A Continuous Span Aluminum Girder Concrete Deck Bridge - Part 1 of 2: Field Test Performance and Evaluation, 1996

This report addresses the field testing and analysis of those results to establish the behavior of the original Clive Road Bridge that carried highway traffic over Interstate 80 (I-80) in the northwest region of Des Moines, Iowa. The bridge was load tested in 1959, shortly after its construction and in 1993, just prior to its demolition. This report presents some of the results from both field tests, finite element predictions of the behavior of aluminum bridge girders, and load distribution studies.

A Continuous Span Aluminum Girder Concrete Deck Bridge - Part 2 of 2: Fatigue Tests of Aluminum Girders, Final Report, 1997

In 1957, the Iowa State Highway Commission, with financial assistance from the aluminum industry, constructed a 220-ft (67-m) long, four-span continuous, aluminum girder bridge to carry traffic on Clive Road (86th Street) over Interstate 80 near Des Moines, Iowa. The bridge had four, welded I-shape girders that were fabricated in pairs with welded diaphragms between an exterior and an interior girder. The interior diaphragms between the girder pairs were bolted to girder brackets. A composite, reinforced concrete deck served as the roadway surface. The bridge, which had performed successfully for about 35 years of service, was removed in the fall of 1993 to make way for an interchange at the same location. Prior to the bridge demolition, load tests were conducted to monitor girder and diaphragm bending strains and deflections in the northern end span. Fatigue testing of the aluminum girders that were removed from the end spans were conducted by applying constant-amplitude, cyclic loads. These tests established the fatigue strength of an existing, welded, flange-splice detail and added, welded, flange-cover plates and horizontal web plate attachment details. This part, Part 2, of the final report focuses on the fatigue tests of the aluminum girder sections that were removed from the bridge and on the analysis of the experimental data to establish the fatigue strength of full-size specimens. Seventeen fatigue fractures that were classified as Category E weld details developed in the seven girder test specimens. Linear regression analyses of the fatigue test results established both nominal and experimental stress-range versus load cycle relationships (SN curves) for the fatigue strength of fillet-welded connections. The nominal strength SN curve obtained by this research essentially matched the SN curve for Category E aluminum weldments given in the AASHTO LRFD specifications. All of the Category E fatigue fractures that developed in the girder test specimens satisfied the allowable SN relationship specified by the fatigue provisions of the Aluminum Association. The lower-bound strength line that was set at two standard deviations below the least squares regression line through the fatigue fracture data points related well with the Aluminum Association SN curve. The results from the experimental tests of this research have provided additional information regarding behavioral characteristics of full-size, aluminum members and have confirmed that aluminum has the strength properties needed for highway bridge girders.

