyst has been attributed to the different distribution of surface defects (determined from FTIR studies) and its increased capacity to yield H2O2

Performance evaluation and characterization of symmetric capacitors with carbon black, and asymmetric capacitors using a carbon foam supported nickel electrode

This thesis evaluates a novel asymmetric capacitor incorporating a carbon foam supported nickel hydroxide positive electrode and a carbon black negative electrode. A series of symmetric capacitors were prepared to characterize the carbon black (CB) negative electrode. The influence of the binder, PTFE, content on the cell properties was evaluated. X-ray diffraction characterization of the nickel electrode during cycling is also presented. The 3 wt% and 5 wt% PTFE/CB symmetric cells were examined using cyclic voltammetry (CV) and constant current charge/discharge measurements. As compared with symmetric cells containing more PTFE, the 3 wt% cell has the highest average specific capacitance, energy density and power density over 300 cycles, 121.8 F/g, 6.44 Wh/kg, and 604.1 W/kg, respectively. Over the 3 to 10 wt% PTFE/CB range, the 3 wt% sample exhibited the lowest effective resistance and the highest BET surface area. Three asymmetric cells (3 wt% PTFE/CB negative electrode and a nickel positive) were fabricated; cycle life was examined at 3 current densities. The highest average energy and power densities over 1000 cycles were 20 Wh/kg (21 mA/cm2) and 715 W/kg (31 mA/cm2), respectively. The longest cycle life was 11,505 cycles (at 8 mA/cm2), with an average efficiency of 79% and an average energy density of 14 Wh/kg. The XRD results demonstrate that the cathodically deposited nickel electrode is a typical α-Ni(OH)2 with the R3m structure (ABBCCA stacking); the charged electrodes are 3γ-NiOOH with the same stacking as the α-type; the discharged electrodes (including as-formed electrode) are aged to β’-Ni(OH)2 (a disordered β) with the P3m structure (ABAB stacking). A 3γ remnant was observed.

Graphite exfoliation by supercritical carbon dioxide extraction

Supercritical carbon dioxide is used to exfoliate graphite, producing a small, several-layer graphitic flake. The supercritical conditions of 2000, 2500, and 3000 psi and temperatures of 40°, 50°, and 60°C, have been used to study the effect of critical density on the sizes and zeta potentials of the treated flakes. Photon Correlation Spectroscopy (PCS), Brunauer-Emmett-Teller (BET) surface area measurement, field emission scanning electron microscopy (FE-SEM), and atomic force microscopy (AFM) are used to observe the features of the flakes. N-methyl-2-pyrrolidinone (NMP), dimethylformamide (DMF), and isopropanol are used as co-solvents to enhance the supercritical carbon dioxide treatment. As a result, the PCS results show that the flakes obtained from high critical density treatment (low temperature and high pressure) are more stable due to more negative charges of zeta potential, but have smaller sizes than those from low critical density (high temperature and low pressure). However, when an additional 1-hour sonication is applied, the size of the flakes from low critical density treatment becomes smaller than those from high critical density treatment. This is probably due to more CO2 molecules stacked between the layers of the graphitic flakes. The zeta potentials of the sonicated samples were slightly more negative than nonsonicated samples. NMP and DMF co-solvents maintain stability and prevented reaggregation of the flakes better than isopropanol. The flakes tend to be larger and more stable as the treatment time increases since larger flat area of graphite is exfoliated. In these experiments, the temperature has more impact on the flakes than pressure. The BET surface area resultsshow that CO2 penetrates the graphite layers more than N2. Moreover, the negative surface area of the treated graphite indicates that the CO2 molecules may be adsorbed between the graphite layers during supercritical treatment. The FE-SEM and AFM images show that the flakes have various shapes and sizes. The effects of surfactants can be observed on the FE-SEM images of the samples in one percent by weight solution of SDBS in water since the sodium dodecylbenzene sulfonate (SDBS) residue covers all of the remaining flakes. The AFM images show that the vertical thickness of the graphitic flakes can ranges from several nanometers (less than ten layers thick), to more than a hundred nanometers. In conclusion, supercritical carbon dioxide treatment is a promising step compared to mechanical and chemical exfoliation techniques in the large scale production of thin graphitic flake, breaking down the graphite flakes into flakes only a fewer graphene layers thick.