Enzyme convertedstarch in pigment coating

Tämän diplomityön tavoitteena oli selvittää entsyymikonvertoinnin mahdollisuudet vaikuttaa sideainetärkkelyksen toiminnallisiin ominaisuuksiin. Tärkein tehtävä oli etsiä vastaukset kysymykseen, kuinka paljon entsyymikonvertointia optimoimalla voidaan maksimoida tärkkelyksen positiivisia vaikutuksia. Tavoitteena oli myös tutkia, voiko lisäaineita käyttämällä ja tärkkelystä plastisoimalla säilyttää tärkkelyksen vaikutus paperin jäykkyyteen ja saada tärkkelysfilmille joustavuutta. Kirjallisuusosassa tarkasteltiin tärkkelyksen entsyymikonvertointiin vaikuttavia tekijöitä, eri tärkkelysraaka-aineiden eroja, sekä konvertoinnissa käytettävien entsyymien ominaisuuksia. Kirjallisuusosassa tarkasteltiin myöstärkkelyksen käyttöä sideaineena pigmenttipäällystyksessä. Kokeellisessa osassakeskityttiin selvittämään entsyymikonvertoinnin olosuhteiden, käytettävän raakatärkkelyksen ja entsyymin vaikutusta konvertoidun tärkkelyksen ominaisuuksiin. Konvertoiduista tärkkelyksistä valmistettiin päällystyspastat, ja tutkittiin niinpastan kuin päällystetyn paperin ominaisuuksia. Myös erilaisten pehmentimien vaikutusta niin päällystyspastaan, kuin paperin pinnalle tutkittiin. Havaittiin, että konvertoimalla tärkkelysketjua entsymaattisesti, voidaan tärkkelysketjun pituutta säädellä. Tarkoituksena oli konvertoida tärkkelystä niin, että tärkkelyksen molekyyliketjujakaumat sisältävät lyhyitä, keskipitkiä sekäpitkiä molekyylejä. Päällystämisen havaittiin olevan vaikeaa Helicoaterilla varsinkin pitkäketjuista tärkkelystä suuren määrän sisältävillä pastoilla. Myös tärkkelys/lateksi-suhde vaihteli eri pastoilla. Päällystyspastojen reologisia ominaisuuksia testattaessa huomattiin, että tärkkelysketjun pituuden kasvaessa pastanviskositeetti lisääntyy ja vesiretentio vähenee. Havaittiin vain muutamia teknisiä paperiominaisuuksia, jotka korreloivat hyvin tärkkelysketjun pituuden kanssa. Näitä olivat kiilto, Gurley-Hill huokoisuus, taivutusvastus, taivutuspituus sekä IGT pintalujuus. Pehmentimien ei havaittu vaikuttavan moneenkaan paperin eri tekniseen ominaisuuteen. Suurimmat erot huomattiin paperin taivutuspituudessa ja taivutusvastuksessa.

Spray coating technique asa surface treatment for woodcontaining paper grades

The objective of this work was to introduce the emerging non-contacting spray coating process and compare it to the existing coating techniques. Particular emphasis was given to the details of the spraying process of paper coating colour and the base paper requirements set by the new coating method. Spraying technology itself is nothing new, but the atomisation process of paper coating colour is quite unknown to the paper industry. The differences between the rheology of painting and coating colours make it very difficult to utilise the existing information from spray painting research. Based on the trials, some basic conclusion can be made:The results of this study suggest that the Brookfield viscosity of spray coating colour should be as low as possible, presently a 50 mPas level is regarded as an optimum. For the paper quality and coater runnability, the solids level should be as high as possible. However, the graininess of coated paper surface and the nozzle wear limits the maximum solids level to 60 % at the moment. Most likelydue to the low solids and low viscosity of the coating colour the low shear Brookfield viscosity correlates very well with the paper and spray fan qualities. High shear viscosity is also important, but yet less significant than the low shear viscosity. Droplet size should be minimized and besides keeping the brrokfield viscosity low that can be helped by using a surfactant or dispersing agent in the coating colour formula. Increasing the spraying pressure in the nozzle can also reduce the droplet size. The small droplet size also improves the coating coverage, since there is hardly any levelling taking place after the impact with the base paper. Because of the lack of shear forces after the application, the pigment particles do not orientate along the paper surface. Therefore the study indicates that based on the present know-how, no quality improvements can be obtained by the use of platy type of pigments. The other disadvantage of them is the rapid deterioration of the nozzle lifetime. Further research in both coating colour rheology and nozzle design may change this in the future, but so far only round shape pigments, like typically calcium carbonate is, can be used with spray coating. The low water retention characteristics of spray coating, enhanced by the low solids and low viscosity, challenge the base paper absorption properties.Filler level has to be low not to increase the number of small pores, which have a great influence on the absorption properties of the base paper. Hydrophobic sizing reduces this absorption and prevents binder migration efficiently. High surface roughness and especially poor formation of the base paper deteriorate thespray coated paper properties. However, pre-calendering of the base paper does not contribute anything to the finished paper quality, at least at the coating colour solids level below 60 %. When targeting a standard offset LWC grade, spraycoating produces similar quality to film coating, but yet blade coating being on a slightly better level. However, because of the savings in both investment and production costs, spray coating may have an excellent future ahead. The porousnature of the spray coated surface offers an optimum substrate for the coldset printing industry to utilise the potential of high quality papers in their business.

An Optimum Coating Colour Formula for CSWO-printing

Pigmenttipäällystyksen tarkoituksena on parantaa painopapereiden pintaominaisuuksia. Tämän työn tarkoituksena oli löytää sopiva päällystyspasta päällystetylle coldset-paperille. Kirjallisuusosassa on käsitelty coldset-painatusta ja sen ongelmia. Päällystysmenetelmän perusteita, pastan ominaisuuksia ja niiden vaikutusta päällystystulokseen on myös käsitelty. Lisäksi on esitelty joitakin päällystetyn paperin pinnantutkimusmenetelmiä. Kokeellisessa osassa on tutkittu erilaisten pastakoostumusten ja päällystemäärien sekä kalanteroinnin vaikutusta paperin painettavuuteen. Paperit on päällystetty Helicoaterilla ja joitakin pastoja on testattu myös pilot-mittakaavaisessa päällystyksessä. Selitystä paperin käyttäytymiseen painatuksessa on etsitty päällystetyn paperin pintarakenteesta. Paras painettavuus saavutetaan päällysteellä, jossa pigmenttinä on vain karbonaatti. Painojälkeä voidaan parantaa käyttämällä kalsinoitua kaoliinia yhdessä karbonaatin kanssa, mutta tämän päällysteen pintalujuus ei ole riittävä CSWO-painatukseen. Tärkkipigmentti parantaa veden ja painovärin absorptiota ja siten tekee painetun tuotteen kuivemmaksi ja miellyttävämmän tuntuiseksi, mutta aiheuttaa smearingia. Tämä johtuu liian nopeasta musteen asettuvuudesta. "Pehmeä" SB-lateksi soveltuu paremmin offset-painatukseen kuin "kova" lateksi, joka sisältää myös PVAc:ta. "Pehmeällä" lateksilla saadaan parempi pintalujuus ja painojälki kuin "kovalla" lateksilla. Paperin pölyävyyttä painatuksessa voidaan vähentää nostamalla päällystemäärää ja laskemalla pastan kuiva-ainepitoisuutta. Kalanteroinnilla ei pintalujuutta tai painojälkeä voida parantaa. Selitys tutkimuksessa käsiteltyjen papereiden painojäljelle ja painettavuudelle löydetään tutkimalla päällysteen pintarakennetta. Painojälkeen vaikuttaa eniten päällysteen peittoaste. Huonoa peittävyyttä voidaan parantaa nostamalla päällystemäärää. Pölyäminen painatuksessa johtuu pigmenteistä, jotka eivät ole sidottuja paperin pintaan. Tämä taas johtuu pastan huonosta vesiretentiosta. Hyödyllisintä tietoa näiden papereiden pintarakenteesta saadaan tutkimalla pintaa pyyhkäisyelektonimikroskoopilla (SEM), atomivoimamikroskoopilla (AFM) ja laserindusoidulla plasmaspektrometrilla (LIPS). LIPSin etuna on se, että päällystemääräjaukauma voidaan määrittää sekä x-y- että z-suunnassa samanaikaisesti samasta kohdasta. LIPSissä myös näytteen preparointitarve on hyvin vähäinen.

Motorcycle helmets: what about their coating?

In traffic accidents involving motorcycles, paint traces can be transferred from the rider's helmet or smeared onto its surface. These traces are usually in the form of chips or smears and are frequently collected for comparison purposes. This research investigates the physical and chemical characteristics of the coatings found on motorcycles helmets. An evaluation of the similarities between helmet and automotive coating systems was also performed.Twenty-seven helmet coatings from 15 different brands and 22 models were considered. One sample per helmet was collected and observed using optical microscopy. FTIR spectroscopy was then used and seven replicate measurements per layer were carried out to study the variability of each coating system (intravariability). Principal Component Analysis (PCA) and Hierarchical Cluster Analysis (HCA) were also performed on the infrared spectra of the clearcoats and basecoats of the data set. The most common systems were composed of two or three layers, consistently involving a clearcoat and basecoat. The coating systems of helmets with composite shells systematically contained a minimum of three layers. FTIR spectroscopy results showed that acrylic urethane and alkyd urethane were the most frequent binders used for clearcoats and basecoats. A high proportion of the coatings were differentiated (more than 95%) based on microscopic examinations. The chemical and physical characteristics of the coatings allowed the differentiation of all but one pair of helmets of the same brand, model and color. Chemometrics (PCA and HCA) corroborated classification based on visual comparisons of the spectra and allowed the study of the whole data set at once (i.e., all spectra of the same layer). Thus, the intravariability of each helmet and its proximity to the others (intervariability) could be more readily assessed. It was also possible to determine the most discriminative chemical variables based on the study of the PCA loadings. Chemometrics could therefore be used as a complementary decision-making tool when many spectra and replicates have to be taken into account. Similarities between automotive and helmet coating systems were highlighted, in particular with regard to automotive coating systems on plastic substrates (microscopy and FTIR). However, the primer layer of helmet coatings was shown to differ from the automotive primer. If the paint trace contains this layer, the risk of misclassification (i.e., helmet versus vehicle) is reduced. Nevertheless, a paint examiner should pay close attention to these similarities when analyzing paint traces, especially regarding smears or paint chips presenting an incomplete layer system.

Transmission properties of high barrier coated paperboard packages

High barrier materiaaleilla pyritään pidentämään pakattujen elintarvikkeiden hyllyikää. Barrierin tärkein tehtävä on elintarvikkeen suojaaminen hapelta ja kosteudelta. Alumiinin käyttöä barriermateriaalina pyritään vähentämään korvaamalla alumiini polymeereillä, jotka täyttävät elintarvikkeiden asettamat korkeat säilyvyysvaatimukset. Etyylivinyylialkoholin (EVOH) hapenläpäisevyys on kuivissa olosuhteissa alhaisin kaupallisista muovilaaduista. EVOH tarjoaa myös erinomaisen suojan muita kaasuja, rasvoja, hajuja ja aromeja vastaan ja sitä on helppo prosessoida. Polyamideilla on erinomainen kaasutiiveys sekä hyvä lujuus ja sitkeys. Eri muovilaatuja sekoittamalla voidaan vähentää hapenläpäisyä ja parantaa prosessointia. Polyolefiineja käytetään yleisesti päällystysmateriaaleina, koska ne suojaavat tuotetta erinomaisesti kosteudelta. Hapenläpäisyllä tarkoitetaan hapen kulkeutumista materiaalin läpi joko permeaation kautta tai reikien ja vuotojen läpi. Kaasun permeoitumiseen materiaalin läpi vaikuttavat materiaalin vapaa tilavuus, kiteisyysaste, orientaatio, substituointi, suhteellinen kosteus, lämpötila, barrierkerroksen paksuus, paine-ero ja permeoituvan molekyylin ominaisuudet. Kokeellisessa osassa analysoitiin ja vertailtiin kartonkipohjaisia mehutölkkejä, joissa käytettävät high barrier materiaalit olivat EVOH ja PA. Kartonkipohjaisia alumiinitölkkejä käytettiin referenssinä. Pakkausten hapenläpäisevyysmittauksissa saatiin samasta näytteestä toistettavia tuloksia, vaikka vuotomittauksissa saadut tulokset eivät olleet vertailukelpoisia hapenläpäisytulosten kanssa. Tölkkien valmistus vaikutti oleellisesti pakkausten tiiveysominaisuuksiin. Hapenläpäisy vuotojen ja reikien läpi oli merkittävämpää kuin hapenläpäisy materiaalin läpi. Pakkausten tiiveysominaisuuksia analysoitiin mittaamalla appelsiinimehun askorbiini-happopitoisuus. Askorbiinihapon hajoaminen mitattiin koetölkkeihin pakatusta appelsiinimehusta, ja lämpötilan, valon ja hapen vaikutusta askorbiinihapon hajoamiseen tutkittiin 12 viikon ajan. Lämpötilalla oli suurin vaikutus askorbiinihapon hajoamiseen huolimatta käytetystä pakkausmateriaalista.

Determination of compression behaviour of coating layer

The strength properties of paper coating layer are very important in converting and printing operations. Too great or low strength of the coating can affect several problems in printing. One of the problems caused by the strength of coating is the cracking at the fold. After printing the paper is folded to final form and the pages are stapled together. In folding the paper coating can crack causing aesthetic damage over printed image or in the worst case the centre sheet can fall off in stapling. When folding the paper other side undergoes tensile stresses and the other side compressive stresses. If the difference between these stresses is too high, the coating can crack on the folding. To better predict and prevent cracking at the fold it is good to know the strength properties of coating layer. It has measured earlier the tensile strength of coating layer but not the compressive strength. In this study it was tried to find some way to measure the compressive strength of the coating layer and investigate how different coatings behave in compression. It was used the short span crush test, which is used to measure the in-plane compressive strength of paperboards, to measure the compressive strength of the coating layer. In this method the free span of the specimen is very small which prevent buckling. It was measured the compressive strength of free coating films as well as coated paper. It was also measured the tensile strength and the Bendtsen air permeance of the coating film. The results showed that the shape of pigment has a great effect to the strength of coating. Platy pigment gave much better strength than round or needle-like pigment. On the other hand calcined kaolin, which is also platy but the particles are aggregated, decreased the strength substantially. The difference in the strength can be explained with packing of the particles which is affecting to the porosity and thus to the strength. The platy kaolin packs up much better than others and creates less porous structure. The results also showed that the binder properties have a great effect to the compressive strength of coating layer. The amount of latex and the glass transition temperature, Tg, affect to the strength. As the amount of latex is increasing, the strength of coating is increasing also. Larger amount of latex is binding the pigment particles better together and decreasing the porosity. Compressive strength was increasing when the Tg was increasing because the hard latex gives a stiffer and less elastic film than soft latex.

Calcination of aluminum hydroxide over pressure and residence time

This work investigates the possible effect of pressure and residence time to the reaction of aluminum hydroxide into aluminum oxide. Various pressurized conditions are used as well as the help of various residence times. The aim is to increase the conversion of the reaction with the use of different pressures and residence times. The tests were performed with a laboratory scale fluidized bed reactor at the Outotec R&D Center in Frankfurt. Additional test work such as particle size analysis and differential thermal analysis were also carried out. Some calcined samples were also characterized with X-ray diffraction at the University of Auckland to obtain a reaction pathway when using pressurized conditions. All of the results are then compared with previous results.

Filmes de titânio-silício preparados por "spin" e "dip-coating"

The conditions for the preparation of luminescent materials, consisting of Eu3+ ions entrapped in a titanium matrix, in the forma of a thin film, using the sol-gel process, are described. The films were obtained from sols prepared with TEOS and TEOT, in the presence of acetylacetone as the hidrolysis-retarding agent, using the dip-coating and spin-coating techniques. The influence of these techniques on the films based on titanium and silicon are presented. The Eu3+ was used as a luminescent probe. The films have been characterized by luminescence, reflection and transmittance. The thickness of the films could be related to the preparation procedure. Transparent thin films have been prepared by dip-coating technique.

Comparative effects of macro-sized aluminum oxide and aluminum oxide nanoparticles on erythrocyte hemolysis: influence of cell source, temperature and size

Al2O3 is the most abundantly produced nanomaterial and has been used in diverse fields, including the medical, military and industrial sectors. As there are concerns about the health effects of nanoparticles, it is important to understand how they interact with cells, and specifically with red blood cells. The hemolysis induced by three commercial nano-sized aluminum oxide particles (nanopowder 13 nm, nanopowder <50 nm and nanowire 2-6 nm × 200-400 nm) was compared to aluminum oxide and has been studied on erythrocytes from humans, rats and rabbits, in order to elucidate the mechanism of action and the influence of size and shape on hemolytic behavior. The concentrations inducing 50% hemolysis (HC50) were calculated for each compound studied. The most hemolytic aluminum oxide particles were of nanopowder 13, followed by nanowire and nanopowder 50. The addition of albumin to PBS induced a protective effect on hemolysis in all the nano-forms of Al2O3, but not on Al2O3. The drop in HC50 correlated to a decrease in nanomaterial size, which was induced by a reduction of aggregation Aluminum oxide nanoparticles are less hemolytic than other oxide nanoparticles, and behave differently depending on the size and shape of the nanoparticles. The hemolytic behavior of aluminum oxide nanoparticles differs from that of aluminum oxide.

Um procedimento simples e barato para a construção de um equipamento "dip-coating" para deposição de filmes em laboratório

In this work we show how to build a piece of equipment for depositing thin films by the dip-coating process, using inexpensive components easily found on the market. This equipment allows us to control the dipping and pulling velocity at which the substrate is put in the film precursor solution, two very important parameters for obtain thin films. This article discusses the construction of the mechanical and electric parts of the equipment, a simple method to interface it to a computer and the development of the software to control the dip-coating parameters.

Comparative effects of macro-sized aluminum oxide and aluminum oxide nanoparticles on erythrocyte hemolysis: influence of cell source, temperature and size

Al2O3 is the most abundantly produced nanomaterial and has been used in diverse fields, including the medical, military and industrial sectors. As there are concerns about the health effects of nanoparticles, it is important to understand how they interact with cells, and specifically with red blood cells. The hemolysis induced by three commercial nano-sized aluminum oxide particles (nanopowder 13 nm, nanopowder <50 nm and nanowire 2-6 nm × 200-400 nm) was compared to aluminum oxide and has been studied on erythrocytes from humans, rats and rabbits, in order to elucidate the mechanism of action and the influence of size and shape on hemolytic behavior. The concentrations inducing 50% hemolysis (HC50) were calculated for each compound studied. The most hemolytic aluminum oxide particles were of nanopowder 13, followed by nanowire and nanopowder 50. The addition of albumin to PBS induced a protective effect on hemolysis in all the nano-forms of Al2O3, but not on Al2O3. The drop in HC50 correlated to a decrease in nanomaterial size, which was induced by a reduction of aggregation Aluminum oxide nanoparticles are less hemolytic than other oxide nanoparticles, and behave differently depending on the size and shape of the nanoparticles. The hemolytic behavior of aluminum oxide nanoparticles differs from that of aluminum oxide.

Síntese hidrotermal de sodalita básica a partir de um rejeito de caulim termicamente ativado

Basic sodalite was successfully synthesized by hydrothermal method using kaolin waste as source of Aluminum and Silicon. This waste is mainly composed by kaolinite and is produced in large amount by kaolin processing industries for paper coating from the Amazon region. Initially, the waste has been calcined at 700 ºC for 2 h and then reacted with the following solutions: Na2CO3 and mixture of Na2CO3 + NaOH to 150 ºC with autogenous pressure for 24 h. The raw materials and transformed materials were characterized by XRD, FTIR and SEM. In both studied media, well-crystallized, basic sodalite was the only phase synthesized, while in the literature usually a mixture of zeolites is obtained.